Boundary effect of relief structure on crystallization of diblock copolymer in thin films

In this Letter, crystal growth of a symmetric crystalline-amorphous diblock copolymer, poly(styrene-b-epsilon-caprolactone) (PS-b-PCL), in thin films was investigated by atomic force microscopy (AFM), Relief structures of holes and islands were formed during annealing the film at the molten state, and the in situ observation of subsequent crystal growth at room temperature indicated that the crystals were preferred to occur at the edge of holes or islands and grew into the interior area. It was concluded that the stretched PCL blocks at the edge of relief structures, caused by material transportation or deformation of the interface, could act as nucleation agents during polymer crystallization. The crystal growth rate of individual lamellae varied both from lamellae to lamellae and in time, but the area occupied by crystals increased constantly with time. At 22 degreesC, the growth rate was 1.2 x 10(-2) mum(2)/min with the scan size 2 x 2 mum(2).

Crystallization of weakly segregated poly(styrene-b-epsilon-caprolactone) diblock copolymer in thin films

The surface morphology and crystallization behavior of a weakly segregated symmetric diblock copolymer, poly(styrene-b-6-caprolactone) (PS-b-PCL), in thin films were investigated by optical microscopy, X-ray photoelectron spectroscopy, and atomic force microscopy (AFM). When the samples were annealed in the molten state, surface-induced ordering, that is, relief structures with uniform thickness or droplets in the adsorbed monolayer, were observed depending on the annealing temperature. The polar PCL block preferred to wet the surface of a silicon wafer, while the PS block wet the air interface. This asymmetric wetting behavior led to the adsorbed monolayer with a PCL block layer having a thickness of around 4.0 nm. The crystallization of PCL blocks could overwhelm the microphase-separated structure because of the weak segregation. In situ observation of crystal growth indicated that the nucleation process preferred to occur at the edge of the thick parts of the film, that is, the relief structures or droplets. The crystal growth rate was presented by the time dependence of the distance between the tip of crystal clusters and the edge. At 22 and 17 degreesC, the average crystal growth rates were 55 +/- 10 and 18 +/- 4 nm/min, respectively.

Melting behaviors, isothermal and non-isothermal crystallization kinetics of nylon 1212

Isothermal crystallization, subsequent melting behavior and non-isothermal crystallization of nylon 1212 samples have been investigated in the temperature range of 160-171 degreesC using a differential scanning calorimeter (DSC). Subsequent DSC scans of isothermally crystallized samples exhibited three melting endotherms. The commonly used Avrami equation and that modified by Jeziorny were used, respectively, to fit the primary stage of isothermal and non-isothermal crystallizations of nylon 1212. The Avrami exponent n was evaluated, and was found to be in the range of 1.56-2.03 for isothermal crystallization, and of 2.38-3.05 for non-isothermal crystallization. The activation energies (DeltaE) were determined to be 284.5 KJ/mol and 102.63 KJ/mol, respectively, for the isothermal and non-isothermal crystallization processes by the Arrhenius' and the Kissinger's methods.

Crystallization and melting behaviors of PPC-BS/PVA blends

The isothermal crystallization and melting behaviors of poly(propylene carbonate) end-capped with benzenesulfonyl/poly (vinyl alcohol) (PPC-BS/PVA) blends over rich PVA composition range were first investigated by differential scanning calorimetry (DSC). PPS-BS/PVA interaction parameter, chi(12), calculated from equilibrium melting temperature depression was -0.44, revealing miscibility of PPC-BS with PVA in the melt and favorable interactions. The temperature dependence of crystallization rate constant at initial crystallization stage was analyzed using the modified Lauritzen-Hoffman expression. The chain width, a(0), the thickness of a monomolecular layer, b(0), the fold and lateral surface-free energies, sigma(e) and sigma, and the work of chain folding, q, for neat PVA were first reckoned to be 4.50 Angstrom, 4.78 Angstrom, 76.0 erg.cm(-2), and 4.70 kcal.mol(-1), respectively. The values of sigma(e) and q for PVA in PPC-BS/PVA blends exhibited a maximum in the neighborhood of 10/90 PPC-BS/PV, respectively.

Isothermal crystallization of poly(3-hydroxybutyrate-co-3-hydroxyvalerate)

Isothermal crystallization behavior of poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) was investigated by means of differential scanning calorimetry and polarized optical microscopy (POM). The Avrami analysis can be used successfully to describe the isothermal crystallization kinetics of PHBV, which indicates that the Avrami exponent n = 3 is good for all the temperatures investigated. The spherulitic growth rate, G, was determined by POM. The result shows that the G has a maximum value at about 353 K. Using the equilibrium melting temperature (448 K) determined by the Flory equation for melting point depression together with U-* = 1500 cal mol(-1), T-infinity = 30 K and T-g = 278 K, the nucleation parameter K-g was determined, which was found to be 3.14+/-0.07 x 10(5) (K-2), lower than that for pure PHB. The surface-free energy sigma = 2.55 x 10(-2) J m(-2) and sigma(e) = 2.70+/-0.06 x 10-2 J m(-2) were estimated and the work of chain-folding (q = 12.5+/-0.2 kJ mol(-1)) was derived from sigma(e), and found to be lower than that for PHB. This implies that the chains of PHBV are more flexible than that of PHB.

Miscibility and crystallization behavior of poly(3-hydroxyvalerate-co-3-hydroxyvalerate)/poly(propylene carbonate) blends

Blends of synthetic poly(propylene carbonate) (PPC) with a natural bacterial copolymer of 3-hydroxybutyrate with 3-hydroxyvalerate (PHBV) containing 8 mol % 3-hydroxyvalerate units were prepared with a simple casting procedure. PPC was thermally stabilized by end-capping before use. The miscibility, morphology, and crystallization behavior of the blends were investigated by differential scanning calorimetry, polarized optical microscopy, wide-angle X-ray diffraction (WAXD), and small-angle Xray scattering (SAXS). PHBV/PPC blends showed weak miscibility in the melt, but the miscibility was very low. The effect of PPC on the crystallization of PHBV was evident. The addition of PPC decreased the rate of spherulite growth of PHBV, and with increasing PPC content in the PHBV/PPC blends, the PHBV spherulites became more and more open. However, the crystalline structure of PHBV did not change with increasing PPC in the PHBV/PPC blends, as shown from WAXD analysis. The long period obtained from SAXS showed a small increase with the addition of PPC.

Multiple melting behavior of isotactic polypropylene and poly(propylene-co-ethylene) after stepwise isothermal crystallization

The multiple melting behavior of several commercial resins of isotactic polypropylene (iPP) and random copolymer, poly(propylene-co-ethylene) (PPE), after stepwise isothermal crystallization (SIC) were studied by differential scanning calorimeter and wide-angle X-ray diffraction (WAXD). For iPP samples, three typical melting endotherms appeared after SIC process when heating rate was lower than 10 degreesC/min. The WAXD experiments proved that only alpha-form crystal was formed during SIC process and no transition from alpha1- to alpha2-form occurred during heating process. Heating rate dependence for each endotherm was discussed and it was concluded that there were only,two major crystals with different thermal stability. For the PPE sample, more melting endotherms appeared after stepwise isothermal crystallization. The introduction of ethylene comonomer in isotactic propylene backbone further decreased the regularity of molecular chain, and the short isotactic propylene sequences could crystallize into gamma-form crystal having a low melting temperature whereas the long sequences crystallized into alpha-form crystal having high melting temperature.

Direct formation of form I poly(1-butene) single crystals from melt crystallization in ultrathin films

The morphologies and crystalline structures of melt-crystallized ultrathin isotactic poly(1-butene) films have been studied with transmission electron microscopy and electron diffraction. It is demonstrated that a bypass of form II crystallization can be achieved with an increase in its crystallization temperature. Electron microscopy observations show that melt-grown isotactic poly(1-butene) single crystals have a well-shaped hexagonal form, whereas form I crystals converted from form II display the morphologies of their tetragonal precursors. Electron diffraction results indicate that, instead of the twinned hexagonal pattern of the converted form I crystal, the directly formed form I single crystals exhibit an untwinned hexagonal pattern.

Effect of nucleating agents on the crystallization of poly(3-hydroxybutyrate-co-3-hydroxyvalerate)

The effect of nucleating agents on the crystallization behavior of poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) was studied. A differential scanning calorimeter was used to monitor the energy of the crystallization process from the melt and melting behavior. During the crystallization process from the melt, nucleating agent led to an increase in crystallization temperature (T-c) of PHBV compared with that for plain PHBV (without nucleating agent). The melting temperature of PHBV changed little with addition of nucleating agent. However, the areas of two melting peaks changed considerably with added nucleating agent. During isothermal crystallization, dependence of the relative degree of crystallization on time was described by the Avrami equation. The addition of nucleating agent caused an increase in the overall crystallization rate of PHBV, but did not influence the mechanism of nucleation and growth of the PHB crystals. The equilibrium melting temperature of PHBV was determined as 187degreesC. Analysis of kinetic data according to nucleation theories showed that the increase in crystallization rate of PHBV in the composite is due to the decrease in surface energy of the extremity surface.

Effect of PMR-POI on the melt behavior and isothermal crystallization of poly(phenylene sulfide)

The crystallization behavior of neat PPS and PPS in blends with PMR-POI prepared by melt mixing were investigated by differential scanning calorimetry (DSC). It was found that POI was an effective nucleation agent of the crystallization for PPS. The enthalpy of crystallization of PPS in the blends increased compared with that of neat PPS. During isothermal crystallization from melt, the dependence of relative degree of crystallinity on time was described by the Avrami equation. It has been shown that the addition of POI causes an increase in the overall crystallization rate of PPS; it also changed the mechanism of nucleation of the PHB crystals from homogeneous nucleation to heterogeneous nucleation. The equilibrium melting temperature of PPS and PPS/POI blends were determined. The analysis of kinetic data according to nucleation theories shows that the increase in crystallization rate of PPS in the composite is due to the decrease in surface energy of the extremity surface.

The influence of nucleating agent on crystallization behavior and properties of polypropylene and its copolymer with ethylene

The influences of nucleating agent EDBS on crystallization behavior and properties of polypropylene UP) and its copolymer with a small amount (4. 48 %, molar fraction) of ethylene (CPP) were studied. DSC results indicated that the crystallization temperature of iPP and CPP samples with 0.5 % (mass fraction) EDBS obviously increased and the degree of crystallinity of these samples became higher. In addition, adding small amount of EDBS enhanced the crystallization of the low isotacticity and low molecular weight segments of the CPP. PLM results showed that their spherulite size decreased markedly, and as a result, the transmittance and haze of the films were all improved.

Isothermal and nonisothermal crystallization kinetics of nylon-46

Isothermal and nonisothermal crystallization kinetics of nylon-46 were investigated with differential scanning calorimetry. The equilibrium melting enthalpy and the equilibrium melting temperature of nylon-46 were determined to be 155.58 J/g and 307.10 degreesC, respectively. The isothermal crystallization process was described by the Avrami equation. The lateral surface free energy and the end surface free energy of nylon-46 were calculated to be 8.28 and 138.54 erg/cm(2), respectively. The work of chain folding was determined to be 7.12 kcal/mol. The activation energies were determined to be 568.25 and 337.80 kJ/mol for isothermal and nonisothermal crystallization, respectively. A convenient method was applied to describe the nonisothermal crystallization kinetics of nylon-46 by a combination of the Avrami and Ozawa equations.

Non-isothermal crystallization behavior and kinetics of metallocene short chain branched polyethylene

The non-isothermal crystallization behavior and kinetics of metallocene short chain branched polyethylene were investigated via DSC at cooling rates from 2.5 to 20 degreesC/min, and subsequent heating at rate of 10 degreesC/min. To verify the effect of molecular weight and branching content on crystallization, three group samples were chosen: (1) linear polyethylene with low molecular weight and high molecular weight; (2) low molecular weight polyethylene with low branching content and high branching content; (3) high molecular weight polyethylene with low branching content and high branching content. The results show that crystallization temperature, crystallinity, melting temperature and crystallization rate are highly branching content-dependent. Molecular weight effect is less important, compared to branching content. A dramatic decrease of crystallization temperature, crystallinity, crystallization rate and melting temperature was observed for branched samples. The non-isothermal kinetics was analyzed via the methods, developed by Gupta and Mo Zhi-shen, and good agreement was obtained.

Nonisothermal crystallization and melting behavior of poly(3-hydroxybutyrate) and maleated poly(3-hydroxybutyrate)

Nonisothermal crystallization and melting behavior of poly(3-hydroxybutyrate) (PHB) and maleated PHB were investigated by differential scanning calorimetry using various cooling rates. The results show that the crystallization behavior of maleated PHB from the melt greatly depends on cooling rates and its degree of grafting. With the increase in cooling rate, the crystallization process for PHB and maleated PHB begins at lower temperature. For maleated PHB, the introduction of maleic anhydride group hinders its crystallization, causing crystallization and nucleation rates to decrease, and crystallite size distribution becomes wider. The Avrami analysis, modified by Jeziorny, was used to describe the nonisothermal crystallization of PHB and maleated PHB. Double melting peaks for maleated PHB were observed, which was caused by recrystallization during the heating process.