928 resultados para Mesoporous Zeolite
Resumo:
The secondary pores in the nanosized HZSM-5 zeolite have been observed for the first time via Xe-129 NMR spectroscopy using xenon as a probe; the location of non-framework Al can also be identified.
Resumo:
Framework titanium in Ti-silicalite-1 (TS-1) zeolite was selectively identified by its resonance Raman bands using ultraviolet (W) Raman spectroscopy. Raman spectra of the TS-1 and silicalite-1 zeolites were obtained and compared using continuous wave laser lines at 244, 325, and 488 nm as the excitation sources. It was only with the excitation at 244 nm that resonance enhanced Raman bands at 490, 530, and 1125 cm(-1) appeared exclusively for the TS-1 zeolite. Furthermore, these bands increased in intensity with the crystallization time of the TS-1 zeolite. The Raman bands at 490, 530, and 1125 cm(-1) are identified as the framework titanium species because they only appeared when the laser excites the charge-transfer transition of the framework titanium species in the TS-1. No resonance Raman enhancement was detected for the bands of silicalite-1 zeolite and for the band at 960 cm(-1) of TS-1 with any of the excitation sources ranging from the visible tb UV regions. This approach can be applicable for the identification of other transition metal ions substituted in the framework of a zeolite or any other molecular sieve.
Resumo:
A series of aluminosilicate zeolites are characterized by UV Raman spectroscopy for the first time, and UV Raman spectra of various zeolites give strong and clear bands with high resolution, while conventional Raman spectra of these zeolites are difficult to obtain because of a strong background fluorescence. Additionally, these zeolites show several new bands in UV Raman spectroscopy. A summary of these UV Raman spectra over various zeolites suggests that the bands at 470-530, 370-430, 290-410, and 220-280 cm(-1) can be assigned to the bending modes of 4-, 5-, 6-, and 8-membered rings of aluminosilicate zeolites, respectively. Furthermore, it is found that the band intensity of zeolites in UV Raman spectroscopy is dependent on the Si/Al ratio. Moreover, the UV Raman spectra of crystallization, for zeolite X at various times show that, in the initial stage of crystallization, the 4-membered rings (510 cm(-1)) interconnect each other to form beta -cages with 6-membered rings (390 cm(-1)), which further crystallize to zeolite X. (C) 2001 Elsevier Science B.V. All rights reserved.
Resumo:
A novel sol-gel process for preparing oxides and mixed oxides sols from precipitation and peptization process is reported in this article. Inorganic salts are used as raw materials in this study. It is found that the amount of acid has great influence on the stability and particle diameter distribution of the precursor sols. Ultrasonic treatment is used to prepare alumina sol at room temperature. The result of Al-27 NMR shows that there exist Al-13(7+) species in the sol. By controlling the sol particles with narrow particle diameter distribution, alumina, titania and silica-alumina (SA) materials with narrow mesoporous distribution are formed by regular packing of sol particles during gelation without using any templates. The results also show that the structure and particle diameter distribution of precursor sol determine the final materials' texture.