Characterization of ceramic powders used in the inCeram systems to fixed dental Prosthesis

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Plasma immersion ion implantation of nitrogen into H13 steel under moderate temperatures

Ion implantation of nitrogen into samples of tempered and quenched H13 steel was carried out by plasma immersion technique. A glow discharge plasma of nitrogen species was the ion source and the negative high voltage pulser provided 10-12 kV, 60 mu s duration and 1.0-2.0 kHz frequency, flat voltage pulses. The temperatures of the samples remained between 300 and 450 degrees C, sustained solely by the ion bombardment. In some of the discharges, we used a N-2 + H-2 gas mixture with 1:1 ratio. PIII treatments as long as 3, 6, 9 and up to 12 h were carried out to achieve as thickest treated layer as possible, and we were able to reach over 20 mu m treated layers, as a result of ion implantation and thermal (and possibly radiation enhanced) diffusion. The nitrogen depth profiles were obtained by GDOS (Glow Discharge Optical Spectroscopy) and the exact composition profiles by AES (Auger Electron Spectroscopy). The hardness of the treated surface was increased by more than 250%, reaching 18.8 GPa. No white layer was seen in this case. A hardness profile was obtained which corroborated a deep hardened layer, confirming the high efficacy of the moderate temperature PIII treatment of steels. (c) 2005 Elsevier B.V. All rights reserved.

Numerical simulation of magnetic-field-enhanced plasma immersion ion implantation in cylindrical geometry

Recent studies have demonstrated that the sheath dynamics in plasma immersion ion implantation (PIII) is significantly affected by an external magnetic field. In this paper, a two-dimensional computer simulation of a magnetic-field-enhanced PHI system is described. Negative bias voltage is applied to a cylindrical target located on the axis of a grounded vacuum chamber filled with uniform molecular nitrogen plasma. A static magnetic field is created by a small coil installed inside the target holder. The vacuum chamber is filled with background nitrogen gas to form a plasma in which collisions of electrons and neutrals are simulated by the Monte Carlo algorithm. It is found that a high-density plasma is formed around the target due to the intense background gas ionization by the magnetized electrons drifting in the crossed E x B fields. The effect of the magnetic field intensity, the target bias, and the gas pressure on the sheath dynamics and implantation current of the PHI system is investigated.

Long-term histopathologic evaluation of inferior vena cava after modified Greenfield filter implantation - Experimental study in sheep

Aim. The authors assess a modified Greenfield filter (GF) for the long-term patency, filter tilting and histopathologic alterations of the inferior vena cava (IVC).Methods. Adult sheep (n=7) underwent modified GF placement in the IVC. Cavograms were obtained every 3 months and pulmonary angiography at 12 months. Histopathologic and scanning electron microscopy (SEM) analyses were performed on the IVC explanted at 12 months.Results. Cavograms showed that all IVC were patent at the end of the study. Filter tilting occurred in 2/7 animals and extrusion of struts was not observed. Macroscopic examination at explantation showed minimal venous wall thickening. Microscopic examination showed minimal IVC fibrosis and intimal hyperplasia. SEM showed endothelium on the IVC surface at the filter implantation site and a presumed endothelial layer covering partially or totally the struts. The interface filter-IVC was covered by deposits of leucocytes and platelets. No signs of pulmonary embolism were found in all pulmonary angiograms of both groups.Conclusion. The modified filter presented good biocompatibility, stability and absence of thrombogenicity at 12 months. It presented low tendency to tilting and extrusion of struts. The long-term histopathologic alterations in vena caval wall were minimal and the appearance of the studied filters in the IVC was similar to stents placed in the arterial system.

Effects of the high-temperature plasma immersion ion-implantation treatment on corrosion behavior of Ti-6Al1-4V

Nitrogen implantation into Ti alloys at higher temperatures improves their mechanical and corrosion resistance properties by forming a thicker nitride layer. In this paper, two different sets of Ti-6Al-4V samples were plasma immersion ion implantation (PIII)-treated using nitrogen plasma, varying the treatment time from 30 to 150 min (800 degrees C) and the process temperature from 400 degrees C to 800 degrees C (t = 60 min). Nanoindentation measurements of the PIII-treated samples at 800 C during 150 min showed the highest hardness value, 24 GPa, which is about four times bigger than untreated sample hardness. The N penetration at these conditions reached approximately 150 nm as analyzed by Auger spectroscopy. on the other hand, the lowest passive current density (3 x 10(-7) A. cm(-2)) was obtained for a PIII-treated sample during 30 min at higher temperature (800 degrees C). The corrosion resistance of this sample is almost the same as for the untreated specimen. Corrosion behavior evidenced that in strong oxidizing media, all PIII-treated samples are more corrosion resistant than the untreated one. PIII processing at higher temperatures promotes smoothing of the sample surface as observed by scanning electron microscopy (SEM). Grazing incidence X-ray diffraction analyses of the untreated samples identified the two typical Ti phases, Ti alpha and Ti beta. After the implantation, Ti2N and TiO2 phases were also detected.

Hydrophilization of PVC surfaces by argon plasma immersion ion implantation

Commercial polyvinylchloride (PVC) sheets were treated by plasma immersion ion implantation, PIII. Samples were immersed in argon glow discharges and biased with 25 kV negative pulses. Exposure time to the bombardment plasma changed from 900 to 10,800 s. Through contact angle measurements, the effect of the exposure time on the PVC wettability was investigated. Independent of t, all samples presented contact angles, theta, equal to zero after the treatment. However, in some cases, surface hydrophilization was not stable, as revealed by the temporal evolution of theta. Samples bombarded for shorter periods recovered partially or totally the hydrophobic character while the one exposed for the longest time stayed highly hydrophilic. These modifications are ascribed to the Cl loss and O incorporation as shown by XPS measurements. Furthermore, the mobility of surface polar groups and the variation in the cross-linking degree can also affect the PVC wettability.

All-on-four concept and immediate loading for simultaneous rehabilitation of the atrophic maxilla and mandible with conventional and zygomatic implants

We report the simultaneous rehabilitation of an edentulous patient with a hybrid (zygomatic and conventional implants) all-on-four implant-supported prosthesis for the maxilla and a standard (conventional implants) all-on-four implant-supported prosthesis for the mandible. The transfer impression was made with a multifunctional guide and the upper and lower prostheses were placed 24 h postoperatively. Clinical and radiographic examinations showed no infection or bony resorption 2 years later. Simultaneous maxillary and mandibular rehabilitation with all-on-four immediate loading is a viable, fast and effective option for edentulous patients. (C) 2009 Published by Elsevier Ltd on behalf of The British Association of Oral and Maxillofacial Surgeons.

Ocular Reconstruction After Zygomatic Complex Fracture With Retention of a Foreign Body

Facial injuries with the retention of foreign bodies inside the tissues, both in soft and hard ones, can cause major functional and aesthetic damage. Among the different etiological agents, cutting tools, fragments of a firearm, the splinter of wood, steel, or iron, launched by misuse, or even caused by defects in equipment, are the main cause of these injuries. The aim of this study was to discuss the peculiarity of the multidisciplinary approach in caring of a 33-year-old man, victim of an accident at work, by the rupture of an emery disc and consequent penetration of the fragments in violation of the tissues in the orbital and zygomatic region of the left side, with perforation of the eyeball and orbital-zygomatic fracture. Urgent treatment consisted of debridement of wounds, bleeding control, removal of foreign bodies, fracture reduction with rigid internal fixation, and suture, performed by the oral and maxillofacial surgical team. Reconstruction of orbital tissues by the ophthalmology team consisted of suture of the injuries. About 1 month after the trauma, phthisis bulbi was noted, and the patient underwent a new procedure under general anesthesia for eye evisceration and installation of an alloplastic prosthesis associated with the homogenous sclera. Facial harmony was restored, especially in aesthetics and function of the zygomatic-orbital complex.