Performance improvement in direct methanol fuel cell cathode using high mesoporous area catalyst support

Black Pearls 2000 (designated as BP- 2000) and Vulcan XC-72 (designated as XC-72) carbon blacks were chosen as supports to prepare 40 wt % (the targeted value) Pt/C catalysts by a modified polyol process. The carbon blacks were characterized by N-2 adsorption and Fourier tranform infrared spectroscopy. The prepared catalysts were characterized by inductively coupled plasma atomic emission spectroscopy, transmission electron microscopy, scanning electron microscopy (SEM), in situ cyclic voltammetry, and current-voltage curves. On BP- 2000, Pt nanoparticles were larger in size and more unevenly distributed than on XC-72. It was observed by SEM that the corresponding catalyst layer on BP- 2000 was thicker than that of XC-72 based catalyst at almost the identical catalyst loading. And the BP- 2000 supported catalyst gave a better single cell performance at high current densities. These results suggest that the performance improvement is due to the enhanced oxygen diffusion and water removal capability when BP- 2000 is used as cathode catalyst support. (C) 2004 The Electrochemical Society.

Formation of a novel type of reverse microemulsion system and its application in synthesis of the nanostructured La0.95Ba0.05MnAl11O19 catalyst

In the study, a novel microemulsion system, consisting of water, iso-propanol and n-butanol, was developed to synthesize the nanostructured La0.95Ba0.05MnAl11O19 catalyst with high surface area and catalytic activity for methane combustion.

The role of coke in the deactivation of Mo/MCM-22 catalyst for methane dehydroaromatization with CO2

The effect of space velocity on reaction performance and coke deposition over 6Mo/MCM-22 catalyst in methane dehydro-aromatization (MDA) with CO2 were studied. The characterization of catalysts reacted at different space velocity after the same amount of methane feed by TG, TPO and Benzene/NH3-TPD techniques suggested that the inert coke maybe responsible for the deactivation of catalyst because of its blockage effect for pore system.

Promotional effect of colloidal alumina on the activity of the In/HZSM-5 catalyst for the selective reduction of NO with methane

Colloidal alumina was used to improve the activity of an In/HZSM-5 catalyst for the selective reduction of NO with CH4 in the excess of oxygen. Compared with In/HZSM-5, the In/HZSM-5/Al2O3 catalyst showed higher activity in a wide range of reaction temperatures. It is visualized that a synergetic effect between In/HZSM-5 and Al2O3 enhances the conversion of NOx. The addition of Al2O3 improved the conversion of NO to NO2 and facilitated the activation of methane. An In/HZSM-5/Al2O3 pre-treated with steam for 15 h at 700 degreesC still showed a high activity for the removal of NOx with methane, while an In/HZSM-5 similarly pre-treated with steam showed a lower activity than the fresh sample. The activity of the In/HZSM-5/Al2O3 catalyst could be restored completely after water vapor was removed from the feed gas. Furthermore, it was found that the In/HZSM-5/Al2O3 remained fairly active under high GHSV and O-2 concentration conditions. It was also interesting to find that an increase in NO content could enhance the conversion of methane, and this illustrates that the existence of NO is beneficial for the activation of methane. (C) 2002 Elsevier Science B.V. All rights reserved.

Unique properties of Ir/ZSM-5 catalyst for NO reduction with CO in the presence of excess oxygen

The reduction of NO with CO in the presence of excess oxygen was investigated over different noble metal catalysts for probing the relationship between catalytic properties and adsorption behaviors. Among the four precious metal catalysts investigated, Ir/ZSM-5 was found to be the only active one for NO reduction with CO under lean conditions. With the decreasing of the Ir content, higher NO conversion and CO selectivity was obtained. Temperature-programmed reaction (TPR) studies of NO/H-2/O-2 and NO/CO/O-2 showed that the Pt/ZSM-5 was active when H-2 was used as the reductant, whereas, the Ir/ZSM-5 was active when CO was the reducing agent. This difference is due to the different mechanisms of the two reactions. Temperature-programmed desorption (TPD) of NO, CO and O-2 showed that NO could dissociate more easily over the Ir/ZSM-5 than on the Pt/ZSM-5, while the oxidation of CO by O-2 proceeded more rapidly on the Pt/ZSM-5 than on the Ir/ZSM-5. The presence of excess O-2 inhibited drastically the dissociation of NO, which is considered as the key step for the NO-CO reaction. The high dissociation rate of NO over the Ir/ZSM-5 is visualized as the key factor for its superior high activity in NO reduction with CO under lean conditions. (C) 2002 Elsevier Science B.V. All rights reserved.

Influence of composition of heteropolyphosphatotungstate catalyst on epoxidation of propylene

A series of heteropolyphosphatotungstate catalysts with different W/P ratio were prepared by different means. P-31 MAS NMR spectra show every heteropolyphosphatotungstate contains several species with different W/P ratio. Combined with propylene epoxidation results, it is shown that the band at chemical shift ca. delta = 5 ppm maybe corresponds to a catalyst precursor which can be the most efficiently converted to the structure {PO4 [WO(O-2)(2)](4)}(3-). Characterization results of ICP show, the catalysts with low W/P ratio show a good reactivity for propylene epoxidation. (C) 2004 Elsevier B.V. All rights reserved.

A new quaternary ammonium heteropolyoxotungstate catalyst for propylene epoxidation to propylene oxide

A new quaternary ammonium heteropolyoxotungstant (cat.C) is prepared and characterized. And the cat.C also is an reaction-controlled phase-transfer catalyst. The catalytic system of O-2/EAHQ (2-ethylanthrahydroquinone)/cat.c is used for the epoxidation of propylene. Under the optimal conditions, the yield of propylene oxide based on EAHQ is 84.1%, the selectivity for propylene oxide based on propylene is 99.8% and the conversion of propylene based on EAHQ is 84.3%. The cat.c precipitates after the epoxidation reaction for easy separation. The cat. C is stable enough to be recycled three times without any loss in selectivity.