Extended Stoney'S Formula For A Film-Substrate Bilayer With The Effect Of Interfacial Slip

The curvature-stress relation is studied for a film-substrate bilayer with the effect of interfacial slip and compared with that of an ideal interface without interfacial slip. The interfacial slip together with the dimensions, elastic and interfacial properties of the film and substrate layers can cause a significant deviation of curvature-stress relation from that with an ideal interface. The interfacial slip also results in the so-called free edge effect that the stress, constraint force, and curvature vary dramatically around the free edges. The constant curvature as predicted by Stoney's formula and the Timoshenko model of an ideal interface is no longer valid for a bilayer with a nonideal interface. The models with the assumption of an ideal interface can also lead to an erroneous evaluation on the true stress state inside a bilayer with a nonideal interface. The extended Stoney's formula incorporating the effects of both the layer dimensions and interfacial slip is presented.

Effect Of Load Triaxiality On Polymorphic Transitions In Zinc Oxide

Molecular dynamics (MD) simulations and first-principles calculations are carried out to analyze the stability of both newly discovered and previously known phases of ZnO under loading of various triaxialities. The analysis focuses on a graphite-like phase (FIX) and a body-centered-tetragonal phase (BCT-4) that were observed recently in [0 1 (1) over bar 0]- and [0 0 0 1]-oriented nanowires respectively under uniaxial tensile loading as well as the natural state of wurtzite (WZ) and the rocksalt (RS) phase which exists under hydrostatic pressure loading. Equilibrium critical stresses for the transformations are obtained. The WZ -> HX transformation is found to be energetically favorable above a critical tensile stress of 10 GPa in [0 1 (1) over tilde 0] nanowires. The BCT-4 phase can be stabilized at tensile stresses above 7 GPa in [0 0 0 1] nanowires. The RS phase is stable at hydrostatic pressures above 8.2 GPa. The identification and characterization of these phase transformations reveal a more extensive polymorphism of ZnO than previously known. A crystalline structure-load triaxiality map is developed to summarize the new understanding. (c) 2007 Elsevier Ltd. All rights reserved.

Asymptotic analysis of plane-strain mode I steady-state crack growth in transformation toughening ceramics (II)

Based on a constitutive law which includes the shear components of transformation plasticity, the asymptotic solutions to near-tip fields of plane-strain mode I steadity propagating cracks in transformed ceramics are obtained for the case of linear isotropic hardening. The stress singularity, the distributions of stresses and velocities at the crack tip are determined for various material parameters. The factors influencing the near-tip fields are discussed in detail.

Effect of phase-transformation on mechanical-behavior of dual-phase steel plate

The mechanical behavior of dual phase steel plates is affected by internal stresses created during martensite transformation. Analytical modelling of this effect is made by considering a unit cell made of martensite inclusion in a ferrite matrix. A large strain finite element analysis is then performed to obtain the plane stress deformation state. Displayed numerically are the development of the plastic zone and distribution of local state of stress and strain. Studied also are the shape configuration of the martensite (hard-phase) that influences the interfacial condition as related to stress transmission and damage. Internal stresses are found to enhance the global flow stress after yield initiation in the ferrite matrix. Good agreement is obtained between the analytical results and experimental observations.

The Oxidative State of Chylomicron Remnants Influences Their Modulation of Human Monocyte Activation

8 p.

Effect of Cattail (Typha domingensis) Extracts, Leachates, and Selected Phenolic Compounds on Rates of Oxygen Production by Salvinia (Salvinia minima)

Salvinia (Salvinia minima Willd.) is a water fern found in Florida waters, usually associated with Lemna and other small free-floating species. Due to its buoyancy and mat-forming abilities, it is spread by moving waters. In 1994, salvinia was reported to be present in 247 water bodies in the state (out of 451 surveyed public waters, Schardt 1997). It is a small, rapidly growing species that can become a nuisance due to its explosive growth rates and its ability to shade underwater life (Oliver 1993). Any efforts toward management of salvinia populations must consider that, in reasonable amounts, its presence is desirable since it plays an important role in the overall ecosystem balance. New management alternatives need to be explored besides the conventional herbicide treatments; for example, it has been shown that the growth of S. molesta can be inhibited by extracts of the tropical weed parthenium (Parthenium hysterophorus) and its purified toxin parthenin (Pande 1994, 1996). We believe that cattail, Typha spp. may be a candidate for control of S. minima infestations. Cattail is an aggressive aquatic plant, and has the ability to expand over areas that weren't previously occupied by other species (Gallardo et al. 1998a and references cited there). In South Florida, T. domingensis is a natural component of the Everglades ecosystem, but in many cases it has become the dominant marsh species, outcompeting other native plants. In Florida public waters, this cattail species is the most dominant emergent species of aquatic plants (Schardt 1997). Several factors enable it to accomplish opportunistic expansion, including size, growth habits, adaptability to changes in the surroundings, and the release of compounds that can prevent the growth and development of other species. We have been concerned in the past with the inhibitory effects of the T. domingensis extracts, and the phenolic compounds mentioned before, towards the growth and propagation of S. minima (Gallardo et al. 1998b). This investigation deals with the impact of cattail materials on the rates of oxygen production of salvinia, as determined through a series of Warburg experiments (Martin et al. 1987, Prindle and Martin 1996).

Global Climate Change Impacts in the United States: a state of knowledge report from the U.S. Global Change Research Program

Executive Summary: Observations show that warming of the climate is unequivocal. The global warming observed over the past 50 years is due primarily to human-induced emissions of heat-trapping gases. These emissions come mainly from the burning of fossil fuels (coal, oil, and gas), with important contributions from the clearing of forests, agricultural practices, and other activities. Warming over this century is projected to be considerably greater than over the last century. The global average temperature since 1900 has risen by about 1.5ºF. By 2100, it is projected to rise another 2 to 11.5ºF. The U.S. average temperature has risen by a comparable amount and is very likely to rise more than the global average over this century, with some variation from place to place. Several factors will determine future temperature increases. Increases at the lower end of this range are more likely if global heat-trapping gas emissions are cut substantially. If emissions continue to rise at or near current rates, temperature increases are more likely to be near the upper end of the range. Volcanic eruptions or other natural variations could temporarily counteract some of the human-induced warming, slowing the rise in global temperature, but these effects would only last a few years. Reducing emissions of carbon dioxide would lessen warming over this century and beyond. Sizable early cuts in emissions would significantly reduce the pace and the overall amount of climate change. Earlier cuts in emissions would have a greater effect in reducing climate change than comparable reductions made later. In addition, reducing emissions of some shorter-lived heat-trapping gases, such as methane, and some types of particles, such as soot, would begin to reduce warming within weeks to decades. Climate-related changes have already been observed globally and in the United States. These include increases in air and water temperatures, reduced frost days, increased frequency and intensity of heavy downpours, a rise in sea level, and reduced snow cover, glaciers, permafrost, and sea ice. A longer ice-free period on lakes and rivers, lengthening of the growing season, and increased water vapor in the atmosphere have also been observed. Over the past 30 years, temperatures have risen faster in winter than in any other season, with average winter temperatures in the Midwest and northern Great Plains increasing more than 7ºF. Some of the changes have been faster than previous assessments had suggested. These climate-related changes are expected to continue while new ones develop. Likely future changes for the United States and surrounding coastal waters include more intense hurricanes with related increases in wind, rain, and storm surges (but not necessarily an increase in the number of these storms that make landfall), as well as drier conditions in the Southwest and Caribbean. These changes will affect human health, water supply, agriculture, coastal areas, and many other aspects of society and the natural environment. This report synthesizes information from a wide variety of scientific assessments (see page 7) and recently published research to summarize what is known about the observed and projected consequences of climate change on the United States. It combines analysis of impacts on various sectors such as energy, water, and transportation at the national level with an assessment of key impacts on specific regions of the United States. For example, sea-level rise will increase risks of erosion, storm surge damage, and flooding for coastal communities, especially in the Southeast and parts of Alaska. Reduced snowpack and earlier snow melt will alter the timing and amount of water supplies, posing significant challenges for water resource management in the West. (PDF contains 196 pages)

A preliminary investigation into the effect of different storage methods on the keeping quality of smoked Oreochromis niloticus

The study was carried out to asses the nutritional qualities of smoked O. niloticus and to discover the best methods of storage to minimize spoilage and infestation of smoked fish. Result showed that the protein contents in A and D decreased while the protein contents of b and C increased. The lipid content increased only in A while it decreased in B-C and D. The moisture content generally increased over the period of storage and there was an increase in ash content only in C while it decreased in A, B and D. The samples packed in polythene bag suffered about 35% mould infection and a few were attached by rodents with some fouling. Samples packed in jute bag were in good condition but were slightly attached by insect. All samples packed in carton and basket were still in good state but there were insect attack in those packed in carton

Preparing for and adapting to climate change impacts: Next steps for the Washington state department of National Resources Aquatic Resources Program

In response to a growing body of research on projected climate change impacts to Washington State’s coastal areas, the Washington State Department of Natural Resources’ (DNR) Aquatic Resources Program (the Program) initiated a climate change preparedness effort in 2009 via the development of a Climate Change Adaptation Strategy (the Strategy)i. The Strategy answers the question “What are the next steps that the Program can take to begin preparing for and adapting to climate change impacts in Washington’s coastal areas?” by considering how projected climate change impacts may effect: (1) Washington’s state-owned aquatic landsii, (2) the Program’s management activities, and (3) DNR’s statutorily established guidelines for managing Washington’s state-owned aquatic lands for the benefit of the public. The Program manages Washington’s state-owned aquatic lands according to the guidelines set forth in Revised Code of Washington 79-105-030, which stipulates that DNR must manage state-owned aquatic lands in a manner which provides a balance of the following public benefits: (1) Encouraging direct public uses and access; (2) Fostering water-dependent uses; (3) Ensuring environmental protection; (4) Utilizing renewable resources. (RCW 79-105-030) The law also stipulates that generating revenue in a manner consistent with these four benefits is a public benefit (RCW 79-105-030). Many of the next steps identified in the Strategy build off of recommendations provided by earlier climate change preparation and adaptation efforts in Washington State, most notably those provided by the Preparation and Adaptation Working Group, which were convened by Washington State Executive Order 70-02 in 2007, and those made in the Washington Climate Change Impacts Assessment (Climate Impacts Group, 2009). (PDF contains 4 pages)

I. Rigid body penetration into brittle materials. II. Phase change effect on shock wave propagation

Part I.

We have developed a technique for measuring the depth time history of rigid body penetration into brittle materials (hard rocks and concretes) under a deceleration of ~ 10⁵ g. The technique includes bar-coded projectile, sabot-projectile separation, detection and recording systems. Because the technique can give very dense data on penetration depth time history, penetration velocity can be deduced. Error analysis shows that the technique has a small intrinsic error of ~ 3-4 % in time during penetration, and 0.3 to 0.7 mm in penetration depth. A series of 4140 steel projectile penetration into G-mixture mortar targets have been conducted using the Caltech 40 mm gas/ powder gun in the velocity range of 100 to 500 m/s.

We report, for the first time, the whole depth-time history of rigid body penetration into brittle materials (the G-mixture mortar) under 10⁵ g deceleration. Based on the experimental results, including penetration depth time history, damage of recovered target and projectile materials and theoretical analysis, we find:

1. Target materials are damaged via compacting in the region in front of a projectile and via brittle radial and lateral crack propagation in the region surrounding the penetration path. The results suggest that expected cracks in front of penetrators may be stopped by a comminuted region that is induced by wave propagation. Aggregate erosion on the projectile lateral surface is < 20% of the final penetration depth. This result suggests that the effect of lateral friction on the penetration process can be ignored.

2. Final penetration depth, P_max, is linearly scaled with initial projectile energy per unit cross-section area, e_s , when targets are intact after impact. Based on the experimental data on the mortar targets, the relation is P_max(mm) 1.15e_s (J/mm² ) + 16.39.

3. Estimation of the energy needed to create an unit penetration volume suggests that the average pressure acting on the target material during penetration is ~ 10 to 20 times higher than the unconfined strength of target materials under quasi-static loading, and 3 to 4 times higher than the possible highest pressure due to friction and material strength and its rate dependence. In addition, the experimental data show that the interaction between cracks and the target free surface significantly affects the penetration process.

4. Based on the fact that the penetration duration, t_max, increases slowly with e_s and does not depend on projectile radius approximately, the dependence of t_max on projectile length is suggested to be described by t_max(μs) = 2.08e_s (J/mm² + 349.0 x m/(πR²), in which m is the projectile mass in grams and R is the projectile radius in mm. The prediction from this relation is in reasonable agreement with the experimental data for different projectile lengths.

5. Deduced penetration velocity time histories suggest that whole penetration history is divided into three stages: (1) An initial stage in which the projectile velocity change is small due to very small contact area between the projectile and target materials; (2) A steady penetration stage in which projectile velocity continues to decrease smoothly; (3) A penetration stop stage in which projectile deceleration jumps up when velocities are close to a critical value of ~ 35 m/s.

6. Deduced averaged deceleration, a, in the steady penetration stage for projectiles with same dimensions is found to be a(g) = 192.4v + 1.89 x 10⁴, where v is initial projectile velocity in m/s. The average pressure acting on target materials during penetration is estimated to be very comparable to shock wave pressure.

7. A similarity of penetration process is found to be described by a relation between normalized penetration depth, P/P_max, and normalized penetration time, t/t_max, as P/P_max = f(t/t_max, where f is a function of t/t_max. After f(t/t_max is determined using experimental data for projectiles with 150 mm length, the penetration depth time history for projectiles with 100 mm length predicted by this relation is in good agreement with experimental data. This similarity also predicts that average deceleration increases with decreasing projectile length, that is verified by the experimental data.

8. Based on the penetration process analysis and the present data, a first principle model for rigid body penetration is suggested. The model incorporates the models for contact area between projectile and target materials, friction coefficient, penetration stop criterion, and normal stress on the projectile surface. The most important assumptions used in the model are: (1) The penetration process can be treated as a series of impact events, therefore, pressure normal to projectile surface is estimated using the Hugoniot relation of target material; (2) The necessary condition for penetration is that the pressure acting on target materials is not lower than the Hugoniot elastic limit; (3) The friction force on projectile lateral surface can be ignored due to cavitation during penetration. All the parameters involved in the model are determined based on independent experimental data. The penetration depth time histories predicted from the model are in good agreement with the experimental data.

9. Based on planar impact and previous quasi-static experimental data, the strain rate dependence of the mortar compressive strength is described by σ_f/σ⁰_f = exp(0.0905(log(έ/έ_0) ^1.14, in the strain rate range of 10^-7/s to 10³/s (σ⁰_f and έ are reference compressive strength and strain rate, respectively). The non-dispersive Hugoniot elastic wave in the G-mixture has an amplitude of ~ 0.14 GPa and a velocity of ~ 4.3 km/s.

Part II.

Stress wave profiles in vitreous GeO₂ were measured using piezoresistance gauges in the pressure range of 5 to 18 GPa under planar plate and spherical projectile impact. Experimental data show that the response of vitreous GeO₂ to planar shock loading can be divided into three stages: (1) A ramp elastic precursor has peak amplitude of 4 GPa and peak particle velocity of 333 m/s. Wave velocity decreases from initial longitudinal elastic wave velocity of 3.5 km/s to 2.9 km/s at 4 GPa; (2) A ramp wave with amplitude of 2.11 GPa follows the precursor when peak loading pressure is 8.4 GPa. Wave velocity drops to the value below bulk wave velocity in this stage; (3) A shock wave achieving final shock state forms when peak pressure is > 6 GPa. The Hugoniot relation is D = 0.917 + 1.711u (km/s) using present data and the data of Jackson and Ahrens [1979] when shock wave pressure is between 6 and 40 GPa for ρ₀ = 3.655 gj cm³ . Based on the present data, the phase change from 4-fold to 6-fold coordination of Ge⁺⁴ with O^-2 in vitreous GeO₂ occurs in the pressure range of 4 to 15 ± 1 GPa under planar shock loading. Comparison of the shock loading data for fused SiO₂ to that on vitreous GeO₂ demonstrates that transformation to the rutile structure in both media are similar. The Hugoniots of vitreous GeO₂ and fused SiO₂ are found to coincide approximately if pressure in fused SiO₂ is scaled by the ratio of fused SiO₂to vitreous GeO₂ density. This result, as well as the same structure, provides the basis for considering vitreous Ge0₂ as an analogous material to fused SiO₂ under shock loading. Experimental results from the spherical projectile impact demonstrate: (1) The supported elastic shock in fused SiO₂ decays less rapidly than a linear elastic wave when elastic wave stress amplitude is higher than 4 GPa. The supported elastic shock in vitreous GeO₂ decays faster than a linear elastic wave; (2) In vitreous GeO₂ , unsupported shock waves decays with peak pressure in the phase transition range (4-15 GPa) with propagation distance, x, as α 1/x^-3.35 , close to the prediction of Chen et al. [1998]. Based on a simple analysis on spherical wave propagation, we find that the different decay rates of a spherical elastic wave in fused SiO₂ and vitreous GeO₂ is predictable on the base of the compressibility variation with stress under one-dimensional strain condition in the two materials.

Effect of phases on the dynamic evolution of a Lambda system with spontaneously generated coherence

The dynamic evolution of a A system coupled by two strong coherent fields is investigated by taking spontaneously generated coherence (SGC) into account. By numericaly simulation, it is shown that the relative phase of the two coherent fields affects significantly the time scale to the coherent population trapping state. In addition, an analytical expression to the evolution rate which is consistent with the numerical results is given. (c) 2005 Elsevier B.V. All rights reserved.

Poverty alleviation among fishermen within the floodplains of Kaduna River: implication for introducing commercial fish farming at village level in Doko local government area of Niger State, Nigeria

A diagnostic survey was conducted among the fishermen in six selected villages in Doko Local Government Area of Niger State. One hundred and fifty fishermen were randomly selected and interviewed to find out whether or not they had interest in commercial fish farming aimed at improving their livelihood. The dwindling fish catches in the natural flood plain ponds and Ex-bow Lakes continue to have a serious negative effect on the socio-economic well being of the village communities in question. A break on natural regular annual flooding of the plains had resulted into very low natural fish recruitment. Data analysis using simple descriptive statistics revealed that land tenure system, educational status, inadequate infrastructural facilities, religious taboos, existing fish species among others were found to be favourable indices for commercial fish farming. However, serious conflicts among the fishermen concerning the ownership status of these natural fish ponds are found to be major obstacles to commercial fish farming despite that the traditional ownership of the ponds were vested in the lands of individuals and village communities. Extensive fish farming and small-scale fish farming in the ponds and Ex-bow Lake with improved management practices are considered to be profitable venture. Despite the fact that fish seeds supply and extension effort are still inadequate, the fish farmers have indicated willingness to adopt commercial fish farming in the Ex-bow Lakes and flood plains in order to restore abundant fish production thereby providing for their food security and also increasing the daily income

Neuronal mechanism of state control in Drosophila melanogaster

The changes in internal states, such as fear, hunger and sleep affect behavioral responses in animals. In most of the cases, these state-dependent influences are “pleiotropic”: one state affects multiple sensory modalities and behaviors; “scalable”: the strengths and choices of such modulations differ depending on the imminence of demands; and “persistent”: once the state is switched on the effects last even after the internal demands are off. These prominent features of state-control enable animals to adjust their behavioral responses depending on their internal demands. Here, we studied the neuronal mechanisms of state-controls by investigating energy-deprived state (hunger state) and social-deprived state of fruit flies, Drosophila melanogaster, as prototypic models. To approach these questions, we developed two novel methods: a genetically based method to map sites of neuromodulation in the brain and optogenetic tools in Drosophila.

These methods, and genetic perturbations, reveal that the effect of hunger to alter behavioral sensitivity to gustatory cues is mediate by two distinct neuromodulatory pathways. The neuropeptide F (NPF) – dopamine (DA) pathway increases sugar sensitivity under mild starvation, while the adipokinetic hormone (AKH)- short neuropeptide F (sNPF) pathway decreases bitter sensitivity under severe starvation. These two pathways are recruited under different levels of energy demands without any cross interaction. Effects of both of the pathways are mediated by modulation of the gustatory sensory neurons, which reinforce the concept that sensory neurons constitute an important locus for state-dependent control of behaviors. Our data suggests that multiple independent neuromodulatory pathways are underlying pleiotropic and scalable effects of the hunger state.

In addition, using optogenetic tool, we show that the neural control of male courtship song can be separated into probabilistic/biasing, and deterministic/command-like components. The former, but not the latter, neurons are subject to functional modulation by social experience, supporting the idea that they constitute a locus of state-dependent influence. Interestingly, moreover, brief activation of the former, but not the latter, neurons trigger persistent behavioral response for more than 10 min. Altogether, these findings and new tools described in this dissertation offer new entry points for future researchers to understand the neuronal mechanism of state control.

Proximity effect in Ag-Pb alloys

The superconducting properties and the microstructure of the Ag_100-xPb_x alloys, 1 ≤ x ≤ 5, prepared by rapid quenching from the liquid state with and without subsequent heat treatments, have been studied. The x-ray diffraction measurements show that supersaturated solid solutions of Pb in Ag can be obtained up to 3.2 at.% Pb as compared to less than 0.1 at.% Pb at equilibrium. It was found that by suitable heat treatment it is possible to vary the size and distribution of the Pb precipitates in the Ag matrix and reproducible superconducting properties in the alloy can be observed. The superconducting transition temperature of these samples can be qualitatively explained by the Silvert and Singh's theoretical calculation. The theory developed for the case of layer structure can be extended to three dimensions to explain the critical current versus temperature behavior. The critical current versus field behavior of these alloys can be explained by the modification of the Josephson effect. Combining these results together with the critical magnetic field measurements and the microstructure studies of the alloys, it can be concluded that the three-dimensional proximity effect is the main mechanism for the superconductivity in the Ag-Pb alloys. Based on the Hilsch empirical formula which was based on experimental results obtained on layer structures, the experimental data in this investigation show that the electron-phonon-electron interaction in silver is attractive. The interaction parameter NV obtained is approximately 0.06, which would lead to a value of 10^-5 °K for the superconducting transition temperature of Ag. These values are in agreement with other determinations which were done on vapor-deposited metallic film sandwiches. Hence, the Hilsch empirical relation valid for layer structures is also valid in the three-dimensional case. Because the transition temperature and the critical current can be varied in a wide range by controlling the heat treatments, the Ag-Pb superconductors might have some useful applications.

Effect of absorption on the diffraction efficiency in Fe : LiNbO3 crystal with 90 degrees recording geometry

In this paper the saturated diffraction efficiency has been optimized by considering the effect of the absorption of the recording light on a crossed-beam grating with 90 degrees recording geometry in Fe:LiNbO3 crystals. The dependence of saturated diffraction efficiency on the doping levels with a known oxidation-reduction state, as well as the dependence of saturated diffraction efficiency on oxidation-reduction state with known doping levels, has been investigated. Two competing effects on the saturated diffraction efficiency were discussed, and the intensity profile of the diffracted beam at the output boundary has also been investigated. The results show that the maximal saturated diffraction efficiency can be obtained in crystals with moderate doping levels and modest oxidation state. An experimental verification is performed and the results are consistent with those of the theoretical calculation.