Caracterização mecânica e microestrutural do aço MARAGING 300, soldado a plasma e submetidas a reparos

Pós-graduação em Engenharia Mecânica - FEG

Treatment of polycarbonate by dielectric barrier discharge (DBD) at atmospheric pressure

Generally most plastic materials are intrinsically hydrophobic, low surface energy materials, and thus do not adhere well to other substances. Surface treatment of polymers by discharge plasmas is of great and increasing industrial application because it can uniformly modify the surface of sample without changing the material bulk properties and is environmentally friendly. The plasma processes that can be conducted under ambient pressure and temperature conditions have attracted special attention because of their easy implementation in industrial processing. Present work deals with surface modification of polycarbonate (PC) by a dielectric barrier discharge (DBD) at atmospheric pressure. The treatment was performed in a parallel plate reactor driven by a 60Hz power supply. The DBD plasmas at atmospheric pressure were generated in air and nitrogen. Material characterization was carried out by contact angle measurements, and X-ray photoelectron spectroscopy (XPS). The surface energy of the polymer surface was calculated from contact angle data by Owens-Wendt method using distilled water and diiodomethane as test liquids. The plasma-induced chemical modifications are associated with incorporation of polar oxygen and nitrogen containing groups on the polymer surface. Due to these surface modifications the DBD-treated polymers become more hydrophilic. Aging behavior of the treated samples revealed that the polymer surfaces were prone to hydrophobic recovery although they did not completely recover their original wetting properties.

Supplementary corpora lutea monitoring allows progestin treatment interruption on day 70 of pregnancy in non-cyclic recipient mares

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

The effect of chronic treatment with fluoride on salivary activity, tooth, and bone in spontaneously hypertensive rats (SHR)

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Pharmacokinetics of Hydroxymethylnitrofurazone, a Promising New Prodrug for Chagas' Disease Treatment

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Surface modification of polymeric materials by cold atmospheric plasma jet

In this work we report the surface modification of different engineering polymers, such as, polyethylene terephthalate (PET), polyethylene (PE) and polypropylene (PP) by an atmospheric pressure plasma jet (APPJ). It was operated with Ar gas using 10 kV, 37 kHz, sine wave as an excitation source. The aim of this study is to determine the optimal treatment conditions and also to compare the polymer surface modification induced by plasma jet with the one obtained by another atmospheric pressure plasma source the dielectric barrier discharge (DBD). The samples were exposed to the plasma jet effluent using a scanning procedure, which allowed achieving a uniform surface modification. The wettability assessments of all polymers reveal that the treatment leads to reduction of more than 40 degrees in the water contact angle (WCA). Changes in surface composition and chemical bonding were analyzed by x-ray photoelectron spectroscopy (XPS) and Fourier-Transformed Infrared spectroscopy (FTIR) that both detected incorporation of oxygen-related functional groups. Surface morphology of polymer samples was investigated by Atomic Force Microscopy (AFM) and an increase of polymer roughness after the APPJ treatment was found. The plasma-treated polymers exhibited hydrophobic recovery expressed in reduction of the O-content of the surface upon rinsing with water. This process was caused by the dissolution of low molecular weight oxidized materials (LMWOMs) formed on the surface as a result of the plasma exposure. (C) 2014 Elsevier B.V. All rights reserved.

Amorphous silicon carbonitride films modified by plasma immersion ion implantation

Amorphous silicon carbonitride (a-SiCN:H) films were deposited from hexamethyldisilazane (HMDSN) organic compounds via radio-frequency (RF) glow discharges. Afterwards the films were bombarded, from 15 to 60 min, with nitrogen ions using Plasma Immersion Ion Implantation (PIII) technique. X-ray photoelectron spectroscopy (XPS) showed that O-containing groups increased, while C-C and/or C-H groups decreased with treatment time. This result indicates chemical alterations of the polymeric films with the introduction of polar groups on the surface, which changes the surface wettability. In fact, the hydrophobic nature of a-SiCN:H films (contact angle of 100 degrees) was changed by nitrogen ion implantation and, and after aging in atmosphere air, all samples preserved the hydrophilic character (contact angle <80 degrees) independently of treatment time. The exposure of the films to oxygen plasma was performed to evaluate the etching rate, which dropped from 24% to 6% while the implantation time increased from 15 to 60 min. This data suggests that Pill increased the film structure strength, probably due to crosslinking enhancement of polymeric chains. Therefore, the treatment with nitrogen ions via Pill process was effective to modify the wettability and oxidation resistance of a-SiCN:H films. (C) 2014 Elsevier Ltd. All rights reserved.

Acetylene plasma polymer treated by atmospheric dielectric barrier discharge

Plasma polymer films are very attractive for industrial applications in several sectors such as in the electronic, mechanic, biomedic, coating and others, due to its good adhesion, being insoluble in mild acids and bases and having a high crosslinking structure. This work reports the physical, structural, and surface properties of the polymer obtained from an acetylene plasma polymerization technique and treated by dielectric barrier discharge (DBD). The film was deposited in a reactor supplied by a radio-frequency power source at low pressure. After deposition, the nanofilms were treated in a DBD plasma reactor operating in air. The treatment times varied from 1 to 5 min. The analysis of molecular structure of the samples was investigated by FTIR spectroscopy, showing absorption bands in 3480, 2930, 1720, 1450 and 1380 cm(-1). The water contact-angle was investigated by goniometric technique and presented values from 5 to 65 degrees. The aging effect of these films was also studied. The alteration in the films surface morphology was assessed by an atomic force microscopy (AFM) which indicated that the roughness increased from 60 nm to 160 nm as a result of the DBD treatment. The refractive index of the samples presented values near 1.7, measured by UV-Visible spectroscopy. (C) 2014 Elsevier Ltd. All rights reserved.

Impact of adrenalectomy and dexamethasone treatment on testicular morphology and sperm parameters in rats: insights into the adrenal control of male reproduction

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Treatment of osteochondral injuries with platelet gel

OBJECTIVES: Treatments for injured articular cartilage have not advanced to the point that efficient regeneration is possible. However, there has been an increase in the use of platelet-rich plasma for the treatment of several orthopedic disorders, including chondral injuries. Our hypothesis is that the treatment of chondral injuries with platelet gel results in higher-quality repair tissue after 180 days compared with chondral injuries not treated with gel.METHODS: A controlled experimental laboratory study was performed on 30 male rabbits to evaluate osteochondral injury repair after treatment with or without platelet gel. Osteochondral injuries were surgically induced in both knees of each rabbit at the medial femoral condyle. The left knee injury was filled with the platelet gel, and the right knee was not treated. Microscopic analysis of both knee samples was performed after 180 days using a histological grading scale.RESULTS: The only histological evaluation criterion that was not significantly different between treatments was metachromasia. The group that was treated with platelet gel exhibited superior results in all other criteria (cell morphology, surface regularity, chondral thickness and repair tissue integration) and in the total score.CONCLUSION: The repair tissue was histologically superior after 180 days in the study group treated with platelet gel compared with the group of untreated injuries.

Tratamento da superfície do alumínio via eletrólise a plasma

This paper presents the study on the application of the electrolytic plasma for surface treatment of aluminum. A bibliographical study on the material of interest was preliminarily performed and later designed and built an electrolytic cell, including the excitation source. Unlike conventional electrolysis process, the plasma assisted carry on in the non-linear region of characteristic current/voltage curve. Therefore it requires for the on set of the process that the power supply operates on harder conditions than those on high current process. The plasma produced during the present investigation has temperatures in the range o 6,0.10 3 -7,0 .10 3 K, well above those found in conventional chemical process. It also shows a particular dynamic to promote changes on surface and to produce new materials. The plasma is generated by microdischarge in vapor or gas bubbles involved in physic-chemical processes in electrode regions of the electrolytic cell. The electrode material was the aluminum (7075). The Process Electrolytic Plasma Processing (EPP) is sensitive to various parameters such as operating voltage, current density, electrolyte, concentration of electrolyte, geometry of reactor, temperature of electrolytic solution and dynamic of the fluid in the cell. The experiments were carried on in order to find parameters for a stable abd steady operation. The choice for the electrolytic was silicate/alkali solution in various concentrations to operate in various voltage as well. Plasma was produced on negative (cathode) and positive (anode) electrode, in specific conditions. A stable operation on the cathode process was obtained with low concentration of the electrolytic in aqueous solution, current density around 250V effective voltage. For the evolution of plasma in anodic process it was required higher concentrations and higher... (Complete abstract click electronic access below)

Estudo da superfície de fibras de carbono após tratamento de implantação iônica por imersão em plasma (3IP)

In this work, plasma immersion ion implantation (PIII) treatments of carbon fibers (CFs) were performed in order to induce modifications of chemical and physical properties of the CF surface aimed to improve the performance of thermoplastic composite. The samples to be treated were immersed in nitrogen or air glow discharge plasma and pulsed at −3.0 kV for 2.0, 5.0, 10.0, and 15.0 min. After PIII processing, the specimens were characterized by atomic force microscopy (AFM), scanning electron microscopy, Raman spectroscopy, and X-ray photoelectron spectroscopy (XPS). After CFs treatments, the CF/Polypropylene (PP) composites were produced by hot pressing method. Surface morphology of as-received CFs exhibited some scratches aligned along the fibers due to the fiber manufacturing process. After both treatments, these features became deeper, and also, a number of small particles nonuniformly distributed on the fiber surface can be observed. These particles are product of CF surface sputtering during the PIII treatment, which removes the epoxy layer that covers as-received samples. AFM analyses of CF samples treated with nitrogen depicted a large increase of the surface roughness (Rrms value approximately six times higher than that of the untreated sample). The increase of the roughness was also observed for samples treated by air PIII. Raman spectra of all samples presented the characteristic D- and G-bands at approximately 1355 and 1582 cm−1, respectively. Analysis of the surface chemical composition provided by the XPS showed that nitrogen and oxygen were incorporated onto the surface. The polar radicals formed on the surface lead to increasing of the CF surface energy. Both the modification of surface roughness and the surface oxidation contributed for the enhancement of CF adhesion to the polymeric matrix. These features were confirmed ... (Complete abstract click electronic access below)

Fadiga axial do aço inoxidável 15-5 PH tratado pela implantação iônica por imersão em plasma

When materials for application in aircraft structural components are studied, it must be considered that they will be submitted to cyclic loading, and this is an important parameter to design the study in fatigue life of the materials. Whereas, for example, a landing gear operation, the study of fatigue life and corrosion in the materials used in it is essential, especially when you want to use new techniques for surface treatments. The objective is to study the influence of surface treatment of immersion ion implantation nitrogen plasma, in axial fatigue of Stainless steel 15-5 PH in 39-42 HRC condition. Stainless steel 15-5 PH was tested in axial fatigue and corrosion in salt spray. It was also performed microindentation tests, optical microscopy for microstructural analysis and scanning electron microscopy for fractographic analysis. It was observed that the 3IP had no effect on the thickness of the material and not the hardness of it, and still provided a significant increase in fatigue life of the material

Efeito do recobrimento de filmes de carbono tipo diamante depositados a plasma na manutenção do torque de parafusos protéticos

Pós-graduação em Odontologia Restauradora - ICT

Estudo comparativo da utilização de PRP (Plasma Rico em Plaquetas) autólogo na cicatrização de feridas metacarpianas em equinos: aspectos macroscópicos, histopatológicos, imunoistoquímicos e morfométricos

Pós-graduação em Medicina Veterinária - FMVZ