Preparation of ZnO nanoparticles: Structural study of the molecular precursor

The structure of zinc acetate derived precursor currently used in the sol-gel synthesis of ZnO nanoparticles is described. The reaction products obtained before and after reflux of ethanolic zinc acetate solution have been studied by UV-Vis, photoluminescence, FTIR and EXAFS at the Zn K edge. EXAFS results evidence for both precursor solutions a change from the octahedral coordination sphere of oxygen atoms characteristic of the solid zinc acetate dihydrate compound into a four-fold environment. The EXAFS spectra of precursor solutions can be satisfactorily reproduced using the molecular structure reported for Zn4O(Ac)(6) (Ac = COOCH3). UV-Vis and FTIR measurements are also in agreement with the formation of this oligomeric precursor. The structural modification is more pronounced after reflux at 80degreesC, because the increase of the Zn4O(Ac)(6) amount and the formation of nearly 3.0 nm sized ZnO nanoparticle.

In situ and simultaneous nanostructural and spectroscopic studies of ZnO nanoparticle and Zn-HDS formations from hydrolysis of ethanolic zinc acetate solutions induced by water

The simultaneous formation of nanometer sized zinc oxide (ZnO), and acetate zinc hydroxide double salt (Zn-HDS) is described. These phases, obtained using the sol-gel synthesis route based on zinc acetate salt in alcoholic media, were identified by direct characterization of the reaction products in solution using complementary techniques: nephelometry, in situ Small-Angle X-ray Scattering (SAXS), UV-Vis spectroscopy and Extended X-ray Absorption Fine Structures (EXAFS). In particular, the hydrolytic pathway of ethanolic zinc acetate precursor solutions promoted by addition of water with the molar ratio N = [H2O]/[Zn2+] = 0.05 was investigated in this paper. The aim was to understand the formation mechanism of ZnO colloidal suspension and to reveal the factors responsible for the formation of Zn-HDS in the final precipitates. The growth mechanism of ZnO nanoparticles is based on primary particle (radius approximate to 1.5 nm) rotation inside the primary aggregate (radius < 3.5 nm) giving rise to an epitaxial attachment of particles and then subsequent coalescence. The growth of second ZnO aggregates is not associated with the Otswald ripening, and could be associated with changes in equilibrium between solute species induced by the superficial etching of Zn-HDS particles at the advanced stage of kinetic.

Luminescence properties of Eu(3+)- and Mg(2+)-doped LiTaO(3) obtained via the polymeric precursor method

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Controlled Cisplatin Delivery from Ureasil-PEO1900 Hybrid Matrix

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Theoretical investigation of the electronic structure and absorption spectra of carbon cluster nanotubes

Electronic and optical properties of recently discovered single-shell carbon cluster nanotubes are studied through a semiempirical INDOCI method. The calculations are performed within the cluster model and include up to 196 atoms. The trend of the forbidden band gap with the number of carbon atoms (Cn n = 60, 10, 140) for a fixed diameter is analyzed. With increasing n the band gap decreases, as expected. The tubule, with diameter of 7.2Å (as C60-Buckyball) is predicted to be a metal or a narrow-gap semiconductor. The calculated absorption spectra of the clusters show a characteristic strong peak around 40,000 cm-1. Other features of the calculated UV-visible absorption spectra are discussed. © 1994.

Structural and optical properties of Eu3+ and Mg2+ doped LiTaO3 obtained via the polymeric precursor method

This work reports on the pure lithium tantalate (LiTaO3), europium (III)-doped LiTaO3 and magnesium (II)-europium (III)-doped LiTaO3 preparared by the polymeric precursor method, using four different powered samples of Eu3+ ion concentrations 0.1 to 1at %. Structural and optical properties of powders have been studied. The different possible sites occupied by the rare earth were examined. The phase contents and lattice parameters were studied by the Rietveld method and the structural disorder in the LiTaO3 host caused by Eu3+ ions was analyzed. Results indicated LiTaO3 free of secondary phases at 650°C and the photoluminescence (PL) emission spectra showed the characteristic sharp emission bands given by Eu3+ ions when they are excited at a wavelength of 399 nm. An increase of dopants contents caused a non-homogeneous broadening and showed a slightly larger one when Mg was added. A displacement of the transition 5D0-7F0 to shorter wavelengths as function of Eu3+ concentration was also noticed.

Rietveld analyses and piezoelectric properties of niobium doped bismuth titanate systems

Bi 4Ti 3- xNbxO 12 (BITNb) samples, with × ranging from 0 to 0.40 were obtained using a polymeric precursor solution. Rietveld analyses confirmed that the powders crystallize in an orthorhombic structure free of secondary phases with space group Fmmm. Raman analysis evidenced a sharp increase in the bands intensity located at 129 cm -1 and 190 cm -1 due the lattice distortion in BIT02Nb and BIT04Nb compositions. UV-vis spectra indicated that addition of niobium causes a reduction of defects in the BIT lattice due the suppression of oxygen vacancies located at BO-6 octahedral. Size and morphology of particles as well as electrical behavior of BIT ceramics were affected by addition of donor dopant. Polarization reversal was investigated by applying dc voltage through a conductive tip during the area scanning and was investigated by piezoresponse force microscopy (PFM). PFM measurements revealed a decrease in piezoelectric response with increasing Nb concentration originating from a reduced polarizability along the a-axis. High spontaneous polarization is noted for the less doped sample due the reduction of strain energy and pin charged defects after niobium addition. Copyright © 2010 American Scientific Publishers.

Lanthanum cobaltite black pigments with perovskite structure

In this work La1-xCaxCoO3 (x = 0-0.4) pigments were synthesized by the polymeric precursor method with heat treatments at 700, 800 and 900 C for 4 h. The powders were characterized by colorimetry, UV-vis spectroscopy and powder X-ray diffraction (XRD). The X-ray diffraction patterns showed the presence of a single phase perovskite, changing its structure from rhombohedral to cubic, when calcium was added to the lattice. All of the pigments had a black colour with a strong absorption over the whole of the visible spectrum as a consequence of the different oxidation states of cobalt and the high short-range disorder. The substitution of Ca2+ for La3+ did not influence the pigment colour but decreased its final cost. © 2013 Elsevier Ltd. All rights reserved.

TiO2-Cu photocatalysts: A study on the long- and short-range chemical environment of the dopant

In this study, the short- and long-range chemical environments of Cu dopant in TiO2 photocatalyst have been investigated. The Cu-doped and undoped TiO2 specimens were prepared by the sol-gel approach employing CuSO4·5H2O and Ti(O-iPr)4 precursors and subjecting the dried gels to thermal treatment at 400 and 500 C. The photocatalytic activity, investigated by methylene blue degradation under sunlight irradiation, showed a significantly higher efficiency of Cu-doped samples than that of pure TiO2. The X-ray diffraction results showed the presence of anatase phase for samples prepared at 400 and 500 C. No crystalline CuSO4 phase was detected below 500 C. It was also found that doping decreases the crystallite size in the (004) and (101) directions. Infrared spectroscopy results indicated that the chemical environment of sulfate changes as a function of thermal treatment, and UV-vis spectra showed that the band gap decreases with thermal treatment and Cu doping, showing the lowest value for the 400 C sample. X-ray absorption fine structure measurements and analysis refinements revealed that even after thermal treatment and photocatalytic assays, the Cu2+ local order is similar to that of CuSO4, containing, however, oxygen vacancies. X-ray photoelectron spectroscopy data, limited to the near surface region of the catalyst, evidenced, besides CuSO4, the presence of Cu1+ and CuO phases, indicating the active role of Cu in the TiO2 lattice. © 2013 Springer Science+Business Media New York.

Deposition and photo-induced electrical resistivity of dip-coated NiO thin films from a precipitation process

Thin films of the semiconductor NiO are deposited using a straightforward combination of simple and versatile techniques: the co-precipitation in aqueous media along with the dip- coating process. The obtained material is characterized by gravimetric/differential thermal analysis (TG-DTA) and X-ray diffraction technique. TG curve shows 30 % of total mass loss, whereas DTA indicates the formation of the NiO phase about 578 K (305 C). X-ray diffraction (XRD) data confirms the FCC crystalline phase of NiO, whose crystallinity increases with thermal annealing temperature. UV-Vis optical absorption measurements are carried out for films deposited on quartz substrate in order to avoid the masking of bandgap evaluation by substrate spectra overlapping. The evaluated bandgap is about 3.0 eV. Current-voltage (I-V) curves measured for different temperatures as well as the temperature-dependent resistivity data show typical semiconductor behavior with the resistivity increasing with the decreasing of temperature. The Arrhenius plot reveals a level 233 meV above the conduction band top, which was attributed to Ni2+ vacancy level, responsible for the p-type electrical nature of NiO, even in undoped samples. Light irradiation on the films leads to a remarkable behavior, because above bandgap light induced a resistivity increase, despite the electron-hole generation. This performance was associated with excitation of the Ni 2+ vacancy level, due to the proximity between energy levels. © 2012 Springer Science+Business Media New York.

'Ti''O IND.2'/'Sn''O IND. 2 modificado com 'Ag IND. 2''O', para obtenção de fotocatalisadores

Pós-graduação em Química - IQ

Caracterização dielétrica de partículas nanométricas e nanoestruturadas de óxido de niobato da família tetragonal tungstênio bronze com estequiometria K'Sr IND. 2' N'b IND. 5' 'O IND. 15'

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Estudo da arquitetura molecular de filmes layer-by-layer de ftalocianina tetrasulfonada de cobre

Pós-graduação em Ciência e Tecnologia de Materiais - FC

Síntese, processamento em hidrotermal convencional/microondas e propriedades fotoluminescentes dos pós de BaW 'O IND. 4'

Pós-graduação em Ciência e Tecnologia de Materiais - FC

Ácido fólico: validação do método espectrofotométrico

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)