Continuity of plastic strain rate in stress relaxation tests

Stress relaxation testing is often utilised for determining whether athermal straining contributes to plastic flow; if plastic strain rate is continuous across the transition from tension to relaxation then plastic strain is fully thermally activated. This method was applied to an aged type 316 stainless steel tested in the temperature range 973–1123 K and to a high purity Al in the recrystallised annealed condition tested in the temperature range 274–417 K. The results indicated that plastic strain is thermally activated in these materials at these corresponding test temperatures. For Al, because of its high strain rate sensitivity, it was necessary to adopt a back extrapolation procedure to correct for the finite period that the crosshead requires to decelerate from the constant speed during tension to a dead stop for stress relaxation.

Criteria for prediction of flow instabilities and microstructural manifestations during warm working of AISI 304L stainless steel

The deformation characteristics of 304L stainless steel in compression in the temperature range 20–700°C and strain rate range 0·001–100 s−1 have been studied with the aim of characterising the .flow instabilities occurring in the microstructure. At higher temperatures and strain rates the stainless steel exhibits flow localisation, whereas at temperatures below 500°C and strain rates lower than 0·1 s−1 the flow instabilities are due to dynamic strain aging. Strain induced martensite formation is responsible for the flow instabilities at room temperature and low strain rates (0·01 s−1). In view of the occurrence of these instabilities, cold working is preferable to warm working to achieve dimensional tolerance and reproducible properties in the product. Among the different criteria tested to explain the occurrence of instabilities, the continuum criterion, developed on the basis of the principles of maximum rate of entropy production and separability of the dissipation function, predicts accurately all the above instability features.

Effect of microstructure and hardness on the grinding abrasive wear resistance of a ball bearing steel

Grinding media wear appears to be non-linear with the time of grinding in a laboratory-scale ball mill. The kinetics of wear can be expressed as a power law of the type w=atb, where the numerical constant a represents wear of a particular microstructure at time t = 1 min and b is the wear exponent which is independent of the particle size prevailing inside a ball mill at any instant of time of grinding. The wear exponent appears to be an indicator of the cutting wear mechanism in dry grinding: a plot of the inverse of the normalised wear exponent (Image ) versusHs (where Hs is the worn surface hardness of the media) yields a curve similar to that of a wear resistance plot obtained in the case of two-body sliding abrasive wear. This method of evaluating the cutting wear resistance of media is demonstrated by employing 15 different microstructures of AISI-SAE 52100 steel balls in dry grinding of quartz in a laboratory-scale ball mill.

Influence of cast versus wrought microstructure on the processing map for hot working of stainless steel type AISI 304

Processing maps for hot working of as-cast and wrought stainless steels of type AISI 304 have been developed in the temperature range 600 to 1250°C and strain rate range 0.001 to 100 s−1. The domain of dynamic recrystallization (DRX) in as-cast material occurs at higher temperatures (1250°C) and lower strain rates (0.001 s−1) than in the wrought steel (1100°C and 0.01 s−1). The effect is explained in terms of enhanced nucleation rate of DRX due to the carbide, ferrite particles, stable oxides/nitrides and second-phase intermetallics in the as-cast microstructure. The DRX domain is wider in the wrought material although the peak efficiency is less (32%) than in the as-cast case (40%). The flow instability regime is not significantly affected by the initial microstructure

Influence of state of stress on the processing map for hot working of stainless steel type AISI 304L: compression vs. torsion

Processing maps for hot working of stainless steel of type AISI 304L have been developed on the basis of the flow stress data generated by compression and torsion in the temperature range 600–1200 °C and strain rate range 0.1–100 s−1. The efficiency of power dissipation given by 2m/(m+1) where m is the strain rate sensitivity is plotted as a function of temperature and strain rate to obtain a processing map, which is interpreted on the basis of the Dynamic Materials Model. The maps obtained by compression as well as torsion exhibited a domain of dynamic recrystallization with its peak efficiency occurring at 1200 °C and 0.1 s−1. These are the optimum hot-working parameters which may be obtained by either of the test techniques. The peak efficiency for the dynamic recrystallization is apparently higher (64%) than that obtained in constant-true-strain-rate compression (41%) and the difference in explained on the basis of strain rate variations occurring across the section of solid torsion bar. A region of flow instability has occurred at lower temperatures (below 1000 °C) and higher strain rates (above 1 s−1) and is wider in torsion than in compression. To achieve complete microstructure control in a component, the state of stress will have to be considered.

Method of Analysis if Uniaxial Deformation Data

A comprehensive scheme for analysing uniaxial deformation data, taking into account the finite stiffness of the testing machine is presented. Equations relevant to tension and stress relaxation tests carried out under cross head speed control, and to creep testing under constant load, are described. For the first two cases, the implications of not using gauge length extensometry but relying upon cross head displacement for inferring specimen extension, and the role of uncertainty in machine stiffness are also examined. The final section touches upon the extension of the present scheme to account for specimen anelasticity.

Processing map for hot working of stainless steel type AISI 316L

Processing and instability maps using a dynamic materials model have been developed for stainless steel type AISI 316L in the temperature range 600-1250-degrees-C and strain rate range 0.001-100 s-1 with a view to optimising its hot workability. Stainless steel type AISI 316L undergoes dynamic recrystallisation, with a peak efficiency of 35% at 1250-degrees-C and 0.05 s-1, which are the optimum parameters for hot working this material. The material undergoes dynamic recovery at 900-degrees-C and 0.001 s-1. The increase in the dynamic recrystallisation and dynamic recovery temperatures in comparison with stainless steel type AISI 304L is attributed to the presence of a backstress caused by the molybdenum additions. These results are in general agreement with those reported elsewhere on stainless steel type 316 deformed in hot extrusion and hot torsion. At temperatures < 850-degrees-C and strain rates > 10 s-1, the material exhibits flow localisation owing to adiabatic shear band formation, whereas at higher temperatures (> 850-degrees-C) and strain rates (> 10 s-1) mechanical twinning and wavy slip bands are observed. (C) 1993 The Institute of Materials.

A numerical investigation of ductile fracture initiation in a high-strength low-alloy steel

In this work, static and drop-weight impact experiments, which have been conducted using three-point bend fracture specimens of a high-strength low-alloy steel, are analysed by performing finite-element simulations. The Gurson constitutive model that accounts for the ductile failure mechanisms of microvoid nucleation, growth and is employed within the framework of a finite deformation plasticity theory. Two populations of second-phase particles are considered, including large inclusions which initiate voids at an early stage and small particles which require large strains to nucleate voids. The most important objective of the work is to assess quantitatively the effects of material inertia, strain rate sensitivity and local adiabatic temperature rise (due to conversion of plastic work into heat) on dynamic ductile crack initiation. This is accomplished by comparing the evolution histories of void volume fraction near the notch tip in the static analysis with the dynamic analyses. The results indicate that increased strain hardening caused by strain rate sensitivity, which becomes important under dynamic loading, plays a benign role in considerably slowing down the void growth rate near the notch tip. This is partially opposed by thermal softening caused by adiabatic heating near the notch tip.

Effect of surfactant dispersed in oil on interaction force between an oil film and a steel substrate in water

The oil phase, in an oil-in-water emulsion on a steel substrate, is strongly repelled by the substrate. The oil in this situation does not wet the steel and steel/steel friction is high. In this work we disperse anionic surfactants in an oil film and study the effect of this dispersion on the force of interaction between a silica colloid probe (AFM) carrying the oil film and a steel substrate in water. It is observed that when the surfactant is oil insoluble and the interaction time is short the strong entropic repulsion (without the surfactant) is replaced by a strong attraction. The steel on steel sliding friction in this case is low compared to that what is achieved when the surfactant is soluble in oil. The rationale underlying these interactions is explored here. (C) 2011 Elsevier B.V. All rights reserved.

Industrial validation of processing maps of 316L stainless steel using hot forging, rolling, and extrusion

The development of microstructure in 316L stainless steel during industrial hot forming operations including press forging (strain rate of 0 . 15 s(-1)), rolling/extrusion (strain rate of 2-8 . 8 s(-1)), and hammer forging (strain rate of 100 s(-1)) at different temperatures in the range 600-1200 degrees C was studied with a view to validating the predictions of the processing map. The results showed that good col relation existed between the regimes indicated in the map and the product microstructures. The 316L stainless steel exhibited unstable flow in the form of flow localisation when hammer forged at temperatures above 900 degrees C, rolled below 1000 degrees C, or press forged below 900 degrees C. All these conditions must therefore be avoided in mechanical processing of the material. Conversely, in order to obtain defect free microstructures, ideally the material should be rolled at temperatures above 1100 degrees C, press forged at temperatures above 1000 degrees C, or hammer forged in the temperature range 600-900 degrees C. (C) 1996 The Institute of Materials.