Screening of CO2 Laser (10.6 mu m) Parameters for Prevention of Enamel Erosion

Objective: The aim of this study was to screen CO2 laser (10.6 mu m) parameters to increase enamel resistance to a continuous-flow erosive challenge. Background data: A new clinical CO2 laser providing pulses of hundreds of microseconds, a range known to increase tooth acid-resistance, has been introduced in the market. Methods: Different laser parameters were tested in 12 groups (n = 20) with varying fluences from 0.1 to 0.9 J/cm(2), pulse durations from 80 to 400 mu s and repetition rates from 180 to 700 Hz. Non-lased samples (n = 30) served as controls. All samples were eroded by exposure to hydrochloric acid (pH 2.6) under continuous acid flow (60 mu L/min). Calcium and phosphate release into acid was monitored colorimetrically at 30 sec intervals up to 5 min and at 1 min intervals up to a total erosion time of 15 min. Scanning electron microscopic (SEM) analysis was performed in lased samples (n = 3). Data were statistically analysed by one-way ANOVA (p < 0.05) and Dunnett's post-hoc tests. Results: Calcium and phosphate release were significantly reduced by a maximum of 20% over time in samples irradiated with 0.4 J/cm(2) (200 mu s) at 450 Hz. Short-time reduction of calcium loss (<= 1.5 min) could be also achieved by irradiation with 0.7 J/cm(2) (300 mu s) at 200 and 300 Hz. Both parameters revealed surface modification. Conclusions: A set of CO2 laser parameters was found that could significantly reduce enamel mineral loss (20%) under in vitro erosive conditions. However, as all parameters also caused surface cracking, they are not recommended for clinical use.

Microhardness of a dental restorative composite resin containing nanoparticles polymerized with argon ion laser

The objective of this study was to compare the microhardness of two resin composites (microhybrid and nanoparticles). Light activation was performed with argon ion laser 1.56J (L) and halogen light 2.6J (H) was used as control. Measurements were taken on the irradiated surfaces and those opposite them, at thicknesses of 1, 2 and 3 mm. To evaluate the quality of polymerization, the percentages of maximum hardness were calculated (PMH). For statistical analysis the ANOVA and Tukey tests were used (p <= 0.05). To microhybrid was shown that the hardness with laser was inferior to the hardness achieved with halogen light, for both the 1 mm and 2 mm. The nanoparticles polymerized with laser, presented lower hardness even on the irradiated surface, than the same surface light activated with halogen light. The microhybrid attained a minimum PMH of 80% up to the thickness of 2 mm with halogen light, and with laser, only up to 1 mm. The nanoparticles attained a minimum PMH of 80% up to 3 mm thickness with halogen light and with laser this minimum was not obtained at any thickness. Based on these results, it could be concluded that light activation with argon ion laser is contra-indicated for the studied nanoparticles. Published by Elsevier GmbH.

The erosion and abrasion-inhibiting effect of TiF4 and NaF varnishes and solutions on enamel in vitro

Objective. Previous in vitro study has shown that TiF(4) varnish might reduce enamel erosion. No data regarding the effect of this experimental varnish on enamel erosion plus abrasion, however, are available so far. Thus, this in vitro study aimed to analyse the effect of TiF4 compared with NaF varnishes and solutions, to protect against enamel erosion with or without abrasion. Methods. Enamel specimens were pre-treated with experimental-TiF4 (2.45% F), experimentalNaF (2.45% F), NaF-Duraphat (2.26% F), and placebo varnishes; NaF (2.26% F) and TiF4 (2.45% F) solutions. Controls remained untreated. The erosive challenge was performed using a soft drink (pH 2.6) 4 u 90 s / day (ERO) and the toothbrushing abrasion (ERO+ ABR) 2 u 10 s / day, for 5 days. Between the challenges, the specimens were exposed to artificial saliva. Enamel loss was measured profilometrically (lm). Results. Kruskal-Wallis / Dunn tests showed that all fluoridated varnishes (TiF4-ERO: 0.53 +/- 0.20, ERO+ ABR: 0.65 +/- 0.19/ NaF-ERO: 0.94 +/- 0.18, ERO+ ABR: 1.74 +/- 0.37 / Duraphat-ERO: 1.00 +/- 0.37, ERO+ ABR: 1.72 +/- 0.58) were able to significantly reduce enamel loss when compared with placebo varnish (ERO: 3.45 +/- 0.41 / ERO+ ABR: 3.20 +/- 0.66) (P < 0.0001). Placebo varnish, control (ERO: 2.68 +/- 0.53 / ERO+ ABR: 3.01 +/- 0.34), and fluoridated (NaF-ERO: 2.84 +/- 0.09 / ERO+ ABR: 2.40 +/- 0.21 / TiF4-ERO: 3.55 +/- 0.59 / ERO+ ABR: 4.10 +/- 0.38) solutions did not significantly differ from each other. Conclusion. Based on the results, it can be concluded that the TiF4 varnish seems to be a promising treatment to reduce enamel loss under mild erosive and abrasive conditions in vitro.

Impact of experimental Nano-HAP pastes on bovine enamel and dentin submitted to a pH cycling model

This in vitro study evaluated the preventive potential of experimental pastes containing 10% and 20% hydroxyapatite nanoparticles (Nano-HAP), with or without fluoride, on dental demineralization. Bovine enamel (n=15) and root dentin (n=15) specimens were divided into 9 groups according to their surface hardness: control (without treatment), 20 Nanop paste (20% HAP), 20 Nanop paste plus (20% HAP + 0.2% NaF), 10 Nanop paste (10% HAP), 10 Nanop paste plus (10% HAP + 0.2% NaF), placebo paste (without fluoride and HAP), fluoride paste (0.2% NaF), MI paste (CPP-ACP, casein phosphopeptide-amorphous calcium phosphate), and MI paste plus (CPP-ACP + 0.2% NaF). Both MI pastes were included as commercial control products containing calcium phosphate. The specimens were treated with the pastes twice a day (1 min), before and after demineralization. The specimens were subjected to a pH-cycling model (demineralization–6-8 h/ remineralization-16-18 h a day) for 7 days. The dental subsurface demineralization was analyzed using cross-sectional hardness (kgf/mm 2 , depth 10-220 µm). Data were tested using repeated-measures two-way ANOVA and Bonferroni's test (p<0.05). The only treatment able to reduce the loss of enamel and dentin subsurface hardness was fluoride paste (0.2% NaF), which differed significantly from the control at 30- and 50-µm depth (p<0.0001). The other treatments were not different from each other or compared with the control. The experimental Nanop pastes, regardless of the addition of fluoride, were unable to reduce dental demineralization in vitro.

Minimal alterations on the enamel surface by micro-abrasion: in vitro roughness and wear assessments

Objective: To evaluate the in vitro changes on the enamel surface after a micro-abrasion treatment promoted by different products. Material and Methods: Fifty (50) fragments of bovine enamel (15 mm × 5 mm) were randomly assigned to five groups (n=10) according to the product utilized: G1 (control)= silicone polisher (TDV), G2= 37% phosphoric acid (3M/ESPE) + pumice stone (SS White), G3= Micropol (DMC Equipment), G4= Opalustre (Ultradent) and G5= Whiteness RM (FGM Dental Products). Roughness and wear were the responsible variables used to analyze these surfaces in four stages: baseline, 60 s and 120 s after the micro-abrasion and after polishing, using a Hommel Tester T1000 device. After the tests, a normal distribution of data was verified, with repeated ANOVA analyses (p?0.05) which were used to compare each product in different stages. One-way ANOVA and Tukey tests were applied for individual comparisons between the products in each stage (p?0.05). Results: Means and standard deviations of roughness and wear (µm) after all the promoted stages were: G1=7.26(1.81)/13.16(2.67), G2=2.02(0.62)/37.44(3.33), G3=1.81(0.91)/34.93(6.92), G4=1.92(0.29)/38.42(0.65) and G5=1.98(0.53)/33.45(2.66). At 60 seconds, all products tended to produce less surface roughness with a variable gradual decrease over time. After polishing, there were no statistically significant differences between the groups, except for G1. Independent of the product utilized, the enamel wear occurred after the micro-abrasion. Conclusions: In this in vitro study, enamel micro-abrasion presented itself as a conservative approach, regardless of the type of the paste compound utilized. These products promoted minor roughness alterations and minimal wear. The use of phosphoric acid and pumice stone showed similar results to commercial products for the micro-abrasion with regard to the surface roughness and wear.

Prevalence of enamel defects in permanent teeth of patients with complete cleft lip and palate

Objective: To evaluate the prevalence, types, location, and characteristics of enamel defects in anterior permanent teeth of patients with complete unilateral and bilateral cleft lip and palate, as well as the relation with the cleft. Setting: Hospital for Rehabilitation of Craniofacial Anomalies, Bauru, São Paulo, Brazil. Participants: Eighty patients of both genders, 12 years and older, with unilateral or bilateral cleft lip and palate. Methods: A single examiner carried out clinical examination under artificial light with a dental probe and mirror after drying teeth according to the modified DDE index. Results: Seventy-four of 80 patients presented with at least one tooth affected by enamel defects: 165 of 325 evaluated teeth (50.8%) presented enamel defects, with hypoplasia being the most prevalent (50.7%), followed by diffuse opacity (23.1%) and demarcated opacity (18.4%). The most affected tooth was 21 (36.5%), followed by 11 (34%), located at the middle (40%) and incisal (33%) thirds. Most defects occur at the buccal surface (47.7%), followed by the distal (22.7%), the mesial (19%), and the palatal (10.6%) surfaces. A significant relationship was found between the cleft side and enamel defects. Conclusion: Upper anterior teeth of patients with complete cleft lip and palate present a high prevalence of enamel defects; the highest percentage on the cleft side suggests that the cleft does influence the occurrence of enamel defects in permanent teeth.

Effects of enamel matrix derivative and transforming growth factor-β1 on human osteoblastic cells

Abstract Background Extracellular matrix proteins are key factors that influence the regenerative capacity of tissues. The objective of the present study was to evaluate the effects of enamel matrix derivative (EMD), TGF-β1, and the combination of both factors (EMD+TGF-β1) on human osteoblastic cell cultures. Methods Cells were obtained from alveolar bone of three adult patients using enzymatic digestion. Effects of EMD, TGF-β1, or a combination of both were analyzed on cell proliferation, bone sialoprotein (BSP), osteopontin (OPN) and alkaline phosphatase (ALP) immunodetection, total protein synthesis, ALP activity and bone-like nodule formation. Results All treatments significantly increased cell proliferation compared to the control group at 24 h and 4 days. At day 7, EMD group showed higher cell proliferation compared to TGF-β1, EMD + TGF-β1 and the control group. OPN was detected in the majority of the cells for all groups, whereas fluorescence intensities for ALP labeling were greater in the control than in treated groups; BSP was not detected in all groups. All treatments decreased ALP levels at 7 and 14 days and bone-like nodule formation at 21 days compared to the control group. Conclusions The exposure of human osteoblastic cells to EMD, TGF-β1 and the combination of factors in vitro supports the development of a less differentiated phenotype, with enhanced proliferative activity and total cell number, and reduced ALP activity levels and matrix mineralization.

Chitosan: effect of a new chelating agent on the microhardness of root dentin

The effect of solutions of 0.2% chitosan, 15% EDTA and 10% citric acid on the microhardness of root dentin was evaluated comparatively in this study. Thirteen sound human maxillary central incisors were selected and decoronated at the cementoenamel junction. Ten roots were set into rapid polymerization acrylic resin and the root/resin block was fitted to the cutting machine to obtain slices from the cervical third. The first slice was discarded and the second slice was divided into four quadrants. Each quadrant was used to construct a sample, so that 4 specimens were obtained from each root slice, being one for each chelating solution to be tested: 15% EDTA, 10% citric acid, 0.2% chitosan and distilled water (control). The specimens were exposed to 50 μL of the solution for 5 min, and then washed in distilled water. A microhardness tester (Knoop hardness) with a 10 g load was used for 15 s. Data were analyzed statistically by one-way ANOVA and Tukey-Kramer test (α=0.05). The other 3 roots had the canals instrumented and irrigated at the end of the biomechanical preparation with the test solutions, and then examined by scanning electron microscopy (SEM) for qualitative analysis. All solutions reduced the microhardness of root dentin in a way that was statistically similar to each other (p>0.05) but significantly different from the control (p>0.05). The SEM micrographs showed that the three solutions removed smear layer from the middle third of the root canal. In conclusion, 0.2% chitosan, 15% EDTA and 10% citric acid showed similar effects in reducing dentin microhardness.

Effect of sodium hypochlorite and edta irrigation, individually and in alternation, on dentin microhardness at the furcation area of mandibular molars

The aim of this study was to evaluate the effect of irrigation regimens on dentin microhardness at the furcation area of mandibular molars, using sodium hypochlorite and ethylenediaminetetraacetic acid (EDTA), individually and in alternation. The occlusal surface and the roots of 20 non-carious extracted human permanent mandibular molars were cut transversally and discarded. The tooth blocks were embedded in acrylic resin and randomly assigned to 4 groups (n=5) according to the irrigating regimens: 1% NaOCl solution, 17% EDTA solution, 1% NaOCl and 17% EDTA and distilled water (control). Knoop microhardness of dentin at the furcation area was evaluated. Data were analyzed using one-way ANOVA and Tukey's multiple comparison tests (α=0.05). The results of this study indicated that all irrigation solutions, except for distilled water (control), decreased dentin microhardness. EDTA did not show a significant difference with NaOCl/EDTA (p>0.05), but showed a significant difference with NaOCl (p<0.01). EDTA and NaOCl/EDTA showed a maximum decrease in microhardness. The 17% EDTA solution, either alone or in combination with 1% NaOCl reduced significantly dentin microhardness at the furcation area of mandibular molars.

Evaluation of fluid transport processes in dental enamel. Methods to assess the relevance of enamel permeability in caries prevention and etching treatments.

This thesis evaluated in vivo and in vitro enamel permeability in different physiological and clinical conditions by means of SEM inspection of replicas of enamel surface obtained from polyvinyl siloxane impressions subsequently later cast in polyether impression ma-terial. This technique, not invasive and risk-free, allows the evaluation of fluid outflow from enamel surface and is able to detect the presence of small quantities of fluid, visu-alized as droplets. Fluid outflow on enamel surface represents enamel permeability. This property has a paramount importance in enamel physiolgy and pathology although its ef-fective role in adhesion, caries pathogenesis and prevention today is still not fully under-stood. The aim of the studies proposed was to evaluate enamel permeability changes in differ-ent conditions and to correlate the findings with the actual knowledge about enamel physiology, caries pathogenesis, fluoride and etchinhg treatments. To obtain confirmed data the replica technique has been supported by others specific techniques such as Ra-man and IR spectroscopy and EDX analysis. The first study carried out visualized fluid movement through dental enamel in vivo con-firmed that enamel is a permeable substrate and demonstrated that age and enamel per-meability are closely related. Examined samples from subjects of different ages showed a decreasing number and size of droplets with increasing age: freshly erupted permanent teeth showed many droplets covering the entire enamel surface. Droplets in permanent teeth were prominent along enamel perikymata. These results obtained through SEM inspection of replicas allowed innovative remarks in enamel physiology. An analogous testing has been developed for evaluation of enamel permeability in primary enamel. The results of this second study showed that primary enamel revealed a substantive permeability with droplets covering the entire enamel sur-face without any specific localization accordingly with histological features, without changes during aging signs of post-eruptive maturation. These results confirmed clinical data that showed a higher caries susceptibility for primary enamel and suggested a strong relationship between this one and enamel permeability. Topical fluoride application represents the gold standard for caries prevention although the mechanism of cariostatic effect of fluoride still needs to be clarified. The effects of topical fluoride application on enamel permeability were evaluated. Particularly two dif-ferent treatments (NaF and APF), with different pH, were examined. The major product of topical fluoride application was the deposition of CaF2-like globules. Replicas inspec-tion before and after both treatments at different times intervals and after specific addi-tional clinical interventions showed that such globule formed in vivo could be removed by professional toothbrushing, sonically and chemically by KOH. The results obtained in relation to enamel permeability showed that fluoride treatments temporarily reduced enamel water permeability when CaF2-like globules were removed. The in vivo perma-nence of decreased enamel permeability after CaF2 globules removal has been demon-strated for 1 h for NaF treated teeth and for at least 7 days for APF treated teeth. Important clinical consideration moved from these results. In fact the caries-preventing action of fluoride application may be due, in part, to its ability to decrease enamel water permeability and CaF2 like-globules seem to be indirectly involved in enamel protection over time maintaining low permeability. Others results obtained by metallographic microscope and SEM/EDX analyses of or-thodontic resins fluoride releasing and not demonstrated the relevance of topical fluo-ride application in decreasing the demineralization marks and modifying the chemical composition of the enamel in the treated area. These data obtained in both the experiments confirmed the efficacy of fluoride in caries prevention and contribute to clarify its mechanism of action. Adhesive dentistry is the gold standard for caries treatment and tooth rehabilitation and is founded on important chemical and physical principles involving both enamel and dentine substrates. Particularly acid etching of dental enamel enamel has usually employed in bonding pro-cedures increasing microscopic roughness. Different acids have been tested in the litera-ture suggesting several etching procedures. The acid-induced structural transformations in enamel after different etching treatments by means of Raman and IR spectroscopy analysis were evaluated and these findings were correlated with enamel permeability. Conventional etching with 37% phosphoric acid gel (H3PO4) for 30 s and etching with 15 % HCl for 120 s were investigated. Raman and IR spectroscopy showed that the treatment with both hydrochloric and phosphoric acids induced a decrease in the carbonate content of the enamel apatite. At the same time, both acids induced the formation of HPO42- ions. After H3PO4 treatment the bands due to the organic component of enamel decreased in intensity, while in-creased after HCl treatment. Replicas of H3PO4 treated enamel showed a strongly reduced permeability while replicas of HCl 15% treated samples showed a maintained permeability. A decrease of the enamel organic component, as resulted after H3PO4 treatment, involves a decrease in enamel permeability, while the increase of the organic matter (achieved by HCl treat-ment) still maintains enamel permeability. These results suggested a correlation between the amount of the organic matter, enamel permeability and caries. The results of the different studies carried out in this thesis contributed to clarify and improve the knowledge about enamel properties with important rebounds in theoretical and clinical aspects of Dentistry.

Removal of enamel caries with an air abrasion powder

This study compared the efficiency of air abrasion on enamel caries with selective enamel powder (SEP) or with alumina powder and a negative and positive control group. Ninety-three extracted molars with non-cavitated incipient enamel lesions were selected. After embedding the roots in resin, each lesion was sectioned perpendicular to the surface and photographed. Each lesion was classified microscopically as having or not having dentin involvement. The lesions were distributed into four groups with an equal number of enamel caries with or without dentin involvement. Each group was treated differently: Group 1 had SEP abrasion, Group 2 had alumina abrasion, Group 3 had sodium bicarbonate abrasion (negative control) and Group 4 had bur treatment (positive control). The surface was rephotographed after treatment. Superimposition of the photographs identified areas of "correct-excavation," "under-excavation" and "over-excavation." There were no statistical differences between lesions treated with or without dentin involvement for Groups 2 through 4. However, in the SEP group, all measured areas were significantly influenced by dentin involvement. In pairwise comparisons, no statistical differences were found between the alumina and bur groups. The SEP group, however, showed statistically significant differences for each area compared to the alumina group in enamel caries without dentin involvement. SEP performed as well as alumina and bur in lesions with dentin involvement. SEP is different in its ablative properties toward caries with dentin involvement or no dentin involvement. In terms of dental treatment, SEP seems to have a diagnostic potential for enamel lesions before operative intervention in patients with high caries risk.

Thickness of softened human enamel removed by toothbrush abrasion: an in vitro study

The aim of the study was to assess the thickness of softened enamel removed by toothbrushing. Human enamel specimens were indented with a Knoop diamond. Softening was performed with citric acid or orange juice. The specimens were brushed in a brushing machine with a manual soft toothbrush in toothpaste slurry or in artificial saliva. Enamel loss was calculated from the change in indentation depth of the same indent before and after abrasion. Mean surface losses (95% confidence interval) were recorded in treatment groups (in nanometers): (1) citric acid, abrasion with slurry = 339 (280-398); (2) citric acid, abrasion with artificial saliva = 16 (5-27); (3) orange juice, abrasion with slurry = 268 (233-303); (4) orange juice, abrasion with artificial saliva = 14 (5-23); (5) no softening, abrasion with slurry = 28 (10-46). The calculated thickness of the softened enamel varied between 254 and 323 nm, depending on the acid used.

Remineralization of initial carious lesions in deciduous enamel after application of dentifrices of different fluoride concentrations

The aim of the present study was to evaluate the remineralization potential of five dentifrices with different fluoride concentrations. Initial caries lesions were created in 72 cylindrical enamel blocks from deciduous teeth. The specimens were randomly distributed among six experimental groups corresponding to six experimental periods. Each of the six volunteers carried two deciduous enamel specimens fixed in an intraoral appliance for a period of 4 weeks. They brushed their teeth and the enamel blocks at least two times a day with dentifrices containing 0 ppm (period 1), 250 ppm (period 2), and 500 ppm fluoride (period 3), respectively. A second group of volunteers (n = 6) used dentifrices with a fluoride content of 0 ppm (period 4), 1,000 ppm (period 5), or 1,500 ppm (period 6). At the end of the respective period, the mineral content was determined by transversal microradiography (TMR). The use of dentifrices containing 500 ppm fluoride (38% MR), 1,000 ppm fluoride (42% MR), and 1,500 ppm fluoride (42% MR) resulted in a statistically significant higher mineral recovery compared to the control group (0 ppm fluoride). Mineral recovery was similar after use of dentifrices containing 0 and 250 ppm fluoride (24%; 25%). It is concluded that it is possible to remineralize initial carious lesions in deciduous enamel in a similar way as it has been described for enamel of permanent teeth.

Effects of pH and acid concentration on erosive dissolution of enamel, dentine, and compressed hydroxyapatite

The aims of this study were to determine the effects of pH and acid concentration on the dissolution of enamel, dentine, and compressed hydroxyapatite (HA) in citric acid solutions (15.6 and 52.1 mmol l(-1) ; pH 2.45, 3.2, and 3.9), using a pH-stat system. After an initial adjustment period, the dissolution rates of enamel and HA were constant, while that of dentine decreased with time. The dissolution rate increased as the pH decreased, and this was most marked for enamel. To compare substrates, the rate of mineral dissolution was normalized to the area occupied by mineral at the specimen surface. For a given acid concentration, the normalized dissolution rate of HA was always less than that for either dentine or enamel. The dissolution rate for dentine mineral was similar to that for enamel at pH 2.45 and greater at pH 3.2 and pH 3.9. The concentration of acid significantly affected the enamel dissolution rate at pH 2.45 and pH 3.2, but not at pH 3.9, and did not significantly affect the dissolution rates of dentine or HA at any pH. The variation in response of the dissolution rate to acid concentration/buffer capacity with respect to pH and tissue type might complicate attempts to predict erosive potential from solution composition.

Clinical Outcomes Following Treatment of Non-contained Intrabony Defects with Enamel Matrix Derivative (EMD) or Guided Tissue Regeneration (GTR). A 12-month Randomized Controlled Clinical trial

The purpose of this study is to compare the healing of deep, non-contained intrabony defects (i.e., with a ?80% 1-wall component and a residual 2- to 3-wall component in the most apical part) treated with either an enamel matrix derivative (EMD) or guided tissue regeneration (GTR) after 12 months.