Effect of high temperature, biaxial stretching on the thermal and mechanical properties of HDPE/MWCNT sheet

High density polyethylene (HDPE)/multi-walled carbon nanotube (MWCNT) composites containing 4 wt% MWCNTs were prepared by melt mixing followed by compression moulding into sheet. Compression moulded sheets were heated to just below the melting temperature and biaxially stretched at ratios (SRs) of 2, 2.5 and 3.0. The effect of stretching on the thermal and mechanical properties of the sheet was studied by differential scanning calorimetry (DSC) and tensile testing. DSC results show that the crystallinity of all the stretched samples increases by approximately 13% due to strain induced crystallization. The melting temperature of the biaxially stretched samples increases only slightly while crystallization temperature is not affected. Tensile test results indicate that at a SR of 2.5 the elastic modulus of the stretched composites increases by 17.6% relative to the virgin HDPE, but the breaking strength decreases by 33%. While the elastic modulus and breaking strength of the HDPE/MWCNT samples continue to increase as SR increases they drop off after a SR of 2.5 for the virgin HDPE. This is probably due to the constraining influence of the nanotubes preventing the relaxation of polymer chains caused by adiabatic heating at high SRs. The addition of MWCNTs results in significant strain hardening during deformation. While this will lead to increased energy requirement in forming it will also result in a more stable process and the ability to produce deep draw containers with more uniform wall thickness

Phonon spectra and thermodynamic properties of rare gas solids based on empirical and semi-empirical (ab initio) two-body potentials : a comparative study /

We study the phonon dispersion, cohesive and thermal properties of raxe gas solids Ne, Ar, Kr, and Xe, using a variety of potentials obtained from different approaches; such as, fitting to crystal properties, purely ab initio calculations for molecules and dimers or ab initio calculations for solid crystalline phase, a combination of ab initio calculations and fitting to either gas phase data or sohd state properties. We explore whether potentials derived with a certain approaxih have any obvious benefit over the others in reproducing the solid state properties. In particular, we study phonon dispersion, isothermal ajid adiabatic bulk moduli, thermal expansion, and elastic (shear) constants as a function of temperatiue. Anharmonic effects on thermal expansion, specific heat, and bulk moduli have been studied using A^ perturbation theory in the high temperature limit using the neaxest-neighbor central force (nncf) model as developed by Shukla and MacDonald [4]. In our study, we find that potentials based on fitting to the crystal properties have some advantage, particularly for Kr and Xe, in terms of reproducing the thermodynamic properties over an extended range of temperatiures, but agreement with the phonon frequencies with the measured values is not guaranteed. For the lighter element Ne, the LJ potential which is based on fitting to the gas phase data produces best results for the thermodynamic properties; however, the Eggenberger potential for Ne, where the potential is based on combining ab initio quantum chemical calculations and molecular dynamics simulations, produces results that have better agreement with the measured dispersion, and elastic (shear) values. For At, the Morse-type potential, which is based on M0ller-Plesset perturbation theory to fourth order (MP4) ab initio calculations, yields the best results for the thermodynamic properties, elastic (shear) constants, and the phonon dispersion curves.

Photopyroelectric study of thermal properties and phase transitions in selected solids

This thesis presents in detail. the theoretical developments and calculations which are used for the simultaneous determination of thermal parameters, namely thermal diffusivity (a). thermal effusivity (e), thermal conductivity (K) and heat capacity (cr ) employing photopyroelectric technique. In our calculations. we have assumed that the pyroelectric detector is supported on a copper backing. so that there will be sufficient heat exchange between the heated pyroelectric detector and the backing so that the signal fluctuations are reduced to a minimum. Since the PPE signal depends on the properties of the detector that are also temperature dependent. a careful temperature calibration of the system need to be carried out. APPE cell has been fabricated for the measurements that can be used to measure the thermal properties of solid samples from ~ 90 K to ~ 350 K. The cell has been calibrated using standard samples and the accuracy of the technique is found to be of the order of± 1%.In this thesis, we have taken up work n photopyroelectric investigation of thermal parameters of ferroelectric crystals such as Glycine phosphite (NH3CH2COOH3P03), Triglycine sulfate and Thiourea as well as mixed valence perovskites samples such as Lead doped Lanthanum Manganate (Lal_xPb~Mn03) Calcium doped (Lal_xCaxMnOJ) and Nickel doped Lanthanum Stroncium Cobaltate (Lao~Sro5Ni,Col_x03).The three ferroelectric crystals are prepared by the slow evaporation technique and the mixed valence perovskites by solid state reaction technique.Mixed valence perovskites, with the general formula RI_xA~Mn03 (R = La. Nd or Pr and A = Ba, Ca, Sr or Pb) have been materials of intense experimental and theoretical studies over the past few years. These materials show . colossal magneloresis/ance' (CMR) in samples with 0.2 < x < 0.5 in such a doping region, resistivity exhibits a peak at T = T p' the metal - insulator transition temperature. The system exhibits metallic characteristics with d %T > Oabove Tp (wherep is the resistivity) and insulating characteristics with d % T < 0 above T p. Despite intensive investigations on the CMR phenomena and associated electrical properties. not much work has been done on the variation of thermal properties of these samples. We have been quite successful in finding out the nature of anomaly associated with thermal properties when the sample undergoes M-I transition.The ferroelectric crystal showing para-ferroelectric phase transitions - Glycine phosphite. Thiourea and Triglycine sulfate - are studied in detail in order to see how well the PPE technique enables one to measure the thermal parameters during phase transitions. It is seen that the phase transition gets clearly reflected in the variation of thermal parameters. The anisotropy in thermal transport along different crystallographic directions are explained in terms of the elastic anisotropy and lattice contribution to the thermal conductivity. Interesting new results have been obtained on the above samples and are presented in three different chapters of the thesis.In summary. we have carried investigations of the variations of the thermal parameters during phase transitions employing photopyroelectric technique. The results obtained on different systems are important not only in understanding the physics behind the transitions but also in establishing the potentiality of the PPE tool. The full potential of PPE technique for the investigation of optical and thermal properties of materials still remains to be taken advantage of by workers in this field.

Shot noise anomalies in elastic nondegenerate diffusive conductors

We present a theoretical investigation of shot-noise properties in nondegenerate elastic diffusive conductors. Both Monte Carlo simulations and analytical approaches are used. Two interesting phenomena are found: (i) the display of enhanced shot noise for given energy dependences of the scattering time, and (ii) the recovery of full shot noise for asymptotic high applied bias. The first phenomenon is associated with the onset of negative differential conductivity in energy space that drives the system towards a dynamical electrical instability in excellent agreement with analytical predictions. The enhancement is found to be strongly amplified when the dimensionality in momentum space is lowered from three to two dimensions. The second phenomenon is due to the suppression of the effects of long-range Coulomb correlations that takes place when the transit time becomes the shortest time scale in the system, and is common to both elastic and inelastic nondegenerate diffusive conductors. These phenomena shed different light in the understanding of the anomalous behavior of shot noise in mesoscopic conductors, which is a signature of correlations among different current pulses.

Electronic structure and properties of Cu2O

The structural and electronic properties of Cu2O have been investigated using the periodic Hartree-Fock method and a posteriori density-functional corrections. The lattice parameter, bulk modulus, and elastic constants have been calculated. The electronic structure of and bonding in Cu2O are analyzed and compared with x-ray photoelectron spectroscopy spectra, showing a good agreement for the valence-band states. To check the quality of the calculated electron density, static structure factors and Compton profiles have been calculated, showing a good agreement with the available experimental data. The effective electron and hole masses have been evaluated for Cu2O at the center of the Brillouin zone. The calculated interaction energy between the two interpenetrated frameworks in the cuprite structure is estimated to be around -6.0 kcal/mol per Cu2O formula. The bonding between the two independent frameworks has been analyzed using a bimolecular model and the results indicate an important role of d10-d10 type interactions between copper atoms.

On the magnetic, mechanical and rheological properties of rubber–nickel nanocomposites

Rubber–nickel nanocomposites were synthesized by incorporating freshly prepared nanometric nickel particles in two different matrices namely natural rubber and neoprene rubber according to specific recipes for various loadings of nano nickel and the cure characteristics of these composites were evaluated. The maximum torque values register an increase with the increase in loading of nickel in both composites and this is attributed to the non-interacting nature of nickel nanoparticles with rubber matrices. The cure time of natural rubber composites decreases with increase in the content of nickel, and in neoprene rubber cure, time increases with increase in filler content. In natural rubber, the curing reaction seems to be activated by the presence of nickel particles. The magnetization studies of the composites reveal that the magnetic properties of nickel are retained in the composite samples. The elastic modulus of natural rubber and neoprene rubber are largely improved by the incorporation of nickel particles

Comparison of mechanical properties of tension and opposite wood in Populus

In this paper we focused on the differences of mechanical properties of tension and normal wood of 1-year-old poplar trees, artificially tilted. Elastic and fracture properties have been measured and linked to the anatomy. Tension wood is well known because it prevents good surface finishing and leads to difficulties with sawing. We studied three main mechanical properties: young modulus, energy of cutting and longitudinal residual strain of maturation (with strain gauges) because of their importance in wood technology. Moreover, this work takes place in a larger project of study, the phenomena of axes re-orientation in trees (allowing by the production of reaction wood), where these data are required for biomechanical modelling. The results show that tension wood has a higher young modulus, needs a higher energy to be cut and exhibited a higher level of longitudinal residual strain of maturation than those of normal wood. The results suggest that these differences require deeper analysis of the wood than anatomy: measurement of microfibril orientation in the S2 layer and also the lignin composition in monomeric units.

Relationships between gluten rheological properties and hearth loaf characteristics

The rheological properties of fresh gluten in small amplitude oscillation in shear (SAOS) and creep recovery after short application of stress was related to the hearth breadbaking performance of wheat flours using the multivariate statistics partial least squares (PLS) regression. The picture was completed by dough mixing and extensional properties, flour protein size distribution determined by SE-HPLC, and high molecular weight glutenin subunit (HMW-GS) composition. The sample set comprised 20 wheat cultivars grown at two different levels of nitrogen fertilizer in one location. Flours yielding stiffer and more elastic glutens, with higher elastic and viscous moduli (G' and G") and lower tan 8 values in SAOS, gave doughs that were better able to retain their shape during proving and baking, resulting in breads of high form ratios. Creep recovery measurements after short application of stress showed that glutens from flours of good breadmaking quality had high relative elastic recovery. The nitrogen fertilizer level affected the protein size distribution by an increase in monomeric proteins (gliadins), which gave glutens of higher tan delta and flatter bread loaves (lower form ratio).

Comparison of small and large deformation rheological properties of wheat dough and gluten

The rheological properties of dough and gluten are important for end-use quality of flour but there is a lack of knowledge of the relationships between fundamental and empirical tests and how they relate to flour composition and gluten quality. Dough and gluten from six breadmaking wheat qualities were subjected to a range of rheological tests. Fundamental (small-deformation) rheological characterizations (dynamic oscillatory shear and creep recovery) were performed on gluten to avoid the nonlinear influence of the starch component, whereas large deformation tests were conducted on both dough and gluten. A number of variables from the various curves were considered and subjected to a principal component analysis (PCA) to get an overview of relationships between the various variables. The first component represented variability in protein quality, associated with elasticity and tenacity in large deformation (large positive loadings for resistance to extension and initial slope of dough and gluten extension curves recorded by the SMS/Kieffer dough and gluten extensibility rig, and the tenacity and strain hardening index of dough measured by the Dobraszczyk/Roberts dough inflation system), the elastic character of the hydrated gluten proteins (large positive loading for elastic modulus [G'], large negative loadings for tan delta and steady state compliance [J(e)(0)]), the presence of high molecular weight glutenin subunits (HMW-GS) 5+10 vs. 2+12, and a size distribution of glutenin polymers shifted toward the high-end range. The second principal component was associated with flour protein content. Certain rheological data were influenced by protein content in addition to protein quality (area under dough extension curves and dough inflation curves [W]). The approach made it possible to bridge the gap between fundamental rheological properties, empirical measurements of physical properties, protein composition, and size distribution. The interpretation of this study gave indications of the molecular basis for differences in breadmaking performance.

Viscoelastic properties of high pressure and heat induced tofu gels

Tofu gels were rheologically examined to determine their storage or elastic (G′) and loss or viscous (G″) moduli as a function of frequency within their linear viscoelastic limits. The tofu gels were made using either glucono-δ-lactone (GDL) or calcium sulphate (CaSO4·2H2O), followed by either heat treatment (heated soymilk at 97 °C prior to coagulation and subsequently held at 70 °C for 60 min, HT) or high pressure treatment (400 MPa at 20 °C for 10 min, HP). The overall moduli values of the GDL gels and CaSO4·2H2O gels of both physical treatments were similar, each gave frequency profiles expected for weak viscoelastic materials. However, although both temperature and high pressure treatments could be used to produce tofu gels, the final products were not the same. Pressure formed gels, despite having a higher overall “consistency” (increasing values of their moduli), had a proportionately higher contribution from the loss modulus (increased tan δ). Differences could also be observed using confocal scanning laser microscopy. While such treatment may give rise to differing systems/structures, with new or modified organoleptic properties, the more “open” structures obtained by pressure treatment may well cause processing difficulties if subsequent reworking or moulding is required.

Viscoelastic properties of high pressure and heat induced tofu gels

Tofu gels were rheologically examined to determine their storage or elastic (G') and loss or viscous (G '') moduli as a function of frequency within their linear viscoelastic limits. The tofu gels were made using either glucono-delta-lactone (GDL) or calcium sulphate (CaSO4 center dot 2H(2)O), followed by either heat treatment (heated soymilk at >= 97 degrees C prior to coagulation and subsequently held at 70 degrees C for 60 min, HT) or high pressure treatment (400 MPa at 20 degrees C for 10 min, HP). The overall moduli values of the GDL gels and CaSO4 center dot 2H(2)O gels of both physical treatments were similar, each gave frequency profiles expected for weak viscoelastic materials. However, although both temperature and high pressure treatments could be used to produce tofu gels, the final products were not the same. Pressure formed gels, despite having a higher overall "consistency" (increasing values of their moduli), had a proportionately higher contribution from the loss modulus (increased tan delta). Differences could also be observed using confocal scanning laser microscopy. While such treatment may give rise to differing systems/structures, with new or modified organoleptic properties, the more "open" structures obtained by pressure treatment may well cause processing difficulties if subsequent reworking or moulding is required. (c) 2007 Elsevier Ltd. All rights reserved.

Transient development of whipped cream properties

Commercially available UHT cream was tempered at 4 degrees C for 24 h and whipped for different times: 3. 6. 9 and 12 nun. The following properties of cream were measured: rheological and interfacial properties. overrun and size distribution of air bubbles. The whipping process changes the properties of cream, which exhibits viscoelastic behaviour with a high influence of elastic component. The air bubbles incorporated during the process result in forming stronger foam containing smaller bubbles. and also give a higher overrun. These changes are observed around 9 min of whipping. when the amount of air is sufficient to create a stable structure. Further whipping reduces the overrun and the foam partly collapses: this may be caused by aggregation of fat droplets. (c) 2005 Elsevier Ltd. All rights reserved.

Mucoadhesive and elastic films based on blends of chitosan and hydroxyethylcellulose

Mucoadhesive polymeric films have been prepared based on blends of chitosan and hydroxyethylcellulose. The blends have been characterized by IR spectroscopy, DSC, WAXD, TGA, SEM, and mechanical testing. It is demonstrated that the mechanical properties of chitosan are improved significantly upon blending with hydroxyethylcellulose. An increase in hydroxyethylcellulose content in the blends makes the materials more elastic. The thermal treatment of the blends at 100 degrees C leads to partial cross-linking of the polymers and formation of water-insoluble but swellable materials. The adhesion of the films towards porcine buccal mucosa decreases with increasing hydroxyethylcellulose content in the blends.

Ex vivo expansion of limbal stem cells is affected by substrate properties

Limbal epithelial stem cells play a key role in the maintenance and regulation of the corneal surface. Damage or destruction of these cells results in vascularisation and corneal opacity. Subsequent limbal stem cell transplantation requires an ex vivo expansion step and preserving cells in an undifferentiated state remains vital. In this report we seek to control the phenotype of limbal epithelial stem cells by the novel application of compressed collagen substrates. We have characterised the mechanical and surface properties of conventional collagen gels using shear rheology and scanning electron microscopy. In doing so, we provide evidence to show that compressive load can improve the stiffness of collagen substrates. In addition Western blotting and immunohistochemistry display increased cytokeratin 3 (CK3) protein expression relating to limbal epithelial cell differentiation on stiff collagen substrates. Such gels with an elastic modulus of 2900 Pa supported a significantly higher number of cells than less stiff collagen gels (3 Pa). These findings have substantial influence in the development of ocular surface constructs or experimental models particularly in the fields of stem cell research, tissue engineering and regenerative medicine.