EFFECT OF METAL PRIMERS ON MICROTENSILE BOND STRENGTH BETWEEN ZIRCONIA AND RESIN CEMENTS

Statement of problem. There are no established clinical procedures for bonding zirconia to tooth structure using resin cements. Purpose. The purpose of this study was to evaluate the influence of metal primers, resin cements, and aging on bonding to zirconia. Material and methods. Zirconia was treated with commercial primers developed for bonding to metal alloys (Metaltite, Metal Primer II, Alloy Primer or Totalbond). Non-primed specimens were considered as controls. One-hundred disk-shaped specimens (19 x 4 mm) were cemented to composite resin substrates using Panavia or RelyX Unicem (n=5). Microtensile bond strength specimens were tested after 48 hours and 5 months (150 days), and failure modes were classified as type 1 (between ceramic/cement), 2 (between composite resin/cement) or 3 (mixed). Data were analyzed by 3-way ANOVA and Multiple Comparison Tukey test (alpha=.05). Results. The interactions primer/luting system (P=.016) and luting system/storage time (P=.004) were statistically significant. The use of Alloy Primer significantly improved the bond strength of RelyX Unicem (P<.001), while for Panavia, none of the primers increased the bond strength compared to the control group. At 48 hours, Panavia had statistically higher bond strength (P=.004) than Unicem (13.9 +/- 4.4MPa and 10.2 +/- 6.6MPa, respectively). However, both luting systems presented decreasing, statistically similar; values after aging (Panavia: 3.6 +/- 2.2MPa; Unicem: 6.1 +/- 5.3MPa). At 48 hours, Alloy Primer/Unicem had the lowest incidence of type 1 failure (8%). After aging, all the groups showed a predominance of type 1 failures. Conclusions. The use of Alloy Primer improved bond strength between RelyX Unicem and zirconia. Though the initial values obtained with Panavia were significantly higher than RelyX Unicem, after aging, both luting agents presented statistically similar performances. (J Prosthet Dent 2011;105:296-303)

Clinical versus laboratory adhesive performance to wet and dry demineralized primary dentin

Purpose: To evaluate the influence of dentin moisture on bond strengths of an etch-and-rinse bonding agent to primary dentin clinically and in the laboratory. Methods: The sample consisted of two groups of 20 caries-free primary second molars: molars in exfoliation period (clinical group) and extracted molars (laboratory group). Class I cavities were prepared in all specimens leaving a flat dentin surface on the pulpal floor. A two-step etch-and-rinse adhesive was vigorously rubbed on either dry (n= 5) or wet demineralized dentin (n= 5) under clinical or laboratory conditions. After restorative procedures, the teeth from the clinical group were extracted after 20 minutes. All samples were processed and underwent microtensile bond strength test and silver nitrate uptake evaluation under scanning electron microscopy. Results: Statistically higher bond strength values were observed when the bonding was performed under laboratory conditions and on a wet demineralized dentin. Most of the failures were adhesive and mixed irrespective of the experimental condition. Silver nitrate uptake occurred in all groups irrespective of the experimental condition. Resin-dentin bond strengths produced in the laboratory in primary teeth may overestimate those produced under clinical circumstances. (Am J Dent 2011;24:221-225).

Micro-Shear Bond Strength of Different Adhesives to Human Dental Enamel

The aim of this study was to evaluate the micro-shear bond strength of 5 adhesive systems to enamel, one single-bottle acid-etch adhesive (O), two self-etching primers (P) and two all-in-one self-etching adhesives (S). Method: Sixty premolar enamel surfaces (buccal or lingual) were ground flat with 400- and 600-grit SiC papers and randomly divided into 5 groups (n=12), according to the adhesive system.. SB2 - Single Bond 2 (O); CSE - Clearfil SE Bond (P); ADS - AdheSE (P); PLP - Adper Prompt L-Pop (S); XE3 - Xeno III (S). Tygon tubing (inner diameter of 0.8mm) restricted the bonding area to obtain the resin composite (Z250) cylinders. After storage in distilled water at 37 degrees C for 24h and thermocycling, micro-shear testing was performed (crosshead speed of 0.5mm/min). Data were submitted to one-way ANOVA and Tukey test (a=5%). Samples were also subjected to stereomicroscopic and SEM evaluations after micro-shear testing. Mean bond strength values (MPa +/- SD) and the results of Tukey test were: SB2: 36.36(+/- 3.34)a; ADS: 33.03(+/- 7.83)a; XE3: 32.76(+/- 5.61)a; CSE: 30.61(+/- 6.68)a; PLP: 22.17(+/- 6.05)b. Groups with the same letter were not statistically different. It can be concluded that no significant difference was there between SB2, ADS, XE3 and CSE, in spite of different etching patterns of these adhesives. Only PLP presented statistically lower bond strengths compared with others. J Clin Pediatr Dent 35(3): 301-304, 2011

Scanning Electron Microscopy In Vitro Study on the Effect of Carisolv Application on Periodontally Diseased Root Surfaces

The purpose of this study was to evaluate the characteristics of diseased root surfaces treated by the association of scaling and the application of Carisolv. Twenty-four uniradicular periodontally involved teeth were used in this study The teeth were divided randomly into three groups: eight teeth were scaled and root planed until there was a complete visible removal of calculus (group 1), Carisolv was applied on the root surfaces of eight teeth twice for 30 seconds before scaling with a sharp curette (group 2), and eight teeth received the same treatment as in group 2 but with a blunt curette (group 3). Specimens were examined using scanning electron microscopy The superficial aspect of the roots from group 1 presented scratches that mirrored the curette cutting edge, and the smear layer completely covered the surface. Root surfaces from groups 2 and 3 also presented a smear layer that covered the surface completely but it was somewhat smoother than group 1. The use of Carisolv as an adjunct to scaling and root planing presented no advantage for smear layer removal over scaling alone, suggesting that no benefit is obtained by the use of Carisolv during periodontal mechanical treatment. (Int J Periodontics Restorative Dent 2011;31:91-95.)

Photoinitiator content in restorative composites: Influence on degree of conversion, reaction kinetics, volumetric shrinkage and polymerization stress

Purpose: To determine the influence of rate of polymerization, degree of conversion and volumetric shrinkage on stress development by varying the amount of photoinitiators in a model composite. Methods: Volumetric shrinkage (with a mercury dilatometer), degree of conversion, maximum rate of reaction (RP(max)) (with differential scanning calorimetry) and polymerization stress (with a controlled compliance device) were evaluated. Bis-GMA/TEGDMA (equal mass ratios) were mixed with a tertiary amine (EDMAB) and camphorqpinone, respectively, in three concentrations (wt%): high= 0.8/1.6; intermediate= 0.4/0.8 and low= 0.2/0.4. 80 wt% filler was added. Composites were photoactivated (400 mW/cm(2) x 40 seconds; radiant exposure=16J/cm(2)). A fourth experimental group was included in which the low concentration formulation was exposed for 80 seconds (32 J/cm(2)). Results: For the same radiant exposure, conversion, RP(max) and stress increased with photoinitiator concentration (P< 0.001). When the low concentration group exposed to 32 J/cm(2) was compared with the high and intermediate groups (exposed to 16 J/cm(2)), RPmax Still increased with the photoinitiator concentration between all levels (P< 0.001) but conversion and stress did not vary (P> 0.05). Shrinkage did not vary regardless of the photoinitiator concentration or radiant exposure. For the photoinitiator concentrations used in this study. Polymerization stress was influenced by conversion but not by rate of reaction. (Am J Dent 2009;22:206-210).

Clinical, Histological, and Microbiological Findings in Peri-Implant Disease: A Pilot Study

Objectives: This study is intended to verify the correlation among clinical indices of the peri-implant soft tissues, the histological condition and the presence of 3 pathogens commonly associated with peri-implant diseases (Aggregatibacter actinomycetemcomitans, Porphyromonas gingivalis, and Tannerella forsythia). Materials: Four clinical indices, Gingival Index (GI), Sulcus Bleeding Index, GI modified by Mombelli, and Plaque Index modified by Mombelli (mPI) were evaluated around I dental implant of each subject (n = 10). Subgingival plaque was collected for bacterial analysis (polymerase chain reaction) and a biopsy of peri-implant soft tissues for histological analysis was harvested. The clinical indices and detected pathogens correlated with a developed histological index (HI). Results: There was no statistically significant relationship between the clinical indices (GI, Sulcus Bleeding Index, and GI modified by Mombelli) and the HI, except for the mPI on the central area of lingual aspects (r = 0.85, P = 0.0029). There was a tendency for a positive correlation between the mPI on the central area of buccal aspects and the HI (r = 0.63, P = 0.0544). The counting of lymphocytes and plasmocytes correlated positively with 111, thus suggesting the index reliability. The prevalence of A. actinomycetemcomitans, P. gingivalis, and T. forsythia did not present a significant relationship with the HI. Conclusion: Despite the small number of samples and the poor statistical significance, the mPI seems to be useful for evaluation of inflammatory severity on soft tissue around dental implants as demonstrated by its relationship with the HI. Further studies are necessary to elucidate this subject. (Implant Dent 2009;18:334-344)

Influence of curing rate on softening in ethanol, degree of conversion, and wear of resin composite

Purpose: To investigate the effect of curing rate on softening in ethanol, degree of conversion, and wear of resin composites. Methods: With a given energy density and for each of two different light-curing units (QTH or LED), the curing rate was reduced by modulating the curing mode. Thus, the irradiation of resin composite specimens (Filtek Z250, Tetric Ceram, Esthet-X) was performed in a continuous curing mode and in a pulse-delay curing mode. Wallace hardness was used to determine the softening of resin composite after storage in ethanol. Degree of conversion was determined by infrared spectroscopy (FTIR). Wear was assessed by a three-body test. Data were submitted to Levene`s test, one and three-way ANOVA, and Tukey HSD test (alpha= 0.05). Results: Immersion in ethanol, curing mode, and material all had significant effects on Wallace hardness. After ethanol storage, resin composites exposed to the pulse-delay curing mode were softer than resin composites exposed to continuous cure (P< 0.0001). Tetric Ceram was the softest material followed by Esthet-X and Filtek Z250 (P< 0.001). Only the restorative material had a significant effect on degree of conversion (P< 0.001): Esthet-X had the lowest degree of conversion followed by Filtek Z250 and Tetric Ceram. Curing mode (P= 0.007) and material (P< 0.001) had significant effect on wear. Higher wear resulted from the pulse-delay curing mode when compared to continuous curing, and Filtek Z250 showed the lowest wear followed by Esthet-X and Tetric Ceram. (Am J Dent 2011;24:115-118).

Effect of oxalate desensitizers and dentin moisture during total-etch bonding

Purpose: To evaluate the effect of oxalate during total-etch bonding, under different dentin moisture conditions, over time. The null hypothesis tested was that microtensile bond strength (mu TBS) was not affected by oxalate treatment and dentin moisture during two evaluation periods. Methods: Extracted human third molars had their mid-coronal dentin exposed flat and polished with 600-grit SiC paper. The surfaces were etched with 35% phosphoric acid for 15 seconds, washed and blot dried. After etching, a 3% potassium oxalate gel was applied for 120 seconds, except for the control group (no desensitizer). The surface was then washed and left moist (Wet bonding) or air-dried for 30 seconds (Dry bonding). The surfaces were bonded with: (I) two 2-step etch-and-rinse adhesives: Single Bond (SB); Prime & Bond NT (PBNT) and (2) one 3-step etch-and-rinse adhesive: Scotchbond Multi Purpose (SBMP). Composite buildups were constructed incrementally with Tetric Ceram resin composite. Each increment was cured for 40 seconds. After storage in water for 24 hours or 1 year at 37 C, the specimens were prepared for mu TBS testing with a cross-sectional area of approximately 1 mm(2). They were then tested in tension in an Instron machine at 0.5 mm/minute. Data were analyzed by ANOVA and Student-Newman-Keuls at alpha = 0.05. Results: Application of potassium oxalate had no significant effect on the bond strengths of SBMP and PBNT, regardless of the surface moisture condition (P > 0.05). Conversely, reduced bond strengths were observed after oxalate treatment for SB in both moisture conditions, that being significantly lower when using a dry-bonding procedure (P < 0.05). Lower bond strength was obtained for PBNT when a dry-bonding technique was used, regardless of the oxalate treatment (P < 0.05). After aging the specimens for 1 year, bond strengths decreased. Smaller reductions were observed for SBMP, regardless of moisture conditions. For the WB technique, smaller reductions after 1 year were observed without oxalate treatment for SB and after oxalate treatment for PBNT. (Am J Dent 2010;23:137-141).

HYPERZINCEMIA FROM INGESTION OF DENTURE ADHESIVES

The purpose of this article is to review the recent literature that documents the serious adverse systemic effects of prolonged, excessive zinc ingestion from the overuse of denture adhesives. This condition causes elevation of serum zinc levels that result in depression of serum copper. The low serum copper levels cause bone marrow depression and widespread sensory and motor neuropathies. Epidemiologic studies revealed the source of excessive zinc intake to be from overuse of denture adhesives. Denture patients must be advised of the risks of prolonged overuse of denture adhesives. (J Prosthet Dent 2010;103:380-383)

Experimental Surgical and Orthodontic Extrusion of Teeth in Dogs

The purpose of this study was to evaluate histologically the root surfaces of teeth submitted to orthodontic and surgical extrusion procedures in a dog model. Eighteen adult male dogs, divided into six groups of three dogs each, were used in the study Each animal underwent two procedures: rapid orthodontic extrusion and surgical extrusion of the maxillary lateral incisors. The animals were sacrificed to produce samples at 7, 14, 45, 90, 120, and 180 days after surgery for assessment of cross sections of the coronal, medial, and apical thirds of the treated teeth. At early time points, some active surface and inflammatory resorption was observed exclusively in the surgical extrusion group; however, samples collected at later times demonstrated functional repair of the resorption gaps in both groups. Ankylosis was observed as a minor event and was apparently of a transient nature in samples of the surgical extrusion group. The results demonstrate the importance of maintaining the periodontal ligament and cementum surface; both are vital for the prevention of root resorption. It may be postulated that orthodontic extrusion is more conservative and physiologic than surgical extrusion; however the results showed that function was restored in both groups. (Int J Periodontics Restorative Dent 2009;29:435-443.)

Cytotoxicity of resin-based light-cured liners

Purpose: To evaluate the cytotoxic effects of resin-based light-cured liners on culture of pulp cells. Methods: Discs measuring 4 mill in diameter and 2 mm thick were fabricated from TheraCal (TCMTA), Vitrebond (VIT), and Ultrablend Plus (UBP). These specimens were immersed in serum-free culture medium (DMEM) for 24 hours or 7 days to produce the extracts. After incubating the pulp cells for 72 hours, the extracts were applied on the cells and the cytotoxic effects were determined based on the cell metabolism (MTT), total protein expression and cell morphology (SEM). In the control group, fresh DMEM was used. Data from MTT analysis and protein expression were submitted to Kruskal-Wallis and Mann-Whitney tests at the preset level of significance of 5%. Results: When in contact with the 24-hour extract, TCMTA, VIT, and UBP decreased the cell metabolism by 31.5%, 73.5% and 71.0%, respectively. The total protein expressed by the cells in contact with VIT and UBP was lower than TCMTA and DMEM (Mann-Whitney, P< 0.05). When in contact with the 7-day extract, TCMTA, VIT, and UBP decreased the metabolic activity by 45.9%, 77.1% and 64.4%, respectively. All the liners expressed statistically lower amounts of proteins when compared to the control. A reduction in the number of cells was observed for all liners. The remaining cells from TCMTA group resembled those from the control group while for VIT and UBP the cells presented significant morphological alterations. (Ani J Dent 2009;22:137-142).

A Combined Regenerative Approach for the Treatment of Aggressive Periodontitis: Long-term Follow-up of a Familial Case

This article reports the longitudinal follow-up of a familial case of aggressive periodontitis treated by a combined regenerative approach that consisted of root conditioning, bone grafting, and membrane positioning. Treatment resulted in attachment level gain, reduction of probing depth, absence of bleeding on probing, and complete bone filling of the defect. The short-term results obtained after surgery were maintained after 6 years, suggesting that the combined regenerative approach is able to completely arrest the disease with long-term stability. (Int J Periodontics Restorative Dent 2009; 29: 69-79.)

Robust parameter settings of evolutionary algorithms for the optimisation of agricultural systems models

Numerical optimisation methods are being more commonly applied to agricultural systems models, to identify the most profitable management strategies. The available optimisation algorithms are reviewed and compared, with literature and our studies identifying evolutionary algorithms (including genetic algorithms) as superior in this regard to simulated annealing, tabu search, hill-climbing, and direct-search methods. Results of a complex beef property optimisation, using a real-value genetic algorithm, are presented. The relative contributions of the range of operational options and parameters of this method are discussed, and general recommendations listed to assist practitioners applying evolutionary algorithms to the solution of agricultural systems. (C) 2001 Elsevier Science Ltd. All rights reserved.

A 24-month randomized clinical trial of a two- and three-step etch-and-rinse technique

Purpose This 24-month randomized paired tooth clinical study evaluated the performance of All Bond 3 used in the simplified (2-step) and full (3-step) versions Methods 33 patients, with at least two similar sized non-carious cervical lesions participated in this study A total of 66 restorations were placed, half using the 2-step All Bond 3 (AB3-2) and the other half using 3-step All Bond 3 (AB3-3) The restorations were placed incrementally using the composite resin Aelite The restorations were evaluated at baseline and after 6, 12 and 24 months following the modified USPHS criteria Statistical differences between the adhesive were tested using with McNemar`s test and clinical performance over time for each material with the Fisher`s exact test (alpha= 0 05) Results After 24 months, six AB3-2 and four AB3-3 were rated as bravo for marginal discoloration but did not differ from each other significantly (P> 0 05) The retention rates at 24 months of AB3-2 and AB3-3 were 90 9% and 97 0%, respectively (P> 0 05) (Am J Dent 2010,23 231-236)

Direct and transdentinal antibacterial activity of chlorhexidine

Purpose: To evaluate the antibacterial effect of different chlorhexidine (CHX) concentrations against Streptococcus mutans using the agar-diffusion method with and without human dentin discs placed between the bacteria and the test substances. Methods: For the direct application (agar-well technique), a base layer containing 15 mL of BHI agar and 300 mu L. of S. mutans inoculum (10(9) cfu/mL) was prepared in Petri dishes. Six wells per dish were made at equidistant points and immediately filled with CHX gels (0.12%, 0.2%, 1% and 2%), 35% phosphoric acid and pure natrosol (n=6 wells/substance). Paper discs soaked in sterile distilled water served as control group (n=6). For the indirect application (transdentinal diffusion), 0.2 mm- and 0.5 mm-thick human dentin discs (36 discs/thickness) had the hydraulic conductance determined, which allowed the homogeneous allocation of them to the experimental and control groups. The discs were placed at equidistant points on the Petri dishes containing BHI with the S. mutans inoculum (six discs per dish; one per substance) with the pulpal side in contact with the bacteria. In the discs treated with CHX gels, dentin surface was etched with H(3)PO(4) and rinsed with distilled water before CHX gel application for 1 minute. After both direct and indirect application, the dishes were incubated for 24 hours and the bacterial growth inhibition zones formed around the wells and dentin discs were measured. Data were analyzed statistically by the non-parametric Kruskal-Wallis and Mann-Whitney tests at 5% significance level. Results: In the direct test, all CHX concentrations presented a dose-dependent antibacterial activity against S. mutans. In the indirect test, there were statistically significant differences (P< 0.05) among all groups and the largest microbial growth inhibition zones were observed when 2% CHX was applied on 0.2 mm-thick discs (P< 0.05). It was concluded that all evaluated CHX gels exhibited both direct and transdentinal antibacterial activity against S. mutans. This effect of CHX was strongly influenced by the CHX concentration as well as the dentin barrier thickness. (Am J Dent 2010;23:255-259).