Evaluation of mineral trioxide aggregate and calcium hydroxide cement as pulp-capping agents in human teeth

This study evaluated the histomorphologic response of human dental pulps capped with mineral trioxide aggregate (MTA) and Ca(OH)(2) cement (CH). Pulp exposures were performed on the occlusal floor of 40 human permanent premolars. After that, the pulp was capped either with CH or MTA and restored with composite resin. After 30 and 60 days, teeth were extracted and processed for histologic exam and categorized in a histologic score system. The data were subjected to Kruskal-Wallis and Conover tests (alpha = .05). All groups performed well in terms of hard tissue bridge formation, inflammatory response, and other pulpal findings. However, a lower response of CH30 was observed for the dentin bridge formation, when compared with MTA30 and MTA60 groups. Although the pulp healing with calcium hydroxide was slower than that of MTA, both materials were successful for pulp capping in human teeth.

Human pulp response after an adhesive system application in deep cavities

Objectives: To evaluate the pulpo-dentin complex response to a dentin adhesive application in deep cavities performed in human teeth.Methods: Deep class V cavities were prepared on the buccal surface of 46 premolars. The remaining dentin of the axial wall received 10% phosphoric acid and dentin adhesive (group DA), or was protected before the acid and dentin adhesive application with calcium hydroxide cement (group CH). Half of the teeth, which received the acid application directly over the axial wall, were contaminated prior to the procedures with dental plaque collected from the patient's own teeth (group DAC). The plaque was placed on the dentin for 5 min and then the cavity was washed. All teeth were restored with a light-cured composite resin. The teeth were extracted after 7, 30 or 60 days and prepared according to normal histologic techniques. Serial sections were stained with WE, Masson's trichrome and Brown & Brenn technique for demonstration of bacteria.Results: the histopathologic evaluation showed that in groups DA and DAC, the inflammatory response was more evident than in group CH. Also, the intensity of the pulp reaction increased as the remaining dentin thickness decreased. There was no statistical difference in the inflammatory response between the groups DA and DAC.Conclusion: Based on the experimental conditions, we concluded that the All Bond 2 adhesive system, when applied on dentin in deep cavities, showed an acceptable biocompatibility. However, the intensity of the pulpo-dentin complex response depends on the remaining dentin thickness. (C) 1999 Elsevier B.V. Ltd. All rights reserved.

Effect of Ultrasonic Excitation on the Porosity of Glass Ionomer Cement: A Scanning Electron Microscope Evaluation

Background: Ultrasonic excitation (US) was applied to glass ionomer cement (GIC) during early set time to increase the advantageous properties of this material. Purpose: The aim of this in vitro study was to assess the inner porosity of GIC after US. Study design: A total of 16 specimens, for each material, were prepared from high-viscosity GIC Fuji IX GP, Ketac Molar, and Ketac Molar Easymix. Half of these specimens (n = 8) received 30 s of US during the initial cement setting. After completion of the material setting, specimens were fractured and observed by scanning electronic microscopy to quantitatively assay porosity inside the material using Image J software. Results: Statistical data analysis revealed that US reduced the porosity for all tested materials (P <= 0.05). The following reductions (expressed in percentages) were achieved: Fuji IX-from 3.9% to 2.8%; Ketac Molar Easy Mix-from 4.4% to 2.6%, and Ketac Molar-from 2.4% to 1.6%. Conclusion: Under the tested conditions, US was an effective method for porosity reduction inside the material. Microsc. Res. Tech. 74:54-57, 2011. (C) 2010 Wiley-Liss, Inc.

Influences of the insertion method in glass ionomer cement porosity

The aim of this study was to evaluate the presence of porosities inside the glass ionomer cement (GIC) after different techniques of material insertion. MATERIAL and METHOD: Specimens were prepared with high-viscosity GIC Ketac Molar Easymix and divided into three groups according to the insertion method: spatula (PI), Centrix injector (CI), and low-cost syringe (LCS). The specimens were fractured and observed with scanning electronic microscopy to quantitatively evaluate porosity inside the material using Image J Software. RESULTS: Statistical analysis, ANOVA application, and Tukey test to significance level of 5%, revealed that there was no statistical difference between the groups. CONCLUSION: Although the use of LCS has not decreased the porosity of the material, this insertion method is easy, accessible, and low cost, which makes it a viable alternative of use in the ART technique and in others bucal health programs. Microsc. Res. Tech., 2012. (c) 2012 Wiley Periodicals, Inc.

Influence of the activation mode of a self-etch resin-based luting cement upon the metabolism of odontoblast-like cells

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Mechanical and biological characterization of resin-modified glass-ionomer cement containing doxycycline hyclate

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Utilization of autogenous bone, bioactive glasses, and calcium phosphate cement in surgical mandibular bone defects in Cebus apella monkeys

Purpose: the purpose of the present study was to evaluate the histologic results of bone cavities that were surgically created in the mandibles of Cebus apella monkeys and filled with autogenous bone, PerioGlas, FillerBone, or Bone Source. Materials and Methods: Surgical cavities 5 mm in diameter were prepared through both mandibular cortices in the mandibular angle region. The cavities were randomly filled, and the animals were divided into groups according to the material employed: Group 1 cavities were filled with autogenous corticocancellous bone; group 2 cavities were filled with calcium phosphate cement (BoneSource); and group 3 and group 4 cavities were filled with bioactive glass (FillerBone and PerioGlas, respectively). After 180 days the animals were sacrificed, and specimens were prepared following routine laboratory procedures for hematoxylin/eosin staining and histologic evaluation. Results: the histologic analysis showed that autogenous bone allowed total repair of the bone defects; bioactive glasses (FillerBone and PerioGlas) allowed total repair of the defects with intimate contact of the remaining granules and newly formed bone; and the cavities filled with calcium phosphate cement (BoneSource) were generally filled by connective fibrous tissue, and the material was almost totally resorbed. Discussion: the autogenous bone, FillerBone, and PerioGlas provided results similar to those in the current literature, showing that autogenous bone is the best Choice for filling critical-size defects. Synthetic implanted materials demonstrated biocompatibility, but the bioglasses demonstrated osteoconductive activity that did not occur with calcium phosphate (BoneSource). Conclusion: According to the methodology used in this study, it can be concluded that the utilization of autogenous bone and bioactive glasses permitted the repair of surgically created critical-size defects by newly formed bone; the synthetic implanted materials demonstrated biocompatibility, and the bioactive glasses demonstrated osteoconductive activity. The PerioGlas was mostly resorbed and replaced by bone and the remaining granules were in close contact with bone; the FillerBone showed many granules in contact with the newly formed bone; BoneSource did not permit repair of the critical-size defects, and the defects were generally filled by connective fibrous tissue.

Cytotoxicity of Portland Cement with Different Radiopacifying Agents: A Cell Death Study

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Biocompatibility of a resin-modified glass-ionomer cement applied as pulp capping in human teeth

Purpose: to evaluate the human pulp response following pulp capping with calcium hydroxide (CI-I, Group 1), and the resin-modified glass-ionomer Vitrebond (VIT, Group 2). Materials and Methods: Intact teeth with no cavity preparation were used as control Group (ICG, Group 3). Buccal Class V cavities were prepared in 34 sound human premolars. After exposing the pulps, the pulp capping materials were applied and the cavities were Filled using Clearfil Liner Bond 2 bonding agent and Z100 resin-based composite. The teeth were extracted after 5, 30, and from 120 to 300 days, fixed in 10% buffered formalin solution, and prepared according to routine histological techniques. 6-mu m sections were stained with hematoxylin and eosin, Masson's trichrome, or Brown gr Brenn technique for bacterial observation. Results: At 5 days, CH caused a large zone of coagulation necrosis, the mononuclear inflammatory reaction underneath the necrotic zone was slight to moderate. VIT caused a moderate to intense inflammatory pulp response with a large necrotic zone. A number of congested venules associated with plasma extravasation and neutrophilic infiltration was observed. Over time, only CH allowed pulp repair and complete dentin bridging around the pulp exposure site. VIT components displaced into the pulp tissue triggered a persistent inflammatory reaction which appeared to be associated with a lack of dentin bridge formation. After 30 days a few histological sections showed a number of bacteria on the lateral dentin walls. In these samples the pulp response was similar to those samples with no microleakage. VIT was more irritating to pulp tissue than CH, which allowed pulp repair associated with dentin bridge formation. These results suggested that VIT is not an appropriate dental material to be used in direct pulp capping for mechanically exposed human pulps.

Human pulp response to resin cements used to bond inlay restorations

Objective. The aim of this study was to evaluate the pulp response following cementation of inlays using two different resin cements.Methods. Deep Class V cavities were prepared on the buccal surface of 34 sound human premolars. impressions were taken and inlays were prepared which were cemented with the following luting materials-Group 1: Rely X(TM) Unicem. (3M ESPE); Group 2: Variolink(R) II (Ivoclar Vivadent). in Group 3 (control), after lining the cavity floor with Dycal(R) (Dentsply Caulk) the inlays were cemented with Rely X(TM) Unicem. Four additional teeth were used as an intact control group. For Variolink(R) II, the adhesive system Excite was used as part of the cementation procedure. After 7 or 60 days, the teeth were extracted and processed for histological assessment.Results. At 7 days, Rely X(TM) Unicern and Variolink(R) II system triggered in two samples a mild and moderate inflammatory response, respectively. At 60 days, the pulpal response decreased for both groups. A discrete persistent inflammatory response occurred in Group 2 in which displacement of resin components across the dentin tubules was observed. In the control group, normal histological characteristics were observed. The inflammatory response and tissue disorganization were related to the remaining dentin thickness between the cavity floor and the pulp tissue.Significance. Techniques for inlay cementation using distinct luting cements may cause specific pulpal damage. Variolink(R) II associated with the adhesive system Excite cause more aggressive effects to the pulp-dentin complex than Rely X(TM) Unicern cement when both are used to cement inlay restorations. (C) 2005 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

EFFECT of DIFFERENT AIRBORNE-PARTICLE ABRASION/BONDING AGENT COMBINATIONS on THE BOND STRENGTH of A RESIN CEMENT TO A BASE METAL ALLOY

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Efficacy of Air-abrasion Technique and Additional Surface Treatment at Titanium/Resin Cement Interface

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influence of Er,Cr: YSGG laser on bond strength of self-adhesive resin cement

The purpose of this study was to investigate the bond strength of fiber post previously laser treated root canals. Forty single-rooted bovine teeth were endodontically treated, randomly and equally divided into two main groups according to the type of pretreatment: G1: 2.5% NaOCl (control group); and G2: Er,Cr:YSGG laser. Each group was further subdivided into 2 groups based on the category of adhesive systems/ luting materials used: a: an etch-and-rinse resin cement (Single Bond/RelyX ARC; 3M ESPE), and b: a self-adhesive resin cement (Rely X Unicem; 3M ESPE). Three 1.5 mm thick slabs were obtained per root and the push-out test was performed at a crosshead speed of 0.5 mm/min until post dislodgement occurred. Data were analyzed by ANOVA and post-hoc Tukey's test at a pre-set alpha of 0.05. Analysis of variance showed no statistically significant difference (p > 0.05) among the groups G1a (25.44 ± 2.35) and G1b (23.62 ± 3.48), G2a (11.77 ± 2.67) and G2b (9.93 ± 3.37). Fractures were observed at the interface between the dentin and the resin in all groups. The Er,Cr:YSGG laser irradiation did not influence on the bond strength of the resin cements and the etch-and-rinse resin cement had better results on bond strength than self-adhesive resin cement.

Radiographic effect of different radiopacifiers on a potential retrograde filling material

Objective. The objective of this study was to evaluate the radiopacity of white Portland cement (PC) associated with bismuth oxide (Bi(2)O(3)), barium sulfate (BaSO(4)), iodoform (CHI(3)), and zirconium oxide (ZrO(2)). White mineral trioxide aggregate (WMTA) and PC without radiopacifier were used as positive and negative controls, respectively.Study design. Following International Organization for Standardization (ISO) 6876/2001, 5 circular specimens (10 x 1 mm) were made from each material. After the materials set, radiographs were taken using occlusal film and a graduated aluminum step-wedge varying in thickness from 2 to 16 mm. The dental X-ray unit (GE1000) was set at 50 Kvp, 10 mA, 18 pulses/s, and distance of 33.5 cm. The radiographs were digitized, and radiopacity was compared with the aluminum step-wedge, using Wixwin-2000 software (Gendex). Data (mm Al) were analyzed using analysis of variance and Tukey tests.Results. The PC + Bi(2)O(3) and WMTA samples presented greater radiopacity (5.88 and 5.72 mm Al, respectively), followed by PC + ZrO(2) (3.87 mm Al) and PC + CHI(3) (3.50 mm Al). The PC + BaSO(4) and PC samples presented the lowest radiopacity values (2.35 and 1.69 mm Al, respectively), which were below the minimum value recommended by the ISO.Conclusion. Analysis of the present results led to the conclusion that all of the materials tested presented acceptable radiopacity, except PC + BaSO(4) and pure PC. (Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2009; 108: 628-632)