Poly(vinyl methyl ether) poly(methyl methacrylate) blends using diblock copolymer of styrene and methyl methacrylate as compatibilizer

Blends of poly(vinyl methyl ether) (PVME) and poly(methyl methacrylate) (PMMA) compatibilized by poly(styrene-block-methyl methacrylate) (P(S-b-MMA)) ale studied by FT-IR, DSC, excimer fluorescence spectrometry, and scanning electron microscopy (SEM). In FT-IR measurement the ratio of absorption intensity at 1107 cm(-1) to that at 1085 cm(-1) (I-1107/I-1085) reaches a minimum at about 10wt% block copolymer content. DSC results show that the glass transition temperature of PVME in the blends has a maximum at 10 wt% copolymer content. In plots of the ratio of excimer-to-monomer fluorescence emission intensities (I-E/I-M) VS block copolymer content, I-E/I-M increases rapidly above 10%. Ail these phenomena show that PS block chains penetrate into PVME: domains on addition of block copolymer. Above 10% copolymer content, block copolymer chains tend to form micelles in bulk phase.

Effect of gamma-irradiation on brittle-tough transition of PBT/EPDM blends

Irradiation can be applied to crosslink the dispersed elastomer phase to increase the modulus and decrease the voiding ability of the elastomer, which results in increasing critical brittle-tough transition elastomer content at constant temperature. The experimental results show that at 25 degrees C the critical elastomer content of EPDM shifts to higher composition (shift of about 4 wt%) for PBT/EPDM blends after 100 kGy gamma-irradiation. (C) 1997 Elsevier Science Ltd.

The miscibility of homopolymer random copolymer blends .3. Blends of SAA with polymethacrylates and polyesters

The miscibility of blends of poly(styrene-co-allyl alcohol) (SAA) with poly(methyl methacrylate) (PMMA), poly(ethyl methacrylate) (PEMA), poly(n-butyl methacrylate) (PnBMA), poly-epsilon-caprolactone (PCL) or polycarbonate (PC) has been studied by means of NMR, FT-IR and DSC techniques. It was found that SAA and PMMA, PEMA or PCL form miscible blends and SAA is only partially miscible with PC or PnBMA. Both phenyl groups and hydroxyl groups in SAA are involved in the intermolecular interactions between SAA and PMMA, PEMA or PCL. Also the hydroxyl-carbonyl hydrogen bonds existing in all the miscible blends studied are formed partially at the expense of the disruption of self-association of hydroxyl groups in pure SAA. (C) 1997 Elsevier Science Ltd. All rights reserved.

Morphology, thermal behavior, and mechanical properties of PA1010/PP and PA1010/PP-g-GMA blends

The modification of polypropylene (PP) was accomplished by melt grafting glycidyl methacrylate (GMA) on its molecular chains. The resulting PP-g-GMA was used to prepare binary blends of polyamide 1010 (PA1010) and PP-g-GMA. Different blend morphologies were observed by scanning electron microscopy (SEM) according to the nature and content of PA1010 used. Comparing the PA1010/PP-g-GMA and PA1010/PP binary blends, the size of the domains of PP-g-GMA were much smaller than that of PP at the same compositions. It was found that mechanical properties of PA1010/PP-g-GMA blends were obviously better than that of PA1010/PP blends, and the mechanical properties were significantly influenced by wetting conditions for uncompatibilized and compatibilized blends. A different dependence of the flexural modulus on water was found for PA1010/PP and PA1010/PP-g-GMA. These behaviors could be attributed to the chemical interactions between the two components and good dispersion in PA1010/PP-g-GMA blends. Thermal and rheological analyses were performed to confirm the possible chemical reactions taking place during the blending process. (C) 1997 John Wiley & Sons, Inc.

Study of the miscibility and thermodynamics of cellulose diacetate-poly(vinyl pyrrolidone) blends

The miscibility of blends of cellulose diacetate (CDA) and poly(vinyl pyrrolidone) (PVP) was extensively studied by means of differential thermal analysis and dynamic mechanical thermal analysis, tensile test, measuring viscosity of diluted and concentrated solutions of blends in acetone-ethanol mixture and morphological observations. A single glass transition temperature is observed, which is intermediate between the glass transition temperatures associated with each component and depends on composition. A synergism in mechanical properties of blends was found. The absolute viscosity and the intrinsic viscosity of solutions of blends are much higher than the weight average values of solutions of CDA and PVP. Optically clear and thermodynamically stable films were formed in the composition range of CDA/PVP = 100/0 to 50/50w/w. Fourier transform infrared was used to investigate the nature of CDA-PVP interaction. Hydrogen bonds were formed between hydroxyl groups of CDA and carbonyl groups of PVP. Heats of solutions of CDA/PVP blends and their mechanical mixtures were measured by using a calorimeter. Mixing enthalpy obtained with Hess's law approach was used to quantify interaction parameters of this blending system. It was found that mixing enthalpies and interaction parameters were negative and composition dependent. (C) 1997 Elsevier Science Ltd.

Crystallization and intriguing morphologies of compatible mixtures of tetrahydrofuran-methyl methacrylate diblock copolymer with poly(tetrahydrofuran)

The crystallization and unusual crystalline morphologies of compatible mixtures of tetrahydrofuran-methyl methacrylate diblock copolymer with tetrahydrofuran homopolymer were studied. It is shown that the PTHF [poly(tetrahydrofuran)] block of the copolymer cocrystalizes with the PTHF homopolymer in the PTHF microphase of the blend. However, the degree of crystallinity of the PTHF block is always lower than that of the PTHF homopolymer in the PTHF microphase. The crystallizability of the PTHF microphase increases appreciably with increasing PTHF microphase size and PTHF homopolymer weight fraction in the microphase. The morphology study of the blends shows that the crystalline morphology is strongly dependent on blend composition, copolymer composition and PTHF block length, as well as crystallization temperature. When alternating PTHF and PMMA [poly(methyl methacrylate)] lamellae are formed, the macroscopic crystalline morphology could be only observed when the thickness of the PTHF lamellae is large enough (similar to 20 nm). In the blend where PMMA spherical or cylindrical microphases are formed, the crystalline morphology changes dramatically with the change in the PTHF microdomain size and PMMA interdomain distance. Many unusual crystalline morphologies have been observed. A study of the solution-crystallized morphology of the blends at different temperatures shows that the morphology is also strongly dependent on the isothermal crystallization temperature, suggesting that the PMMA microdomains may have different effects on the morphology formation when the blend is crystallized at different rates.

Study on the structure and miscibility of PBPI-E/PTI-E blends

The crystallization, miscibility and structure of polyimide PBPI-E/PTI-E blends were studied by DSC, DMA, NMR and fluorescence techniques, where PBPI-E is a biphenyldianhydride-based polyimide, and PTI-E is a polyimide from 4,4'-thiodiphthalic anhydride and 4,4'-oxydianiline. The results obtained show that PBPI-E/PTI-E blends are miscible at a molecular level for all the compositions studied. However, the glass transition temperature of the blends is well below the value predicted by the Fox equation, and the blends are not stable at high temperature, i.e. phase separation will occur when the blends are annealed about T-g. Moreover, the melting point T-m, differential enthalpy Delta H and spin-lattice relaxation time T-l(c) of the blends increase with the annealing time. (C) 1997 Elsevier Science Ltd. All rights reserved.

Interaction characterization of PA1010/PP blends using PP-g-AA as compatibilizer

The morphology of polyamidelOlO/polypropylene blends was found to significantly depend upon the concentration of the compatibilizer[polypropylene-grafted-acrylic acid (PP-g-AA)]. A significant reduction in phase size was observed because of the interaction that existed between the PP-g-AA and polyamide. These interactions have been confirmed by several methods. The tensile mechanical properties and impact behavior of the prepared blends were investigated and correlated with scanning electron microscope (SEM) analysis of the fracture surfaces. It was found that PP-g-AA as the compatibilizer has a profound effect upon the properties of the blends. This behavior is attributed to a series of chemical and physico-chemical interactions taking place between the two components.

Study on the beta relaxation mechanism of thermosetting polyimide thermoplastic polyimide blends

The thermosetting polyimide PMR-I5 and its blends with thermoplastic polyimides have been studied by dynamic mechanical analysis. The results obtained indicate that the level of beta relaxations in PMR-15 are increased with an increase in cross-linking density. This phenomenon is interpreted as a change of chemical structure during the cross-linking process. Addition of thermoplastic polyimide makes the magnitude of beta relaxations increase when PMR-15 is the major component. This might be due to the strong intermolecular charge-transfer interaction between PI and PI or PMR-15 and PMR-15 molecular chains being partly replaced by the weak intermolecular interaction between PI and PMR-15 in PMR-15/PI blends, resulting in some phenylene rings or imide groups in PIs and PMR-15 chains being able to participate in beta relaxation. However, this increment in beta relaxation magnitude can be reduced by heat treatment of the sample, as a result of phase separation. Hence, it is concluded that the beta relaxation magnitude is determined by the number of groups which can participate in relaxation per unit length, i.e. the magnitude of beta relaxation increases with decreasing interaction between the molecular chains. Copyright (C) 1996 Elsevier Science Ltd

The miscibility of homopolymer random copolymer blends .4. Poly(vinylidene chloride-co-acrylonitrile) poly(methyl methacrylate) blends

The miscibility of blends of poly(vinylidene chloride-co-acrylonitrile) (VDC-AN) and poly(methyl methacrylate) (PMMA) has been studied with DSC, FT-IR, and NMR methods. The results indicate that the VDC-AN/PMMA blends are miscibile on a molecular level, and the dipole-dipole interactions between C=O and C-Cl-2 and/or interpolymer hydrogen bondings between COOCH3 and CN and CCl groups play the role on the miscibility of the blends. It is found that the -CCl2- groups have two different chemical environments in the pure VDC-AN copolymer, which may result from the different configurations of the copolymer, such as -CCl2- groups in the ''alternating'' segments and -CCl2- groups in the ''blocky'' segments as proposed. It is the -CCl2- group in the ''alternating'' segment that takes part in the dipole-dipole interaction with C=O group in PMMA.

Properties of ethylene-propylene copolymer/PA-1010 blends using ethylene-propylene copolymer-graft-acrylic acid as a compatibilizing agent

The modification of ethylene-propylene copolymer (EP) has been accomplished by radical EP-graft-acrylic acid (EP-g-AA) has been used to obtain ternary PA/EP/EP-g-AA blends by melt mixing. Different blend morphologies were observed by scanning electron microscopy; the domain size of the EP-dispersed phase in the polyamide 1010 matrix of compatibilized blends decreased compared with that of uncompatibilized blends. It is found that EP-g-AA used as the third component has a profound effect on the mechanical properties of the resulting blends. This behavior has been attributed to serious chemical interactions taking place between the two components. Thermal analysis shows that some thermal properties of PA in compatibilized PA/EP/EP-g-AA changed because of chemical reactions taken place during the blending process. Wide angle x-ray diffraction measurements also confirmed this result. (C) 1996 John Wiley & Sons, Inc.

Miscibility of poly(ether ether ketone)/poly(ether diphenyl ether ketone) blends

Poly(ether ether ketone) and poly(ether diphenyl ether ketone) homopolymers are prepared by nucleophilic substitution routes. Miscibility of PEEK/PEDEK blends has been studied by wide-angle X-ray diffraction (WAXD) and differential scanning calorimetry (d.s.c.). The results indicate that for PEEK/PEDEK blends, when the PEDEK content (weight fraction) is greater than 0.20 and less than 0.75, PEEK and PEDEK components form independent crystalline regions, i.e. they are immiscible; when the PEDEK content is in the range W-PEDEK less than or equal to 0.20 or greater than or equal to 0.75, a rich PEEK- or PEDEK-rich content crystallizes from a mixed melt and PEEK and PEDEK are miscible. Copyright (C) 1996 Elsevier Science Ltd.

Studies on morphology and crystallization of polypropylene/polyamide 12 blends

Scanning electron microscopy (SEM) and an image analyser are used to study morphologies of the fractured surface, etched by hot phenol, of polypropylene/maleated polypropylene/polyamide 12 PP/PP-MA/PA12) = 65/10/25 blend and PP-MA/PA12 = 75/25 blend. The particle dimension and its distribution of PA12 dispersed phase in these blends are much lower and narrower than that of the PP/PA12. blends. Especially, most of the particles in the PP-MA/PA12 = 75/25 blend are smaller than 0.1 mu m. The effect of the morphology of PP/PA12 blends on their crystallization behaviour is studied using differential scanning calorimetry and SEM. PA12 dispersed phase coarsens during annealing in the PP/PP-MA/PA12 = 65/10/25 blend. The mechanism of coarsening of the PA12 dispersed phase is a coalescence process. The intense mixing between the PP component and the PA12 component through reaction of PP-MA and PA12 leads to a change of dynamic mechanical behaviour of the components. A separation method is used to separate the polyolefin parts (precipitated from hot phenol), from PA12 parts (hot phenol filtrate). Of PP/PP-MA/PA12 = 65/10/25 blend, infra-red measurements and elementary analysis show that the precipitate has a lower PA12 content than the feed, whereas the filtrate has a higher PA12 content. From PP-MA/PA12 = 75/25 blend, PA12 contents in the precipitate and the filtrate are the same as in the feed. This implies that all PA12 has reacted with all PP-MA in the latter case while not in the former case. Using the method of interface exposure, interfacial reaction of PP-MA with PA12 is studied by X-ray photoelectron spectrometry (X.p.s.). Copyright (C) 1996 Elsevier Science Ltd.

Miscibility and crystallization behaviour of poly(ether ether ketone)/polyimide blends

The miscibility and crystallization behaviour of the blends of poly(ether ether ketone) (PEEK) with two thermoplastic polyimides (PI), PEI-E and YS-30, prepared by solution blending were studied by the use of small-angle X-ray scattering (SAXS), differential scanning calorimetry (d.s.c.) and polarizing microscopy techniques. The results obtained show that PEEK/YS-30 is miscible, while PEEK/PEI-E is partially miscible only in the composition range with PEI-E content up to 20 wt%. The crystallization behaviour of PEEK in PEEK/PI blends depends on the crystallization condition of the blend sample as well as the chemical structure and the content of the PI added. Our SAXS results indicate that the segregation of PI molecular chains during crystallization of PEEK chains in the blends is interfibrillar for PEEK/PEI-E blends, but interlamellar for PEEK/YS-30 blends. The compatibility and the crystallization behaviour are discussed in terms of charge transfer interaction between PI and PI molecules and between PI and PEEK molecules.

Miscibility, crystallization, and morphology studies of thermosetting polyimide PMR-15/PEK-C blends

Miscibility, crystallization, and mechanical properties of blends of thermosetting polyimide PMR-15 and phenolphthalein poly(ether ketone) (PEK-C) were examined. With the exception of the 90/10 blend, which has two glass transition peaks, all the blends with PMR-15 less than 90 wt % are miscible in the amorphous state according to DMA results. Addition of PEK-C hindered significantly the crystallization of PMR-15, indicating that there must exist some kind of interaction between molecular chains of PMR-15 and those of PEK-C. The semi-IPN system of PMR-15/PEK-C blends exhibits good toughness. Two distinct microphases, interweaving at the phase boundaries, were found in the PMR-15/PEK-C 60/40 blend. The toughness effect of the blends is discussed in terms of the interface adhesion between the two distinct phases and the domain sizes of the phases. The relation between miscibility and toughness of the blends was investigated. (C) 1996 John Wiley & Sons, Inc.