alpha-SiAlON ceramics with elongated grain morphology using an alternative sintering additive

In this work, the use of a natural yttrium oxide and rare earth oxide solid solution (CRE2O3) as stabilizers of the alpha-Si3N4 phase to form alpha-SiAlON has been investigated. This oxide mix is produced at FAENQUIL-DEMAR, at a cost of only 20% of pure commercial Y2O3. Two alpha-SiAlONs using pure Y2O3 or CRE2O3 have been prepared, using mixes of 20% by volume of a molar fraction of 9:1 of AlN to Y2O3 or AlN to CRE2O3, respectively, with 80% alpha-Si3N4. Samples were gas pressure-sintered at 1900 degreesC, under 1.5 MPa of N-2 for 60 min. Both compositions yielded alpha-SiAlON ceramics with high relative densities (98% t.d.), hardness of 18 GPa and fracture toughness of 5 Mpa m(1/2), with homogeneous microstructures composed of elongated alpha-SiAlON grains with aspect ratios of 5. It is concluded that the mixed rare earth concentrate (CRE2O3) can be used to produce alpha-SiAlON ceramics with similar microstructures and mechanical properties of alpha-SiAlON ceramics fabricated using pure Y2O3, but with the advantage of its lower production cost. (C) 2004 Elsevier B.V All rights reserved.

Influence of simultaneous addition of MnO2 and CoO on properties of SnO2-based ceramics

This paper reports on a study of the: effect of replacing CoO by MnO2 on the sintering and electrical propel-ties of the 98.95% SnO2 + (1 - x)% CoO + x% MnO2 + 0.05% Ta2O5 system. All the samples were compacted into pellets and sintered at 1300 degrees C for 1 h, when they reached densities of about 98% of the theoretical density. An X-ray diffraction (XRD) analysis showed no other detectable phases other than SnO2. Current-voltage characterization indicated varistor behavior in the systems. The non-linear coefficient (alpha) and breakdown electric field (Eb) increased as the amount of MnO2 was increased. The results are explained in terms of an electric barrier modification, due to the presence of adsorbed negative oxygen species at the grain boundary inter face. (C) 2000 Elsevier B.V. B.V. All rights reserved.

Temperature dependence on the electrical properties of Ba(Ti0.90Zr0.10)O-3:2V ceramics

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Electrical Properties of Textured Niobium-Doped Bismuth Titanate Ceramics

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Structure, microstructure and dielectric properties of 100-x(Bi0.5Na0.5)TiO3-x[SrTiO3] composites ceramics

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Structural and spectroscopic study of oxyfluoride glasses and glass-ceramics using europium ion as a structural probe

Transparent oxyfluoride glasses and beta-PbF(2) nanocrystals containing glass-ceramics were prepared with varying Eu(3+) content (0.3, 0.4, 0.5 and 0.6%). The effect of Eu(3+) content on the preparation of glass-ceramics was investigated. From differential scanning calorimetry, the T(x)-T(g)(T(x)-temperature of the onset of crystallization; T(g)-glass transition temperature) parameter for glasses has shown slight variation, and an exothermic peak near T(g) called the ceramization temperature (T(c)) has been observed. Heat treatments were performed at this temperature to obtain transparent glass-ceramics containing beta-PbF(2) nanocrystals, identified by x-ray diffraction. Heat treatments for different periods of time were performed and were observed to be very important in the control of the crystal size and of the crystallization rate. Based upon the absorption spectra, the scattering level due to the presence of beta-PbF(2) nanocrystals in the glass-ceramics was observed to be similar to that for the mother glasses. Detailed analysis of emission spectra and decay time measurements led to the identification of Eu(3+) ions as the beta-PbF(2) crystalline phase. Excitation spectra at 70 K show the interaction of Eu(3+) ions with the fluorogermanate network.

Characterization of dense lead lanthanum titanate ceramics prepared from powders synthesized by the oxidant peroxo method

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Innovating transparent glass ceramics based on Ga2S3-GeS2-CsCl

In this paper, we describe the preparation of glass ceramics in the Ga2S3 - GeS2 - CsCl system Visible and infrared transmitting glass ceramics were reproducibly obtained by appropriated heat treatment of the base glass Crystals with controllable size of about 40 nm were homogeneously generated in the glassy matrix X-ray diffraction characterizations have shown that gallium acts as nucleating agent in this material, giving rise to alpha-Ga2S3 crystals Improved thermo-mechanical properties such as dilatation coefficient and resistance to fracture propagation have been observed in the prepared glass ceramics

Mechanical strength and subcritical crack growth under wet cyclic loading of glass-infiltrated dental ceramics

Objectives. Evaluate the flexural strength (sigma) and subcritical crack growth (SCG) under cyclic loading of glass-infiltrated alumina-based (IA, In-Ceram Alumina) and zirconia-reinforced (IZ, In-Ceram Zirconia) ceramics, testing the hypothesis that wet environment influences the SCG of both ceramics when submitted to cyclic loading.Methods. Bar-shaped specimens of IA (n = 45) and IZ ( n = 45) were fabricated and loaded in three-point bending (3P) in 37 degrees C artificial saliva (IA(3P) and IZ(3P)) and cyclic fatigued (F) in dry (D) and wet (W) conditions (IA(FD), IA(FW), IZ(FD), IZ(FW)). The initial sigma and the number of cycles to fracture were obtained from 3P and F tests, respectively. Data was examined using Weibull statistics. The SCG behavior was described in terms of crack velocity as a function of maximum stress intensity factor (K(Imax)).Results. The Weibull moduli (m = 8) were similar for both ceramics. The characteristic strength (sigma(0)) of IA and IZ was and 466 MPa 550 MPa, respectively. The wet environment significantly increased the SCG of IZ, whereas a less evident effect was observed for IA. In general, both ceramics were prone to SCG, with crack propagation occurring at K(I) as low as 43-48% of their critical K(I). The highest sigma of IZ should lead to longer lifetimes for similar loading conditions.Significance. Water combined with cyclic loading causes pronounced SCG in IZ and IA materials. The lifetime of dental restorations based on these ceramics is expected to increase by reducing their direct exposure to wet conditions and/or by using high content zirconia ceramics with higher strength. (C) 2010 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

The effect of TiO(2) on the microstructural and electrical properties of low voltage varistor based on (Sn,Ti)O(2) ceramics

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Structural and dielectric properties of Ba0.5Sr0.5(SnxTi1-x)O-3 ceramics obtained by the soft chemical method

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Structural and dielectric relaxor properties of yttrium-doped Ba(Zr0.25Ti0.75)O-3 ceramics

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Mechanochemical synthesis of lead magnesium niobate ceramics in iron media

The possibility of mechanochemical synthesis of the lead magnesium niobate (PMN) powders of the composition Pb(Mg(1/3)Nb(2/3))O(3) in iron vials was investigated. According to X-ray and energy-dispersive spectroscopy (EDS) analysis of the obtained powder mixtures, milling in iron vials resulted in incorporation of Fe and formation of PFN of composition Pb(Fe(1/2)Nb(1/2))O(3) simultaneously with formation of PMN. Relative amounts of PMN and PFN were determined based on values of Curie temperature and lattice constant of perovskite phase. Although only 1 wt pct of Fe was incorporated, a stoichiometry of the system was significantly changed, resulting in formation of pyrochlore phase and excess MgO. Single-phase perovskite was obtained when the excess of PbO and Nb(2)O(5) was added during mechanochemical synthesis. Because the dielectric properties were worse than expected, the alternative ways for improvement of dielectric properties were tried and discussed.

Electrical and microstructural properties of CaTiO3-doped K1/2Na1/2NbO3-lead free ceramics

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Contribution of an extrinsic mechanism for the electrical polarization in BiMn2O5 ceramics

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)