Surface conditioning of a composite used for inlay/onlay restorations: Effect on mu TBS to resin cement

Purpose: To assess the effect of the composite surface conditioning on the microtensile bond strength of a resin cement to a composite used for inlay/onlay restorations.Materials and Methods: Forty-two blocks (6 x 6 x 4 mm) of a microfilled composite (Vita VMLC) were produced and divided into 3 groups (N = 14) by composite surface conditioning methods: Gr1 - etching with 37% phosphoric acid, washing, drying, silanization; Gr2 - air abrasion with 50-Im Al203 particles, silanization; Gr3 - chairside tribochemiCal silica coating (CoJet System), silanization. Single-Bond (one-step adhesive) was applied on the conditioned surfaces and the two resin blocks treated with the same method were cemented using RelyX ARC (dual-curing resin cement). The specimens were stored for 7 days in water at 37 degrees C and then sectioned to produce nontrimmed beam samples, which were submitted to microtensile bond strength testing (mu TBS). For statistical analysis (one-way ANOVA and Tukey's test, = 0.05), the means of the beam samples from each luted specimen were calculated (n = 7).Results: mu TBS values (MPa) of Gr2 (62.0 +/- 3.9a) and Gr3 (60.5 +/- 7.9a) were statistically similar to each other and higher than Gr1 (38.2 +/- 8.9b). The analysis of the fractured surfaces revealed that all failures occurred at the adhesive zone.Conclusion: Conditioning methods with 50-Im Al203 or tribochemical silica coating allowed bonding between resin and composite that was statistically similar and stronger than conditioning with acid etching.

Use of spin label EPR spectra to monitor peptide chain aggregation inside resin beads.

An EPR approach to monitor peptide chain aggregation inside resin beads is introduced. Model low and highly peptide-loaded resins containing an aggregating sequence were labeled with a paramagnetic amino acid derivative and studied with regard to their solvation behavior in different solvent systems. For the first time in the peptide synthesis, EPR spectroscopic has allowed the detection of differentiated levels of peptide chain aggregation as a function of solvent and resin loading. (C) 1997, Elsevier B.V. Ltd. All rights reserved.

Dielectric thermal analysis as a tool for quantitative-evaluation of the viscosity and the kinetics of epoxy resin cure

Dielectric thermal analysis has been proved as a valuable tool for monitoring the epoxy curing process and the related rheological properties in the fabrication of polymer-matrix composite materials. This technique also has the potential to be applied in the monitoring of magnet impregnation processes as well as in quality control. In this work we present the quantitative evaluation of the viscosity changing and the curing kinetics for a commercial Stycast epoxy resin system at different temperatures through the impedance analysis. The results showed correlation between the real component of the complex impedance and the isothermal reaction extent. Comparing the dielectric analysis result with the viscosity measured by rotational rheometer we observed a similar behavior reported for dynamic mechanic analysis. The results comparison have shown that the kinetics parameters obtained from DSC and DETA analysis showed different sensitivities related to the characteristics of curing stages. We concluded that the dielectric thermal analysis should be applied in quantitative evaluation of cure kinetics.

Microtensile bond strength of a resin cement to feldpathic ceramic after different etching and silanization regimens in dry and aged conditions

Objectives. This study evaluated the durability of bond strength between resin cement and a feldspathic ceramic submitted to different etching regimens with and without silane coupling agent application.Methods. Thirty-two blocks (6.4 mm x 6.4 mm x 4.8 mm) were fabricated using a microparticulate feldspathic ceramic (Vita VM7), ultrasonically cleaned with water for 5 min and randomly divided into four groups, according to the type of etching agent and silanization method: method 1, etching with 10% hydrofluoric (HF) acid gel for I min + silanization; method 2, HF only; method 3, etching with 1.23% acidulated phosphate fluoride (APF) for 5 min + silanization; method 4, APF only. Conditioned blocks were positioned in their individual silicone molds and resin cement (Panavia F) was applied on the treated surfaces. Specimens were stored in distilled water (37 degrees C) for 24 h prior to sectioning. After sectioning the ceramic-cement blocks in x- and Y-axis with a bonded area of approximately 0.6 mm(2), the microsticks of each block were randomly divided into two storage conditions: Dry, immediate testing; TC, thermal cycling (12,000 times) + water storage for 150 d, yielding to eight experimental groups. Microtensile bond strength tests were performed in universal testing machine (cross-head speed: 1 mm/min) and failure types were noted. Data obtained (MPa) were analyzed with three-way ANOVA and Tukey's test (alpha = 0.05).Results. Significant influence of the use of silane (p < 0.0001), storage conditions (p = 0.0013) and surface treatment were observed (p = 0.0014). The highest bond strengths were achieved in both dry and thermocycled conditions when the ceramics were etched with HF acid gel and silanized (17.4 +/- 5.8 and 17.4 +/- 4.8 MPa, respectively). Silanization after HF acid gel and APT treatment increased the results dramatically (14.5 +/- 4.2-17.4 +/- 4.8 MPa) compared to non-silanized groups (2.6 +/- 0.8-8.9 +/- 3.1 MPa) where the failure type was exclusively (100%) adhesive between the cement and the ceramic.Significance. Silanization of the feldspathic ceramic surface after APF or HF acid etching increased the microtensile bond strength results significantly, with the latter providing higher results. Long-term thermocycling and water storage did not decrease the results in silanized groups. (C) 2006 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Resin-based composite reinforced sealant

Purpose: To describe and picture a technique for using a resin-bonded sealant reinforced by inclusion of resin-based composite, before polymerization. Method: Using an extracted mandibular molar, embedded in plaster and isolated with a rubber dam, a step-by-step depiction of the technique is shown. Results: A picture of a six-year-old sealant in a first permanent molar, still in perfect condition, is shown. Conclusion: This technique offers a reliable method for treating pits and fissures.