Mo原子溅射能量对Mo／Si薄膜微结构的影响

用磁控溅射法制备了Mo／Si薄膜，用AFM和XRD分别研究了Mo原子的溅射能量不同时，Mo／Si薄膜表面形貌和晶相的变化。通过比较发现，随着Mo原子溅射能量的增大，Mo／Si薄膜表面粗糙度增加，Mo和Si的特征X射线衍射峰也越来越强，并且Mo膜层和Si膜层之间生成了Mo-Si2。Mo原子的溅射能量是诱导非晶Si结晶和MoSi2生成的主要原因。

Measurements of light scattering from glass substrates by total integrated scattering

A total integrated scattering (TIS) measurement was performed to investigate the surface and volume scattering of K9 glass substrates with low reflectance. Ag layers with thicknesses of 60 nm were deposited on the front and back surfaces of the K9 glass substrates by the magnetron sputtering technique. Surface scattering of the K9 glass substrate was obtained by the TIS measurement of the Ag layers on the assumption that the Ag layers and the K9 substrate had the same surface profile. Volume scattering of the substrates was deduced by subtracting the front and back surface scattering from the total scattering of the substrates. (c) 2005 Optical Society of America.

磁控溅射不同厚度银膜的微结构及其光学常数

Ag films with different thickness from 8.2nm to 107.2nm were prepared by DC sputtering deposition and analyzed by X-ray diffraction with the help of optimization program on computer. Microstructrue analysis shows that the films are made of fcc-Ag particles. With the increase of thickness, the mean size of Ag particles increases and the interplaner spacing decreases gradually. The optical constants computed by computer program shows that n value decreases quickly with the increasing thickness below 17.5nm and k value changes in reverse, and then go steadily when the thickness is larger than 17.5nm at the wavelength of 550mn.

Negative dispersion mirrors in Ta2O5/: SiO2 for femtosecond Ti : Sapphire lasers by using gires-tournois interferometers

We design and experimentally demonstrate some negative dispersion mirrors with optimized Gires-Tournois interferometers. The mirror structure is composed of 38 alternating Ta2O5 and SiO2 layers and could be regarded as two sections: high-reflectivity section consisting of a series of quarter-wavelength optical thickness stacks and negative-dispersion section consisting of only 13 layers. The designed mirrors exhibit the expected performance. These mirrors were fabricated by using ion beam sputtering. By adopting such mirrors, dispersion of a mode-locked femtosecond Ti:sapphire laser has been compensated for mostly. With two series of the mirrors, 32 fs and 15 fs pulses have been obtained respectively.

Defect-induced failure of optical coating filters

Optical filters composed of Ag, Al2O3, and ZnSe films were prepared on BK7 substrates by evaporation. By employing spectrophotometer, microscope, scanning electron microscope (SEM), and energy dispersive spectrum (EDS) analysis, the moisture-dependent stability of the samples was tested. The experimental results revealed that filter failure often occurs initially at defect sites. Small sputtering particles and pinhole are found to be two types of defects that induced the optical coating filter failure. The mechanisms of the defect-induced failure of the filters also are discussed in the article. (C) 2005 Elsevier Ltd. All rights reserved.

Influence of different post-treatments on the structure and optical properties of zinc oxide thin films

Zinc oxide (ZnO) films with c-oriented were grown on fused quartz glass substrates at room temperature using dc reactive magnetron sputtering. The as-grown films were annealed at 700 degrees C in air and bombarded by ion beam, respectively. The effects of post-treatments on the structural and optical properties of the ZnO films were investigated by X-ray diffraction (XRD), photoluminescence (PL), optical transmittance and absorption measurements. The XRD spectra indicate that the crystal quality of ZnO films has been improved by both the post-treatments. Compared with the as-grown sample, both annealed and bombarded samples exhibited blueshift in the UV emission peaks, and a strong green emission was found in the annealed ZnO film. In both optical transmittance and absorption spectra, a blueshift of the band-gap edge was observed in the bombarded film, while a redshift was observed in the annealed film. (c) 2004 Elsevier B.V. All rights reserved.

The effects of oxygen partial pressure on the optical absorption edge and the UV emission energy of ZnO films

The optical absorption edge and ultraviolet (UV) emission energy of ZnO films deposited by direct current (DC) reactive magnetron sputtering at room temperature have been investigated. With the oxygen ratio increasing, the structure of films changes from zinc and zinc oxide coexisting phase to single-phase ZnO and finally to the highly (002) orientation. Both the grain size and the stress of ZnO film vary with the oxygen partial pressure. Upon increasing the oxygen partial pressure in the growing ambient, the visible emission in the room-temperature photoluminescence spectra was suppressed without sacrificing the band-edge emission intensity in the ultraviolet region. The peaks of photoluminescence spectra were located at 3.06---3.15 eV. From optical transmittance spectra of ZnO films, the optical band gap edge was observed to shift towards shorter wavelength with the increase of oxygen partial pressure.

钛宝石激光器中用优化Gires-Tournois镜产生15fs脉冲

根据飞秒脉冲锁模钛宝石激光器脉冲压缩的要求，介绍了负色散镜补偿色散的基本原理及其特点。详细阐述了优化Gires-Tournois(OG-T)镜的设计过程，并通过计算机优化得到理想设计膜系。采用离子束溅射的方法镀制了优化Gires—Tournois镜。测量了优化Gires-Tournois镜(编号为OGT#1)的透射率和群延迟色散，并与设计值进行了比较，分析了实测值产生偏差的原因，从而对镀膜参量进行了相应的调整，制造了第二批优化Gires—Tournois镜(编号为OGT#2)。将优化Gires—Tourn

纳米Mo膜的光学特性及最小连续膜厚研究

利用Lambda-900分光光度计，在波长为310～1250nm范围内测量了离子束溅射沉积不同厚度纳米Mo膜的反射率和透射率。选定波长为310nm，350nm，400nm，500nm，550nm，632nm，800nm，1200nm时对薄膜的反射率、透射率和吸收率随膜厚变化的关系进行了讨论。实验结果显示，纳米Mo膜的光学特性有明显的尺寸效应。提出将薄膜对光波长为550nm时的反射率和透射率随Mo膜厚度变化关系的交点对应的厚度作为特征厚度，该厚度可认为是纳米Mo膜生长从不连续膜进入连续膜的最小连续膜厚。利用

不同膜层数的Mo/Si多层膜的表界面粗糙度和软X射线反射率

用磁控溅射法制备了顶层分别是Mo膜层和Si膜层的两个系列的Mo/Si多层膜，它们的周期厚度相同但是膜层数各不相同。Mo/Si多层膜的周期厚度和界面粗糙度由小角X射线衍射（SAXRD）曲线拟和得到。用原子力显微镜测量了Mo/Si多层膜的表面粗糙度。在国家同步辐射实验室测量了Mo/Si多层膜的软X射线反射率。通过理论和试验研究，发现Mo/Si多层膜的软X射线反射率主要由周期数和界面粗糙度决定，表面粗糙度对Mo/Si多层膜的软X射线反射率影响较小。

Influence of vacuum organic contaminations on laser-induced damage of 1064 nm anti-reflective coatings

We investigate the influence of vacuum organic contaminations on laser-induced damage threshold (LIDT) of optical coatings. Anti-reflective (AR) coatings at 1064 nm made by Ta2O5/SiO2 are deposited by the ion beam sputtering method. The LIDTs of AR coatings are measured in vacuum and in atmosphere, respectively. It is exhibited that contaminations in vacuum are easily to be absorbed onto optical surface because of lower pressure, and they become origins of damage, resulting in the decrease of LIDT from 24.5 J/cm(2) in air to 15.7 J/cm(2) in vacuum. The LIDT of coatings in vacuum has is slightly changed compared with the value in atmosphere after the organic contaminations are wiped off. These results indicate that organic contaminations are the main reason of the LIDT decrease in vacuum. Additionally, damage morphologies have distinct changes from vacuum to atmosphere because of the differences between the residual stress and thermal decomposability of filmy materials.

Influence of deposition conditions on the microstructure of oxides thin films

Thin films of ZrO2, HfO2 and TiO2 were deposited on kinds of substrates by electron beam evaporation (EB), ion assisted deposition (IAD) and dual ion beam sputtering (DIBS). Then some of them were annealed at different temperatures. X-ray diffraction (XRD) was applied to determine the crystalline phase and the grain size of these films, and the results revealed that their microstructures strongly depended on the deposition conditions such as substrate, deposition temperature, deposition method and annealing temperature. Theory of crystal growth and migratory diffusion were applied to explain the difference of crystalline structures between these thin films deposited and treated under various conditions. (c) 2007 Elsevier B.V. All rights reserved.

8.0nm反射式偏振膜的设计和制备

讨论了软X射线反射式偏振膜的设计原理和方法,利用设计软件模拟设计了8.0nm处的Mo/B4C偏振膜.对影响多层膜性能的参量进行了详细的误差分析.利用磁控溅射镀膜机进行了偏振膜的制备研究,X射线小角衍射测量了多层膜的周期厚度,测量数据的拟合结果与设计值吻合很好.

用不同的Mo靶溅射功率制备Mo／Si多层膜

用磁控溅射法制备了周期厚度和周期数均相同的Mo／Si多层膜，用原子力显微镜和小角X射线衍射分别研究了Mo靶溅射功率不相同时，Mo／Si多层膜表面形貌和晶相的变化。随后在国家同步辐射实验室测量了Mo／Si多层膜的软X射线反射率。研究发现，随着Mo靶溅射功率的增大，Mo／Si多层膜的表面粗糙度增加，Mo的特征X射线衍射峰也增强，Mo／Si多层膜的软X射线峰值反射率先增大后减小。

Mo／Si软X射线多层膜的界面粗糙度研究

用磁控溅射法分别制备了以Mo膜层和Si膜层为顶层的Mo／Si多层膜系列，利用小角X射线衍射确定了各多层膜的周期厚度。以不同周期数的Mo／Si多层膜的新鲜表面近似等同于同一多层膜的内界面，通过原子力显微镜研究了多层膜界面粗糙度随膜层数的变化规律。并在国家同步辐射实验室测量了各多层膜的软X射线反射率。研究表明：随着膜层数的增加，Mo膜层和Si膜层的界面粗糙度先减小后增加然后再减小，多层膜的峰值反射率先增加后减小。