Influence of Different Ceramics on Resin Cement Knoop Hardness Number

This study evaluated: 1) the effect of different ceramics on light attenuation that could affect microhardness, measured as the Knoop Hardness Number (KHN), of a resin cement immediately and 24 hours after polymerization and 2) the effect of different activation modes (direct light-activation, light activation through ceramics and chemical activation) on the KHN of a resin cement.Resin cement Rely X ARC (3M ESPE) specimens 5.0 mm in diameter and 1.0 nun thick were made in a Teflon mold covered with a polyester film. The cement was directly light activated for 40 seconds with an XL 2500 curing unit (3M ESPE) with 650 mW/cm(2), light activated through ceramic discs of Duceram Plus (DeguDent), Cergogold (DeguDent), IPS Empress (Ivoclar), IPS Empress 2 (Ivoclar), Procera. (NobelBiocare), In Ceram Alumina (Vita) and Cercon (DeguDent), having a 1.2 mm thickness or chemically activated without light application. The resin cement specimens were flattened, and KHN was obtained using an HMV 2 microhardness tester (Shimadzu) with a load of 50 g applied for 15 seconds 100 pin from the irradiated surface immediately and after storage at 37 degrees C for 24 hours. Ten measurements were made for each specimen, with three specimens for each group at each time. The data were submitted to ANOVA and Tukey's test (p=0.05). The KHN of the resin cement was not only affected by the mode of activation, but also by the post-activation testing time. The mean KHN of the resin cement for chemical activation and through all ceramics showed statistically significant lower values compared to direct activation immediately and at 24 hours. The KHN for 24 hours post-activation was always superior to the immediate post-activation test except with direct activation. The most opaque ceramics resulted in the lowest KHN values.

Optical Impression Systems for CAD-CAM Restorations

Computer-aided design/computer-aided manufacturing images can be taken through either direct or indirect imaging. For the indirect systems, the digitalization is obtained from the impression material or cast, and for the direct ones the image is taken directly from the mouth using intraoral scanners.The direct acquisition systems have been constantly improved because these are less invasive, quicker, and more precise than the conventional method. Besides, the digital images can be easily stored for a long time. Therefore, the aim of this paper was to describe and discuss based on the literature the main direct image acquisition systems available on the market: CEREC Bluecam (Sirona), Lava C.O.S. System (3M ESPE), iTero System (Cadent/Straumann), and E4D System (D4D Technologies).

Silver Distribution and Release from an Antimicrobial Denture Base Resin Containing Silver Colloidal Nanoparticles

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Effect of weathering and thickness on the superficial microhardness of acrylic resin and ocular button

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Short-term in situ/ex vivo study of the anticariogenic potential of a resin-modified glass-ionomer cement associated with adhesive systems

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Microleakage of adhesively bonded cervical amalgam restorations

Purpose: To evaluate dye penetration in adhesively bonded cervical amalgam restorations. Materials and Methods: the specimens were randomly divided into four groups and the adhesives Prime & Bond 2. 1, Prime & Bond 2.1 Dual Cure, Scotchbond Multi Purpose Plus and Amalgambond Plus were tested. After being restored and polished, the teeth were thermocycled 1,000 times at temperatures varying between 5degreesC +/- 2degreesC and 55degreesC +/- 2degreesC. Statistical analysis was carried out using the Kruskal-Wallis test and multiple comparisons. Results: Scotchbond Multi-Purpose Plus demonstrated lower levels of microleakage in enamel and dentin. The dual adhesives were more effective than the one bottle adhesive.

Effect of Different Light-Curing Modes on Degree of Conversion, Staining Susceptibility and Stain's Retention Using Different Beverages in a Nanofilled Composite Resin

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Short-term evaluation of the pulpo-dentin complex response to a resin-modified glass-ionomer cement and a bonding agent applied in deep cavities

Objectives. To evaluate the response of the pulpo-dentin complex following application of a resin-modified glass-ionomer cement or an adhesive system in deep cavities performed in human teeth.Methods. Deep class V cavities were prepared on the buccal surface of 26 premolars. In Group I the cavity walls (dentin) and enamel were conditioned with 32% phosphoric acid and the dentin adhesive system One Step (Bisco, Inc., Itasca, IL, USA) was applied. In Groups 2 and 3, before total etching and application of bonding agent, the cavity floor was lined with the resin-modified glass-ionomer cement-Vitrebond (3M ESPE Dental Products Division, St. Paul, MN, USA) or the calcium hydroxide cement-Dycal (control group, Dentsply, Mildford, DE, USA), respectively. The cavities were restored using light-cured Z-100 composite resin (3M ESPE). The teeth were extracted between 5 and 30 days and prepared for microscopic assessment. Serial sections were stained with H/E, Masson's trichrome, and Brown and Brenn techniques.Results. In Group 1, the inflammatory response was more evident than in Groups 2 and 3. Diffusion of dental material components across dentinal tubules was observed only in Group 1, in which the intensity of the pulp response increased as the remaining dentin thickness decreased. Bacteria were evidenced in the lateral walls of two samples (Group 2) which exhibited no inflammatory response or tissue disorganization.Conclusions. Based on the experimental conditions, it was concluded total acid etching followed by application of One Step bonding agent cannot be recommended as adequate procedures. In this clinical condition the cavity walls should be lined with a biocompatible dental material, such as Vitrebond or Dycal. 2003 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Biocompatibility of resin-based materials used as pulp-capping agents

Aim To evaluate and compare the response of pulps of rats capped with resin-modified glass-ionomer cement (RMGIC) or self-etching adhesive system.Methodology Class I cavities were prepared on the occlusal surface of 54 maxillary first molars of 27 rats. Pulp exposure was performed on the cavity floor. The following resin-based materials were applied as pulp-capping agents: G1, Clearfil Liner Bond 2V (CLB 2V; Kuraray Co., Japan); G2, Vitrebond (VIT; 3M/ESPE, USA). In group 3 (control group), a calcium hydroxide/saline paste (CH; Labsynth, Brazil) was used. The cavities were restored with amalgam. After 7, 30 and 60 days, the animals were sacrificed and the jaws were processed for microscopic evaluation.Results Despite the inflammatory response caused by the experimental and the control materials at 7 days, pulpal healing associated with calcified barrier formation was observed at 60 days following the pulp therapy. Both resin-based materials promoted a large zone of cell-rich fibrodentine matrix deposition on the pulp horn related to the pulp exposure site, which was larger to VIT than to CLB 2V specimens. Tertiary dentine underneath the fibrodentine matrix was deposited by a layer of elongated pulpal cells. The remaining pulpal tissue exhibited normal histological characteristics. In the control group, healing and dentine-bridge formation was observed at 30 days. Pulpal breakdown occurred only when bacterial infection occurred.Conclusion Both experimental pulp-capping agents allowed pulpal healing characterized by cell-rich fibrodentine and tertiary dentine deposition as well as calcified barrier formation.

Effects of light-curing time on the cytotoxicity of a restorative composite resin on odontoblast-like cells

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Surface roughness and hardness of a composite resin: influence of finishing and polishing and immersion methods

This study evaluated the finishing and polishing effect on the surface roughness and hardness of the Filtek Supreme XT, in fluoride solutions. Specimens were prepared (n = 140) with half of the samples finished and polished with Super-Snap (R) disks. The experimental groups were divided according to the presence or absence of finishing and polishing and immersion solutions (artificial saliva, sodium fluoride solution at 0.05%-manipulated, Fluordent Reach, Oral B, Fluorgard). The specimens remained immersed in artificial saliva for 24 hours and were then subjected to initial analysis (baseline) of surface roughness and Vickers microhardness. Next, they were immersed in different fluoride solutions for 1 min/day, for 60 days. Afterwards, a new surface roughness and microhardness reading was conducted. The data were submitted to a two-way ANOVA and Tukey's test (5% significance level). For the comparison of mean roughness and hardness at baseline and after 60 days, the paired Student t test was used. The results showed that the surface roughness and microhardness of the Filtek Supreme XT were influenced by the finishing and polishing procedure, independently of the immersion methods.

Chlorhexidine increases the longevity of in vivo resin-dentin bonds

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Clinical and microbiological performance of resin-modified glass-ionomer liners after incomplete dentine caries removal

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Cytotoxicity of resin-based light-cured liners

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Composite resin color stability: influence of light sources and immersion media

Objective: This study evaluated the influence of light sources and immersion media on the color stability of a nanofilled composite resin. Material and Methods: Conventional halogen, high-power-density halogen and high-power-density light-emitting diode (LED) units were used. There were 4 immersion media: coffee, tea, Coke (R) and artificial saliva. A total of 180 specimens (10 mm x 2 mm) were prepared, immersed in artificial saliva for 24 h at 37 +/- 1 degrees C, and had their initial color measured with a spectrophotometer according to the CIELab system. Then, the specimens were immersed in the 4 media during 60 days. Data from the color change and luminosity were collected and subjected to statistical analysis by the Kruskall-Wallis test (p<0.05). For immersion time, the data were subjected to two-way ANOVA test and Fisher's test (p<0.05). Results: High-power-density LED (Delta E=1.91) promoted similar color stability of the composite resin to that of the tested halogen curing units (Jet Lite 4000 plus - Delta E=2.05; XL 3000 - Delta E=2.28). Coffee (Delta E=8.40; Delta L=-5.21) showed the highest influence on color stability of the studied composite resin. Conclusion: There was no significant difference in color stability regardless of the light sources, and coffee was the immersion medium that promoted the highest color changes on the tested composite resin.