I. Reactively sputtered Ti-Si-N thin films for diffusion barrier applications. II. Oxidation, diffusion and crystallization of an amorphous Zr_(60)Al_(15)Ni_(25) alloy.

Films of Ti-Si-N obtained by reactively sputtering a TiSi_2, a Ti_5Si_3, or a Ti_3Si target are either amorphous or nanocrystalline in structure. The atomic density of some films exceeds 10^23 at./cm^3. The room-temperature resistivity of the films increases with the Si and the N content. A thermal treatment in vacuum at 700 °C for 1 hour decreases the resistivity of the Ti-rich films deposited from the Ti_5Si_3 or the Ti_3Si target, but increases that of the Si-rich films deposited from the TiSi_2 target when the nitrogen content exceeds about 30 at. %.

Ti_(34)Si_(23)N_(43) deposited from the Ti_5Si_3 target is an excellent diffusion barrier between Si and Cu. This film is a mixture of nanocrystalline TiN and amorphous SiN_x. Resistivity measurement from 80 K to 1073 K reveals that this film is electrically semiconductor-like as-deposited, and that it becomes metal-like after an hour annealing at 1000 °C in vacuum. A film of about 100 nm thick, with a resistivity of 660 µΩcm, maintains the stability of Si n+p shallow junction diodes with a 400 nm Cu overlayer up to 850 °C upon 30 min vacuum annealing. When used between Si and Al, the maximum temperature of stability is 550 °C for 30 min. This film can be etched in a CF_4/O_2 plasma.

The amorphous ternary metallic alloy Zr_(60)Al_(15)Ni_(25) was oxidized in dry oxygen in the temperature range 310 °C to 410 °C. Rutherford backscattering and cross-sectional transmission electron microscopy studies suggest that during this treatment an amorphous layer of zirconium-aluminum-oxide is formed at the surface. Nickel is depleted from the oxide and enriched in the amorphous alloy below the oxide/alloy interface. The oxide layer thickness grows parabolically with the annealing duration, with a transport constant of 2.8x10^(-5) m^2/s x exp(-1.7 eV/kT). The oxidation rate is most likely controlled by the Ni diffusion in the amorphous alloy.

At later stages of the oxidation process, precipitates of nanocrystalline ZrO_2 appear in the oxide near the interface. Finally, two intermetallic phases nucleate and grow simultaneously in the alloy, one at the interface and one within the alloy.

Photoelectrochemistry of GaAs and Si liquid junctions

A quantitative study has been performed on the stability of GaAs surfaces in a 0.10 M K₂Se-0.01 M K₂Se₂ aqueous solution. In this electrolyte, n-type GaAs electrodes displayed significant photocorrosion in competition with faradaic charge transfer to Se^2-. Chemisorption of group VIIIB metal ions onto the GaAs surfaces yielded improved current-voltage behavior of the GaAs photoanodes, and also resulted in a significant reduction in photocorrosion. This behavior implies that the chemisorbed metal ions act to increase the rate of hole transfer to the Se^2- species. Related experiments on n-GaAs, pGaAs, and Sn-doped In₂O₃ electrodes in Te^2-/- aqueous solutions have also been performed.

The majority carrier (electrons) transfer rate constant at a highly doped n⁺-Si/Co(Cp)₂Cl-methanol junction has been measured directly using the chronoamperometry electrochemical technique. The reduction reaction rate of Co(Cp)₂+ was 0.03 cm-s^-1 at the Si electrode, and was more than 100 times slower than at a hanging mercury electrode. The slower rate was attributed to the smaller optical and static dielectric constants, and the lower density of electrons of the semiconductor. The experimental results were compared to the Marcus theory of charge transfer.

The unique properties of high purity Si/liquid junctions have been investigated under illumination conditions in which the photogenerated carrier concentration exceeds the dopant concentration. Under these high injection conditions, negligible electric fields exist at the semiconductor/liquid interface, and carrier motion is driven by diffusion. Studies of the current-voltage properties of the Si in methanol solutions containing various redox couples suggested that high efficiency photoelectrochemical cells could be established through selective collection of carriers at the semiconductor/liquid junction. The quasi-Fermi levels of electrons and holes were measured directly against the solution potential. Steady-state and transient photovoltage measurements, and theoretical modeliug of the carrier transport, generation, and recombination dynamics indicated that the quasi-Fermi levels were flat across the semiconductor sample. The recombination velocities at the Si/liquid junctions have also been measured, and were shown to vary with the solution potential following the Shockley-Read-Hall theory on recombination.

Studies of noble gases in meteorites and in the earth

The isotopic and elemental abundances of noble gases in the solar system are investigated, using simple mixing models and mass-spectrometric measurements of the noble gases in meteorites and terrestrial rocks and minerals.

Primordial neon is modeled by two isotopically distinct components from the interstellar gas and dust. Neon from the gas dominates solar neon, which contains about ten times more ²⁰Ne than ²²Ne. Neon from the dust is represented in meteorites by neon-E, with ²⁰Ne/²²Ne less than 0.6. Isotopic variations in meteorites require neon from both dust and gas to be present. Mixing dust and gas without neon loss generates linear correlation lines on three-isotope and composition-concentration diagrams. A model for solar wind implantation predicts small deviations from linear mixing, due to preferential sputtering of the lighter neon isotopes.

Neon in meteorites consists of galactic cosmic ray spallation neon and at least two primordial components, neon-E and neon-S. Neon was measured in several meteorites to investigate these end- members. Cosmogenic neon produced from sodium is found to be strongly enriched in ²²Ne. Neon measurements on sodium-rich samples must be interpreted with care so not to confuse this source of ²²Ne with neon-E, which is also rich in ²²Ne.

Neon data for the carbonaceous chondrite Mokoia show that the end member composition of neon-Si in meteorites is ²⁰Ne/²²Ne = 13.7, the same as the present solar wind. The solar wind composition evidently has remained constant since before the compaction of Mokoia.

Ca, Al-rich inclusions from the Allende meteorite were examined for correlation between neon-E and oxygen or magnesium isotopic anomalies. ²²Ne and ³⁶Ar enrichments found in some inclusions are attributed to cosmic- ray-induced reactions on Na and Cl, not to a primordial component. Neon-E is not detectably enriched in Allende.

Measurements were made to determine the noble gas contents of various terrestrial rocks and minerals, and to investigate the cycling of noble gases between different terrestrial reservoirs. Beryl crystals contain a characteristic suite of magmatic gases including nucleogenic ²¹Ne and ²²Ne from (α,n) reactions, radiogenic ⁴⁰Ar, and fissiogenic ^131-136Xe from the decay of K and U in the continental crust. Significant concentrations of atmospheric noble gases are also present in beryl.

Both juvenile and atmospheric noble gases are found in rocks from the Skaergaard intrusion. The ratio ⁴⁰Ar/³⁶Ar (corrected for in situ decay of ⁴⁰K) correlates with δ¹⁸O in plagioclase. Atmospheric argon has been introduced into samples that have experienced oxygen-isotope exchange with circulating meteoric hydrothermal fluids. Unexchanged samples contain juvenile argon with ⁴⁰Ar/³⁶Ar greater than 6000 that was trapped from the Skaergaard magma.

Juvenile and atmospheric gases have been measured in the glassy rims of mid-ocean ridge (MOR) pillow basalts. Evidence is presented that three samples contain excess radiogenic ¹²⁹Xe and fission xenon, in addition to the excess radiogenic ⁴⁰Ar found in all samples. These juvenile gases are being outgassed from the upper-mantle source region of the MOR magma. No isotopic evidence has been found here for juvenile primordial noble gases accompanying the juvenile radiogenic gases in the MOR glasses. Large argon isotopic variations in a single specimen provide a clear indication of the late-stage addition of atmospheric argon, probably from seawater.

The Skaergaard data demonstrate that atmospheric noble gases dissolved in ground water can be transferred into crustal rocks. Subduction of oceanic crust altered by seawater can transport atmospheric noble gases into the upper mantle. A substantial portion of the noble gases in mantle derived rocks may represent subducted gases, not a primordial component as is often assumed.

A hora da estrela: uma narrativa que se desdobra sobre si mesma, tecendo e destecendo retratos do(s) outro(s) e retratos de si

Muito já se disse sobre Clarice Lispector, muito há, no entanto, a se dizer ainda. Com este nosso trabalho, ousamos trilhar um caminho que nos parece duplamente pouco explorado: por um lado, nos debruçamos sobre as pausas, as lacunas, as suspensões do dizer que se materializam em cortes no fio discursivo da literatura clariceana; mais especificamente nas interrupções que comparecem por meio de travessões, parênteses e aí estendemos para a interrogação em A Hora da Estrela. Por outro lado, trazemos, para este nosso objetivo, uma abordagem discursiva, isto é, temos como suporte teórico-metodológico a Análise de Discurso cujos autores basilares são Pêcheux e Orlandi. Esta autora, ao deslocar o estudo da pontuação do campo da gramática para o domínio do discurso, considera a pontuação como o lugar em que o sujeito trabalha seus pontos de subjetivação, o modo como interpreta (Orlandi, 2005). A pontuação, vista discursivamente, abre fendas do não-dizer no dizer, trabalhando sua (in)completude. Os travessões, os parênteses e a interrogação, em Clarice, rompem repetida e sucessivamente a linearidade da língua expondo seus vazios, seus meandros, seus impasses. Analisaremos o funcionamento discursivo desses três sinais de pontuação no dizer do narrador de A Hora da Estrela, assim como investigaremos as posições-sujeito do narrador que se delineiam em cada funcionamento desses sinais: posição-sujeito de narrador onipotente/onisciente, posição-sujeito de narrador impotente e posição-sujeito de narrador vacilante. Para nosso trabalho, apoiamo-nos também nas reflexões teóricas acerca da heterogeneidade da língua, propostas por Authier-Revuz e trazemos o conceito de enunciação vacilante formulado por Paulillo. Podemos dizer que, nas incisas desta novela clariceana, jogam posições-sujeito que se polemizam, que se equivocam. Essas posições refletem uma narrativa que ora descreve a possibilidade de narrar, de descrever o outro, ora confessa a impossibilidade de capturar esse outro pela palavra: narrador vacilante, narrativa vacilante

Memória, imaginação e transpiração no processo de fabricação do passado: a ficcionalização de si em Infância e Angústia, de Graciliano Ramos

O objetivo deste trabalho é investigar a proposta literária do escritor alagoano Graciliano Ramos que conceituamos como ficcionalização de si, a qual consiste na utilização de observação, experiência, imaginação e transpiração como ingredientes da elaboração ficcional. Para atingir a tal objetivo, buscamos traçar um breve panorama político-cultural da década de 1930, no sentido de situar a formação ideológica e a produção mais significativa do autor Caetés (1933), S. Bernardo (1934), Angústia (1936) e Vidas Secas (1938). Prosseguimos com a construção de um amplo painel sobre o papel da memória na escrita de si, concluindo sobre a impossibilidade da fidelidade absoluta na reprodução do real, uma vez que esta passa necessariamente pela subjetividade da linguagem, o que lhe confere um inegável caráter ficcional. Conceituamos autobiografia e refletimos sobre as profundas alterações percebidas no gênero autobiográfico, inserindo a produção de Graciliano Ramos no contexto memorialista. Defendemos a ideia de que o escritor antecipa, na década de 30, o que na década de 70 será denominado como autoficção. Construída a fundamentação teórica necessária, passamos a analisar e discutir trechos do romance Angústia, em contraponto com Infância. Confrontando as leituras destas obras, pudemos perceber o aproveitamento ficcional de acontecimentos traumáticos da infância do autor narrados em Infância na elaboração da fase infantil do personagem Luís da Silva, de Angústia

Sobre o palco, a fera arrebatada, a alma especular e a musa paradoxal: experiências do monólogo, processo criativo, construções de si e autoria.

Esta tese de doutoramento tem como objeto as experiências de atores e atrizes na criação e apresentação de monólogos no Rio de Janeiro, a partir de 2006. Esta experiência artística é refletida aqui a partir de questões clássicas das Ciências Sociais sobre o indivíduo moderno, tais como as da singularidade, autenticidade e originalidade. A questão da autoria de tais monólogos é relacionada a perspectivas ligadas à ideologia individualista ocidental, tais como as da autonomia artística e construção de si, nas complexas imbricações entre o artista (ator/indivíduo criador) e sua obra (monólogo/performance/encenação/texto). O monólogo visto como um amplo projeto artístico, que abrange a experiência de sua elaboração, produção, apresentação e repercussão torna-se um objeto processual de autorreflexão do artista sobre si mesmo e sobre o mundo. O monólogo pode ser visto como uma experiência artística pessoal, onde a perspectiva autoral é posta em primeiro plano, dinamizando e realimentando aspectos associados à crença em um modelo de indivíduo que se expressa por um sujeito capaz de se autodefinir, mas que, neste contexto, encontra expressões particulares. Para esta abordagem, analiso três experiências monológicas: O Animal do Tempo, protagonizada pela atriz Ana Kfouri; A Alma Imoral, adaptada e protagonizada por Clarice Niskier; e Anticlássico: uma desconferência ou o enigma vazio, concebida e encenada pela atriz Alessandra Colasanti.

Si se puede! De la injusticia a la justicia

Duración (en horas): Más de 50 horas Destinatario: Profesor