Influence of Tempered Microstructures on the Transformation Behaviour of Cold Deformed and Intercritically Annealed Medium Carbon Low Alloy Steel

This research is focused on understanding the role of microstructural variables and processing parameters in obtaining optimised dual phase structures in medium carbon low alloy steels. Tempered Martensite structures produced at 300, 500, and 650 degrees C, were cold rolled to varied degrees ranging from 20 to 80% deformation. Intercritical annealing was then performed at 740, 760, and 780 degrees C for various time duration ranging from 60 seconds to 60 minutes before quenching in water. The transformation behaviour was studied with the aid of optical microscopy and hardness curves. From the results, it is observed that microstructural condition, deformation, and intercritical temperatures influenced the chronological order of the competing stress relaxation and decomposition phase reactions which interfered with the rate of the expected alpha -> gamma transformation. The three unique transformation trends observed are systematically analyzed. It was also observed that the 300 and 500 degrees C tempered initial microstructures were unsuitable for the production of dual structures with optimized strength characteristics.

On the athermal nature of the beta to omega transformation

One characteristic feature of the athermal beta -> omega transformation is the short time scale of the transformation. So far, no clear understanding of this issue exists. Here we construct a model that includes contributions from a Landau sixth-order free energy density, kinetic energy due to displacement, and the Rayleigh dissipation function to account for the dissipation arising from the rapid movement of the parent product interface during rapid nucleation. We also include the contribution from omega-like fluctuations to local stress. The model shows that the transformation is complete on a time scale comparable to the velocity of sound. The estimated nucleation rate is several orders higher than that for diffusion-controlled transformations. The model predicts that the athermal omega phase is limited to a certain range of alloying composition. The estimated nucleation rate and the size of ``isothermal'' particles beyond 17% Nb are also consistent with experimental results. The model provides an explanation for the reprecipitation process of the omega particles in the ``cleared'' channels formed during deformation of omega-forming alloys. The model also predicts that acoustic emission should be detectable during the formation of the athermal phase. (C) 2011 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Observation of high pressure o-GeTe phase at ambient pressure in Si-Te-Ge glasses

Te-rich Si15Te85-xGex (1 <= x <= 11) glasses are found to exhibit an anomalous phase separations with germanium composition. The structural transformation of o-GeTe crystalline phase from o-GeTe with a = 11.76 angstrom, b = 16.59 angstrom, c = 17.44 angstrom, to high pressure o-GeTe with a new reduced lattice parameters a = 10.95 angstrom, b = 4.03 angstrom, c = 4.45 angstrom, is observed at T-c3 in the composition range 6 <= x <= 11. Raman studies support the possible existence of high pressure o-GeTe phase which is observed in X-ray diffraction experiments. Copyright 2012 Author(s). This article is distributed under a Creative Commons Attribution 3.0 Unported License. http://dx.doi.org/10.1063/1.3696862]

Strain induced phase transition in CdSe nanowires: Effect of size and temperature

Using all-atom molecular dynamics simulation, we have studied the effect of size and temperature on the strain induced phase transition of wurtzite CdSe nanowires. The wurtzite structure transforms into a five-fold coordinated structure under uniaxial strain along the c axis. Our results show that lower temperature and smaller size of the nanowires stabilize the five-fold coordinated phase which is not a stable structure in bulk CdSe. High reversibility of this transformation with a very small heat loss will make these nanowires suitable for building efficient nanodevices. (C) 2012 American Institute of Physics. http://dx.doi.org/10.1063/1.4734990]

Competing structural phase transition scenarios in the giant tetragonality ferroelectric BiFeO3-PbTiO3: Isostructural vs multiphase transition

A systematic x-ray and neutron powder diffraction study of the giant tetragonality multiferroic (1-x) BiFeO3-(x) PbTiO3 have revealed that the compositions close to the morphotropic phase boundary present two different structural phase transition scenarios on cooling from the cubic phase: (i) cubic -> tetragonal (T-2) + tetragonal (T-1) -> tetragonal (T-1) and (ii) cubic -> tetragonal (T-2) + tetragonal (T-1) + rhombohedral (R3c) -> tetragonal (T-1) + rhombohedral (R3c). The comparatively larger tetragonality (c/a - 1) of the T-1 phase as compared to the coexisting isostructural T-2 phase is shown to be a result of significantly greater degree of overlap of the Pb/Bi-6s and Ti/Fe-3d with the O-2p orbitals as compared to that in the T-2 phase. The formation/suppression of the minor metastable rhombohedral phase seems to be governed by subtle play of local kinetic factors. In the scenario when the minor rhombohedral (R) phase is formed along with the tetragonal phases it is able to accommodate the large transformation stress in the system due to formation of the tetragonal phases, and prevent the solid from disintegration into powder after sintering. When the metastable rhombohedral phase is not formed, the large transformation strain ruptures the grain boundaries leading to fragmentation of the dense solid to powder. (C) 2013 American Institute of Physics. http://dx.doi.org/10.1063/1.4792215]

Heat and mass transfer and chemical transformation in a cerium nitrate droplet

This paper deals with the thermo-physical changes that a droplet undergoes when it is radiatively heated in a levitated environment. The heat and mass transport model has been developed along with chemical kinetics within a cerium nitrate droplet. The chemical transformation of cerium nitrate to ceria during the process is predicted using Kramers' reaction mechanism which justifies the formation of ceria at a very low temperature as observed in experiments. The rate equation modeled by Kramers is modified suitably to be applicable within the framework of a droplet, and predicts experimental results well in both bulk form of cerium nitrate and in aqueous cerium nitrate droplet. The dependence of dissociation reaction rate on droplet size is determined and the transient mass concentration of unreacted cerium nitrate is reported. The model is validated with experiments both for liquid phase vaporization and chemical reaction. Vaporization and chemical conversion are simulated for different ambient conditions. The competitive effects of sensible heating rate and the rate of vaporization with diffusion of cerium nitrate is seen to play a key role in determining the mass fraction of ceria formed within the droplet. Spatially resolved modeling of the droplet enables the understanding of the conversion of chemical species in more detail.

Electron microscopy of microstructural transformation in electrodeposited Ni-rich, Ag-Ni film

Ag-Ni films were electrodeposited over a Cu substrate. Structural characterization revealed a fibrous microstructure with an amorphous structure for the as-deposited film. Isothermal annealing at 400 degrees C of the film inside transmission electron microscope led to amorphous-to-crystalline transition along with the evolution of nano-sized particles in the microstructure. The crystalline phase was Ni-Ag solid solution. The relative volume fraction of the nano-sized particles increased gradually with time. There was however no detectable decomposition of solid solution phase till about 4 h of annealing. Beyond 4 h phase separation initiated and pure Ag and Ni phases formed in the film. This study provides a methodology by which microstructural engineering of as-electrodeposited amorphous Ag-Ni films can be conducted to isolate a particular microstructure in order to tap specific potentially usable functionalities. (C) 2013 Elsevier B.V. All rights reserved.

Phase equilibria in the system Sm-Rh-O and thermodynamic and thermal studies on SmRhO3

Using isothermal equilibration, phase relations are established in the system Sm-Rh-O at 1273 K. SmRhO3 with GdFeO3-type perovskite structure is found to be the only ternary phase. Solid-state electrochemical cells, containing calcia-stabilized zirconia as an electrolyte, are used to measure the thermodynamic properties of SmRhO3 formed from their binary component oxides Rh2O3 (ortho) and Sm2O3 (C-type and B-type) in two different temperature ranges. Results suggest that C-type Sm2O3 with cubic structure transforms to B-type Sm2O3 with monoclinic structure at 1110 K. The standard Gibbs energy of transformation is . Standard Gibbs energy of formation of SmRhO3 from binary component oxides Rh2O3 and Sm2O3 with B-type rare earth oxide structure can be expressed as . The decomposition temperature of SmRhO3 estimated from the extrapolation of electrochemical data is 1665 (+/- 2) K in air and 1773 (+/- 3) K in pure oxygen. Temperature-composition diagrams at constant oxygen pressures are constructed for the system Sm-Rh-O. Employing the thermodynamic data for SmRhO3 from emf measurement and auxiliary data for other phases from the literature, oxygen potential-composition phase diagram and 3-D chemical potential diagram for the system Sm-Rh-O at 1273 K are developed.

High Proton Mobility, Solvent Induced Single Crystal to Single Crystal Structural Transformation, and Related Studies on a Family of Compounds Formed from Mn-3 Oxo-Clusters

The reaction between 4,4'-sulfonyldibenzoic acid (H(2)SDBA) and manganese under mild conditions resulted in the isolation of two new three-dimensional compounds, Mn-4(C14H8O6S)(4)(DMA)(2)]center dot 3DMA, I, and Mn-3(C14H8O6S)(3)(DMA)(2)(MeOH)]center dot DMA, IIa. Both structures have Mn-3 trimer oxo cluster units. While the Mn-3 oxoclusters are connected through octahedral manganese forming one-dimensional Mn-O-Mn chains in I, the Mn-3 units are isolated in IIa. The SDBA units connect the Mn-O-Mn chains and the Mn-3 clusters giving rise to the three-dimensional structure. Both compounds have coordinated and free solvent molecules. In IIa, two different solvent molecules are coordinated, of which one solvent can be reversibly exchanged by a variety of other similar solvents via a solvent-mediated single crystal to single crystal (SCSC) transformation. The free lattice DMA solvent molecules in I can be exchanged by water molecules resulting in hydrophilic channels. Proton conductivity studies on I reveals a high proton mobility with conductivity values of similar to 0.87 x 10(-3) Omega(-1) cm(-1) at 34 degrees C and 98% RH, which is comparable to some of the good proton conductivity values observed in inorganic coordination polymers. We have also shown structural transformation of I to IIa through a possible dissolution and recrystallization pathway. In addition, both I and IIa appear to transform to two other manganese compounds H3O]Mn-3(mu(3)-OH)(C14H8O6S)(3)(H2O)](DMF)(5) and H3O](2)Mn-7(mu 3-OH)(4)(C14H8O6S)(6)(H2O)(4)](H2O)(2)(DMF)(8) under suitable reaction conditions. We have partially substituted Co in place of Mn in the Mn-3 trimer clusters forming CoMn2(C14H8O6S)(3)(DMA)(2)(EtOH)]center dot DMA, III, a structure that is closely related to IIa. All the compounds reveal antiferromagnetic behavior. On heating, the cobalt substituted phase (compound III) forms a CoMn2O4 spinel phase with particle sizes in the nanometer range.

A transmission electron microscopy and X-ray photoelectron spectroscopy study of annealing induced gamma-phase nucleation, clustering, and interfacial dynamics in reactively sputtered amorphous alumina thin films

Pure alpha-Al2O3 exhibits a very high degree of thermodynamical stability among all metal oxides and forms an inert oxide scale in a range of structural alloys at high temperatures. We report that amorphous Al2O3 thin films sputter deposited over crystalline Si instead show a surprisingly active interface. On annealing, crystallization begins with nuclei of a phase closely resembling gamma-Alumina forming almost randomly in an amorphous matrix, and with increasing frequency near the substrate/film interface. This nucleation is marked by the signature appearance of sharp (400) and (440) reflections and the formation of a diffuse diffraction halo with an outer maximal radius of approximate to 0.23 nm enveloping the direct beam. The microstructure then evolves by a cluster-coalescence growth mechanism suggestive of swift nucleation and sluggish diffusional kinetics, while locally the Al ions redistribute slowly from chemisorbed and tetrahedral sites to higher anion coordinated sites. Chemical state plots constructed from XPS data and simple calculations of the diffraction patterns from hypothetically distorted lattices suggest that the true origins of the diffuse diffraction halo are probably related to a complex change in the electronic structure spurred by the a-gamma transformation rather than pure structural disorder. Concurrent to crystallization within the film, a substantially thick interfacial reaction zone also builds up at the film/substrate interface with the excess Al acting as a cationic source. (C) 2015 AIP Publishing LLC.

Phase stability of silver particles embedded calcium phosphate bioceramics

In this paper, we report the compositional variation-dependent phase stability of hydroxyapatite (Ca-10(PO4)(6)(OH)(2)) on doping with silver. The transformation of hydroxyapatite to (beta/alpha) tricalcium phosphate phases during sintering has been explored using Raman spectroscopy and X-ray diffraction techniques. The optical absorption spectroscopy analysis reveals the presence of Ag+ ions at low doping levels. As the doping increases, abundance of Ag particles is enhanced.

Effect of processing route on phase stability in equiatomic multicomponent Ti20Fe20Ni20Co20Cu20 high entropy alloy

The evolution of microstructure and phase formation in equiatomic Ti20Fe20Ni20Co20Cu20 high entropy alloy synthesised by conventional arc melting followed with suction casting and ball milling with spark plasma sintering route is distinctly different. The cast microstructure exhibits one body centre cubic and two face centre cubic high entropy phases based on titanium, cobalt and copper respectively along with a eutectic containing Ti2Ni type Laves phase. On the contrary, spinodal decomposed microstructure consisting of cobalt and copper solid solution is obtained in the sintered sample. However, long term annealing of cast sample at 950 degrees C reveals a eutectoid transformation with different phases than the cast sample. The aforementioned observations are discussed using CALPHAD thermodynamical approach and available literature.

Anomalous reduction in domain wall displacement at the morphotropic phase boundary of the piezoelectric alloy system PbTiO3-BiScO3

A comparative study of field-induced domain switching and lattice strain was carried out by in situ electric-field-dependent high-energy synchrotron x-ray diffraction on a morphotropic phase boundary (MPB) and a near-MPB rhombohedral/pseudomonoclinic composition of a high-performance piezoelectric alloy (1-x) PbTiO3-(x)BiScO3. It is demonstrated that the MPB composition showing large d(33) similar to 425 pC/N exhibits significantly reduced propensity of field-induced domain switching as compared to the non-MPB rhombohedral composition (d(33) similar to 260 pC/N). These experimental observations contradict the basic premise of the martensitic-theory-based explanation which emphasizes on enhanced domain wall motion as the primary factor for the anomalous piezoelectric response in MPB piezoelectrics. Our results favor field-induced structural transformation to be the primary mechanism contributing to the large piezoresponse of the critical MPB composition of this system.

Numerical Investigation on Laser Transformation Hardening with Different Temporal Pulse Shapes

A 3-D numerical model for pulsed laser transformation hardening (LTH) is developed using the finite element method. In this model, laser spatial and temporal intensity distribution, temperature-dependent thermophysical properties of material, and multi-phase transformations are considered. The influence of laser temporal pulse shape on connectivity of hardened zone, maximum surface temperature of material and hardening depth is numerically investigated at different pulse energy levels. Results indicate that these hardening parameters are strongly dependent on the temporal pulse shape. For the rectangular temporal pulse shape, the temperature field obtained from this model is in excellent agreement with analytical solution, and the predicted hardening depth is favorably compared with experimental one. It should be pointed out that appropriate temporal pulse shape should be selected according to pulse energy level in order to achieve desirable hardening quality under certain laser spatial intensity distribution.

Thermodynamics of the displacive mechanism of alpha(1) transformation in a beta

Thermodynamics of the displacive mechanism of plate-shaped phase alpha(1) was analyzed in beta'Cu-Zn alloys. It was proposed that the displacive transformation of the alpha(1) plate took place in the solute-depleted region formed in the parent phase during the incubation period. The thermodynamic analysis indicated that the driving force of alpha(1) transformation, Delta G, increased with the reduction of x(d), the solute concentration of the depleted region. And, Delta G could overcome-the transformation barrier with solute depletion to a certain degree. In addition, x(d) was higher than the equilibrium concentration in the phase diagram. Therefore, the shear formation of alpha(1) plate in the solute-depleted region was thermodynamically supported.