Degree of conversion and hardness of two different systems of the vitrebond™ glass ionomer cement light cured with blue LED

This study investigated the physicochemical properties of the new formulation of the glass ionomer cements through hardness test and degree of conversion by infrared spectroscopy (FTIR). Forty specimens (n = 40) were made in a metallic mold (4 mm diameter × 2 mm thickness) with two resin-modified glass ionomer cements, Vitrebond™ and Vitrebond™ Plus (3M/ ESPE). Each specimen was light cured with blue LED with power density of 500 mW/cm2during 30 s. Immediately after light curing, 24h, 48h and 7 days the hardness and degree of conversion was determined. The Vickers hardness was performed by the MMT-3 microhardness tester using load of 50 gm force for 30 seconds. For degree of conversion, the specimens were pulverized, pressed with KBr and analyzed with FT-IR (Nexus 470). The statistical analysis of the data by ANOVA showed that the Vitrebond™ and Vitrebond™ Plus were no difference significant between the same storage times (p > 0.05). For degree of conversion, the Vitrebond™ and Vitrebond™ Plus were statistically different in all storage times after light curing. The Vitrebond™ showed higher values than Vitrebond™ Plus (p < 0.05). The performance of Vitrebond™ had greater results for degree of conversion than Vitrebond™ Plus. The correlation between hardness and degree of conversion was no evidence in this study.

Si-based thin film coating on Y-TZP: Influence of deposition parameters on adhesion of resin cement

This study evaluated the influence of deposition parameters for Si-based thin films using magnetron sputtering for coating zirconia and subsequent adhesion of resin cement. Zirconia ceramic blocks were randomly divided into 8 groups and specimens were either ground finished and polished or conditioned using air-abrasion with alumina particles coated with silica. In the remaining groups, the polished specimens were coated with Si-based film coating with argon/oxygen magnetron discharge at 8:1 or 20:1 flux. In one group, Si-based film coating was performed on air-abraded surfaces. After application of bonding agent, resin cement was bonded. Profilometry, goniometry, Energy Dispersive X-ray Spectroscopy and Rutherford Backscattering Spectroscopy analysis were performed on the conditioned zirconia surfaces. Adhesion of resin cement to zirconia was tested using shear bond test and debonded surfaces were examined using Scanning Electron Microscopy. Si-based film coating applied on air-abraded rough zirconia surfaces increased the adhesion of the resin cement (22.78 ± 5.2 MPa) compared to those of other methods (0-14.62 MPa) (p = 0.05). Mixed type of failures were more frequent in Si film coated groups on either polished or air-abraded groups. Si-based thin films increased wettability compared to the control group but did not change the roughness, considering the parameters evaluated. Deposition parameters of Si-based thin film and after application of air-abrasion influenced the initial adhesion of resin cement to zirconia. © 2013 Elsevier B.V. All rights reserved.

Influência do sistema de cimentação adesiva e da fonte de luz fotoativadora na resistência à extrusão de pinos de fibra de vidro

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Avaliação in vitro da microinfiltração marginal em restaurações indiretas inlay de porcelana. Efeito de diferentes agentes cimentantes

Pós-graduação em Ciências Odontológicas - FOAR

Efeito da altura do pilar de diferentes cimentos e das ciclagens térmica e mecânica sobre a resistência máxima á tração de infraestruturas metálicas cimentadas

Pós-graduação em Reabilitação Oral - FOAR

Efeito de tratamento de superfície do titânio comercialmente puro na resistência de união com cimentos ionomérico e resinosos

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Resistência de união de cimentos resinosos, ao cisalhamento, variando o substrato e o material restaurador

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Influência da espessura da cerâmica, do tempo de fotopolimerização e do cimento resinoso na resistência de união à microtração de uma cerâmica vítrea cimentada à dentina humana

Pós-graduação em Odontologia Restauradora - ICT

Avaliação por microdureza Vickers da profundidade de polimerização de cimentos resinosos na cimentação de pinos de fibra de vidro empregando diferentes fontes de luz

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Avaliação da dureza superficial de cimentos resinosos após cimentação de pinos de fibra de vidro: efeito de profundidade de polimerização e sistemas adesivos

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Preparation of refractory calcium aluminate cement using the sonochemical process

Calcium aluminate cements (CAC) were prepared using the sonochemical process, followed by heat treatment. A study was made of the action of ultrasonic waves and the influence of thermal treatment conditions on two initial molar compositions of 1:1 and 1:2 of calcia:alumina. The aqueous suspension containing the raw materials (A-50 alumina and CaO) was subjected to an ultrasonic bath, followed by drying and burning at 1000, 1200 and 1300 ºC. These cements were characterized by SEM, XRD and the mechanical strength was evaluated by splitting tensile tests, using commercial cement as a reference. Furthermore, the phases were semi-quantified using the Rietveld method. The results show that hydration and sonochemical action increased the reactivity of the raw materials during firing and that phase formation is dependent on the thermal treatment conditions. The CAC cements were obtained at temperatures at least 200 ºC lower than those used in conventional methods, indicating the potential of this route of synthesis.

Avaliação da resistência à remoção por tração de coroas metálicas fixadas com cimentos resinosos e da dureza desses materiais em função do método de ativação

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influência do tratamento de superfície e do tipo de cimento na retenção de coroas YTZP

Pós-graduação em Odontologia Restauradora - ICT

Comparison of Physicochemical Surface Conditioning Methods for Adhesion of bis-GMA Resin Cement to Particulate Filler Composite and Surface Characterization

This study compared the effect of physicochemical surface conditioning methods on the adhesion of bis-GMA-based resin cement to particulate filler composite (PFC) used for indirect dental restorations. PFC blocks (N (block)=54, n (block)=9 per group) were polymerized and randomly subjected to one of the following surface conditioning methods: a) No conditioning (Control-C), b) Hydrofluoric acid (HF)etching for 60s (AE60), c) HF for 90s (AE90), d) HF for 120s (AE120), e) HF for 180s (AE180), and f) air-abrasion with 30 mu m silica-coated alumina particles (AB). The conditioned surfaces were silanized with an MPS silane, and an adhesive resin was applied. Resin composite blocks were bonded to PFC using resin cement and photo-polymerized. PFC-cement-resin composite blocks were cut under coolant water to obtain bar specimens (1mmx0.8mm). Microtensile bond strength test (mu TBS)was performed in a universal testing machine (1mm/min). After debonding, failure modes were classified using stereomicroscopy. Surface characterization was performed on a set of separate specimen surfaces using Scanning Electron Microscopy (SEM), X-Ray Dispersive Spectroscopy (XDS), X-Ray Photoelectron Spectroscopy (XPS), and Fourier Transform-Raman Spectroscopy (FT-RS). Mean mu TBS (MPa) of C (35.6 +/- 4.9) was significantly lower than those of other groups (40.2 +/- 5.6-47.4 +/- 6.1) (p<0.05). The highest mu TBS was obtained in Group AB (47.4 +/- 6.1). Prolonged duration of HF etching increased the results (AE180: 41.9 +/- 7), but was not significantly different than that of AB (p>0.05). Failure types were predominantly cohesive in PFC (34 out of 54) followed by cohesive failure in the cement (16 out of 54). Degree of conversion (DC) of the PFC was 63 +/- 10%. SEM analysis showed increased irregularities on PFC surfaces with the increased etching time. Chemical surface analyses with XPS and FT-RS indicated 11-70% silane on the PFC surfaces that contributed to improved bond strength compared to Group C that presented 5% silane, which seemed to be a threshold. Group AB displayed 83% SiO2 and 17% silane on the surfaces.