Influence of the degree of grafting on the morphology and mechanical properties of blends of poly(butylene terephthalate) and glycidyl methacrylate grafted poly(ethylene-co-propylene) (EPR)

Poly(ethylene-co-propylene) (EPR) was functionalized to varying degrees with glycidyl methacrylate (GMA) by melt grafting processes. The EPR-graft-GMA elastomers were used to toughen poly(butylene terephthalate) (PBT). Results showed that the grafting degree strongly influenced the morphology and mechanical properties of PBT/EPR-graft-GMA blends. Compatibilization reactions between the carboxyl and/or hydroxyl of PBT and epoxy groups of EPR-graft-GMA induced smaller dispersed phase sizes and uniform dispersed phase distributions. However, higher degrees of grafting (>1.3) and dispersed phase contents (>10 wt%) led to higher viscosities and severe crosslinking reactions in PBT/EPR-graft-GMA blends, resulting in larger dispersed domains of PBT blends. Consistent with the change in morphology, the impact strength of the PBT blends increased with the increase in EPR-graft-GMA degrees of grafting for the same dispersion phase content when the degree of grafting was below 1.8. However, PBT/EPR-graft-GMA1.8 displayed much lower impact strength in the ductile region than a comparable PBT/EPR-graft-GMA1.3 blend (1.3 indicates degree of grafting).

Influence of rubber content in ABS in wide range on the mechanical properties and morphology of PC/ABS blends with different composition

A series of acrylonitrile-butadiene-styrene (ABS) with different rubber content were prepared by diluting ABS grafting copolymer containing 60% rubber with a styrene-acrylonitrile copolymer. ABS prepared were blended with bisphenol-A-polycarbonate (PC) at the ratio of 70/30, 50/50, and 30/70 to prepare PC/ABS blends. Influence of rubber content in ABS on the properties of ABS and PC/ABS blends were investigated. PC/ABS blends with different compositions got good toughness when the rubber in ABS increased to the level that ABS itself got good toughness. The tensile properties and processability of PC/ABS blends decreased with the increase of the total rubber content introduced into the blends. ABS with the rubber content of 30 wt% is most suitable to be used to prepare PC/ABS blends. The rubber content in ABS affected the viscosity of ABS, and subsequently the viscosity ratio of PC to ABS. As a result, the morphology of PC/ABS blends varied. The increase of rubber content in ABS results in finer structure of PC/ABS blends.

Effect of the compatibilization of linear low-density polyethylene-g-acrylic acid on the morphology and mechanical properties of poly(butylene terephthalate)/linear low-density polyethylene blends

A poly(butylene terephthalate) (PBT)/linear low-density polyethylene (LLDPE) alloy was prepared with a reactive extrusion method, For improved compatibility of the blending system, LLDPE grafted with acrylic acid (LLDPE-g-AA) by radiation was adopted in place of plain LLDPE. The toughness and extensibility of the PBT/LLDPE-g-AA blends, as characterized by the impact strengths and elongations at break, were much improved in comparison with the toughness and extensibility of the PBT/LLDPE blends at the same compositions. However, there was not much difference in their tensile (or flexural) strengths and moduli. Scanning electron microscopy photographs showed that the domains of PBT/LLDPE-g-AA were much smaller and their dispersions were more homogeneous than the domains and dispersions of the PBT/ T,T PE blends. Compared with the related values of the PBT/LLDPE blends, the contents and melting temperatures of the usual spherulites of PBT in PBT/LLDPE-g-AA decreased.

Morphology, crystallization behaviors, and mechanical properties of PA1010/HIPS and PA1010/HIPS-g-MA blends

The binary blends of polyamide 1010 (PA1010) with the high-impact polystyrene (HIPS)/maleic anhydride (MA) graft copolymer (HIPS-g-MA) and with HIPS were prepared using a wide composition range. Different blend morphologies were observed by scanning electron microscopy according to the nature and content of PA1010 used. Compared with the PA1010/HIPS binary blends, the domain sizes of dispersed-phase particles in PA1010/HIPS-g-MA blends were much smaller than that in PA1010/HIPS blends at the same compositions. It was found that the tensile properties of PA1010/HIPS-g-MA blends were obviously better than that of PA 1010/HIPS blends. Wide-angle xray diffraction analyses were performed to confirm that the number of hydrogen bonds in the PA1010 phase decreased in the blends of PA1010/HIPS-g-MA. These behaviors could be attributed to the chemical interactions between the two components and good dispersion in PA1010/HIPS-g-MA blends.

Mechanical relaxation time of comblike polymer electrolyte

Using poly(styrene-co-maleic anhydride) as the backbone and poly(ethylene glycol) methyl ether as side chains,three kinds of comblike polymers of different side chain length were synthesized. The Li-salt complexes and their firms were prepared. The dynamic mechanical properties were investigated. It was found that the main chain was rigid and the side chain was flexible in this comblike polymer system. Based on the time-temperature equivalence principle, a master curve was constructed. By selecting T-alpha as reference temperature, Arrhenius plots of shift factor and iso-free-volume plots were attained. The values of WLF parameters C-1 and C-2 increase with increasing salt concentration. By reference to T-0 = 50 degrees C, the relation between the average relaxation time 1g tau(c) and Li-salt concentration C is linear. The master curves are displaced progressively to higher frequencies as the M-w of side chains is increased. The relation between the average relaxation time 1g tau(n) and M-w of side chains is also linear. And the master curves are movable with the change of salts. It shows the effect of different kinds of salt on relaxation time.

Morphology, thermal behavior, and mechanical properties of PA6/UHMWPE blends with HDPE-g-MAH as a compatibilizing agent

A functionalized high-density polyethylene (HDPE) with maleic anhydride (MAH) was prepared using a reactive extruding method. This copolymer was used as a compatibilizer of blends of polyamide 6 (PA6) and ultrahigh molecular weight polyethylene (UHMWPE). Morphologies were examined by a scanning electron microscope. It was found that the dimension of UHMWPE and HDPE domains in the PA6 matrix decreased dramatically, compared with that of the uncompatibilized blending system. The size of the UHMWPE domains was reduced from 35 mu m (PA6/UHMWPE, 80/20) to less than 4 mu m (PA6/UHMWPE/HDPE-g-MAH, 80/20/20). The tensile strength and Izod impact strength of PA6/UHMWPE/HDPE-g-MAH (80/20/20) were 1.5 and 1.6 times as high as those of PA6/UHMWPE: (80/20), respectively. This behavior could be attributed to chemical reactions between the anhydride groups of HDPE-g-MAH and the terminal amino groups of PA6 in PA6/UHMWPE/HDPE-g-MAH blends. Thermal analysis was performed to confirm that the above chemical reactions took place during the blending process. (C) 2000 John Wiley & Sons, Inc.

Mechanical properties of poly(beta-hydroxybutyrate)/poly(ethylene oxide) blends

Tensile properties of poly (P-hydroxybutyrate)/poly (ethylene oxide) (PHB/PEO) blends were reported in this paper. It was found that the blends of PHB with different molecular-weight PEO exhibited different mechanical properties. The mechanical properties of the blends of PHB and PEO3 (M-w=0.3x10(6)) were very poor. However, the blends of PHB and PEO5 (M-w=5x10(6)) showed compatible in mechanical properties. Excellent synergism was observed not only in tensile stress and tensile elongation but also in modulus. Moreover, the ductility of the blends could be improved further under proper heat-treatment.

Radiation effects on the immiscible polymer blend of nylon1010 and high-impact strength polystyrene (II): mechanical properties and morphology

The paper studies the morphology and mechanical properties of immiscible binary blends of the nylon 1010 and HIPS through the radiation crosslinking method. In this blend, the HIPS particles were the dispersed phases in the nylon 1010 matrix. With increasing of dose, the elastic modulus increased, However, the tensile strength. elongation at bleak and the energy of fracture increased to a maximum at a dose of 0.34 MGy, then reduced with the increasing of dose. SEM photographs show that the hole sizes are not changed obviously at low dose and at high dose, remnants that cannot be dissolved in formic acid and THF can be observed in the holes and on the surface. TEM photographs showed that radiation destroys the rubber phases in the polymer blend. (C) 2001 Elsevier Science Ltd. All rights reserved.

A study of the effect of shell content on the mechanical properties of polycarbonate/poly(butyl acrylate)-cs-poly(methyl methacrylate) blends

The toughening effect of the shell content of a core-shell latex polymer poly(butyl acrylate) (PBA)-cs-poly(methyl methacrylate) (PMMA) on its blends with polycarbonate (PC) was studied. The changes of mechanical properties, morphology, and compatibility of the blends of PC/PBA-cs-PMMA with the change of the shell thickness of PBA-cs-PMMA were investigated. It is interesting to notice that mechanical properties of the blends are very sensitive to the shell thickness (i.e., shell content), and that there is a possibility to adjust the impact and tensile properties of the blend by selecting a PBA-cs-PMMA with a proper core/shell ratio. Hence, a modified PC material with balanced mechanical properties may be prepared.

Effect of the core-shell latex polymer content on the compatibility, morphology and mechanical properties of PC/PBA-cs-PMMA blends

The toughening effect of the content of a core-shell poly(butyl acrylate)/poly(methyl methacrylate) latex polymer (PBA-cs-PMMA) on the mechanical properties, morphology and compatibility of its blends with polycarbonate(PC), i.e., PC/PBA-cs-PMMa, was studied. The mechanical properties of the blends are strongly affected by varying the content of PBA-cs-PMMA in the blend. When the PBA-cs-PMMA content is only 5 wt.-%, the impact strength of PC/PBA-cs-PMMA is almost 19 times as high as that of pure PC, indicating that PBA-cs-PMMA is a very good impact modifier for PC. With increasing interphacial layer thickness and decreasing interphacial tension, the interphacial activity becomes more and more effective and, at the same time, miscibility increases too.

Effects of the compatibilizer PP-g-GMA on morphology and mechanical properties of PP/PC blends

Effects of the compatibilizer polypropylene grafted with glycidyl methacrylate(PP-g-GMA) on the morphology, thermal, rheological and mechanical properties of polypropylene and polycarbonate blends (PP/PC) were studied. It was found that the addition of PP-g-GMA significantly changed their morphology. The mean size of domains reduced from 20 mu m to less than 5 mu m. The dispersed domain size is also strongly dependent upon the content of PP-g-GMA. The interfacial tension of PP/PC/PP-g-GMA (50/30/20) is only about one-tenth of PP/PC (70/30). The crystallization temperature of PP in PP/PC/PP-g-GMA is 5-8 degrees C higher than that of PP in PP/PC blends. Characterization studies based on mechanical properties, differential scanning calorimetry, rheology and morphological evidence obtained by using scanning electron microscopy support the hypothesis that an in-situ copolymer PP-g-PC was formed during the blending process. (C) 1997 Elsevier Science Ltd.

Studies on biodegradable poly(hexano-6-lactone) fibers 1. Structure and properties of drawn poly(hexano-6-lactone) fibers

Using high molecular weight (M-n=80,000) Poly(hexano-6-lactone) (PCL'), tough and high tenacity PCL monofilaments with various draw ratios (undrawn to 9 times drawn) were prepared by melt-spinning. The relationship between microstructure and properties of the PCL fibers is described in this current IUPAC Technical Report. Analysis of microstructure of the drawn PCL fibers by wide-angle X-ray diffraction revealed typical c-axis orientation with an increase in crystallinity. It was also supported by sonic velocity measurements. The thermal, mechanical, and dynamic mechanical properties of the PCL fibers were affected significantly by draw ratio. DSC thermograms showed that the melting temperature and the enthalpy of fusion increased with draw ratio. The temperature dependence curves of dynamic viscoelasticity showed that the temperature at tan delta peak of alpha dispersion corresponding to the glass transition temperature shifted toward higher temperature and the peak value of tan delta decreased with draw ratio. The dynamic storage modulus and the sonic modulus increased with draw ratio. These results are due to the increase in crystallinity and molecular orientation with drawing, and are responsible for an increase in tensile tenacity as well as knot tenacity of the PCL fibers.

Morphology, mechanical properties and interfacial behaviour of PA1010/PP/PP-g-GMA ternary blends

Morphology, mechanical properties, and interfacial interaction of polyamide 1010/polypropylene (PA1010/ PP) blends compatibilized with polypropylene grafted with glycidyl methacrylate (PP-g-GMA) were studied. It was found that the size of the PP domains, tensile and impact strength of ternary blends, and adhesion fracture energy between two layers of PA1010 and PP were all significantly dependent on the PP-g-GMA contents in the PP layer. Correlations between morphology and related properties were sought. The improvements in properties have been attributed to chemical and physical interaction occurring between PA1010 and PP-g-GMA. (C) 1997 Elsevier Science Ltd.

Morphologies and mechanical properties of epoxy resins toughened by hydroxyl-terminated butadiene-acrylonitrile copolymer

The morphologies and mechanical properties of epoxy resins toughened by hydroxyl-terminated butadiene-acrylonitrile copolymer (HTBN) and cured with hexahydrophthalic anhydride were studied, The results show that the level of HTBN in epoxy resin, content of acrylonitrile in HTBN and curing temperature influence the morphology and then influence the mechanical properties of cured epoxy resin.

Morphology, thermal behavior, and mechanical properties of PA1010/PP and PA1010/PP-g-GMA blends

The modification of polypropylene (PP) was accomplished by melt grafting glycidyl methacrylate (GMA) on its molecular chains. The resulting PP-g-GMA was used to prepare binary blends of polyamide 1010 (PA1010) and PP-g-GMA. Different blend morphologies were observed by scanning electron microscopy (SEM) according to the nature and content of PA1010 used. Comparing the PA1010/PP-g-GMA and PA1010/PP binary blends, the size of the domains of PP-g-GMA were much smaller than that of PP at the same compositions. It was found that mechanical properties of PA1010/PP-g-GMA blends were obviously better than that of PA1010/PP blends, and the mechanical properties were significantly influenced by wetting conditions for uncompatibilized and compatibilized blends. A different dependence of the flexural modulus on water was found for PA1010/PP and PA1010/PP-g-GMA. These behaviors could be attributed to the chemical interactions between the two components and good dispersion in PA1010/PP-g-GMA blends. Thermal and rheological analyses were performed to confirm the possible chemical reactions taking place during the blending process. (C) 1997 John Wiley & Sons, Inc.