The presence of chloride ions is one of the primary factors causing the degradation of reinforced concrete structures. An investigation to monitor ingress of chlorides during a 24-week wetting and drying exposure regime to simulate conditions in which multiple-mode transport mechanisms are active was conducted on a variety of binders. Penetration was evaluated using free and total chloride profiles. Acid extraction of chlorides is quantitatively reliable and practical for assessing penetration. X-ray diffraction was used to determine the presence of bound chlorides and carbonation. The ability of the cement blends to resist chloride penetration was, from best to worst, ground granulated blast-furnace slag, microsilica, pulverised-fuel ash, Portland cement. The effect of carbonation on binding capability was observed and the relative quantity of chlorides also showed a correlation with the amount of chlorides bound in the form of Friedel’s salt.
Resumo:
We determine the cyclic behaviour of Volterra composition operators, which are defined as $(V_\phif)(x) =\int_0^{\phi(x)}f(t) dt$, $f ? L^p[0, 1]$, 1\leq p <\infty$,
where $?$ is a measurable self-map of [0, 1]. The cyclic behaviour of $V_\phi$ is essentially determined by the behaviour of the inducing symbol $\phi$ at 0 and at 1. As a particular result, we provide new examples of quasinilpotent supercyclic operators, which extend and complement previous ones of Hector Salas.
Resumo:
NiTi wires and their weldments are commonly used in micro-electro-mechanical systems (MEMS), and in such applications, cyclic loading are commonly encountered. In this paper, the bending-rotation fatigue (BRF) test was used to study the bending fatigue behavior of NiTi wire laser weldment in the small-strain regime. The fracture mechanism, which includes crack initiation, crack growth and propagation of the weldment in the BRF test, was investigated with the aid of SEM fractography and discussed in terms of the microstructure. It was found that crack initiation was primarily surface-condition dependent. The cracks were found to initiate at the surface defects at the weld zone (WZ) surface, and the crack propagation was assisted by the gas inclusions in the WZ. The weldment was finally fractured in a ductile manner. The fatigue life was found to decrease with increasing surface strain and also with increasing bending frequency (controlled by the rotational speed in the BRF test). In comparison, the fatigue life of the unwelded NiTi wires was higher than their welded counterparts at all strain levels and bending frequencies. The decrease in fatigue resistance of the weldment could be attributed to the surface and microstructural defects introduced during laser welding.
Resumo:
NiTi wires of 0.5 mm diameter were laser welded using a CW 100-W fiber laser in an argon shielding environment with or without postweld heat-treatment (PWHT). The microstructure and the phases present were studied by scanning-electron microscopy (SEM), transmission-electron microscopy (TEM), and X-ray diffractometry (XRD). The phase transformation behavior and the cyclic stress–strain behavior of the NiTi weldments were studied using differential scanning calorimetry (DSC) and cyclic tensile testing. TEM and XRD analyses reveal the presence of Ni4Ti3 particles after PWHT at or above 623 K (350 °C). In the cyclic tensile test, PWHT at 623 K (350 °C) improves the cyclic deformation behavior of the weldment by reducing the accumulated residual strain, whereas PWHT at 723 K (450 °C) provides no benefit to the cyclic deformation behavior. Welding also reduces the tensile strength and fracture elongation of NiTi wires, but the deterioration could be alleviated by PWHT.
Resumo:
Post-weld heat-treatment (PWHT) has been established as one of the cost-effective ways to improve the functional properties, namely shape memory and super-elastic effects (SME and SE), of laser-welded NiTi alloys. However, the functional performance of the laser-welded joint at different working temperatures has not been explored yet. The purpose of this study is to investigate the effect of different working temperatures on the functional properties of the laser-welded NiTi alloys before and after PWHT by applying cyclic deformation tests. Two laser-welded samples: as-welded and heat-treated sample (after PWHT at 350 oC or 623 K) were tested in this work at room temperature, 50 oC (or 323 K) and 75 oC (or 348 K) respectively. The samples were cyclically loaded and unloaded for 10 cycles up to 4 % strain. The critical stress to induce the martensitic transformation and the residual strain after the cyclic tests were recorded. The results indicate that the heat-treated sample exhibited better functional properties than the as-welded sample at room temperature and 50 oC (or 323 K). However, both the as-welded and heat-treated samples failed in the cyclic tests at 75 oC (or 348 K). These findings are important to determine the feasible working temperature range for the laser-welded NiTi components to exhibit desirable functional properties in engineering applications involving cyclic loading.
Resumo:
Abstract Image
An asymmetric total synthesis of the mast cell inhibitor (+)-monanchorin is reported in which a Sharpless AD on 11 and a cyclic sulfate ring opening with an azide feature as key steps. After further manipulation, a novel guanidine-controlled ester reduction provided the guanidine-hemiaminal 25 which underwent Wittig olefination to give 27. Hydrogenation and a second guanidine-controlled reduction of the ester in 28, to obtain aldehyde 29, then set up a trifluoroacetic acid mediated cyclization to give (+)-monanchorin TFA salt.