Photoluminescence in amorphous PLZ

Amorphous and crystalline powder of PLZ was prepared by using the polymeric precursor method. TGA-DSC (Thermal analysis and Differential Scanning Calorimetry) shows the decomposition of polymeric resin, an amorphous phase and the crystallization of powder. Raman scattering of powder shows an amorphous and semicrystalline phase at 450 and 550 degreesC, respectively. XRD (X-ray diffraction pattern) of powder shows high crystallinity at 700 degreesC/3 h. PL (Photoluminescence) analysis of powder at 300 degreesC/3 h shows a broad asymmetric peak at 585 nm and increases of calcining time led to intense peaks of PL at 300 degreesC/6 h. This emission could be attributed to Zr --> O from the oxygen-2p orbitals to the zirconate-3d orbitals. (C) 2003 Elsevier Ltd and Techna S.r.l. All rights reserved.

Distributed feedback multipeak laser emission in Rhodamine 6G doped organic-inorganic hybrids

Organic-inorganic hybrid materials were prepared from an ureasil precursor (ureapropyltriethoxysilane designated as UPTES) and acrylic acid modified zirconium (IV) n-propoxide. Thin films containing rhodamine 6G (Rh6G) were prepared by spin-coating on glass substrates with different Zr:Si molar ratios (Zr:Si = 75:25, 50:50 and 25:75). Refractive index, thickness, number of propagating modes and attenuation coefficient were measured at 543.5, 632.8 and 1550 nm wavelengths by the prism coupling technique. Distributed feedback (DFB) laser effect was observed and studied as a function of films thickness and refractive index.

Hot-pressed 9.5/65/35 PLZT prepared by the polymeric precursor method

A 9.5/65/35 PLZT ceramic with a Pb-0.905 La-0.095 (Zr-0.65 Ti-0.35)(0.976) O-3 + 35 w% PbO formula was prepared using the Pechini method for powder preparation and two-step sintering in an oxygen atmosphere. Thr first step consisted of sintering at 1200 degrees C for 4 h with slow heating and cooling rates. The second step consisted of hot pressing at 1200 degrees C for 3 h, with slow heating and cooling rates and pressing pressures of 20 MPa (initial pressure) and 40 MPa (at sintering temperature). Investigations were made of the powder phase formation and powder morphology, i.e. The structure of sintered and hot-pressed PLZT ceramics. SEM microstructural analyses were carried out on the sintering and hot-pressing processes. (C) 2000 Elsevier B.V. Ltd and Techna S.r.l. All rights reserved.

Linear low density polyethylene (LLDPE) from ethylene using Tp(Ms)NiCl (Tp(Ms) = hydridotris(3-mesitylpyrazol-1-yl)) and CP2ZrCl2 as a tandem catalyst system

Linear low density polyethylene (LLDPE) with different branching contents were prepared from ethylene, without the addition of alpha-olefin comonomer, using a combination of catalyst precursors {Tp(Ms)}NiCl (1) (Tp(Ms) = hydridotris(3-mesitylpyrazol-1-yl)) and Cp2ZrCl2 (2) activated with MAO/TMA (1:1) in toluene at 0degreesC and by varying the nickel loading mole fraction (x(Ni)). The polymerization results showed that the turnover frequencies are strongly dependent on the x(Ni) varying from 6.6 x 10(3) to 32.1 x 10(3) mol[C2H4]/mol[Zr] h. The C-13 NMR spectra of the copolymers showed that the branch contents of the polymers increase as the x(Ni) increase in the medium promoting the production of polymers with a wide range of melting point (T-m) (C) 2004 Elsevier B.V. All rights reserved.

Procedure optimization of silicate rocks dissolution in open vessels for ICP-AES analysis.

The main variables found on procedure of the dissolution silicate rocks using acid dissolution in teflon open vessel for analysis of micro elements by ICP-AES has been determined. The results obtained for some samples showed strong dependence of the rock mineralogical composition, then it was recommended an alkaline fusion step after acid dissolution. The decomposition procedure use 20 mi of an acid mixture of HF:HNO3 in the proportion 3:1 for a fraction of 250 mg pulverized sample. The recommended temperatures were 60 degrees C for attack and 90 degrees C for acid volatilization. The fusion step with 50 mg LiBO2 at 1000 degrees C may be used if non-attacked residue is observed in the solution. The whole time was 6 h per sample. Nine types os silicate rocks that show mineralogical and chemical different compositions were chosen for obtaining the optimization of the variables. The elements used were Ce, Y, Yb and Zr. In addition, ultrassonic nebulization has been used. The percentual standard deviations obtained for five determinations were 0.7 and 1.4 for triplicate samples. The mineralogical and textural information from the petrographical analysis of the samples indicated the need of increasing the fusion step on the optimized procedure.

Small-angle X-ray scattering study of the smart thermo-optical behavior of zirconyl aqueous colloids

The smart thermo-optical systems studied here are based on the unusual thermoreversible sol-gel transition of zirconyl chloride aqueous solution modified by sulfuric acid in the molar ratio Zr/SO4:3/1. The transparency to the visible light changes during heating due to light scattering. This feature is related to the aggregates growth that occurs during gelation. These reversible changes can be controlled by the amount of chloride ions in solution. The thermoreversible sol-gel transition temperature increases from 323 to 343 K by decreasing the molar ratio Cl/Zr from 7.0 to 1.3. In this work the effect of the concentration of chloride ions on the structural characteristics of the system has been analyzed by in situ SAXS measurements during the sol-gel transition carried out at 323 and 333 K. The experimental SAXS curves of sols exhibit three regions at small, medium and high scattering vectors characteristics of Guinier, fractal and Porod regimes, respectively. The radius of primary particles, obtained from the crossover between the fractal and Porod regimes, remains almost invariable with the chloride concentration, and the value (4 Angstrom) is consistent with the size of the molecular precursor. During the sol-gel transition the aggregates grow with a fractal structure and the fractal dimensionality decreases from 2.4 to 1.8. This last value is characteristic of a cluster-cluster aggregation controlled by a diffusion process. Furthermore, the time exponent of aggregate growth presents values of 0.33 and 1, typical of diffusional and hydrodynamic motions. A crossover between these two regimes is observed.

High sinterability of Ca-PZT, synthesized by polymeric and partial oxalate process

This study includes Ca-PZT in the morphotropic phase boundary, MPB process combining the Pechini method, (ZT) and the Partial oxalate method (Ca-PZT) by obtaining single phase particles of ZT phase with a high specific surface area (similar to 110 m(2)/g at 550 degrees C) and narrow particle size distribution. Lead and calcium oxalates were precipitated onto the ZT particle surface and reacted to a solid state interface ZT/Ca-PZT/PbO-CaO. A deviation of a coexistence region from F-T- and F-R-phases to F-R-phase (Zr rich region) was observed. Strong surface area reduction occurs by Ca-PZT crystallization at about 700 degreesC, and demonstrated high sinterability (2.40 m(2)/g - 350 nm) with apparent densities near to 99.9%. Different processing methods did not demonstrate superior results. Studies of calcined powder shows a high sinterability of powder calcined 3 h at 700 degrees C and sintered 3 h at 1000 degreesC coming up to 99.8% of relative density. (C) 2001 Kluwer Academic Publishers.

Preparation of 9/65/35 PLZT thin films deposited by a dip-coating process

Crack-free polycrystalline PLZT (Pb,a)(Zr,Ti)O-3 thin films with the perovskite structure were prepared by dir-coating using the Pechinis process. Lead acetate, hydrated lanthanum carbonate, zirconium n-propoxide and titanium isopropoxide were used as raw materials. The viscosity of the solution was adjusted in the range of 20 to 56 cP and the films were deposited by a dip-coating process on silicon (100) as substrate. Solutions with ionic concentration of 0.1 and 0.2 M were used. Thin film deposition was accomplished by dipping the substrates in the solution with control of withdrawal speed from 5 to 20 mm/min. The thin films were thermally treated in two steps: at 300 degreesC amid 650 degreesC. The influence of withdrawal speed. viscosity, heating rate and ionic concentration on the morphology of PLZT thin film was discussed. (C) 2001 Elsevier B.V. Ltd. All rights reserved.

Stimuli-responsive controlled growth of mono- and bidimensional particles from basic zirconium sulfate hydrosols

A thermostimulated sol-gel transition in a system prepared by mixing a ZrOCl(2) acidified solution to a hot H(2)SO(4) aqueous solution was studied by dynamic theological measurements and quasi-elastic light scattering. The effect of temperature and of molar ratio R(S) = [Zr]/[SO(4)] on the gelation kinetics was analyzed using the mass fractal aggregate growth model. This study shows that the linear growth of aggregates occurs at the early period of transformation, while bidimensional growth occurs at the advanced stage. The bidimensional growth can be shifted toward monodimensional growth by decreasing the aggregation rate by controlling the temperature and/or molar ratio R(S). EXAFS and Raman results gave evidence that the linear chain growth is supported by covalent sulfate bonding between primary building blocks. At the advanced stage of aggregation, the assembly of linear chains through hydrogen bonding gave rise to the growth of bidimensional particles.

Photopatternable di-ureasil-zirconium oxocluster organic-inorganic hybrids as cost effective integrated optical substrates

Organic-inorganic hybrids containing methacrylic acid (McOH, CH(2)= C(CH(3))COOH)) modified zirconium tetrapropoxide, Zr(OPr(n))(4), classed as di-ureasil-zirconium oxo-cluster hybrids, have been prepared and structurally characterized by X-ray diffraction (XRD), small-angle X-ray scattering (SAXS), Fourier transform infrared (FT-IR) and Raman (FT-Raman) spectroscopies, Si and C nuclear magnetic resonance (NMR), and atomic force microscopy (AFM). XRD and SAXS results have pointed out the presence of Si- and Zr-based nanobuilding blocks (NBBs) dispersed into the organic phase. Inter-NBBs correlation distances have been estimated for the pure di-ureasil and a model compound obtained. by hydrolysis/condensation of Zr(OPr(n))(4):McOH (molar ratio 1: 1): d(Si) approximate to 26 +/- 1 angstrom and d(Zr) approximate to 16 +/- 1 angstrom, respectively. In the case of the di-ureasil-zirconium oxo-cluster hybrids, these distances depend on the Zr relative molar percentage (rel. mol. Zr %) (d(Si) ranges from 18 to 25 angstrom and d(Zr) from 14 to 23 angstrom, as the rel. mol. Zr % increases from 5 to 75), suggesting that the Si- and Zr-based clusters are interconstrained. Complementary data from FT-IR, FT-Raman, (29)Si and (13)C NMR, and AFM support to a structural model where McOH-modified Zr-based NBBs (Zr-OMc) are present over the whole range of composition. At low Zr-OMc contents (rel. mol. Zr % <30) the clusters are well-dispersed within the di-ureasil host, whereas segregation occurs at the 0.1 mu m scale at high Zr-OMc concentration (rel. mol. Zr % = 50). No Zr-O-Si heterocondensation has been discerned. Monomode waveguides, diffractions gratings, and Fabry-Perot cavities have been written through the exposure of the hybrid monoliths to UV light. FT-Raman has shown that the chemical process that takes place under illumination is the polymerization of the methacrylate groups of the Zr-OMc NBBs. The guidance region in patterned channels is a Gaussian section located below the exposed surface with typical dimensions of 320 mu m wide and 88 mu m deep. The effective refractive index is 1.5162 (maximum index contrast on the order of 1 x 10(-4)) and the reflection coeficient of the Fabry-Perot cavity (formed by a grating patterned into a 0.278 cm channel) is 0.042 with a free spectral range value of 35.6 GHz.

Reflux synthesis and hydrothermal processing of ZrO2 nanopowders at low temperature

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Influence of structural disorder on the photoluminescence emission of PZT powders

Intense and broad visible photoluminescent (PL) band was observed at room temperature in disordered Pb(Zr(0.53)Ti(0.47))O(3) powders. Structural order-disorder was evaluated by different methods. XANES results pointed to the presence of different coordination modes of disordered Ti powders, and in the ordered sample the local structure around titanium atoms is characteristic of the structurally ordered PZT with only TiO(6) units. Only samples containing simultaneous structural order and disorder in their network present the intense visible PL emission at room temperature.

Determination of cobalt marker in cow ruminal fluid by EDXRF and SRTXRF

This article describes a comparison of conventional energy-dispersive X-ray fluorescence (EDXRF) and synchrotron radiation total-reflection X-ray fluorescence (SRTXRF) for Co determination in ruminal fluid from Holstein cow. This element is used as marker for animal nutrition studies. For EDXRF, 200 mu l of the sample were dried on 6.35 mu m Mylar filmat 60 degrees C. The excitation was carried out using an X-ray tube with Mo target and Zr filter operated at 30 kV/ 20 mA. For SRTXRF, 10 mu l of the samplewere pipetted on a Lucite carrier and dried at 60 degrees C. In both the techniques, Ga was used as internal standard and the acquisition time was 200 s. The trueness of both techniques was evaluated through the standard addition method, the recoveries obtained by SRTXRF and EDXRF were 76 and 99%, and the limits of detection, 13 and 240 mu g l(-1), respectively. Copyright (C) 2011 John Wiley & Sons, Ltd.

Controlling the growth of zirconia needles precursor from a liquid crystal template

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Structure and optical properties of [Ba1-xY2x/3](Zr0.25Ti0.75)O-3 powders