Synthesis and Upconversion Luminescence Properties of GdF3:Er3+, Yb3+

GdF3:Er3+,Yb-3 with Er3+ ion of 3% and Yb3+ ion concentration of 10%, 20% have been prepared by a hydrothermal method. The results of XRD show that all the samples are of an orthorhombic structure. The average crystallite sizes estimated by Scherrer formula are 28 and 26 nm for Gd0.87Yb0.10Er0.03F3 and Gd0.77Yb0.20Er0.03F3, respectively. The Upconversion luminescence spectra of the samples have been studied under 980 run laser excitation. The results show that the green and red upconversion emission can be attributed to the H-2(11/2),S-4(3/2) -> 4I(15/2) and 4F(9/2) -> 4I(15/2) transitions of Er3+, respectively.

Preparation and upconversion luminescence of nanocrystalline Gd2O3 : Er3+, Yb3+

Nanocrystalline Gd1.77Yb0.2 Er0.03O3 samples were prepared by combustion and precipitation methods. Structures and upconversion luminescence properties of samples were studied. The results of XRD show that all samples are cubic structure, the average crystallite size could be calculated as 23 nm and 39 nm, respectively. The lattice constants were obtained. The FT-IR spectra were measured to investigate the vibrational feature of the samples.

Upconversion luminescence of Y2O3 : Er3+, Yb3+ nanoparticles prepared by a homogeneous precipitation method

Y2O3: Er3+, Yb3+ nanoparticles were synthesized by a homogeneous precipitation method without and with different concentrations of EDTA 2Na. Upconversion luminescence spectra of the samples were studied under 980 nm laser excitation. The results of XRD showed that the obtained Y2O3:Er3+,Yb3+ nanoparticles were of a cubic structure. The average crystallite sizes calculated were in the range of 28-40 nm. Green and red upconversion emission were observed, and attributed to H-2(11/2), S-4(3/2) -> I-4(15/2) and F-4(9/2) -> I-4(15/2) transitions of the Er3+ ion, respectively.

Red and green upconversion luminescence of Gd2O3 : Er3+, Yb3+ nanoparticles

Gd2O3:Er3+, Yb3+ nanoparticles have been synthesized by a homogeneous precipitation method with EDTA 2Na of two different concentrations. Upconversion luminescence spectra of the samples have been studied under 980 nm laser excitation. The results of XRD show that obtained Gd2O3:Er3+, Yb3+ nanoparticles are of a cubic structure. The average crystallite sizes could be calculated as 22 and 29 nm, respectively. The strong green and red upconversion emission were observed, and attributed to the H-2(11/2), S-4(3/2) -> I-4(15/2) and F-4(19/2) -> I-4(15/2) transitions of Er3+ ion, respectively.

Effects of doping lanthanide ions in YAG : Ce system on the spectral properties of Ce3+

(Y0.95Ln(0.01)Ce(0.04))(3)Al5O12 phosphors were synthesized by high-temperature solid state reaction under reducing atmosphere and the doping effects of lanthanide ions (Ln(3+)) on the luminescence properties of phosphors were studied. YAG: Ce, Ln spectra of excitation and emission show that the influence between Ce3+ and Ln(3+) can be divided into the following three types

Ternary lanthanide (Er3+, Nd3+, Yb3+, Sm3+, Pr3+) complex-functionalized mesoporous SBA-15 materials that emit in the near-infrared range

The tertiary lanthanide complexes [Ln(hfth)(3)phen] (Ln=Er, Nd, Yb, Sm) and [Pr(tfnb)(3)phen] have been Successfully covalently attached in the ordered SBA-15 mesoporous materials via a functionalized 1,10-phenanthroline group 5-(N,N-bis-3-(triethoxysilyl)propyl)ureyl-1,10-phenanthroline (Phen-Si). The derivative materials [denoted as Ln(hfth)(3)phen-S15 and Pr(tfnb)(3)phen-S15; Ln=Er, Yb, Nd, Sm; hfth=4,4,5,5,6,6,6-heptafluoro-1-(2-thienyl)hexane-1,3-dionate; tfnb=4,4,4-trifluoro-1-(2-naphthyl)-1,3-butanedionate] were characterized by powder X-ray diffraction (XRD), transmission electron microscopy (TEM), and N-2 adsorption/desorption.

Avidin conjugation to up-conversion phosphor NaYF4:Yb3+, Er3+ by the oxidation of the oligosaccharide chains

NaYF4:Yb3+, Er3+ nanoparticles were successfully prepared by a polyol process using diethyleneglycol (DEG) as solvent. After being functionalized with SiO2-NH2 layer, these NaYF4:Yb3+, Er3+ nanoparticles can conjugate with activated avidin molecules (activated by the oxidation of the oligosaccharide chain). The as-formed NaYF4:Yb3+, Er3+ nanoparticles, NaYF4:Yb3+, Er3+ nanoparticles functionalized with amino groups, avidin conjugated amino-functionalized NaYF4:Yb3+, Er3+ nanoparticles were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), atomic force microscopy (AFM), Fourier transform infrared (FT-IR), UV/Vis absorption spectra, and up-conversion luminescence spectra, respectively.

Relationship between charge transfer energies of Yb3+ and Sm3+ and crystal environmental factor

Relationship between charge transfer energies E-CT of Yb3+ and Sm3+ and environmental factors h(e) in various crystals was investigated using a dielectric chemical bond method. Both results show that they have an exponential relation E-CT = A+B exp(-kh(e)), but the exponential factors are different, which indicates that the interaction between the rare earth ions and environment is connected with the kind of rare earth ion. This result provides a method of determining charge transfer energies of Yb3+ and Sm3+ from a crystal structure.

Controllable Red, Green, Blue (RGB) and Bright White Upconversion Luminescence of Lu2O3:Yb3+/Er3+/Tm3+ Nanocrystals through Single Laser Excitation at 980 nm

Lu2O3:Yb3+/Er3+/Tm3+ nanocrystals have been successfully synthesized by a solvothermal process followed by a subsequent heat treatment at 800 degrees C. Powder X-ray diffraction, transmission electron microscopy, upconversion photoluminescence spectra, and kinetic decay were used to characterize the samples. Under single-wavelength diode laser excitation of 980 nm, the bright blue emissions of Lu2O3:Yb3+, Tm3+ nanocrystals near 477 and 490 nm were observed due to the (1)G(4)-> H-3(6) transition of Tm3+. The bright green UC emissions of Lu2O3:Er3+ nanocrystals appeared near 540 and 565 nm were observed and assigned to the H-2(11/2)-> I-4(15/2) and S-4(3/2)-> I-4(15/2) transitions, respectively, of Er3+. The ratio of the intensity of green luminescence to that of red luminescence decreases with an increase of concentration of Yb3+ in Lu2O3:Er3+ nanocrystals.

Avidin conjugation to up-conversion phosphor NaYF4:Yb3+, Er3+ by the oxidation of the oligosaccharide chains

NaYF4:Yb3+, Er3+ nanoparticles were successfully prepared by a polyol process using diethyleneglycol (DEG) as solvent. After being functionalized with SiO2-NH2 layer, these NaYF4:Yb3+, Er3+ nanoparticles can conjugate with activated avidin molecules (activated by the oxidation of the oligosaccharide chain). The as-formed NaYF4:Yb3+, Er3+ nanoparticles, NaYF4:Yb3+, Er3+ nanoparticles functionalized with amino groups, avidin conjugated amino-functionalized NaYF4:Yb3+, Er3+ nanoparticles were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), atomic force microscopy (AFM), Fourier transform infrared (FT-IR), UV/Vis absorption spectra, and up-conversion luminescence spectra, respectively. The biofunctionalization of the NaYF4:Yb3+, Er3+ nanoparticles has less effect on their luminescence properties, i.e., they still show the up-conversion emission (from Er3+, with S-4(3/2) -> I-4(15/2) at similar to 540 nm and F-4(9/2) -> I-4(15/2) at similar to 653 nm), indicative of the great potential for these NaYF4:Yb3+, Er3+ nanoparticles to be used as fluorescence probes for biological system.

Shape-controllable synthesis and upconversion properties of lutetium fluoride (doped with Yb3+/Er3+) microcrystals by hydrothermal process

Lutetium fluorides with different compositions, crystal phases, and morphologies, such as beta-NaLuF4 hexagonal microprisms, microdisks, mirotubes, alpha-NaLuF4 submicrospheres, LuF3 octahedra, and NH4Lu2F7 icosahedra, prolate ellipsoids and spherical particles have been successfully synthesized via a facile hydrothermal route. X-ray diffraction, scanning electron microscopy, transmission electron microscopy, high-resolution transmission electron microscopy, selected area electron diffraction, and photoluminescence spectra were used to characterize the samples. The intrinsic structural feature of lutetium fluorides, the solution pH values, F- sources, and organic additives (Cit(3-) and EDTA) account for the ultimate shape evolutions of the final products. The possible formation mechanisms for products with various architectures have been presented. Additionally, we investigated the upconversion luminescence properties of beta-NaLuF4: 20% Yb3+/2% Er3+ with different morphologies.

Remarkable changes in the optical properties of CeO2 nanocrystals induced by lanthanide ions doping

Highly uniform and well-dispersed CeO2 and CeO2:Eu3+ (Sm3+, Tb3+) nanocrystals were prepared by a nonhydrolytic solution route and characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), X-ray photoelectron spectra (XPS), UV/vis absorption, and photoluminescence (PL) spectra, respectively. The result of XRD indicates that the CeO2 nanocrystals are well crystallized with a cubic structure. The TEM images illustrate that the average size of CeO2 nanocrystals is about 3.5 nm in diameter. The absorption spectrum of CeO2:Eu3+ nanocrystals exhibits red-shifting with respect to that of the undoped CeO2 nanocrystals. Under the excitation of 440 nm (or 426 nm) light, the colloidal solution of the undoped CeO2 nanocrystals shows a very weak emission band with a maximum at 501 nm, which is remarkably enhanced by doping additional lanthanide ions (Eu3+, Tb3+, Sm3+) in the CeO2 nanocrystals. The emission band is not due to the characteristic emission of the lanthanide ions but might arise from the oxygen vacancy which is introduced in the fluorite lattice of the CeO2 nanocrystals to compensate the effective negative charge associated with the trivalent ions.

Enhanced photoluminescence of Ba2GdNbO6: Eu3+/Dy3+ phosphors by Li+ doping

The Ba2GdNbO6: Eu3+/Dy3+ and Li+-doped Ba2GdNbO6: Eu3+/Dy3+ phosphors were prepared by solid-state reaction process. X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM) and photoluminescence (PL) as well as lifetimes, was utilized to characterize the resulting phosphors. Under the excitation of ultraviolet light, the Ba2GdNbO6: Eu3+/Dy3+ and Li+-doped Ba2GdNbO6: Eu3+/Dy3+ show the characteristic emissions of Eu3+ (D-5(0)-F-7(1,2,3) transitions dominated by D-5(0)-F-7(1) at 593 nm) and Dy3+ (F-4(9/2)-H-6(15/2),(13/2) transitions dominated by F-4(9/2)-H-6(15/2) at 494 nm), respectively. The incorporation of Li+ ions into the Ba2GdNbO6: Eu3+/Dy3+ phosphors has enhanced the PL intensities depending on the doping concentration of Li+, and the highest emission was obtained in Ba2Gd0.9NbO6: 0.10Eu(3+), 0.01Li(+) and Ba2Gd0.95NbO6: 0.05Dy(3+), 0.07Li(+), respectively. An energy level diagram was proposed to explain the luminescence process in the phosphors.