Thermoelectric Properties of In-Doped Cu2ZnGeSe4

Recently, much research has been focused on finding new thermoelectric materials. Cu-based quaternary chalcogenides that belong to A(2)BCD(4) (A = Cu; B = Zn, Cd; C = Sn, Ge; D = S, Se, Te) are wide band gap materials and one of the potential thermoelectric materials due to their complex crystal structures. In this study, In-doped quaternary compounds Cu2ZnGe1-xInxSe4 (x = 0, 0.025, 0.05, 0.075, 0.1) were prepared by a solid state synthesis method. Powder x-ray diffraction patterns of all the samples showed a tetragonal crystal structure (space group I-42m) of the main phase with a trace amount of impurity phases, which was further confirmed by Rietveld analysis. The elemental composition of all the samples showed a slight deviation from the nominal composition with the presence of secondary phases. All the transport properties were measured in the temperature range 373-673 K. The electrical resistivity of all the samples initially decreased up to similar to 470 K and then increased with increase in temperature upto 673 K, indicating the transition from semiconducting to metallic behavior. Positive Seebeck coefficients for all the samples revealed that holes are the majority carriers in the entire temperature range. The substitution of In3+ on Ge4+ introduces holes and results in the decrease of resistivity as well as the Seebeck coefficient, thereby leading to the optimization of the power factor. The lattice thermal conductivity of all the samples decreased with increasing temperature, indicating the presence of phonon-phonon scattering. As a result, the thermoelectric figure of merit (zT) of the doped sample showed an increase as compared to the undoped compound.

Tailored specular reflectance properties of bulk Cu based novel intermetallic alloys

Significant research has been pursued to develop solar selective metallic coatings using a variety of coating deposition techniques, with limited attempts to assess the properties of bulk metallic materials for solar energy applications. In developing bulk solar reflectors with good reflectance in the entire solar range, we report a new class of reflector materials based on Cu-Sn intermetallics with tailored substitution of aluminium or zinc. Our experimental results suggest that the arc melted-suction cast Cu (78.8 at%)-Al (21.2 at%) alloy with nanoscale surface roughness can exhibit a combination of 89% bulk specular reflectance and 83% bulk solar reflectance, together with a hardness of 2 GPa. We show that the present alloy design approach paves the way for further opportunities of tuning the spectral properties of this new class of solar reflector material. (C) 2016 Elsevier B.V. All rights reserved.

Stabilization of a Tetrahedral (Mn5+O4) Chromophore in Ternary Barium Oxides as a Strategy toward Development of New Turquoise/Green-Colored Pigments

An experimental investigation of the stabilization of the turquoise-colored chrornophore (Mn5+O4) in various oxide hosts, viz., A(3)(VO4)(2) (A = Ba, Sr, Ca), YVO4, and Ba2MO4 (M = Ti, Si), has been carried out. The results reveal that substitution of Mn5+O4 occurs in Ba-3(VO4)(2) forming the entire solid solution series Ba-3(V1-x MnxO4)(2) (0 < x <= 1.0), while with the corresponding strontium derivative, only up to about 10% of Mn5+O4 substitution is possible. Ca-3(VO4)(2) and YVO4 do not stabilize Mn5+O4 at all. With Ba2MO4 (M = Ti, Si), we could prepare only partially substituted materials, Ba2M1-xMn5+O4+x/2 for x up to 0.15, that are turquoise-colored. We rationalize the results that a large stabilization of the O 2p-valence band states occurs in the presence of the electropositive barium that renders the Mn5+ oxidation state accessible in oxoanion compounds containing PO43-, VO43-, etc. By way of proof-of-concept, we synthesized new turquoise-colored Mn5+O4 materials, Ba-5(BO3)(MnO4)(2)Cl and Ba-5(BO3)(PO4)(MnO4)Cl, based on the apatite-Ba-5(PO4)(3)Cl-structure.

Absence of branches from xylan in Arabidopsis gux mutants reveals potential for simplification of lignocellulosic biomass.

As one of the most abundant polysaccharides on Earth, xylan will provide more than a third of the sugars for lignocellulosic biofuel production when using grass or hardwood feedstocks. Xylan is characterized by a linear β(1,4)-linked backbone of xylosyl residues substituted by glucuronic acid, 4-O-methylglucuronic acid or arabinose, depending on plant species and cell types. The biological role of these decorations is unclear, but they have a major influence on the properties of the polysaccharide. Despite the recent isolation of several mutants with reduced backbone, the mechanisms of xylan synthesis and substitution are unclear. We identified two Golgi-localized putative glycosyltransferases, GlucUronic acid substitution of Xylan (GUX)-1 and GUX2 that are required for the addition of both glucuronic acid and 4-O-methylglucuronic acid branches to xylan in Arabidopsis stem cell walls. The gux1 gux2 double mutants show loss of xylan glucuronyltransferase activity and lack almost all detectable xylan substitution. Unexpectedly, they show no change in xylan backbone quantity, indicating that backbone synthesis and substitution can be uncoupled. Although the stems are weakened, the xylem vessels are not collapsed, and the plants grow to normal size. The xylan in these plants shows improved extractability from the cell wall, is composed of a single monosaccharide, and requires fewer enzymes for complete hydrolysis. These findings have implications for our understanding of the synthesis and function of xylan in plants. The results also demonstrate the potential for manipulating and simplifying the structure of xylan to improve the properties of lignocellulose for bioenergy and other uses.

Study Of The Damage-Induced Anisotropy Of Quasi-Brittle Materials Using The Component Assembling Model

Damage-induced anisotropy of quasi-brittle materials is investigated using component assembling model in this study. Damage-induced anisotropy is one significant character of quasi-brittle materials coupled with nonlinearity and strain softening. Formulation of such complicated phenomena is a difficult problem till now. The present model is based on the component assembling concept, where constitutive equations of materials are formed by means of assembling two kinds of components' response functions. These two kinds of components, orientational and volumetric ones, are abstracted based on pair-functional potentials and the Cauchy - Born rule. Moreover, macroscopic damage of quasi-brittle materials can be reflected by stiffness changing of orientational components, which represent grouped atomic bonds along discrete directions. Simultaneously, anisotropic characters are captured by the naturally directional property of the orientational component. Initial damage surface in the axial-shear stress space is calculated and analyzed. Furthermore, the anisotropic quasi-brittle damage behaviors of concrete under uniaxial, proportional, and nonproportional combined loading are analyzed to elucidate the utility and limitations of the present damage model. The numerical results show good agreement with the experimental data and predicted results of the classical anisotropic damage models.

Validation of component assembly model and extension to plasticity

Material potential energy is well approximated by '' pair-functional '' potentials. During calculating potential energy, the orientational and volumetric components have been derived from pair potentials and embedding energy, respectively. Slip results in plastic deformation, and slip component has been proposed accordingly. Material is treated as a component assembly, and its elastic, plastic and damage properties are reflected by different components respectively. Material constitutive relations are formed by means of assembling these three kinds of components. Anisotropy has been incorporated intrinsically via the concept of component. Theoretical and numerical results indicate that this method has the capacity of reproducing some results satisfactorily, with the advantages of physical explicitness, etc. (c) 2007 Elsevier Ltd. All rights reserved.

Study of the damage-induced anisotropy of quasi-brittle materials using the component assembling model

Damage-induced anisotropy of quasi-brittle materials is investigated using component assembling model in this study. Damage-induced anisotropy is one significant character of quasi-brittle materials coupled with nonlinearity and strain softening. Formulation of such complicated phenomena is a difficult problem till now. The present model is based on the component assembling concept, where constitutive equations of materials are formed by means of assembling two kinds of components' response functions. These two kinds of components, orientational and volumetric ones, are abstracted based on pair-functional potentials and the Cauchy - Born rule. Moreover, macroscopic damage of quasi-brittle materials can be reflected by stiffness changing of orientational components, which represent grouped atomic bonds along discrete directions. Simultaneously, anisotropic characters are captured by the naturally directional property of the orientational component. Initial damage surface in the axial-shear stress space is calculated and analyzed. Furthermore, the anisotropic quasi-brittle damage behaviors of concrete under uniaxial, proportional, and nonproportional combined loading are analyzed to elucidate the utility and limitations of the present damage model. The numerical results show good agreement with the experimental data and predicted results of the classical anisotropic damage models.

Antitumor activity of Py-Im polyamides

Molecules that inhibit DNA dependent processes are the most commonly used agents for the treatment of cancer. The genotoxicity associated with their mechanisms of action, unfortunately, make them extremely toxic to the patient and cancer cells alike. The work presented in this thesis outlines the development of Py-Im polyamides as non-genotoxic DNA-targeted antitumor molecules that interfere with RNA polymerase II elongation. We initially characterized the pharmacokinetic profiles of two hairpin polyamides to establish their bioavailability in the serum and tissues after a single administration. We next determined the molecular mechanism that contributes to toxicity of a hairpin polyamide in human prostate cancer cells in cell culture and we demonstrated antitumor effects of the compound against LNCaP xenografts in mice. Finally, we conducted animal toxicity experiments on 4 polyamides that vary on the gamma-turn with respect to the substitution of amino and acetamide groups at the alpha and beta positions. From this study we identified a second generation compound that retains antitumor activity with significantly reduce animal toxicity. This work sets the foundation for the development of Py-Im polyamides as DNA targeted therapeutics for the treatment of advanced prostate cancer.

Synthesis, Oxidation and Photophysics of Perfluoroborated Tetrakis(pyrophosphito)diplatinate (II) and Density Functional Theory (DFT) Study of Electrochemical CO2 Reduction by Mn Catalysts

In the first part of this thesis (Chapters I and II), the synthesis, characterization, reactivity and photophysics of per(difluoroborated) tetrakis(pyrophosphito)diplatinate(II) (Pt(POPBF₂)) are discussed. Pt(POP-BF₂) was obtained by reaction of [Pt₂(POP)₄]^4- with neat boron trifluoride diethyl etherate (BF₃·Et₂O). While Pt(POP-BF₂) and [Pt₂(POP)₄]^4- have similar structures and absorption spectra, they differ in significant ways. Firstly, as discussed in Chapter I, the former is less susceptible to oxidation, as evidenced by the reversibility of its oxidation by I2. Secondly, while the first excited triplet states (T₁) of both Pt(POP-BF₂) and [Pt₂(POP)₄]^4- exhibit long lifetimes (ca. 0.01 ms at room temperature) and substantial zero-field splitting (40 cm^-1), Pt(POP-BF₂) also has a remarkably long-lived (1.6 ns at room temperature) singlet excited state (S₁), indicating slow intersystem crossing (ISC). Fluorescence lifetime and quantum yield (QY) of Pt(POP-BF₂) were measured over a range of temperatures, providing insight into the slow ISC process. The remarkable spectroscopic and photophysical properties of Pt(POP-BF₂), both in solution and as a microcrystalline powder, form the theme of Chapter II.

In the second part of the thesis (Chapters III and IV), the electrochemical reduction of CO₂ to CO by [(L)Mn(CO)₃]^- catalysts is investigated using density functional theory (DFT). As discussed in Chapter III, the turnover frequency (TOF)-limiting step is the dehydroxylation of [(bpy)Mn(CO)₃(CO₂H)]^0/- (bpy = bipyridine) by trifluoroethanol (TFEH) to form [(bpy)Mn(CO)₄]^+/0. Because the dehydroxylation of [(bpy)Mn(CO)₃(CO₂H)]^- is faster, maximum TOF (TOF_max) is achieved at potentials sufficient to completely reduce [(bpy)Mn(CO)₃(CO₂H)]⁰ to [(bpy)Mn(CO)₃(CO₂H)]^-. Substitution of bipyridine with bipyrimidine reduces the overpotential needed, but at the expense of TOF_max. In Chapter IV, the decoration of the bipyrimidine ligand with a pendant alcohol is discussed as a strategy to increase CO₂ reduction activity. Our calculations predict that the pendant alcohol acts in concert with an external TFEH molecule, the latter acidifying the former, resulting in a ~ 80,000-fold improvement in the rate of TOF-limiting dehydroxylation of [(L)Mn(CO)₃(CO₂H)]^-.

An interesting strategy for the co-upgrading of light olefins and alkanes into heavier alkanes is the subject of Appendix B. The proposed scheme involves dimerization of the light olefin, operating in tandem with transfer hydrogenation between the olefin dimer and the light alkane. The work presented therein involved a Ta olefin dimerization catalyst and a silica-supported Ir transfer hydrogenation catalyst. Olefin dimer was formed under reaction conditions; however, this did not undergo transfer hydrogenation with the light alkane. A significant challenge is that the Ta catalyst selectively produces highly branched dimers, which are unable to undergo transfer hydrogenation.

Host dependent frequency upconversion of Er3+-doped oxyfluoride germanate glass

Er3+-doped oxyfluoride germanate glasses have been synthesized by the conventional melting and quenching method. The Judd-Ofelt intensity parameters were calculated based on the Judd-Ofelt theory and absorption spectra measurements. With the substitution of PbF2 for PbO, the Omega(2) parameter decreases, while the Omega(6) parameter increases. These change trends indicate that fluoride anions come to coordinate erbium cations and the covalency of the Er-O bond decreases. Structural and thermal stability properties were obtained by Raman spectra and differential thermal analysis, indicating that PbF2 plays an important role in the formation of glass network and has an important influence on the maximum phonon energy and thermal stability of host glasses. Intense green and red emissions centered at 525, 546, and 657 nm, corresponding to the transitions H-2(11/2) -> I-4(15/2), S-4(3/2) -> I-4(15/2), and F-4(9/2) -> I-4(15/2), respectively, were simultaneously observed at room temperature. With increasing PbF2 content, the intensity of red (657nm) emissions increases significantly, while that of the green (525 and 546nm) emission increases slightly. The results indicate that PbF, has more influence on the red (657nm) emission than the green (525 and 546nm) emissions in oxyfluoride germanate glasses. The possible upconversion luminescence mechanisms have also been estimated and discussed. (c) 2005 Elsevier B.V. All rights reserved.

Effect of bismuth oxide introduction on spectroscopic properties of Er3+/Yb3+ co-doped aluminophosphate glasses

The absorption spectra, emission spectra and infrared spectra of Er3+/Yb3+ co-doped xBi(2)O(3)-(65 - x)P2O5-4Yb(2)O(3)-11Al(2)O(3)-5BaO-15Na(2)O were measured and investigated. Spontaneous emission probability, radiative lifetime and branching ratios of Er3+ were calculated according to the Judd-Ofelt theory. The role of substitution of Bi2O3 for P2O5 on luminescence of Er3+/Yb3+ co-doped aluminophosphate glasses has been investigated. The calculated radiative lifetimes (tau(rad)) for I-4(13/2) and I-4(11/2) were decreasing with Bi2O3 content increases, whereas the measured total lifetime (tau(meas)) for I-4(13/2) showed linearly increasing trends. The effect of Bi2O3 introduction on OH- groups was also discussed according to the IR transmittance spectra of glasses. It was found that FWHM of glasses were not affected with the substitution of Bi2O3 for P2O5. The emission spectra intensity increased with Bi2O3 content due to the decreases of phonon energy and OH- content in glasses. (C) 2007 Elsevier B.V. All rights reserved.

Complexity and Uniqueness of the Aromatic Profile of Smoked and Unsmoked Herreno Cheese

In this work, the volatile fraction of unsmoked and smoked Herreno cheese, a type of soft cheese from the Canary Islands, has been characterized for the first time. In order to evaluate if the position in the smokehouse could influence the volatile profile of the smoked variety, cheeses smoked at two different heights were studied. The volatile components were extracted by Solid Phase Microextraction using a divinylbenzene/carboxen/polydimethylsiloxane fiber, followed by Gas Chromatography/Mass Spectrometry. In total, 228 components were detected. The most numerous groups of components in the unsmoked Herreno cheese were hydrocarbons, followed by terpenes and sesquiterpenes, whereas acids and ketones were the most abundant. It is worth noticing the high number of aldehydes and ketones, and the low number of alcohols and esters in this cheese in relation to others, as well as the presence of some specific unsaturated hydrocarbons, terpenes, sesquiterpenes and nitrogenated derivatives. The smoking process enriches the volatile profile of Herreno cheese with ketones and diketones, methyl esters, aliphatic and aromatic aldehydes, hydrocarbons, terpenes, nitrogenated compounds, and especially with ethers and phenolic derivatives. Among these, methylindanones or certain terpenes like a-terpinolene, have not been detected previously in other types of smoked cheese. Lastly, the results obtained suggest a slightly higher smoking degree in the cheeses smoked at a greater height.

Effect of La3+ on microwave dielectric properties of (Pb0.45Ca0.55) (Fe0.5Nb0.5)O-3 ceramics

In this work, microwave dielectric properties of A-site substitution by La3+ in (Pb0.45Ca0.55) (Fe0.5Nb0.5) 03 system were investigated. Microwave dielectric properties of A-site charge unbalance substitution of [(Pb0.45Ca0.55)(1-x) La-x] (Fe0.5Nb0.5)O-3(+) (P45CLFN) were improved because the solid solution of small amount of surplus La3+ with (Pb, Ca)(2+) could eliminate oxygen vacancies, and the formation of secondary phase (pyrochlore) was also caused by surplus La3+. The decreasing of dielectric constant with the increase of La3+ content is due to the formation of pyrochlore. The grain size is changed slightly and Q(f) values (7000 similar to 7300 GHz) are almost unchanged at x = 0.02 similar to 0.10, but the temperature coefficient of resonant frequency (TCF) are increased and changed from negative to positive. TCF is zero at x 0.075 with Q(f) = 7267 GHz and K = 89. TCF of all specimens are within +/- 5 x 10(-6)degrees C-1.

Análise de Economias de Escala na Produção de Leite

Este trabalho procurou analisar o sistema produtivo da atividade leiteira em Minas Gerais, identificando a capacidade dos produtores em permanecer no negócio, a longo prazo, através da estimação da função custo translogarítmica. O estudo demonstrou que os produtores analisados ainda praticam altos custos por unidade produzida, sugerindo baixa eficiência dos estabelecimentos e falhas na administração do empreendimento. Os resultados econométricos revelam a possibilidade de ganhos de escala, no que se refere à alocação e melhor aproveitamento dos recursos, ou seja, as propriedades apresentam economias de escala. No entanto, retornos crescentes de escala não são compatíveis com a existência de mercados competitivos, sinalizando que os produtores enfrentam restrições geradas pelas imperfeições de mercado. O conhecimento dessas imperfeições é essencial à formulação de políticas econômicas e de organizações privadas que visem ao desenvolvimento econômico deste mercado, que atualmente é o sexto maior do mundo. Além disso, os resultados das elasticidades mostram que o produtor é mais sensível às variações de preços na mão-de-obra do que às variações nos demais fatores, reduzindo em maior proporção o uso do trabalho na produção, à medida que seu preço aumenta. Isto evidencia a principal característica regional da produção leiteira no país, que é o uso intensivo do fator trabalho. Também foi identificado que o os medicamentos, alimentos e energia, denominados no estudo de fator dispêndio, são os mais difíceis é o mais difícil de serem substituídos na produção, devido às particularidades no uso dos componentes deste insumo. Por fim, os valores positivos encontrados para as elasticidades parciais de substituição de Allen confirmam a substitutibilidade entre os fatores.

Temporal Changes in a Tropical Nekton Assemblage and Performance of a Prawn Selective Gear

The temporal variation of components of a moderately diverse (H=1.46) tropical estuarine fish assemblage (long. 146°30'E, lat. 8°45'S) was directed by salinities that had been determined by local oceanographic and probably topographic conditions. For this assemblage, two types of intrayear component profiles are predicted. Pooled data (1988-91) reveal a large component of regular/resident species (43%) in an assemblage which has been under a narrow temperature regime «5T). These results facilitate a discussion on the relevance and usefulness of three hypotheses often cited in studies concerning species diversity and component characteristics of the subtropical/tropical coastal nonreef fish assemblages. Manifestations of the assemblage are reflected in catch composition and weights of 39 trials conducted for a selective prawning gear whose performance in bycatch reduction, mainly for finfishes, is judged by an index, E, we have previously proposed. This gear is capable of harvesting the prawn while conserving the demersal fish. Behavioral responses to netting of the prawns and the finfishes, especially the nearshore surface schoolers such as leiognathids, are discussed from several points of view. An adaptation in terms of group selection for leiognathids of their locking mechanism of median fin spines has been interpreted. For the purpose of bycatch reduction or E enhancement, suggestions for improvements in net design and trawl configuration by considering the behavioral features of fish are made. Our original formula of E is modified for general use. Bycatch problems in the regional prawn fisheries and their possible impacts on fishery planning and development in Papua New Guinea as a developing country are discussed. The gear tested may offer enormous ecological and economic benefits. The gear is multipurpose, extremely simple, and can also be used as a biological sampler.