Caracterização microestrutural de uma estrutura tubular aeronáutica submetida a sucessivos reparos de solda TIG

This work examines the possible effects of successive repair procedures on the microstructure of welded steel SAE 4130 by TIG welding process. Discussions and results were made about the metallographic analysis , non-metallic inclusions and microhardness tests , which were conducted on samples taken from the cradle engine component after the end of its life , a model airplane T-27 Tucano , made by EMBRAER and belonging were performed FAB . The choice of such component is due to the fact that this is critical to flight safety since it provides support for the aircraft engine . Thus regions of the weld metal , base metal and heat affected , with samples of the original weld bead , free of weld bead and also with four rework procedures for TIG welding zone were analyzed . It was found that after the fourth rework there is an increase in the amount of martensite , which may weaken the material with respect to resistance to fatigue. It was also found that the regions of the heat affected zone and weld metal have higher microhardness values when compared to those found in the base metal due to favoring the formation of ferritic and tempered martensite microstructures . Moreover, a welding process promotes a region with less non-metallic inclusions than metal base , which also explains the difference in the results obtained

Analise mecânica e microestrutural em estruturas tubulares aeronáuticas soldadas de aço ABNT 4130

Airplane Motor Cradles have a complex geometry, since they require different conbinations between different tubes and TIG welded in several angles. In T-25 aircraft and Universal T-27 Tucano (EMBRAER / FAB), besides having to bear the engine balance, these components maintain fixed the nose landing gear in another extremity. They are considered critical to flight safety, and for this reason, the aviation standards are extremely rigid in their production, imposing a zero index” of defects on the final weld metal quality. These structures may be containing an historical of welding repairs, whose effects on their structural integrity are not computed. In this work we analyzed the standardised AISI 4130 steel and the raw steel of tubes to the Airplane Motor Cradles. First of all, microscopy and microanalysis of the base steel, then we analyzed the effects of the TIG weld. Tensile testing was conducted to measure the difference between the mechanical properties of standardised steel and without this treatment

Alterações microestruturais decorrentes dos sucessivos reparos de solda TIG aplicados ao longo da vida útil de uma estrutura aeronáutica crítica à segurança de vôo

The steel type AISI 4130 (ultra-high strength steel) is an alloy of low carbon and its main alloying elements are chromium and molybdenum, which improves the toughness of the weld metal. It has numerous applications, especially where the need for high mechanical strength. It is widely used in equipment used by the aviation industry, such as cradle-tomotor, and this is the motivation for this study. Cots are of fundamental importance, because the engine supports and maintains balance in the fixed landing gear. This equipment is subjected to intense loading cycles, whose fractures caused by fatigue are constantly observed. Will be determined the effects caused by re-welding the structure of aeronautical equipment, and will also study the microstructure of the metal without welding. The studies will be done on materials used in aircraft, which was given to study. The results provide knowledge of microstructure to evaluate any type of fracture that maybe caused by fatigue. Fatigue is a major cause of aircraft accidents and incidents occurred, which makes the study of the microstructure of the metal, weld and re-solder the knowledge essential to the life of the material. The prevention and control of the process of fatigue in aircraft are critical, since the components are subjected to greater responsibility cyclic loading

Fabricação de rodas: uma análise comparativa

In our country, the majority of freight and people by road happens municipal, state and federal. Thus, the heavy vehicles like buses and trucks are the main means of transporting people and cargo. This graduate work aims to study the process of manufacturing wheels for trucks, because we can see the lack of literature on the manufacturing process of wheels and also the importance of the processes used to manufacture wheels, such as lamination, stamping, puckering, machining, welding and painting

Criação de novo procedimento de engenharia que possibilite a rastreabilidade das tubulações de uma indústria química

The number of piping in an industry is high. Through this piping are conducted several kind of products at several temperature and pressure conditions. In a chemical company, the piping quantity conducting harmful chemical products to human health and to the environment is higher. Nowadays the theme sustainability is often mentioned and harm to environment may cause irreversible damage to the human being, to the fauna, to the flora and to company´s credibility. In this context, controlling over the piping to avoid accidents is mandatory. The objective of this monograph is to create a procedure which enables the chemical companies piping traceability. This monograph analyses the several existent traceability system in the three economy sectors and approaches the technical question of industrial piping in order to create a procedure that achieves its objectives as a technical document and at the same time be economically feasible, with low complexibility level and high practicability. Some possibilities to elaborate this procedure had been studied, as the creation of an alphanumeric code and making with a chisel in the pipeline based on ASTM F2897 and the use of chips to store the information. However, the procedure which best meet the requirement as low cost and high applicability is filling out an electronic plan with information about welding process, welding certification, welding consumables and inspections

Estudo do comportamento em fadiga de um tubo de aço API 5CT soldado por resistência elétrica

The oil extraction in deep waters sparked new areas of knowledge, the creation of engineering courses dedicated just to these processes and a wide field of analysisvoiding multiple impacts in case of faults, mainly the economic and environmental. This paper aims to show on the effects and causes of fatigue failure in steel tubes used for oil and gastransportation (linepipe), mainly caused by vortex induced vibrations, or VIV. To make this, through laboratory tests, it found trough the curve Stress versus Number of Cycles, and thus estimating that with a stress value of 350 MPa or less, the fatigue life cycle of the API 5CT T95 (1% Cr) pipe is estimated infinite. It could conclude that the analyzed material has good fatigue failure resistance for offshore use, taking into account only the influence of VIV's, since there are no stress concentrators

Estudo em fadiga no aço API 5L X80 soldado pelo processo HF/ERW

The technological advancement in order to improve the methods of obtaining energy sources such as oil and natural gas is mainly motivated by the recent discovery of oil reserves. So, increasingly , there is a need for a thorough knowledge of the materials used in the manufacture of pipelines for transportation and exploration of oil and natural gas. The steels which follow the API standard (American Petroleum Institute), also known as high strenght low alloy (hsla), are used in the manufacture of these pipes, as they have, with their welded joints, mechanical properties to withstand the working conditions to which these ducts will be submitted . The objective of this study is to evaluate the fatigue behavior in microalloyed steel grade API 5L X80 welded by process HF / ERW . For this, axial fatigue tests to obtain S-N curve (stress vs. number of cycles ) were conducted. To complement the study, it was performed metallographic , fractographic , Vickers hardness tests and tensile tests to characterize the mechanical properties of the steel and check whether the values satisfy the specifications of the API 5L standard . From the fatigue tests , it was concluded that the surface finish influences directly on the fatigue life of the material

Análise macro e micrográfica da liga AA-356 conforme a taxa de resfriamento

The present work aims to study the characteristics of the alloy Al - 7 % Si - 0 , 3Mg ( AA356 ) , more specifically characterize the macrostructure and microstructure and mechanical properties of the alloy ingots AA356 obtained in metal molds and sand molds for power studying the structures through the difference of cooling rates . This alloy is explained by the fact of referring league has excellent combination of properties such as low solidification shrinkage and good fluidity, good weldability , high wear resistance , high strength to weight ratio, has wide application in general engineering , and particularly in the automotive and aerospace engineering . In this work we will verify this difference in properties through two different cooling rates . We monitor the solid solidification temperatures by thermocouples building with them the cooling curve as a tool that will aid us to evaluate the effectiveness of the grain refining because it achieved with some important properties of the alloy as the latent heat of solidification fraction the liquid and solid temperatures, the total solidification time, and identify the presence of inoculants for grain refinement. Thermal analysis will be supported by the study of graphic software “Origin “will be achieved where the cooling curve and its first derivative that is the cooling rate. Made thermal analysis, analysis will be made in macrographs ingots obtained for observation of macrostructures obtained in both types of ingots and also analysis of micrographs where sampling will occur in strategic positions ingots to correlate with the microstructure. Finally will be collecting data from Brinell hardness of ingots and so then correlating the properties of their respective ingots with cooling rate. We found that obtained with cast metal ingots showed superior properties to the ingots obtained with sand mold

Braquiterapia com sementes de iodo-125: manufatura e tratamento

According to the National Institute of Cancer – INCA, 466.730 new cancer cases will occur in Brazil in 2009. Prostate and Lung cancer in man are the most incident types (in exception of the non-melanoma cancer). The brachytherapy with 125-iodine sources is an important method of prostate cancer treatment. The implant with iodine-125 seeds uses aproximately 100 seeds that are imported impossibilitating the treatment in large scale. For this reason, a multidisciplinary group was created at the Energetic and Nuclear Research Institute – Radiation Technology Center (IPEN –CTR / SP) to develop a national 125-iodine source and established a facility for local production. The seeds manufacture in Brazil will diminish the cost of treatment and prostate brachytherapy will be offered to more patients. This work aim is to observe and discuss the methods used in seeds manufacture there are being developed in Brazil and to present an prostate cancer case folloied in A.C. Camargo Hospital. The 125-iodine is adsorbed in an silver wire, then deposited at titanium coat. The weld is made by an process of plasm sealing. The seeds goes through several test to guarantee that there is no leakage. The result is an high quality and cheaper product. The implant tecnique is an fast and save procedure. The medical physicst preplan the case to stipulate the quantity of seeds there will be used. At the dat of the implant the medical physicst replan the procedure due to changes of volume in the organ. That assure the correct dose distribution in the target. Besides, the 125-iodine low energy is absorbed at the volume of interrest saving sourronding healthy tissues such as the rectum and the urethra

Aplicação de adesivos estruturais em painéis de carros

The automobile industry is increasingly interested in reducing vehicle weight for greater speed, lower fuel consumption and emissions, through innovation of materials and processes. One way to do this is to seek the replacement of conventional processes by the use of structural adhesives. Structural adhesives are highly resistant materials, which can replace rivets, bolts and welds allowing the substrate / adhesive assemble is stronger than the substrate itself. One of the major advantages of gluing with respect to welding is its esthetic appearance, since it does not leave marks. For this reason, parts to be soldered require a minimum thickness so that the marks do not appear, since the pieces from gluing have no restriction as to the thickness. By replacing the vibration welding process for gluing process of the instrument panel parts of an automobile, one obtains a reduction of the thickness of the parts and therefore it decreases the weight of the car. This work aims to study the various structural adhesives that already exist on the market to be applied on the instrument panel. The mechanical test performed to measure the maximum adhesive strength was the Lap Shear Test at 23°C (room temperature), -35°C and 85°C. The types of adhesives used were the hot-melt and the bi-component. By the results obtained, it is in favor using the bi-component for application to the union of instrument panel parts

Estudo de tensões residuais em juntas soldadas utilizando o método dos elementos finitos

Pós-graduação em Engenharia Mecânica - FEG

Síntese e avaliação biológica de novos derivados anti-inflamatórios esteroides

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Antinociceptive, anti-inflammatory and gastroprotective effects of a hydroalcoholic extract from the leaves of Eugenia punicifolia (Kunth) DC. in rodents

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Levantamento da mastofauna terrestre de médio e grande porte em três fragmentos de mata na Fazenda Experimental Lageado - Botucatu, SP

The present study aimed to survey the medium and large land mammals in three fragments at the Fazenda Experimental Lageado - UNESP/Botucatu, through the method of sand plots. 48 plots were used in total, 16 on each track. The paw prints found were photographed and identified from specific guides. 12 different species of mammals were found, these, 7 were classified at the level of species belonging to 9 families and 6 orders. The most representative order was Carnivora. Most of the species found have a generalist or omnivore habit, which can be related with the degree of the forest fragmentation. The only fragment of natural forest (semideciduous), presented the fewer numbers of species, which can be explained due to its isolation. The other fragment, which has near highway and other large fragment (Fazenda Experimental Edgárdia) was the most representative fragment, demonstrating the importance of nearest fragments to the continuity and survival of medium and large mammals

Comparação de junta soldada aço carbono/ aço inox utilizando como metal de adição aço carbono e aço inox

In contemporary industrial, welding processes are widely used, this is the most important process of joining metals used industrially. The welding can be used to build simple structures, like doors and gates for instance, in the same way can be used in situations of high responsibility, such as the nuclear industry and oil industry. Dissimilar welding is a case of welded joints, is characterized by the junction between different materials, for this case, stainless steel and carbon steel that are widely used in steam lines, power plants, nuclear reactors, petrochemical plants. Because their different mechanical and corrosive properties, the join, stainless steel with carbon steel, not only meets environmental requirements and also reduces cost. By using penetrating liquid tests, macrograph, hardness and tensile test was compared the possibility of replacing the current use of 309 rods as filler metal in dissimilar welding between carbon steel and stainless steel by add-on material carbon steel essentially, in this case E7018 coated electrode was used, but without the coating. After analysis of the results and for comparison, was proposed with some certainty that it is possible to replace the addition of materials, thus leading economy in this process widely used in the modern industry