Fracture resistance of bleached teeth restored with different procedures

This study evaluated the fracture resistance of teeth submitted to internal bleaching and restored with different non-metallic post. Eighty mandibular incisors were endodontically treated and randomly divided in 10 groups (n = 8): G1- restored with composite resin (CR), G2- CR + fiber-reinforced composite post (FRC, Everstick post, Sticktech) cemented with resin cement self-etch adhesive (RCS, Panavia F 2.0, Kuraray), G3- CR + FRC + self-adhesive resin cement (SRC, Breeze, Pentral Clinical), G4- CR+ glass fiber post (GF, Exacto Post, Angelus) + RCS, G5- CR + GF + SRC. The G6 to G10 were bleached with hydrogen peroxide (HP) and restored with the same restorative procedures used for G1 to G5, respectively. After 7 days storage in artificial saliva, the specimens were submitted to the compressive strength test (N) at 0.5 mm/min cross-head speed and the failure pattern was identified as either reparable (failure showed until 2 mm below the cement-enamel junction) or irreparable (the failure showed <2 mm or more below the cement-enamel). Data were analyzed by ANOVA and Tukey test (α = 0.05). No significant difference (p < 0.05) was found among G1 to G10. The results suggest that intracoronal bleaching did not significantly weaken the teeth and the failure patterns were predominately reparable for all groups. The non-metallic posts in these teeth did not improve fracture resistance.

Effect of temporary cements on the shear bond strength of luting cements

Objective: The purpose of this study was to evaluate, by shear bond strength (SBS) testing, the influence of different types of temporary cements on the final cementation using conventional and self-etching resin-based luting cements. Material and Methods: Forty human teeth divided in two halves were assigned to 8 groups (n=10): I and V (no temporary cementation); II and VI: Ca(OH)(2)-based cement; III and VII: zinc oxide (ZO)based cement; IV and VIII: ZO-eugenol (ZOE)-based cement. Final cementation was done with RelyX ARC cement (groups I to IV) and RelyX Unicem cement (groups V to VIII). Data were analyzed statistically by ANOVA and Tukey's test at 5% significance level. Results: Means were (MPa): I - 3.80 (+/- 1.481); II - 5.24 (+/- 2.297); III - 6.98 (+/- 1.885); IV - 6.54 (+/- 1.459); V - 5.22 (+/- 2.465); VI - 4.48 (+/- 1.705); VII - 6.29 (+/- 2.280); VIII - 2.47 (+/- 2.076). Comparison of the groups that had the same temporary cementation (Groups II and VI; III and VII; IV and VIII) showed statistically significant difference (p<0.001) only between Groups IV and VIII, in which ZOE-based cements were used. The use of either Ca(OH) 2 based (Groups II and VI) or ZO-based (Groups III and VII) cements showed no statistically significant difference (p>0.05) for the different luting cements (RelyX (TM) ARC and RelyX (TM) Unicem). The groups that had no temporary cementation (Groups I and V) did not differ significantly from each other either (p>0.05). Conclusion: When temporary cementation was done with ZO- or ZOE-based cements and final cementation was done with RelyX ARC, there was an increase in the SBS compared to the control. In the groups cemented with RelyX Unicem, however, the use of a ZOE-based temporary cement affected negatively the SBS of the luting agent used for final cementation.

Effect of Acid Neutralization and Mechanical Cycling on the Microtensile Bond Strength of Glass-ceramic Inlays

Objectives: To evaluate the hypothesis that a process of hydrofluoric acid precipitate neutralization and fatigue load cycling performed on human premolars restored with ceramic inlays had an influence on microtensile bond strength results (MTBS). Methods: MOD inlay preparations were performed in 40 premolars (with their roots embedded in acrylic resin). Forty ceramic restorations were prepared using glass-ceramic (IPS Empress). The inner surfaces of all the restorations were etched with 10% hydrofluoric acid for 60 seconds, rinsed with water and dried. The specimens were divided into two groups (N=20): 1-without neutralization; 2-with neutralization. All the restorations were silanized and adhesively cemented (self-curing and self-etching luting composite system, Multilink). Ten premolars from each group were submitted to mechanical cycling (1,400,000 cycles, 50N, 37 degrees C). After cycling, the samples were sectioned to produce non-trimmed beam specimens (vestibular dentin-restoration-lingual dentin set), which were submitted to microtensile testing. Results: Bond strength was significantly affected by the surface treatment (p<0.0001) (no neutralization > neutralization) and mechanical cycling (p<0.0001) (control > cycling) (2-way ANOVA and Tukey test, alpha=.05). Conclusion: Hydrofluoric acid precipitate neutralization appears to significantly damage the resin bond to glass-ceramic and should not be recommended. The clinical simulation of the specimens, by using mechanical cycling, is important when evaluating the ceramic-dentin bond.

Virulence factors of uropathogenic Escherichia coli from a University Hospital in Ribeirão Preto, São Paulo, Brazil

O objetivo do trabalho foi determinar a ocorrência de fatores de virulência, tais como, a expressão de fímbrias, produção de hemolisina, colicina e aerobactina em 100 cepas de Escherichia coli isoladas de pacientes ambulatoriais e hospitalizados de um hospital universitário de nível de atendimento terciário, entre os meses de julho e agosto de 2000, que apresentavam sinais clínicos e laboratoriais de infecção do trato urinário (ITU). Foram pesquisados os genes pap, afa e sfa responsáveis pela expressão de fímbrias através da técnica de PCR. A freqüência dos fatores de virulência entre as cepas estudadas foi de 96,0%, 76,0% e 24,0% para hemolisina, aerobactina e colicina respectivamente, e a prevalência dos genes para os sistemas de adesinas fimbriais foi de 32,0%, 19,0% e 11,0% para os genes pap, sfa e afa respectivamente. As cepas isoladas dos pacientes ambulatoriais exibiram um número maior de fatores de virulência quando comparadas com aquelas provenientes de indivíduos hospitalizados.

Adhesives with different pHs: Effect on the MTBS of chemically activated and light-activated composites to human dentin

Purpose: To evaluate the bond strength between human dentin and composites, using two light-activated single-bottle total-etch adhesive systems with different pHs combined with chemically activated and light-activated-composites. The tested hypothesis was that the dentin bond strength is not influenced by an adhesive system of low pH, combined with chemically activated or light-activated composites. Material and Method: Flat dentin surfaces of twenty-eight human third molars were allocated in 4 groups (n=7), depending on the adhesive system: (One Step Plus-OS and Prime & Bond NT-PB) and composite (light-activated Filtek Z-100 [Z100] and chemically activated Bisfil 2B [B2B]). Each adhesive system was applied on acid-etched dentin and then one of the composites was added to form a 5 mm-high resin block. The specimens were stored in tap water (37 degrees C/24 h) and sectioned into two axes, x and y. This was done with a diamond disk under coolant irrigation to obtain beams with a cross-section area of approximately 0.8 mm(2). Each specimen was then attached to a custom-made device and submitted to the microtensile test (1 mm.min(-1)). Data were analyzed using two-way ANOVA and Tukey's tests (p<0.05). Results: the anticipated hypothesis was not confirmed (p<0.0001). The bond strengths (MPa) were not statistically different between the two adhesive systems when light-activated composite was used (OS+Z100 = 24.7 +/- 7.1(a); PB+Z100 = 23.8 +/- 5.7(a)). However, with use of the chemically activated composite (B2B), PB (7.8 +/- 3.6(b) MPa) showed significantly lower dentin bond strengths than OS (32.2 +/- 7.6(a)). Conclusion: the low pH of the adhesive system can affect the bond of chemically activated composite to dentin. on the other hand, under the present conditions, the low pH did not seem to affect the bond of light-activated composites to dentin significantly.

Microleakage and nanoleakage: Influence of laser in cavity preparation and dentin pretreatment

Objective: the purpose of this study was to verify if the application of the Nd:YAG laser following pretreatment of dentin with adhesive systems that were not light cured in class V cavities and were prepared with Er:YAG laser would promote better sealing of the gingival margins when compared to cavities prepared the conventional way. Background Data: Previous studies had shown that the pretreatment of dentin with laser irradiation after the application of an adhesive system is efficient in achieving higher shear bond and tensile bond strength. Materials and Methods: Er:YAG laser (Kavo-Key, Germany) with 350 mJ, 4 Hz, and 116.7 J/cm(2) was used for cavity preparation. The conventional preparation was made with diamond bur mounted in high-speed turbine. Dentin treatment was accomplished using an Nd:YAG laser (Pulse Master 1000, ADT. USA) at 60 mJ, 10 Hz, and 74.65/cm(2) following application of the adhesive system. The cavities were stored with Single Bond/Z100 and Prime & Bond NT/TPH. Eighty bovine incisors were used, and class V preparations were done at buccal and lingual surfaces divided into eight groups: (1) Er:YAG preparation + Prime & Bond NT + TPH; (2) Er:YAG preparation + Single Bond + Z100; (3) Er:YAG preparation + Single Bond + Nd:YAG + Z100; (4) Er:YAG preparation + Prime & Bond NT + Nd:YAG + TPH; (5) conventional preparation + Prime & Bond NT + TPH; (6) conventional preparation + Single Bond + Z100; (7) conventional preparation + Single Bond + Nd:YAG + Z100; (8) conventional preparation + Prime & Bond NT + Nd:YAG + TPH. All specimens were thermocycled for 300 full cycles between 5 degreesC +/- 2 degreesC and 55 degreesC +/- 2 degreesC (dwell time of 30 sec), and stored in 50% silver nitrate solution for 24 h soaked in photodeveloping solution and exposed to fluorescent light for 6 h. After this procedure, the specimens were sectioned longitudinally in 3 portions and the extension of microleakage at the gingival wall was determined following a criteria ranging from 0 to 4 using scanning electron microscopy (SEM). The medium portion sectioned of each specimen was polished and prepared for nanoleakage avaliation by SEM. Results: Kruskall-Wallis and Miller statistical tests determined that group 3 presented less microleakage and nanoleakage. Conclusion: Application of the Nd:YAG laser following pretreatment of dentin with adhesive Single Bond non-photocured Single Bond adhesive in cavities prepared with Er:YAG promote better sealing of the gingival margins.

Polymerization shrinkage evaluation of three packable composite resins using a gas pycnometer.

Modern restorative dentistry has been playing an outstanding role lately since composite resins, allied to adhesive systems, have been widely applied on anterior and posterior teeth restorations. The evolution of composite resins has mostly been verified due to the improvement of their aesthetic behavior and the increase in their compressive and abrasive strengths. In spite of these developments, the polymerization shrinkage inherent to the material has been a major deficiency that, so far, has been impossible to avoid. Using a gas pycnometry, this research investigated the polymerization shrinkage of three packable composite resins: Filtek P60 (3M), Prodigy Condensable (Kerr), and SureFil (Dentsply/Caulk), varying the distance from the light source to the surface of the resins (2 mm or 10 mm). The pycnometer Accupyc 1330 (Micromeritics, USA) precisely records helium displacement, allowing fast and reliable measurements of the volume of composite resin immediately before and after polymerization, without interference of temperature or humidity. Results were not found to be statistically different for the three tested resins, either for 2 mm or 10 mm-distance from the light source to the composite surface.

Influence of surface sealants on microleakage of composite resin restorations

Purpose: The purpose of this study was to verify the influence of surface sealants and dentin adhesive systems on the microleakage of composite restorations. Methods: Class V cavities were made on the buccal faces of 100 permanent third molars and restored with Z250. After 24 hours, they were submitted to polishing and finishing processes. The teeth were divided into groups according to the sealant agent: group 1 - Single Bond; group 2 - Opti Bond Solo Plus; group 3 - Fortify; group 4 - Fortify Plus; and group 5 - control without sealant. The analysis of immediate microleakage was performed in 10 restorations from each group, soon after the sealing. The other 10 specimens from each group were submitted to tooth-brushing and thermal cycles. The teeth were isolated and immersed in 2% methylene blue solution, washed in tap water, and sectioned in the buccolingual direction. The percentage of marginal leakage was calculated using an image analysis program, and results were submitted to analysis of variance and Tukey's test. Results: All the sealed groups demonstrated lower microleakage values compared to the control group. Group 3, sealed with Fortify, presented the lowest mean microleakage values. Conclusion: The application of surface sealants effectively decreased the microleakage in composite resin restorations.

In vitro antimicrobial activity of acroseal, polifl and epiphany against Enterococcus faecalis

Using the agar diffusion method, this study evaluated the in vitro antimicrobial activity of the commercial endodontic sealers Acroseal and Epiphany, a castor-oil based experimental sealer, Polifl, and a primer agent (Epiphany self-etching primer), against Enterococcus faecalis. Zinc oxide and eugenol cement (ZOE) served as control. Five wells per dish were made at equidistant points and immediately flled with the test and control materials. After incubation of the dishes at 37°C for 24 h and 48 h, the diameter of the zones of microbial growth inhibition produced around the wells was measured (in mm) with a millimeter rule. After 48 h, the diameters of the zones of microbial growth inhibition were the same as those observed at 24 h, only the substances continued to diffuse. Epiphany and Polifl did not show antibacterial activity (no formation of zones of microbial growth inhibition). The primer produced the largest zones of inhibition (17.62 mm) followed by Acroseal (7.25 mm) and ZOE (7.12 mm). E. faecalis was resistant to Epiphany and Polifl, while the primer and Acroseal sealer were effective against this microorganism under the tested conditions.

Influência de diferentes sistemas adesivos na resistência de união de pinos de fibra à dentina intrarradicular

Objective: To evaluate the influence of three adhesive systems on the bond strength of fiber post luted to root dentine. The hypothesis was that the bond strength is influenced by the adhesive system. Method: The canals of thirty single-root bovine roots (16mm in length) were prepared using the preparation drill (FGM) until 12mm. 14 mm of each root was embedded with acrylic resin and the specimens were allocated into three groups (n=10), considering the factor adhesive (3 levels): Gr1- Scotchbond Multipurpose Plus (3M ESPE), Gr2- One Step (Bisco) and Gr3- Excite DSC (Ivoclar Vivadent). The adhesive systems were applied using a microbrush, according to the manufacture's recommendations. The fiber posts (White Post DC, FGM) were luted with dual resin cement (All-Cem,FGM). After, the cores with composite resin (Llis, FGM) were made and each set of root/post/core was submitted to the mechanical cycling (Erios, Brazil) (10 6 cycles, 84N, 4 Hz, inclination of 45 o, 37 oC, water). Each specimen was cut in 4 samples (1.8mm in thickness), which were submitted to the push-out test in a universal testing machine (ServoPulser - Shimadzu) (50Kgf, 1mm/min). The data (MPa) were analyzed using ANOVA (1-way) and Tukey test (5%). Results: The factor adhesive (P=0.00352) influenced the bond strength significantly (ANOVA). Gr1 (6.8±3.8 MPa) a presented higher bond strength values than Gr2 (3.1±1.5 MPa) b and similar to Gr3 (4.4±3.3) a,b. Moreover, Gr3 and Gr2 were similar between them (Tukey). The hypothesis was accepted. Conclusion: Based on the results it was concluded that chemical and dual polymerization adhesive system should be used for the adhesive luting fiber post procedures.

Clinical evaluation of the failure rate of metallic brackets bonded with orthodontic composites

The purpose of the present study was to evaluate in vivo the failure rate of metallic brackets bonded with two orthodontic composites. Nineteen patients with ages ranging from 10.5 to 38.7 years needing corrective orthodontic treatment were selected for study. The enamel surfaces from second premolars to second premolars were treated with Transbond Plus-Self Etching Primer (3M Unitek). Next, 380 orthodontic brackets were bonded on maxillary and mandibular teeth, as follows: 190 with Transbond XT composite (3M Unitek) (control) and 190 with Transbond Plus Color Change (3M Unitek) (experimental) in contralateral quadrants. The bonded brackets were light cured for 40 s, and initial alignment archwires were inserted. Bond failure rates were recorded over a six-month period. At the end of the evaluation, six bond failures occurred, three for each composite. Kaplan-Meyer method and log-rank test (Mantel-Cox) was used for statistical analysis, and no statistically significant difference was found between the materials (p=0.999). Both Transbond XT and Transbond Plus Color Change composites had low debonding rates over the study period.

Avaliação da formação de fendas marginais e da microinfiltração após envelhecimento artificial, empregando adesivos autocondicionantes fotopolimerizáveis ou duais associados à resinas compostas de diferentes viscosidades

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Avaliação da resistência de união de diferentes sistemas adesivos à dentina bovina: influência de agentes dessensibilizantes

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Análise da microestrutura do amálgama dental quando associado a diferentes materiais intermediários

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Resistência de sistemas de união ao microcisalhamento de sistemas adesivos condiona-e-lava de 2 passos: efeito de diferentes tratamentos da superfície dentinária condicionada

Pós-graduação em Ciências Odontológicas - FOAR