922 resultados para Nickel-titanium alloys


Relevância:

30.00% 30.00%

Publicador:

Resumo:

Mossbauer effect and X-ray measurements are carried out on product samples of the thermogravimetric analysis (TGA) and isothermal decomposition in hydrogen of homogeneously mixed ferrous nickel oxalates with different iron to nickel ratios. The formation of Fe-Ni alloy is obtained at considerably lower temperatures (z 300 "C) in each case. The Fe-Ni alloys obtained shift from iron-rich to nickel-rich composition as the nickel ratio in the mixed metal oxalates is increased. The formation of Pe-Ni Invar from mixed metal oxalate with Fe:Ni = 1:l is indicated in the early stages but not from those with Fe:Ni = 2: 1 or 64:36. An Produktproben von homogen verteilten Eisen-Nickeloxalaten mit unterschiedlichem Eisen- Nickel-Verhaltnis nach thermogravimetrischer Analyse (TGA) und isothermem Zerfall in Wasserst off werden Mollbauereffekt- und Rontgenmessnngen durchgefuhrt. In allen Fiillen wird die Bildung der Fe-Ni-Legierung bei betriichtlich niedrigeren Temperaturen (= 300 "C) erhalten. Die erhaltenen Fe-Ni-Legierungen verschieben sich von der eisenreichen zur nickelreichen Zusrtmmensetzung, wenn das Nickelverhaltnis in dem BIetall-Mischoxalat erhoht wird. Die Bildung der Fe-Ni-lnvar-Legierung aus dem Metall-Mischoxalat mit Fe:Ni = 1 : 1 wird in fruhen Zu Zustanden beobachtet, iedoch nicht aus Oxalaten mit Fe:Ni = 2:1 oder 64:36.

Relevância:

30.00% 30.00%

Publicador:

Resumo:

Mossbauer effect and X-ray measurements are carried out on product samples of the thermogravimetric analysis (TGA) and isothermal decomposition in hydrogen of homogeneously mixed ferrous nickel oxalates with different iron to nickel ratios. The formation of Fe-Ni alloy is obtained at considerably lower temperatures (z 300 "C) in each case. The Fe-Ni alloys obtained shift from iron-rich to nickel-rich composition as the nickel ratio in the mixed metal oxalates is increased. The formation of Pe-Ni Invar from mixed metal oxalate with Fe:Ni = 1:l is indicated in the early stages but not from those with Fe:Ni = 2: 1 or 64:36. An Produktproben von homogen verteilten Eisen-Nickeloxalaten mit unterschiedlichem Eisen- Nickel-Verhaltnis nach thermogravimetrischer Analyse (TGA) und isothermem Zerfall in Wasserstoff werden Mollbauereffekt- und Rontgenmessnngen durchgefuhrt. In allen Fiillen wird die Bildung der Fe-Ni-Legierung bei betriichtlich niedrigeren Temperaturen (= 300 "C) erhalten. Die erhaltenen Fe-Ni-Legierungen verschieben sich von der eisenreichen zur nickelreichen Zusrtmmensetzung, wenn das Nickelverhaltnis in dem BIetall-Mischoxalat erhoht wird. Die Bildung der Fe-Ni-lnvar-Legierung aus dem Metall-Mischoxalat mit Fe:Ni = 1 : 1 wird in fruhen Zustanden beobachtet, iedoch nicht aus Oxalaten mit Fe:Ni = 2:1 oder 64:36.

Relevância:

30.00% 30.00%

Publicador:

Resumo:

Rapid solidification of Ti-7.3wt.%Cu (near-eutectoid composition), Ti-36.2wt.%Ni and Ti-34.3wt.% Ni-5.8wt.%Si alloys has been carried out by electron beam melting and splat quenching on a water-cooled rotating copper disc. The product obtained was in the form of thin ribbons 60–100 μm thick. Transmission electron microscopy studies of Ti---Cu alloy splats showed that the microstructure consisted of a mixture of martensite and a lamellar eutectoid product. The formation of the intermetallic compound Ti2Cu involved a diffusionless ω transformation and spinodal clustering. In the case of Ti---Ni alloy the as-quenched microstructure is complex, consisting of α, transformed β and intermetallic phases. This could have arisen possibly as a result of local variation in cooling rates. Rapid solidification of Ti---Ni---Si alloy resulted in partial quenching of an amorphous phase. The amorphous phase was seen to be extremely hard (a Vickers hardness of about 800 HV).

Relevância:

30.00% 30.00%

Publicador:

Resumo:

Wear rates of several cast aluminium base alloys have been measured for lubricated rubbing against a rotating hardened steel disk. Wear rates of cast graphitic aluminium-silicon-nickel alloys were lower than those of pure Al, Al-Si and Al-Si-Ni alloys especially above pressures of 0.02 kg/mm2. The high wear resistance is attributed to the presence of graphite particles in the matrix which act as a solid lubricant. Additions of nickel alone to Al-Si alloys decrease the wear resistance. Graphitic aluminium-silicon-nickel alloys containing above 2% graphite can be mated unlubricated against the rotating steel disk after a one minute lubricated run-in period. Graphite particles may be potentially suitable to replace part of all of the tin in aluminium-tin bearing alloys.

Relevância:

30.00% 30.00%

Publicador:

Resumo:

Seizure resistance of several cast aluminium base alloys has been examined using a standard Hohman Wear Tester. Disks of aluminium base alloys were run against a standard aluminium 12% silicon base alloy. The seizure resistance of the alloys (as measured by the lowest bearing parameter reached before seizure) increased with hardness, yield and tensile strength. In Al-Si-Ni alloys where silicon and nickel have little solid solubility in α-aluminium and Si and Ni Al3 hard phases are formed, the minimum bearing parameter decreased with the parameter V (The product of vol. % of hard phases in the disk and the shoe). Apparently the silicon and NiAl3 particles provided discontinuities in the matrix and reduced the probability (1 − V) of the α-aluminium phase in the disk coming into contact with the α-aluminium phase in the shoe. The copper and magnesium containing Al-Si-Ni alloys with lesser volumes of hard phases exhibit considerably better seizure resistance indicating that a slight increase in the solute content or the hardness of the primary α-phase leads to a considerable increase in seizure resistance. Deformation during wear and seizure leads to fragmentation of the original hard particles into considerably smaller particles uniformly dispersed in the deformed α-aluminium matrix.

Relevância:

30.00% 30.00%

Publicador:

Resumo:

Wear rates of several cast aluminium base alloys have been measured for lubricated rubbing against a rotating hardened steel disk. Wear rates of cast graphitic aluminium-silicon-nickel alloys were lower than those of pure Al, Al-Si and Al-Si-Ni alloys especially above pressures of 0.02 kg/mm2. The high wear resistance is attributed to the presence of graphite particles in the matrix which act as a solid lubricant. Additions of nickel alone to Al-Si alloys decrease the wear resistance. Graphitic aluminium-silicon-nickel alloys containing above 2% graphite can be mated unlubricated against the rotating steel disk after a one minute lubricated run-in period. Graphite particles may be potentially suitable to replace part of all of the tin in aluminium-tin bearing alloys.

Relevância:

30.00% 30.00%

Publicador:

Resumo:

Hot deformation behavior of a hypoeutectic Ti-6Al-4V-0.1B alloy in (alpha + beta) phase field is investigated in the present study with special reference to flow response, kinetics and microstructural evolution. For a comparison, the base alloy Ti-6Al-4V was also studied under identical conditions. Dynamic recovery of alpha phase occurs at low temperatures while softening due to globularization and/or dynamic recrystallization dominates at high temperatures irrespective of boron addition. Microstructural features for both the alloys display bending and kinking of alpha lamellae for near alpha test temperatures. Unlike Ti-6Al-4V, no sign of instability formation was observed in Ti-6Al-4V-0.1B for any deformation condition except for cavitation around TiB particles, due to deformation incompatibility and strain accumulation at the particle-matrix interface. The absence of macroscopic instabilities and early initiation of softening mechanisms as a result of boron addition has been attributed to microstructural features (e.g. refined prior beta grain and alpha colony size, absence of grain boundary alpha layer, presence of TiB particles at prior beta boundaries, etc.) of the respective alloys prior to deformation. (C) 2012 Elsevier B.V. All rights reserved.

Relevância:

30.00% 30.00%

Publicador:

Resumo:

The basic framework and - conceptual understanding of the metallurgy of Ti alloys is strong and this has enabled the use of titanium and its alloys in safety-critical structures such as those in aircraft and aircraft engines. Nevertheless, a focus on cost-effectiveness and the compression of product development time by effectively integrating design with manufacturing in these applications, as well as those emerging in bioengineering, has driven research in recent decades towards a greater predictive capability through the use of computational materials engineering tools. Therefore this paper focuses on the complexity and variety of fundamental phenomena in this material system with a focus on phase transformations and mechanical behaviour in order to delineate the challenges that lie ahead in achieving these goals. (C) 2012 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Relevância:

30.00% 30.00%

Publicador:

Resumo:

Ni2+ ion induced unusual conductivity reversal and an enhancement in the gas sensing properties of ferrites based gas sensors, is reported. The Co1-xNixFe2O4 (for x = 0, 0.5 and 1) nanoparticles were synthesized by wet chemical co-precipitation method and gas sensing properties were studied as a function of composition and temperature. The structural, morphological and microstructural characterization revealed crystallite size of in the range 10-20 nm with porous morphology consisting of nano-sized grains. The Energy Dispersive X-ray (EDX) mapping confirms homogeneous distribution of Co, Ni, Fe and O elements in the ferrites. The non-stoichiometry of the inverse spinel type ferrites and the relative concentration of Ni3+/Co3+ defects were studied using X-ray photoelectron spectroscopy. It is found that the addition of Ni2+ ions into cobalt ferrite shows preferred selectivity towards CO gas at high temperature (325 degrees C) and ethanol gas at low temperature (250 degrees C), unlike undoped cobalt ferrite or undoped nickel ferrite, which show similar response for both these gases. Moreover, an unusual conductivity reversal is observed, except cobalt ferrite due to the difference in reactivity of the gases as well as characteristic non-stoichiometry of ferrites. This behavior is highly gas ambient dependent and hence can be well-exploited for selective detection of gases. (C) 2015 Elsevier B.V. All rights reserved.

Relevância:

30.00% 30.00%

Publicador:

Resumo:

Titanium carbide reinforced nickel aluminide matrix in situ composites were produced using a newly patented laser melting furnace. Microstructure of the laser melted TiC/(Ni3Al–NiAl) in situ composites was characterized by optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD) and transmission electron microscopy (TEM). Results showed that the constituent phases in the laser melted in situ composites are TiC, Ni3Al and NiAl. Volume fraction of TiC and NiAl increase with increasing content of titanium and carbon. The growth morphology of the reinforcing TiC carbide has typically faceted features, indicating that the lateral growth mechanism is still predominant growth mode under rapid.

Relevância:

30.00% 30.00%

Publicador:

Resumo:

The mechanism of fatigue crack nucleation for nanocrystalline (nc) nickel was experimentally investigated in this paper. The samples of electrodeposited ne nickel were loaded cyclically by using a three point bending instrument at first. Then, atomic force microscopy (AFM) was used to scanning the sample surface after fatigue testing. The results indicated that, after fatigue testing, there are vortex-like cells with an average size of 108nm appeared along the crack on nc nickel sample. And, the roughness of sample surface increased with the maximum stress at the surface.

Relevância:

30.00% 30.00%

Publicador:

Resumo:

The cyclic deformation behavior Of ultrafine-grained (UFG) Ni samples synthesized by the electrodeposition method was studied. Different from those made by severely plastic deformation, the UFG samples used in this study are characterized by large-angle grain boundaries. Behaviors from nanocrystalline Ni and coarse-grained Ni samples were compared with that Of Ultrafine-grained Ni. With in situ neutron diffraction. unusual evolutions of residual lattice strains as well as cyclic hardening and softening behavior were demonstrated during the cyclic deformation. The microstructural changes investigated by TEM are discussed with respect to the unusual lattice strain and cyclic hardening/softening. (C) 2008 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Relevância:

30.00% 30.00%

Publicador:

Resumo:

Low strain hardening has hitherto been considered an intrinsic behavior for most nanocrystalline (NC) metals, due to their perceived inability to accumulate dislocations. In this Letter, we show strong strain hardening in NC nickel with a grain size of 20 nm under large plastic strains. Contrary to common belief, we have observed significant dislocation accumulation in the grain interior. This is enabled primarily by Lomer-Cottrell locks, which pin the lock-forming dislocations and obstruct islocation. motion. These observations may help with developing strong and ductile NC metals and alloys.

Relevância:

30.00% 30.00%

Publicador:

Resumo:

Ternary alloys of nickel-palladium-phosphorus and iron-palladium- phosphorus containing 20 atomic % phosphorus were rapidly quenched from the liquid state. The structure of the quenched alloys was investigated by X-ray diffraction. Broad maxima in the diffraction patterns, indicative of a glass-like structure, were obtained for 13 to 73 atomic % nickel and 13 to 44 atomic % iron, with palladium adding up to 80%.

Radial distribution functions were computed from the diffraction data and yielded average interatomic distances and coordination numbers. The structure of the amorphous alloys could be explained in terms of structural units analogous to those existing in the crystalline Pd3P, Ni3P and Fe3P phases, with iron or nickel substituting for palladium. A linear relationship between interatomic distances and composition, similar to Vegard's law, was shown for these metallic glasses.

Electrical resistivity measurements showed that the quenched alloys were metallic. Measurements were performed from liquid helium temperatures (4.2°K) up to the vicinity of the melting points (900°K- 1000°K). The temperature coefficient in the glassy state was very low, of the order of 10-4/°K. A resistivity minimum was found at low temperature, varying between 9°K and 14°K for Nix-Pd80-x -P20 and between 17°K and 96°K for Fex-Pd80-x -P20, indicating the presence of a Kondo effect. Resistivity measurements, with a constant heating rate of about 1.5°C/min,showed progressive crystallization above approximately 600°K.

The magnetic moments of the amorphous Fe-Pd-P alloys were measured as a function of magnetic field and temperature. True ferromagnetism was found for the alloys Fe32-Pd48-P20 and Fe44-Pd36-P20 with Curie points at 165° K and 380° K respectively. Extrapolated values of the saturation magnetic moments to 0° K were 1.70 µB and 2.10 µB respectively. The amorphous alloy Fe23-Pd57-P20 was assumed to be superparamagnetic. The experimental data indicate that phosphorus contributes to the decrease of moments by electron transfer, whereas palladium atoms probably have a small magnetic moment. A preliminary investigation of the Ni-Pd-P amorphous alloys showed that these alloys are weakly paramagnetic.

Relevância:

30.00% 30.00%

Publicador:

Resumo:

Este trabalho avaliou o comportamento eletroquímico do metal de base (MB) de uma liga a base de níquel-cromo em relação a juntas soldadas desta liga obtidas pelos processos de brasagem (BRA) e Tungsten Inert Gas (TIG), imersos em saliva artificial com pH 2,5 e 5,5. Foram também realizados ensaios de microdureza e caracterização microestrutural, por meio de microscopia óptica e eletrônica de varredura e análise química semi-quantitativa por EDS, nos grupos MB, TIG, BRA e no cordão de solda a laser (LAS). O MB apresentou uma matriz rica em níquel e cromo, distribuída em um arranjo dendrítico típico, apresentando inclusões metálicas de silício e titânio, além de porosidades. As soldas TIG e LAS revelaram uma microestrutura mais refinada que o MB, mostrando, entretanto, uma mesma composição química e distribuição de seus elementos. A solda BRA apresentou diferenças marcantes em sua microestrutura, composição química e distribuição de seus elementos em relação ao MB. Os dados de microdureza Vickers (HV), potencial de corrosão (Ecorr) e densidade de corrente de corrosão (jcorr) foram analisados com ANOVA e teste de Tukey (p<0,05). Para determinação da influência do pH quanto a resistência à corrosão dos grupos MB, TIG e BRA, empregou-se o teste t de Student (p<0,05). O MB apresentou menor média de microdureza (256,13 9,39 HV), seguido pelos grupos TIG (271,53 8,07 HV), LAS (303,73 13,93 HV) e BRA (551,99 37,73 HV). Em pH 2,5 as médias do Ecorr (mV) para o MB, TIG e BRA foram, respectivamente, -67,9 8,43, -52,78 16,74, e -284,33 19,04; e em pH 5,5, médias de -54,03 21,15, -62,08 20,16 e -278,8 28,96. Os valores médios de jcorr (A.cm-2) para o MB, TIG e BRA em pH 2,5 foram, respectivamente, 2,49 0,95, 5,584 1,64 e 27,45 4,9; e em pH 5,5, médias de 1,929 0,83, 4,267 1,51 e 54,2 11,96. Os grupos MB e TIG apresentaram boa resistência à corrosão, com maior módulo de impedância em relação ao grupo BRA. As diferenças no pH da saliva artificial não alteraram o comportamento corrosivo dos grupos MB e TIG. Entretanto, observou-se uma redução marcante na jcorr e no módulo de impedância nas soldas obtidas pelo processo de brasagem. O grupo BRA apresentou corrosão galvânica ao ser analisado formando par com o MB, mostrando uma jcorr de 5,3 A.cm-2. Entretanto, o mesmo não foi observado quando o MB foi associado à solda TIG, onde a jcorr foi cerca de 150 vezes menor. O grupo BRA, além de apresentar um comportamento eletroquímico muito diferente do MB, revelou diferenças marcantes quanto a composição química, aspecto microestrutural e microdureza. As juntas TIG e LAS mostraram semelhanças químicas e microestruturais em relação ao MB, sendo que na solda TIG esta semelhança foi ainda mais evidente. Além disto, a solda TIG apresentou um comportamento eletroquímico muito semelhante ao MB e, portanto, parecendo ser mais recomendável para soldar ligas odontológicas de níquel-cromo em relação aos demais processos de soldagem aqui avaliados.