Field-induced dielectric properties of laser ablated antiferroelectric (Pb0.99Nb0.02)(Zr0.57Sn0.38Ti0.05)0.98O3 thin films

Niobium-modified lead zirconate stannate titanate antiferroelectric thin films with the chemical composition of (Pb0.99Nb0.02)(Zr0.57Sn0.38Ti0.05)0.98O3 were deposited by pulsed excimer laser ablation technique on Pt-coated Si substrates. Field-induced phase transition from antiferroelectric to ferroelectric properties was studied at different fields as a function of temperature. The field forced ferroelectric phase transition was elucidated by the presence of double-polarization hysteresis and double-butterfly characteristics from polarization versus applied electric field and capacitance and voltage measurements, respectively. The measured forward and reverse switching fields were 25 kV/cm and 77 kV/cm, respectively. The measured dielectric constant and dissipation factor were 540 and 0.001 at 100 kHz, respectively, at room temperature.

Signature of a silver phase percolation threshold in microscopically phase separated ternary Ge0.15Se0.85-xAgx (0≤x≤0.20) glasses

Temperature modulated alternating differential scanning calorimetric studies show that Se rich Ge0.15Se0.85−xAgx (0 x 0.20) glasses are microscopically phase separated, containing Ag2Se phases embedded in a Ge0.15Se0.85 backbone. With increasing silver concentration, Ag2Se phase percolates in the Ge–Se matrix, with a well-defined percolation threshold at x = 0.10. A signature of this percolation transition is shown up in the thermal behavior, as the appearance of two exothermic crystallization peaks. Density, molar volume, and microhardness measurements, undertaken in the present study, also strongly support this view of percolation transition. The superionic conduction observed earlier in these glasses at higher silver proportions is likely to be connected with the silver phase percolation.

Realization of biferroic properties in La0.6Sr0.4MnO3/0.7Pb(Mg1/3Nb2/3)O3–0.3(PbTiO3) epitaxial superlattices

A set of symmetric and asymmetric superlattices with ferromagnetic La0.6Sr0.4MnO3 (LSMO) and ferroelectric 0.7Pb(Mg1/3Nb2/3)O3–0.3(PbTiO3) as the constituting layers was fabricated on LaNiO3 coated (100) oriented LaAlO3 substrates using pulsed laser ablation. The crystallinity, and magnetic and ferroelectric properties were studied for all the superlattices. All the superlattice structures exhibited a ferromagnetic behavior over a wide range of temperatures between 10 and 300 K, whereas only the asymmetric superlattices exhibited a reasonably good ferroelectric behavior. Strong influence of an applied magnetic field was observed on the ferroelectric properties of the asymmetric superlattices. Studies were conducted toward understanding the influence of conducting LSMO layers on the electrical responses of the heterostructures. The absence of ferroelectricity in the symmetric superlattice structures has been attributed to their high leakage characteristics. The effect of an applied magnetic field on the ferroelectric properties of the asymmetric superlattices indicated strong influence of the interfaces on the properties. The dominance of the interface on the dielectric response was confirmed by the observed Maxwell-Wagner-type dielectric relaxation in these heterostructures.

Interface dominated biferroic La0.6Sr0.4MnO3/0.7Pb(Mg1/3Nb2/3)O3–0.3PbTiO3 epitaxial superlattices

Superlattices composed of ferromagnetic La0.6Sr0.4MnO3 and ferroelectric 0.7Pb(Mg1/3Nb2/3)O3–0.3(PbTiO3) layers were fabricated on (100) LaAlO3 substrates by pulsed laser deposition technique. The ferromagnetic and frequency independent ferroelectric hysteresis characteristics established the biferroic nature of the superlattices. Influence of magnetic field was observed in tuning the P-E characteristics of the superlattices. A similar effect was observed on application of a high dc electric field to the samples. The nature of the observed ferroelectric properties and their modulation by applied magnetic and electric fields were thus discussed in connection to the ferroelectric/ferromagnetic interfaces.

Evolution of sub-micron grain size and weak texture in magnesium alloy Mg-3Al-0.4Mn by a modified multi-axial forging process

This is the first successful attempt to produce simultaneously ultrafine grain size and weak texture in a single-phase magnesium alloy Mg-3Al-0.4Mn through an optimal choice of processing parameters in a modified multi-axial forging (MAF) process. An average grain size of similar to 0.4 mu m and a weak texture could be achieved. This has led to an increase in the strength as well as room-temperature ductility (55%). The plot of the yield loci shows a decrease in anisotropy after MAF. (C) 2011 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Structural and dielectric behavior of pulsed laser ablated Sr(0.6)Ca(0.4)TiO(3) thin film and asymmetric multilayer of SrTiO(3) and CaTiO(3)

Homogeneous thin films of Sr(0.6)Ca(0.4)TiO(3) (SCT40) and asymmetric multilayer of SrTiO(3) (STO) and CaTiO(3) (CTO) were fabricated on Pt/Ti/SiO(2)/Si substrates by using pulsed laser deposition technique. The electrical behavior of films was observed within a temperature range of 153 K-373 K. A feeble dielectric peak of SCT40 thin film at 273 K is justified as paraelectric to antiferroelectric phase transition. Moreover, the Curie-Weiss temperature, determined from the epsilon'(T) data above the transition temperature is found to be negative. Using Landau theory, the negative Curie-Weiss temperature is interpreted in terms of an antiferroelectric transition. The asymmetric multilayer exhibits a broad dielectric peak at 273 K. and is attributed to interdiffusion at several interfaces of multilayer. The average dielectric constants for homogeneous Sr(0.6)Ca(0.4)TiO(3) films (similar to 650) and asymmetric multilayered films (similar to 350) at room temperature are recognized as a consequence of grain size effect. Small frequency dispersion in the real part of the dielectric constants and relatively low dielectric losses for both cases ensure high quality of the films applicable for next generation integrated devices. (C) 2011 Elsevier B.V. All rights reserved.

Synthesis, structural characterization and ferroelectric properties of Pb(0.76)Ca(0.24)TiO(3) nanotubes

A capillary-enforced template-based method has been applied to fabricate Pb(0.76)Ca(0.24)TiO(3) (PCT24) nanotubes via filling PCT24 precursor solution, prepared by modified sol-gel method, into nanochannels of anodic aluminum oxide templates. The morphology and structure of as-prepared PCT24 were examined by scanning electron microscopy, transmission electron microscopy (TEM) and X-ray diffraction techniques. The obtained PCT24 nanotubes with diameter of similar to 200 nm and wall thickness of similar to 20 nm exhibited a tetragonal perovskite structure. High resolution TEM (HRTEM) analysis confirmed that as-obtained PCT24 nanotubes made up of nanoparticles (5-8 nm) which were randomly aligned in the nanotubes. Formation of some solid crystalline PCT24 nanorods, Y-junctions and multi-branches were observed. Interconnections in the pores of template are responsible for the growth of Y-junctions and multi-branches. The possible formation mechanism of PCT24 nanotubes/nanorods was discussed. Ferroelectric hysteresis loops of PCT24 nanotube arrays were measured, showing a room temperature ferroelectric characteristic of as-prepared PCT24 nanotubes. (C) 2011 Elsevier B.V. All rights reserved.

Kinetics of carbon monoxide oxidation with Sn(0.95)M(0.05)O(2-delta) (M = Cu, Fe, Mn, Co) catalysts

Base metal substituted Sn(0.95)M(0.05)O(2-delta) (M = Cu, Fe, Mn, Co) catalysts were synthesized by the solution combustion method and characterized by XRD, XPS, TEM and BET surface area analysis. The catalytic activities of these materials were investigated by performing CO oxidation. The rates and the apparent activation energies of the reaction for CO oxidation were determined for each catalyst. All the substituted catalysts showed high rates and lower activation energies for the oxidation of CO as compared to unsubstituted SnO(2). The rate was found to be much higher over copper substituted SnO(2) as compared to other studied catalysts. 100% CO conversion was obtained below 225 degrees C over this catalyst. A bifunctional reaction mechanism was developed that accounts for CO adsorption on base metal and support ions and O(2) dissociation on the oxide ion vacancy. The kinetic parameters were determined by fitting the model to the experimental data. The high rates of the CO oxidation reactions at low temperatures were rationalized by the high dissociative chemisorption of adsorbed O(2) over these catalysts.

Perovskite phase transformation in 0.65Pb(Mg1/3Nb2/3)O-3-0.35PbTiO(3) nanoparticles derived by sol-gel

Fabrication of 0.65Pb(Mg1/3Nb2./3)O-3-0.35PbTiO(3) (PMN-PT) nanoparticles with an average size of about 40 nm and their phase transformation behavior from pyrochlore to perovskite phase is investigated. A novel sol-gel method was used for the synthesis of air-stable and precipitate-free diol-based sol of PMN-PT which was dried and partially calcined at 450 degrees C for 1 h to decompose organics and bring down the free energy barrier for perovskite crystallization and then finally annealed in the temperature range 600 to 700 degrees C. Annealed at around 700 degrees C for 1 h, PMN-PT gel powder exhibited nanocrystalline morphology with perovskite phase as confirmed by the transmission electron microscopy and X-ray diffraction techniques. (C) 2012 American Institute of Physics. [doi: 10.1063/1.3677974]

Fragment Finder 2.0: a computing server to identify structurally similar fragments

Fragment Finder 2.0 is a web-based interactive computing server which can be used to retrieve structurally similar protein fragments from 25 and 90% nonredundant data sets. The computing server identifies structurally similar fragments using the protein backbone C alpha angles. In addition, the identified fragments can be superimposed using either of the two structural superposition programs, STAMP and PROFIT, provided in the server. The freely available Java plug-in Jmol has been interfaced with the server for the visualization of the query and superposed fragments. The server is the updated version of a previously developed search engine and employs an in-house-developed fast pattern matching algorithm. This server can be accessed freely over the World Wide Web through the URL http://cluster.physics.iisc.ernet.in/ff/.

Tuning of phonon anharmonicity in pyrochlore titanates: temperature-dependent Raman studies of Sm2Ti2-xZrxO7 (x=0, 1/2, 3/4, and 2)and stuffed spin-ice Ho2+xTi2-xO7-x/2 (x=0, 1/3, and 2/3)

Anomalous temperature dependence of Raman phonon wavenumbers attributed to phononphonon anharmonic interactions has been studied in two different families of pyrochlore titanates. We bring out the role of the ionic size of titanium and the inherent vacancies of pyrochlore in these anomalies by studying the effect of replacement of Ti4?+ by Zr4?+ in Sm2Ti2O7 and by stuffing Ho3?+ in place of Ti4?+ in Ho2Ti2O7 with appropriate oxygen stoichiometry. Our results show that an increase in the concentration of the larger ion, i.e. Zr4?+ or Ho3?+, reduces the phonon anomalies, thus implying a decrease in the phononphonon anharmonic interactions. In addition, we find signatures of coupling between a phonon and crystal field transition in Sm2Ti2O7, manifested as an unusual increase in the phonon intensity with increasing temperature. Copyright (c) 2011 John Wiley & Sons, Ltd.

Studies on Field Dependent Domain Structures in Multi-Grained 0.85PbMg(1/3)Nb(2/3)O3-0.15PbTiO(3) Thin Films by Scanning Force Microscopy

0.85PbMg(1/3)Nb(2/3)O(3)-0.15PbTiO(3) (0.85PMN-0.15PT) ferroelectric relaxor thin films have been deposited on La0.5Sr0.5CoO3/(111) Pt/TiO2/SiO2/Si by pulsed laser ablation by varying the oxygen partial pressures from 50 mTorr to 400 mTorr. The X-ray diffraction pattern reveals a pyrochlore free polycrystalline film. The grain morphology of the deposited films was studied using scanning electron microscopy and was found to be affected by oxygen pressure. By employing dynamic contact-electrostatic force microscopy we found that the distribution of polar nanoregions is majorly affected by oxygen pressure. Finally, the electric field induced switching in these films is discussed in terms of domain wall pinning.

Synthesis dependent characteristics of Sr1-xMnxTiO3 (x=0.03, 0.05, 0.07 and 0.09)

Sr1-xMnxTiO3 (where x=0.03, 0.05, 0.07 and 0.09) was synthesized via different routes that include solid-state, oxalate precipitation and freeze drying. In oxalate precipitation technique, compositions corresponding to 3 and 5 mol% doping of Mn were monophasic whereas the higher compositions revealed the presence of the secondary phases such as MnO, Mn3O4 etc., as confirmed by high resolution X-ray diffraction (XRD) studies. The decomposition behavior of the precursors prepared using oxalate precipitation method corresponding to the above mentioned compositions was studied. Nanopowders of compositions pertaining to 5 to 9 mol% of Mn doping were obtained using freeze-drying technique. The average crystallite size of these nanopowders was found to be in the 35 to 65 nm range. The microstructural studies carried out on the sintered ceramics, fabricated using powders synthesized by different routes established the fine grained nature ( < 1 mu m) of the one obtained by freeze drying method. Raman scattering studies were carried out in order to complement the observations made from XRD regarding the phase purity. The dielectric properties of the ceramics obtained by different synthesis routes were studied in the 80-300 K temperature range at 100 kHz and the effect of grain size has been discussed. (C) 2012 Elsevier Inc. All rights reserved.

Comments on ``Effects of current density on the formation and microstructure of Sn-9Zn, Sn-8Zn-3Bi and Sn-3Ag-0.5Cu solder joints''

Othman et al. (Intermetallics 2012;22:1-6) recently published a manuscript on ``Effects of current density on the formation and microstructure of Sn-9Zn, Sn-8Zn-3Bi and Sn-3Ag-0.5Cu solder joints''. We found problems in calculation of diffusion parameters. Even the comment on the formation of Cu5Zn8 instead of Cu6Sn5 is not correct. In this comment, we have explained the correct procedure to calculate the diffusion coefficients. Further, we have also explained the reason for the formation of Cu5Zn8 instead of Cu6Sn5 in the Cu/Sn-9Zn system. (C) 2012 Elsevier Ltd. All rights reserved.

Ferrimagnetism, antiferromagnetism, and magnetic frustration in La2-xSrxCuRuO6 (0 <= x <= 1)

We studied structural and magnetic properties of a series of insulating double perovskite compounds, La2-xSrxCuRuO6 (0 <= x <= 1), representing doping via A-site substitution. The end members La2CuRuO6 and LaSrCuRuO6 form in monoclinic structure while the intermediate Sr doped compounds stabilize in triclinic structure. The Cu and Ru ions sit on alternate B sites of the perovskite lattice with similar to 15% antisite defects in the undoped sample while the Sr-doped samples show a tendency to higher ordering at B sites. The undoped (x = 0) compound shows a ferrimagnetic-like behavior at low temperatures. In surprising contrast to the usual expectation of an enhancement of ferromagnetic interaction on doping, an antiferromagnetic-like ground state is realized for all doped samples (x > 0). Heat capacity measurements indicate the absence of any long-range magnetic order in any of these compounds. The magnetic relaxation and memory effects observed in all compounds suggest glassy dynamical properties associated with magnetic disorder and frustration. We show that the observed magnetic properties are dominated by the competition between the nearest-neighbor Ru-O-Cu 180 degrees superexchange interaction and the next-nearest-neighbor Ru-O-O-Ru 90 degrees superexchange interaction as well as by the formation of antisite defects with interchanged Cu and Ru positions. Our calculated exchange interaction parameters from first principles calculations for x = 0 and x = 1 support this interpretation.