Performance of calcium deficient hydroxyapatite-polyglycolic acid composites: An in vitro study

The strategic incorporation of bioresorbable polymeric additives to calcium-deficient hydroxyapatite cement may provide short-term structural reinforcement and modify the modulus to closer match bone. The longer-term resorption properties may also be improved, creating pathways for bone in-growth. The aim of this study was to investigate the resorption process of a calcium phosphate cement system containing either in polyglycolic acid tri-methylene carbonate particles or polyglycolic acid fibres. This was achieved by in vitro aging in physiological conditions (phosphate buffered solution at 37°C) over 12 weeks. The unreinforced CPC exhibited an increase in compressive strength at 12 weeks, however catastrophic failure was observed above a critical loading. The fracture behaviour of cement was improved by the incorporation of PGA fibres; the cement retained its cohesive structure after critical loading. Gravimetric analysis and scanning electron microscopy showed a large proportion of the fibres had resorbed after 12 weeks allowing for the increased cement porosity, which could facilitate cell infiltration and faster integration of natural bone. Incorporating the particulate additives in the cement did not provide any mechanism for mechanical property augmentation or did not demonstrate any appreciable level of resorption after 12 weeks.

The synthesis and characterization of nanophase hydroxyapatite using a novel dispersant-aided precipitation method

The synthesis of nanophase hydroxyapatite (nHA) is of importance in the field of biomaterials and bone tissue engineering. The bioactive and osteoconductive properties of nHA are of much benefit to a wide range of biomedical applications such as producing bone tissue engineered constructs, coating medical implants, or as a carrier for plasmid DNA in gene delivery. This study aimed to develop a novel low-temperature dispersant-aided precipitation reaction to produce nHA particles (

SEM-EDX of morphology of electroless nickel coatings with tin and tungsten

Electroless plating of binary Ni-P, ternary Ni-Sn-P and Ni-W-P, and quaternary Ni-W-Sn-P alloy coatings was carried out in alkalicitrate baths. After the plating, several kinds of test were carried out to determine the improvement in the characteristics and properties due to the additional elements as well as to study the change in behaviour when heat treatment was applied to these coatings. The coatings were subjected to X-ray diffraction analysis where it was found that all the coatings were amorphous. Interesting surface morphology features were examined using scanning electron microscopy. Addition of a third element improved the hardness.

Thin catalytic coatings on microreactor walls A way to make industrial processes more efficient

Current trends in the development of microstructured reactors with thin catalytic films (from 100 nm up to several microns) that have self-assembled nanostructures are discussed. A major technique that is used to prepare such films is sol-gel processing. This involves depositing a complex fluid on a microstructured substrate by dip, spin, or spray coating, followed by surfactant removal to form the porous nanostructures. A novel methodology has been developed by which a uniform coating containing controlled amounts of (poly) metallic nanoparticles can be obtained. This elegant strategy is based on the condensation of metal oxide species by self-assembly in the presence of metallic colloids. The potential microreactor applications brought forth by this innovative protocol are placed in perspective in the light of its versatility.