A comparison of microhardness of indirect composite restorative materials

The purpose of this study was to compare the microhardness of four indirect composite resins. Forty cylindrical samples were prepared according to the manufacturer s recommendations using a Teflon mold. Ten specimens were produced from each tested material, constituting four groups (n=10) as follows: G1 - Artglass; G2 - Sinfony; G3 - Solidex; G4 - Targis. Microhardness was determined by the Vickers indentation technique with a load of 300g for 10 seconds. Four indentations were made on each sample, determining the mean microhardness values for each specimen. Descriptive statistics data for the experimental conditions were: G1 - Artglass (mean ±standard deviation: 55.26 ± 1.15HVN; median: 52.6); G2 - Sinfony (31.22 ± 0.65HVN; 31.30); G3 - Solidex (52.25 ± 1.55HVN; 52.60); G4 - Targis (72.14 ± 2.82HVN; 73.30). An exploratory data analysis was performed to determine the most appropriate statistical test through: (I) Levene's for homogeneity of variances; (II) ANOVA on ranks (Kruskal-Wallis); (III) Dunn's multiple comparison test (0.05). Targis presented the highest microhardness values while Sinfony presented the lowest. Artglass and Solidex were found as intermediate materials. These results indicate that distinct mechanical properties may be observed at specific materials. The composition of each material as well as variations on polymerization methods are possibly responsibles for the difference found in microhardness. Therefore, indirect composite resin materials that guarantee both good esthetics and adequate mechanical properties may be considered as substitutes of natural teeth.

Resin tag length of one-step and self-etching adhesives bonded to unground enamel

Length of resin tags yielded by utilization of an one-step conventional adhesive system and self-etching adhesive system on unground enamel was observed. In study Groups I and III, the enamel surface was etched for 60 seconds with 35% phosphoric acid gel and adhesive systems PQ1 (Ultradent Products, Inc) and Adper Prompt L Pop (3M/ESPE) were applied. Adper Prompt L Pop (3M/ESPE) was also applied in Group II in accordance with the manufacturer's recommendations. After application of these adhesive systems to dental enamel, specimens were prepared for light microscopy analysis to ascertain degree of penetration (x400). The results were submitted to an analysis of variance at the 5% level; whenever there was significance, the Tukey test was applied at the 5% level. It was found that acid etching prior to application of conventional and self-etching adhesive materials provided higher penetration of the adhesive into the unground enamel surface compared to that achieved solely by application of self-etching adhesive.

Evaluation of the bleached human enamel by scanning electron microscopy

Since bleaching has become a popular procedure, the effect of peroxides on dental hard tissues is of great interest in research. Purpose: The aim of this in vitro study was to perform a qualitative analysis of the human enamel after the application of in-office bleaching agents, using Scanning Electron Microscopy (SEM). Materials and Methods: Twenty intact human third molars extracted for orthodontic reasons were randomly divided into four groups (n=5) treated as follows: G1- storage in artificial saliva (control group); G2- four 30-minute applications of 35% carbamide peroxide (total exposure: 2h); G3- four 2-hour exposures to 35% carbamide peroxide (total exposure: 8h); G4- two applications of 35% hydrogen peroxide, which was light-activated with halogen lamp at 700mW/cm2 during 7min and remained in contact with enamel for 20min (total exposure: 40min). All bleaching treatments adopted in this study followed the application protocols advised by manufacturers. Evaluation of groups submitted to 35% carbamide peroxide was carried out after two time intervals (30 minutes and 2 hours per session), following the extreme situations recommended by the manufacturer. Specimens were prepared for SEM analysis performing gold sputter coating under vacuum and were examined using 15kV at 500x and 2000x magnification. Results: Morphological alterations on the enamel surface were similarly detected after bleaching with either 35% carbamide peroxide or 35% hydrogen peroxide. Surface porosities were characteristic of an erosive process that took place on human enamel. Depression areas, including the formation of craters, and exposure of enamel rods could also be detected. Conclusion: Bleaching effects on enamel morphology were randomly distributed throughout enamel surface and various degrees of enamel damage could be noticed. Clinical significance: In-office bleaching materials may adversely affect enamel morphology and therefore should be used with caution.

Anticariogenic potencial of acidulate solutions with low fluoride concentration

Objetives: The aim of this study was to verify the anticariogenic effect of acidulate solutions with low NaF concentration, using pH-cycling model and bovine enamel. Material and Methods: Enamel blocks were submitted to the surface microhardness (SMH) test and randomly divided in 12 experimental and one placebo groups. The blocks were submitted to pH cycling for 7 days, with daily applications once/day of 0.05% NaF and 0.1% NaF and twice/day of 0.02% NaF solutions. Four different pH: 4.0, 5.0, 6.0 and 7.0 were used. Next, SMH test was again used to determine the surface microhardness percentage change (%SMH). Data obtained for %SMH were homogeneous and passed through variance analyses and Tukey's test (5%) as far as fluoride concentrations and pH. Results: The results showed that pH influenced %SMH in 0.02% NaF and 0.05% NaF solutions with pH 4.0, which had less mineral loss compared to pH 7.0 (p<0.05). The 0.02% NaF - pH 4.0, and 0.05% NaF – pH 7.0 groups showed similar results (p>0.05). A dose-response relationship was observed among the tested solutions, with better anticariogenic effect for the 0.1% NaF solution. Conclusion: The results suggest that the addition of citric acid to acidulate mouth rinses reduce mineral loss.

Dental mineralization and salivary activity are reduced in offspring of spontaneously hypertensive rats (SHR)

Several pathologies have been diagnosed in children of hypertensive mothers; however, some studies that evaluated the alterations in their oral health are not conclusive. This study analyzed the salivary gland activity and dental mineralization of offsprings of spontaneously hypertensive rats (SHR). Thirty-day-old SHR males and Wistar rats were studied. The salivary flow was evaluated by injection of pilocarpine, the protein concentration and salivary amylase activity, by the Lowry method and kinetic method at 405 nm, respectively. Enamel and dentin mineralization of the mandibular incisors was quantified with aid of the microhardness meter. The results were analyzed by the ANOVA or Student's t test (p<0.05). It was noticed that the salivary flow rate (0.026 mL/min/100 g ± 0.002) and salivary protein concentration (2.26 mg/mL ± 0.14) of SHR offspring were reduced compared to Wistar normotensive offspring (0.036 mL/min/100 g ± 0.003 and 2.91 mg/mL ± 0.27, respectively), yet there was no alteration in amylase activity (SHR: 242.4 U/mL ± 36.9; Wistar: 163.8 U/mL ± 14.1). Microhardness was lower both in enamel (255.8 KHN ± 2.6) and dentin (59.9 KHN ± 0.8) for the SHR teeth compared to the Wistar teeth (enamel: 328.7 KHN ± 3.3 and dentin: 67.1 KHN ± 1.0). These results suggest that the SHR offspring are more susceptible to development of pathologies impairing oral health, once they presented lesser flow and salivary protein concentration and lower dental mineralization.

Effects of dental bleaching on the color, translucency and fluorescence properties of enamel and dentin

The objective of this study was to evaluate the color, translucency and fluorescence of bovine enamel and dentin submitted to different bleaching modalities. Pairs of enamel and dentin discs (3 mm in diameter) were obtained from 150 bovine teeth. In 75 of the pairs, one specimen had the enamel removed (Dentin Group). The dentin was removed from one specimen of the remaining 75 pairs (Enamel Group) and the other specimen was left unaltered (Enamel + Dentin). The evaluation of color, translucency and fluorescence was performed with a spectrophotometer using the CIE L* a* b*. Each group was subdivided into three subgroups: Control, composed of specimens that were not bleached, and two experimental subgroups, bleached with either 10% carbamide peroxide (CP10%) or 35% hydrogen peroxide (HP35%). The CP10% bleaching gel was applied 2 h/day for 14 days. The HP35% bleaching agent was applied using two applications of 30 min each, with a one week interval between each application. When not being bleached, the specimens were immersed in artificial saliva. The color, translucency and fluorescence ratings were assessed using spectrophotometry 7 days after the treatment. Regarding color, significant differences were found between bleaching techniques in the groups Enamel and Enamel + Dentin, with a higher color difference for HP35%. Bleaching did not change the translucency of the dental tissues. There were significant differences for fluorescence for the HP35% subgroups of Dentin and Enamel + Dentin, and for the CP10% subgroup of Enamel. Dental bleaching changed the color and fluorescence of the dental tissues, however translucency was not affected.

In vitro enamel remineralization capacity of composite resins containing sodium trimetaphosphate and fluoride

This study evaluated the in vitro enamel remineralization capacity of experimental composite resins containing sodium trimetaphosphate (TMP) combined or not with fluoride (F). Bovine enamel slabs were selected upon analysis of initial surface hardness (SH1) and after induction of artificial carious lesions (SH2). Experimental resins were as follows: resin C (control-no sodium fluoride (NaF) or TMP), resin F (with 1.6 % NaF), resin TMP (with 14.1 % TMP), and resin TMP/F (with NaF and TMP). Resin samples were made and attached to enamel slabs (n = 12 slabs per material). Those specimens (resin/enamel slab) were subjected to pH cycling to promote remineralization, and then final surface hardness (SH3) was measured to calculate the percentage of surface hardness recovery (%SH). The integrated recovery of subsurface hardness (ΔKHN) and F concentration in enamel were also determined. Data was analyzed by ANOVA and Student-Newman-Keuls test (p < 0.05). Resins F and TMP/F showed similar SH3 values (p = 0.478) and %SH (p = 0.336) and differed significantly from the other resins (p < 0.001). Considering ΔKHN values, resin TMP/F presented the lowest area of lesion (p < 0.001). The presence of F on enamel was different among the fluoridated resins (p = 0.042), but higher than in the other resins (p < 0.001). The addition of TMP to a fluoridated composite resin enhanced its capacity for remineralization of enamel in vitro. The combination of two agents with action on enamel favored remineralization, suggesting that composite resins containing sodium trimetaphosphate and fluoride could be indicated for clinical procedures in situations with higher cariogenic challenges.

In vitro effect of sodium trimetaphosphate additives to conventional toothpastes on enamel demineralization

The aim of this study was to evaluate the ability of conventional toothpastes (1100 ppm F) supplemented with sodium trimetaphosphate (TMP) in demineralization. Blocks of enamel were selected and then divided into seven experimental groups of 12: toothpaste without F and TMP (placebo), toothpaste with 1100 ppm F (1100), and toothpaste with 1100 ppm F supplemented with TMP-1 % (1100 1 % TMP), 3 % (1100 3 % TMP), 4.5 % (1100 4.5 % TMP), 6 % (1100 6 % TMP), and 9 % (1100 9 % TMP). Blocks were subjected to five pH cycles (demineralizing/remineralizing solutions) at 37 °C and treated with toothpaste slurries twice daily, after which the blocks were maintained for 2 days in fresh remineralizing solution. Following treatments, surface hardness (SHf) and cross-sectional hardness were determined for calculating the integrated loss of subsurface hardness (ΔKHN). The fluoride present in the enamel was also measured. The SHf and ΔKHN measurements showed that supplementation with 3 % TMP was the most effective (p < 0.001) and showed greater concentration of F in the enamel (p < 0.001). Addition of 3 % TMP to a conventional toothpaste (1100 ppm F) showed greater efficacy in reducing enamel demineralization. Fluoride toothpastes containing trimetaphosphate possess good anticaries potential required to reduce the prevalence of dental caries in high-risk patients.

Synergistic effect of fluoride and sodium hexametaphosphate in toothpaste on enamel demineralization in situ

To evaluate the effect of a fluoride dentifrice containing sodium hexametaphosphate (HMP) on enamel demineralization in situ. This double-blind and cross-over study consisted of 3 phases (7 days each) in which 12 volunteers wore intraoral appliances containing four enamel bovine blocks. Specimens were treated (3×/day) with placebo (no F or HMP), 1100ppm F (1100F) and 1100F plus HMP1% (1100F-HMP1%) toothpastes, and the cariogenic challenge was performed using a 30% sucrose solution (6×/day). Final surface hardness, the percentage of surface hardness loss (%SH), the integrated loss of subsurface hardness (ΔKHN), as well as enamel calcium (Ca), phosphorus (P) and firmly-bound fluoride (F) were determined. Also, biofilm formed on the blocks were analyzed for F, Ca, P and insoluble extracellular polysaccharide (EPS) concentrations. Data were submitted 1-way ANOVA, followed by Student-Newman-Keuls' test (p<0.05). 1100F-HMP1% promoted the lowest %SH and ΔKHN among all groups (p<0.001). The addition of HMP1% to 1100F did not enhance enamel F uptake, but significantly increased enamel Ca concentrations (p<0.001). Similar EPS concentrations were seen for 1100F-HMP1% and 1100F groups (p>0.05). All the groups were supersaturated with respect to HA. However, only 1100F-HMP1% group was supersaturated with respect to CaF2 (p<0.05). The ionic activities of F(-), CaF(+) and HF(0) for the 1100F-HMP1% group were the highest among all groups (p<0.001). The addition of HMP1% to a conventional toothpaste significantly reduces enamel demineralization in situ when compared to 1100F. This dentifrice could be a viable alternative to patients at high risk of caries.

Amoxicillin diminishes the thickness of the enamel matrix that is deposited during the secretory stage in rats

The use of amoxicillin during early childhood has been associated with molar incisor hypomineralization. The objective of this study was to determine whether the use of amoxicillin interferes with enamel development, during secretion and early mineralization stages. Fifteen pregnant rats were randomly assigned to three groups that received physiological solution (sham group), 100 mg/kg/day amoxicillin (A100G), and 500 mg/kg/day amoxicillin (A500G). After birth, the pups in each group received the same treatment until post-natal day 7 or 12. The upper first molars were analyzed histomorphometrical and immunostaining with amelogenin on day 7, and MMP-20 on day 12 was performed using a semiquantitative method (H-score). At 7 days, several vacuolar structures were observed in the ameloblasts in the A100G and A500G groups. A significant reduction of the enamel thickness (P < 0.001) was found in amoxicillin-treated rats compared with the sham group. Significant differences were not observed in enamel thickness (P > 0.05) between the groups of 12-day-old rats. Moreover, significant differences were not observed in the number of amelogenin- and MMP-20-immunolabeled ameloblasts (P > 0.05) between groups. The present results suggest that amoxicillin interferes with the initial stages of amelogenesis by causing structural changes in the ameloblasts and a reduction of the enamel matrix.

Responses of human dental pulp cells after application of a low-concentration bleaching gel to enamel

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of home-bleaching gels modified by calcium and/or fluoride and the application of nano-hydroxyapatite paste on in vitro enamel erosion susceptibility

This in vitro study compared the effect of bleaching agents modified by the addition of calcium and/or fluoride and the application of a nano-hydroxyapatite paste after bleaching, on the susceptibility of enamel to erosion. Bovine enamel cylindrical samples (3 mm diameter) were assigned to six groups (n = 20 specimens/group) according to the bleaching agent: no bleaching (C-control), 7.5% hydrogen peroxide gel (HP), HP with 0.5% calcium gluconate (HP+Ca), HP with 0.2% sodium fluoride (HP+F), HP with calcium and fluoride (HP+Ca+F) and HP followed by the application of a nano-hydroxyapatite agent (HP+NanoP). The gels were applied on the enamel surface (1 h) followed by cyclic erosive challenges (Sprite Zero®-2 min), for 14 days. The paste was applied after bleaching for 5 min (HP+NanoP). The enamel surface alteration was measured by contact profilometry (µm) (after 7 and 14 days). C-control (mean ± SD: 2.29 ± 0.37 at 7 days/4.86 ± 0.72 at 14 days) showed significantly lower loss compared to the experimental groups. HP+Ca (3.34 ± 0.37/6.75 ± 1.09) and HP+F (4.49 ± 0.92/7.61 ± 0.90) presented significantly lower enamel loss than HP (4.18 ± 0.50/10.30 ± 1.58) only for 14 days and HP+Ca+F (4.92 ± 1.03/8.12 ± 1.52) showed values similar to the HP+F group. The HP+NanoP (5.51 ± 1.04/9.61 ± 1.21) resulted in enamel loss similar to the HP after 14 days. It was found that 7.5% hydrogen peroxide increased the susceptibility of enamel to erosion. The addition of calcium or fluoride to the bleaching gel reduced the erosion effect, while the nano-hydroxyapatite agent did not provide any protective effect.

Effectiveness of a toothpaste with low fluoride content combined with trimetaphosphate on dental biofilm and enamel demineralization in situ

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Fluoride gel supplemented with sodium hexametaphosphate reduces enamel erosive wear in situ

This study evaluated the effect of fluoride gels, supplemented or not with sodium hexametaphosphate (HMP), on enamel erosive wear in situ. Twelve healthy volunteers wore palatal appliances containing four bovine enamel discs. Subjects were randomly allocated into four experimental phases (double-blind, crossover protocol) according to the gels: Placebo (no fluoride or HMP), 1% NaF, 2% NaF, and 1% NaF+9% HMP. Enamel discs were selected after polishing and surface hardness analysis, and treated only once with the respective gels prior to each experimental phase. Erosion (ERO) was performed by extra-oral immersion of the appliance in 0.05M citric acid, pH 3.2 (four times/day, five minutes each, 5 days). Additional abrasion (ERO+ABR) was produced on only two discs by toothbrushing with fluoridated dentifrice after ERO (four times/day, 30s, 5 days). The specimens were submitted to profilometry and hardness analysis. The results were analyzed by two-way ANOVA and the Student-Newman-Keuls test (p<0.05). The 1% NaF+9% HMP gel promoted significantly lower enamel wear for ERO compared to the other groups, being statistically lower than 1% NaF and Placebo for ERO+ABR. Similarly, the lowest values of integrated lesion area were found for 1% NaF+9% HMP and 2% NaF, respectively, for ERO and ERO+ABR. The addition of HMP to the 1% NaF gel promoted greater protective effect against ERO and ERO+ABR compared to the 1% NaF gel, achieving similar protective levels to those seen for the 2% NaF gel. Gel containing 1% NaF+9% HMP showed a high anti-erosive potential, being a safer alternative when compared to a conventional 2% NaF gel.

In vitro effect of low-fluoride toothpastes containing sodium trimetaphosphate on enamel erosion