DISCUSSION OF MECHANISMS OF ACCELERATED AND RETARDED FATIGUE CRACK GROWTH.

The relevance of the effective stress intensity range to crack growth is considered for constant and for variable amplitude loading. The accelerated and retarded growth associated with simple programmed loadings is reported for two steels and an aluminium alloy. The load interaction effects are due to several competing mechanisms, and not due to the single, popular mechanism of crack closure.

FATIGUE CRACK GROWTH - THE COMPLICATIONS.

A vast body of experimental data has been accumulated on the constant amplitude crack growth response of structural metals in moist laboratory air. Usually the data is presented as plots of crack growth rate, da/dN, against stress intensity range, DELTA K. In order to extrapolate this data to fatigue crack growth in more active or more inert environments, to crack growth under variable amplitude loading, or to crack growth under multi-axial or mixed mode loading, the mechanisms of crack advance and crack closure should be considered. This paper briefly reviews the crack closure phenomenon and discusses the dominant causes of accelerated and retarded growth under changes in environment or type of loading. It is argued that simple constant amplitude data is often surprisingly accurate when used to predict crack growth in more complex situations. However, there are some cases where constant amplitude data lead to dangerously non-conservative predictions of fatigue life.