Reverse flotation of silica from Kudremukh iron ore .2. Optimization of flotation process

An experimental programme based on statistical analysis was used for optimizing the reverse Rotation of silica from non-magnetic spiral preconcentrate of Kudremukh iron ore. Flotation of silica with amine and starch as the Rotation reagents was studied to estimate the optimum reagent levels at various mesh of grind. The experiments were first carried out using a two level three factor design. Analysis of the results showed that two parameters namely, the concentration level of the amine collector and the mesh of grind, were significant. Experiments based on an orthogonal design of the hexagonal type were then carried out to determine the effects of these two variables, on recovery and grade of the concentrate. Regression equations have been developed as models. Response contours have been plotted using the 'path of steepest ascent', maximum response has been optimized at 0.27 kg/ton of amine collector, 0.5 kg/ton of starch and mesh of grind of 48.7% passing 300 mesh to give a recovery of 83.43% of Fe in the concentrate containing 66.6% Fe and 2.17% SiO2.

Some unusual features in the Raman spectrum of amorphous-carbon films obtained by pyrolysis of maleic anhydride

Laser micro-Raman spectroscopic measurements were done on the amorphous conducting carbon films obtained from maleic anhydride by pyrolysis process. We have found a predominant broad peak around 1140 cm(-1), in addition to the normally observed peaks in amorphous carbons around 1350 and 1600 cm(-1), and peak of medium intensity around 800 cm(-1). Here we discuss the possibility of conjugated polymer like bond alternating structure which can give rise to these unusual Raman features. (C) 1997 American Institute of Physics.

Structure of highly conducting amorphous carbon

We report on neutron diffraction study of a new form of conducting amorphous carbon up to Q similar to 14.5 Angstrom(-1). The bond distances from first two peaks in g(r) are 1.45 and 2.49 Angstrom, very similar to those in sputtered truly amorphous carbon films (Li and Lannin, Phys. Rev. Lett. 65 (1990) 1905). The first coordination number is 3.1 (+/- 0.1) indicating predominantly sp(2) hybridisation (ideal no. = 3). However, S(Q) itself shows vestiges of (0 0 2), (1 0) and (1 1) peaks, typical of glassy carbon (Mildner, J. Non-Cryst. Solids 47 (1982) 391). (C) 1998 Elsevier Science B.V. All rights reserved.

Size effect on the superconducting transition of embedded lead particles in an Al-Cu-V amorphous matrix

We have synthesized specimens of nanometric lead dispersion in a glassy Al-Cu-V matrix by rapid solidification of the corresponding melt. The microstructure has been designed to avoid superconducting percolation due to coupling of the neighboring particles by the proximity effect. Using these specimens, we have determined quantitatively the effect of size of the ultrafine lead particles on the superconducting transition. (C) 1999 American Institute of Physics. [S0003-6951(99)02037-9].

A new layered iron fluorophosphate

A new iron fluorophosphate of the composition, [C6N4H21] [Fe2F2(HPO4)(3)][H2PO4](.)2H(2)O, I has been prepared by the hydrothermal route. This compound contains iron fluorophosphate layers and the H2PO4- anions are present in the interlayer space along with the protonated amine and water molecules. The compound crystallizes in the monoclinic space group P2(1)/c. (a = 13-4422(10) Angstrom, b = 9 7320(10) Angstrom, c = 18-3123(3) Angstrom, beta = 92-1480degrees, V = 2393-92(5) Angstrom 3, Z = 4, M = 719-92, d(calc). = 1.997 g cm(-3), R-1 = 0.03 and wR(2) = 0,09).

An organically templated iron sulfate with a distorted Kagome lattice exhibiting unusual magnetic properties

A layered iron sulfate of the composition [H3N(CH2)(2)NH2(CH2)(2)NH2(CH2)(2)NH3][(Fe3F6)-F-II(SO4)(2)], possessing a distorted Kagome lattice, prepared hydrothermally, is found to exhibit magnetic hysteresis like a ferrimagnet besides the characteristics of a frustrated system, like those of a spin glass.

Barkhausen jumps and related magnetic properties of iron nanowires encapsulated in aligned carbon nanotube bundles

Iron nanowires encapsulated in aligned carbon nanotube bundles show interesting magnetic properties. Besides the increased coercivity, Barkhausen jumps with 5 emu/g steps in magnetization are observed due to magnetization reversal or depinning of domains. (C) 2002 Elsevier Science B.V. All rights reserved.

Hydrothermal synthesis and structure of organically templated one-dimensional and three-dimensional iron fluorophosphate

Two new open-framework iron fluorophosphates, [C(4)N(2)H(12)](0.5) [FeF(HPO(4))(H(2)PO(4))] (I) and [C(4)N(2)H(12)][Fe(4)F(2)(H(2)O)(4)(PO(4))(4)]. 0.5H(2)O (II), were synthesized hydrothermally using piperazine as a templating agent. The structures were determined by single-crystal X-ray diffraction. Compound I crystallizes in the orthorhombic space group Pbca, a = 7.2126(2) Angstrom, b = 14.2071(4) Angstrom, c = 17.1338(2) Angstrom, Z = 8. The structure is composed of infinite anionic chains of [FeF(HPO(4))(H(2)PO(4))](n)(-) built by trans-fluorine sharing FeF(2)O(4) octahedra. These chains are similar to those found in tancoite-type minerals. Compound II crystallizes in the monoclinic space group P2(1)/n, a = 9.9045(3) Angstrom, b = 12.3011(3) Angstrom, c = 17.3220(4) Angstrom, beta = 103.7010(10)degrees, Z = 4. The structure of compound II has a three-dimensional (3D) architecture with an eight-membered channel along the b axis, in which protonoted piperazine molecules reside. The complex framework is built from two types of secondary building unit (SBU): one hexamer [Fe(3)F(2)(H(2)O)(2)(PO(4))(3)] (SBU6), and one dimer [FeO(4)(H(2)O)(2)PO(4)] (SBU2). The vertex sharing between these SBUs create the 3D structure.

Synthesis of crystallites of carbon nitride in amorphous carbon

We report the successful synthesis of crystalline carbon nitride by chemical vapor deposition of certain nitrogen containing organic precursors. The precursor is heated and the vapors enter the hot deposition zone where they are pyrolysed and deposited in the form of thin films over pretreated substrates. The powder x-ray diffraction analysis shows clear peaks corresponding to the carbon nitride crystals of tetragonal form in addition to a broad hump corresponding to the amorphous nitrogenated carbon. The crystallites size is similar to300Angstrom and the volume fraction of the crystallites is about similar to7%. The optimum conditions of preparation are found out. The Infrared spectra of these samples also suggest the formation of Carbon Nitride crystals. The analysis reconfirms that the material contains crystallites of Carbon Nitride embedded in an amorphous matrix of nitrogenated carbon. Further the material is characterized by C,H,N elemental analysis, EDX and Raman spectra. Since all the above analyses probe the bulk material, the background amorphous matrix in this case, expecting a clear evidence of nanometer sized crystallites from these tests are unlikely. Attempts are being made to increase the yield of these carbon nitride crystallites.

The effect of mischmetal addition on the structure and mechanical properties of a cast Al-7Si-0.3Mg alloy containing excess iron (up to 0.6 Pct)

The effect of Fe content (0.2 to 0.6 pct) on the microstructure and mechanical properties of a cast Al-7Si-0.3Mg (LM 25/356) alloy has been investigated. Further, 1 pct mischmetal (MM) additions (a mixture of rare-earth (RE) elements) were made to these alloys, and their mechanical properties at room and at elevated temperatures (up to 200 degreesC) were evaluated. A structure-property correlation on this alloy was attempted using optical microstructure analysis, fractographs, X-ray diffraction, energy-dispersive analysis of X-rays (EDX), and quantitative metallography by image analysis. An increase in Fe content increased the volume percentage of Fe-bearing intermetallic compounds (beta and pi phases), contributing to the lower yield strength (YS), ultimate tensile strength (UTS), percentage elongation, and higher hardness. An addition of 1 pct MM to the alloys containing 0.2 and 0.6 pct Fe was found to refine the microstructure; modify the eutectic silicon and La, Ce, and Nd present in the MM; form different intermetallic compounds with Al, Si, Fe, and Mg; and improve the mechanical properties of the alloys both at room and elevated temperatures.

Formation of amorphous xenon nanoclusters and microstructure evolution in pulsed laser deposited Ti(62.5)Si(37.5) thin films during Xe ion irradiation

As deposited amorphous and crystallized thin films of Ti 37.5% Si alloy deposited by pulsed laser ablation technique were irradiated with 100 keV Xe(+) ion beam to an ion fluence of about 10(16) ions-cm(-2). Transmission electron microscopy revealed that the implanted Xe formed amorphous nanosized clusters in both cases. The Xe ion-irradiation favors nucleation of a fcc-Ti(Si) phase in amorphous films. However, in crystalline films, irradiation leads to dissolution of the Ti(5)Si(3) intermetallic phase. In both cases, Xe irradiation leads to the evolution of similar microstructures. Our results point to the pivotal role of nucleation in the evolution of the microstructure under the condition of ion implantation.

Superconductivity of embedded lead nano particles in metallic and amorphous matrices

Nanodispersed lead in metallic and amorphous matrices was synthesized by rapid solidification processing. The optimum microstructure was tailored to avoid percolation of the particles. With these embedded particles it is possible to study quantitatively the effect of size on the superconducting transition temperature by carrying out quantitative microstructural characterization and magnetic measurements. Our results suggest the role of the matrices in enhancement or depression of superconducting transition temperature of lead. The origin of this difference in behavior with respect to different matrices and sizes is discussed.

Formation of amorphous xenon nanoclusters and microstructure evolution in pulsed laser deposited Ti62.5Si37.5 thin films during Xe ion irradiation

As deposited amorphous and crystallized thin films of Ti 37.5% Si alloy deposited by pulsed laser ablation technique were irradiated with 100 keV Xe+ ion beam to an ion fluence of about 1016 ions-cm−2. Transmission electron microscopy revealed that the implanted Xe formed amorphous nanosized clusters in both cases. The Xe ion-irradiation favors nucleation of a fcc-Ti(Si) phase in amorphous films. However, in crystalline films, irradiation leads to dissolution of the Ti5Si3 intermetallic phase. In both cases, Xe irradiation leads to the evolution of similar microstructures. Our results point to the pivotal role of nucleation in the evolution of the microstructure under the condition of ion implantation.

Studies of the wetting characteristics of liquid iron on dense alumina by the X-ray sessile drop technique

In the present work, the reaction between a molten iron drop and dense alumina was studied using the X-ray sessile-drop method under different oxygen partial pressures in the gas atmosphere. The changes in contact angles between the iron drop and the alumina substrate were followed as functions of temperature and varying partial pressures of oxygen in the temperature range 1823 to 1873 K both in static and dynamic modes. The results of the contact angle measurements with pure iron in contact with dense alumina in extremely well-purified argon as well as under different oxygen partial pressures in the gas atmosphere showed good agreement with earlier measurements reported in the literature. In the dynamic mode, when argon was replaced by a CO-CO2-Ar mixture with a well-defined PO, in the gas, the contact angle showed an initial decrease followed by a period of nearly constant contact angle. At the end of this period, the length of which was a function of the P-O2 imposed, a further steep decrease in the contact angle was noticed. An intermediate layer of FeAl2O4 was detected in the scanning electron microscope (SEM) analysis of the reacted substrates. An interesting observation in the present experiments is that the iron drop moved away from the site of the reaction once the product layer covered the interface. The results are analyzed on the basis of the various forces acting on the drop.

Rule-based modelling of iron homeostasis in tuberculosis

To establish itself within the host system, Mycobacterium tuberculosis (Mtb) has formulated various means of attacking the host system. One such crucial strategy is the exploitation of the iron resources of the host system. Obtaining and maintaining the required concentration of iron becomes a matter of contest between the host and the pathogen, both trying to achieve this through complex molecular networks. The extent of complexity makes it important to obtain a systems perspective of the interplay between the host and the pathogen with respect to iron homeostasis. We have reconstructed a systems model comprising 92 components and 85 protein-protein or protein-metabolite interactions, which have been captured as a set of 194 rules. Apart from the interactions, these rules also account for protein synthesis and decay, RBC circulation and bacterial production and death rates. We have used a rule-based modelling approach, Kappa, to simulate the system separately under infection and non-infection conditions. Various perturbations including knock-outs and dual perturbation were also carried out to monitor the behavioral change of important proteins and metabolites. From this, key components as well as the required controlling factors in the model that are critical for maintaining iron homeostasis were identified. The model is able to re-establish the importance of iron-dependent regulator (ideR) in Mtb and transferrin (Tf) in the host. Perturbations, where iron storage is increased, appear to enhance nutritional immunity and the analysis indicates how they can be harmful for the host. Instead, decreasing the rate of iron uptake by Tf may prove to be helpful. Simulation and perturbation studies help in identifying Tf as a possible drug target. Regulating the mycobactin (myB) concentration was also identified as a possible strategy to control bacterial growth. The simulations thus provide significant insight into iron homeostasis and also for identifying possible drug targets for tuberculosis.