The influence of current density on the morphology and corrosion properties of MAO coatings on AZ31B magnesium alloy

Micro-arc oxidation (MAO) coatings were prepared on AZ31B magnesium alloy using alkaline silicate electrolyte at different current densities (0.026, 0.046 and 0.067 A/cm(2)). Field Emission Scanning Electron Microscopy (FESEM) analysis of the coating revealed an irregular porous structure with cracked morphology. Compositional analysis carried out for MAO coating showed the presence of almost an equal amount of Mg and 0 (34 wt.%) apart from other elements such as F, Si and AI. The cross-sectional FESEM images clearly portrayed that the MAO coating was dense along with the presence of very few fine pores. The surface roughness (R-a) of the coatings increased with an increase in the current density. Potentiodynamic polarization and electrochemical impedance spectroscopic (EIS) studies were carried out for both the bare and MAO coated AZ31B Mg alloy in 3.5% NaCl solution. The corrosion potential (E-corr) and corrosion current density (i(corr)) values obtained for the bare substrate were -1.49 V and 46 mu A/cm(2), respectively. The coating prepared at 0.046 A/cm(2) exhibited the lowest i(corr) value of 7.79 x 10(-10) A/cm(2) and highest polarization resistance (41.6 M Omega cm(2)) attesting to the better corrosion resistance of the coating compared to other samples. EIS results also indicated almost similar corrosion behavior for the MAO coatings. Mott-Schottky analysis showed n-type and p-type semiconductor behavior for the oxide layer present on the bare magnesium alloy and MAO coatings respectively. (C) 2016 Published by Elsevier B.V.

Lateral field emitters fabricated using carbon nanotubes

We report on the fabrication of lateral emitters using carbon nanotubes (CNTs) grown via plasma enhanced chemical vapour deposition (PECVD). Carbon nanotubes are dispersed randomly onto a substrate, mapped, contacted with metal, and by etching the substrate, a suspended lateral emitter structure is formed. Field emission measurements from the lateral emitters show a turn-on voltage as low as 12 V. The emission characteristics showed good fits to the Fowler-Nordheim (FN) theory indicating that conventional field emission was indeed observed from these devices. © 2003 Elsevier Science B.V. All rights reserved.

Fabrication of carbon nanotube lateral field emitters

We report on the fabrication and field emission of carbon nanotube lateral field emitters. Due to its high aspect ratio and mechanical strength, we use vertically aligned multi-wall carbon nanotubes prepared by plasma-enhanced chemical vapour deposition as cathodes, which makes the fabrication of cantilever type lateral field emitters possible. The emission characteristics show that the field emission initiates at 11-17 V. The device has high geometrical enhancement factors (9.3 × 106 cm-1) compared to standard Spindt tips, which may be due to increased field concentration at the nanotube tip and the close proximity of the anode (<1 μm). The relative ease of fabrication compared to vertical field emitters and enhanced field emission characteristics observed makes the carbon nanotube lateral field emitter a good candidate for future integrated nano-electronic devices.

超分辨远场生物荧光成像——突破光学衍射极限

长期以来,远场光学荧光显微镜凭借其非接触、无损伤、可探测样品内部等优点,一直是生命科学中最常用的观测工具。但由于衍射极限的存在,使传统的宽场光学显微镜横向和纵向的分辨率分别仅约为230 nm和1000 nm。为了揭示细胞内分子尺度的动态和结构特征,提高光学显微镜分辨率成为生命科学发展的迫切要求,在远场荧光显微镜的基础上,科学家们已经发展出许多实用的提高分辨率甚至超越分辨率极限的成像技术。例如,采用横向结构光照明提高横向分辨率到约100 nm,利用纵向驻波干涉效应将纵向分辨率提高5~10倍。然而,直到在光学荧光显微镜中引入非线性效应后,衍射极限才被真正突破,如受激荧光损耗显微镜利用非线性效应实现了30~50 nm的三维分辨率。另外应用荧光分子之间能量转移共振原理以及单荧光分子定位技术也可以突破衍射极限,甚至可以将分子定位精度提高到几个纳米的量级。

Electron emission from arrays of carbon nanotubes/fibres

The overall aim of this work is to produce arrays of field emitting microguns, based on carbon nanotubes, which can be utilised in the manufacture of large area field emitting displays, parallel e-beam lithography systems and electron sources for high frequency amplifiers. This paper will describe the work carried out to produce patterned arrays of aligned multiwall carbon nanotubes (MWCNTs) using a dc plasma technique and a Ni catalyst. We will discuss how the density of the carbon nanotube/fibres can be varied by reducing the deposition yield through nickel interaction with a diffusion layer or by direct lithographic patterning of the Ni catalyst to precisely define the position of each nanotube/fibre. Details of the field emission behaviour of the different arrays of MWCNTS will also be presented. © 2002 Published by Elsevier Science B.V.

Investigating carbon materials for use as the electron emission source in a parallel electron-beam lithography system

A microelectronic parallel electron-beam lithography system using an array of field emitting microguns is currently being developed. This paper investigates the suitability of various carbon based materials for the electron source in this device, namely tetrahedrally bonded amorphous carbon (ta-C), nanoclustered carbon and carbon nanotubes. Ta-C was most easily integrated into a gated field emitter structure and various methods, such as plasma and heavy ion irradiation, were used to induce emission sites in the ta-C. However, the creation of such emission sites at desired locations appeared to be difficult/random in nature and thus the material was unsuitable for this application. In contrast, nanoclustered carbon material readily field emits with a high site density but the by-products from the deposition process create integration issues when using the material in a microelectronic gated structure. Carbon nanotubes are currently the most promising candidate for use as the emission source. We have developed a high yield and clean (amorphous carbon by-product free) PECVD process to deposit single free standing nanotubes at desired locations with exceptional uniformity in terms of nanotube height and diameter. Field emission from an array of nanotubes was also obtained. © 2001 Elsevier Science B.V.

Stabilization of carbon nanotube field emitters

Carbon nanotubes (CNTs) have been determined to be field emitters of high quality, but CNTs produced by chemical vapour deposition can produce emission currents with high instability and noise. This work finds that adsorbates and amorphous carbon deposited during the growth process are the primary contributors to field emission instability, and shows that burning off the amorphous carbon in air at 450 °C removes the amorphous carbon, resulting in stabilities of better than 3 per cent over 1 h. This work removes one of the major barriers to the use of CNTs in field emission devices.

Angular distribution of field emitted electrons from vertically aligned carbon nanotube arrays

Angular field emission (FE) properties of vertically aligned carbon nanotube arrays have been measured on samples grown by plasma enhanced chemical vapor deposition and characterized by scanning electron microscope and I-V measurements. These properties determine the angular divergence of electron beams, a crucial parameter in order to obtain high brilliance FE based cathodes. From angular distributions of the electron beam transmitted through extraction grids of different mesh size and by using ray-tracing simulations, the maximum emission angle from carbon nanotube tips has been determined to be about ± 30 around the tube main axis. © 2012 American Institute of Physics.

Ballasted & electrically steerable carbon nanotube field emitters

Here we present our on-going efforts toward the development of stable ballasted carbon nanotube-based field emitters employing hydrothermally synthesized zinc oxide nanowires and thin film silicon-on-insulator substrates. The semiconducting channel in each controllably limits the emission current thereby preventing detrimental burn-out of individual emitters that occurs due to unavoidable statistical variability in emitter characteristics, particularly in their length. Fabrication details and emitter characterization are discussed in addition to their field emission performance. The development of a beam steerable triode electron emitter formed from hexagonal carbon nanotube arrays with central focusing nanotube electrodes, is also described. Numerical ab-initio simulations are presented to account for the empirical emission characteristics. Our engineered ballasted emitters have shown some of the lowest reported lifetime variations (< 0.7%) with on-times of < 1 ms, making them ideally-suited for next-generation displays, environmental lighting and portable x-rays sources. © 2012 SPIE.

Novel nanostructured carbon nanotube electron sources

In this chapter, we present a review of our continuing efforts toward the development of discrete, low-dimensional nanostructured carbon-based electron emitters. Carbon nanotubes and nanofibers, herein referred to simply as CNTs, are one-dimensional carbon allotropes formed from cylindrically rolled and nested graphene sheets, have diameters between 1 and 500 nm and lengths of up to several millimeters, and are perfect candidates for field emission (FE) applications. By virtue of their extremely strong sp2 C-C bonding, intrinsic to the graphene hexagonal lattice, CNTs have demonstrated impressive chemical inertness, unprecedented thermal stabilities, significant resistance to electromigration, and exceptionally high axial current carrying capacities, even at elevated temperatures. These near ideal cold cathode electron emitters have incredibly high electric field enhancing aspect ratios combined with virtual point sources of the order of a few nanometers in size. The correct integration and judicious development of suitable FE platforms based on these extraordinary molecules is critical and will ultimately enable enhanced technologies. This chapter will review some of the more recent platforms, devices and structures developed by our group, as well as our contributions towards the development of industry-scalable technologies for ultra-high-resolution electron microscopy, portable x-ray sources, and flexible environmental lighting technologies. © 2012 by Pan Stanford Publishing Pte. Ltd. All rights reserved.

Excellent oxidation endurance of boron nitride nanotube field electron emitters

Boron nitride nanotubes (BNNTs) are considered as a promising cold electron emission material owing to their negative electron affinity. BNNT field emitters show excellent oxidation endurance after high temperature thermal annealing of 600 °C in air ambient. There is no damage to the BNNTs after thermal annealing at a temperature of 600 °C and also no degradation of field emission properties. The thermally annealed BNNTs exhibit a high maximum emission current density of 8.39mA/cm2 and show very robust emission stability. The BNNTs can be a promising emitter material for field emission devices under harsh oxygen environments. © 2014 AIP Publishing LLC.

Effects of In surfactant on the crystalline and photoluminescence properties of GaN nanowiires

GaN nanowires have been grown with and without In as an additional source. The effects of In surfactant on the crystal quality and photoluminescence property of GaN nanowires are reported for the first time. X-ray diffraction, field emission scanning electron microscopy, high-resolution transmission electron microscopy, energy-dispersive x-ray spectroscopy, and photoluminescence measurements are employed to analyse the products. The results show that introducing a certain amount of In surfactant during the growth process can improve the crystal quality of the GaN nanowires, and enhance the photolurainescence of them. In addition, the as-prepared GaN nanowires have the advantage of being easy to be separated, which will benefit the subsequent nanodevice fabrication.

Synthesis of GaN nanowires and nano-pyramids in a two-hot-boat chemical vapor deposition system via an in-doping technique

A two-hot-boat chemical vapor deposition system was modified from a thermal evaporation equipment. This system has the advantage of high vacuum, rapid heating rate and temperature separately controlled boats for the source and samples. These are in favor of synthesizing compound semiconducting nano-materials. By the system, we have synthesized high-quality wurtzite single crystal GaN nanowires and nanotip triangle pyramids via an in-situ doping indium surfactant technique on Si and 3C-SiC epilayer/Si substrates. The products were analyzed by x-ray diffraction, field emission scanning electron microscopy, highresolution transmission electron microscopy, energy- dispersive x-ray spectroscopy, and photoluminescence measurements. The GaN nanotip triangle pyramids, synthesized with this novel method, have potential application in electronic/ photonic devices for field-emission and laser.

Synthesis of GaN nanotip triangle pyramids on 3C-SiC epilayer/Si substrates via an in situ In-doping technique

GaN nanotip triangle pyramids were synthesized on 3C-SiC epilayer via an isoelectronic In-doping technique. The synthesis was carried out in a specially designed two-hot-boat chemical vapor deposition system. In (99.999%) and molten Ga (99.99%) with a mass ratio of about 1:4 were used as the source, and pieces of Si (111) wafer covered with 400-500 nm 3C-SiC epilayer were used as the substrates. The products were analyzed by x-ray diffraction, field emission scanning electron microscopy, high-resolution transmission electron microscopy, selected area electron diffraction, Raman spectroscopy, and photoluminescence measurements. Our results show that the as-synthesized GaN pyramids are perfect single crystal with wurtzite structure, which may have potential applications in electronic/photonic devices.

Effect of substrate temperature on the growth and photoluminescence properties of vertically aligned ZnO nanostructures

Vertically well-aligned ZnO nanoridge, nanorod, nanorod-nanowall junction, and nanotip arrays have been successfully synthesized on Si (100) substrates using a pulsed laser deposition prepared ZnO film as seed layer by thermal evaporation method. Experimental results illustrated that the growth of different morphologies of ZnO nanostructures was strongly dependent upon substrate temperature. X-ray diffraction (XRD) and transmission electron microscopy (TEM) studies showed that the ZnO nanostructures were single crystals with a wurtzite structure. Compared with those of the other nanostructures, the photoluminescence (PL) spectrum of nanorod-nanowall junctions showed the largest intensity ratio of ultraviolet (UV) to yellow-green emission and the smallest full-width at half-maximum (FWHM) of the UV peak, reflecting the high optical quality and nearly defect free of crystal structure. The vertical alignment of the nanowire array on the substrate is attributed to the epitaxial growth of the nanostructures from the ZnO buffer layer. The growth mechanism was also discussed in detail. (c) 2006 Elsevier B.V. All rights reserved.