Distribution of ionic charge carriers and migration barriers in binary alkali silicate glasses

Likely spatial distributions of network-modifying (and mobile) cations in (oxide) glasses are discussed here. At very low modifier concentrations, the ions form dipoles with non-bridging oxygen centres while, at higher levels of modification, the cations tend to order as a result of Coulombic interactions. Activation energies for cation migration are calculated, assuming that the ions occupy (face-sharing) octahedral sites. It is found that conductivity activation energy decreases markedly with increasing modifier content, in agreement with experiment.

Preparation, Structural, and Electrical Studies of Polyaniline/ZnFe2O4 Nanocomposites

Polyaniline/ZnFe2O4 nanocomposites were synthesized by a simple and inexpensive one-step in situ polymerization method in the presence of ZnFe2O4 nanoparticles. The structural, morphological, and electrical properties of the samples were characterized by wide angle X-ray diffraction (WAXD), Fourier transform infrared (FTIR) spectroscopy, scanning electron microscopy (SEM), and thermogravimetric analysis (TGA). WAXD and SEM revealed the formation of polyaniline/ZnFe2O4 nanocomposites. Infrared spectroscopy indicated that there was some interaction between the ZnFe2O4 nanoparticles and polyaniline. The dc electrical conductivity measurements were carried in the temperature range of 80 to 300 K. With increase in the doping concentration of ZnFe2O4, the conductivity of the nanocomposites found to be decreasing from 5.15 to 0.92 Scm(-1) and the temperature dependent resistivity follows ln rho(T) similar to T-1/2 behavior. The nanocomposites (80 wt % of ZnFe2O4) show a more negative magnetoresistance compared with that of pure polyaniline (PANI). These results suggest that the interaction between the polymer matrix PANI and zinc nanoparticles take place in these nanocomposites. (C) 2011 Wiley Periodicals, Inc. J Appl Polym Sci 120: 2856-2862, 2011

The role of additives in a complex lithium silicate glass-ceramic

Several glass-ceramic compositions based on lithium silicates have been examined using thermal expansivity, X-ray diffraction, electrical conductivity, electron microscopy and solid state NMR studies. Role of P2O5 in nucleation and of Al2O3 in smoothening expansion behaviour have been particularly highlighted. Magic angle spinning NMR has been used to ascertain presence of Al in tetrahedral positions in the glassy phase

Nanocomposites by rapid solidification route

Nanometric aggregates of solids can be classified into two types, nanograined or nanophased materials and nanocomposites. In the present paper after a brief review including the relation between size and boundary fraction, the basic principles that can be utilized to synthesize these materials from liquid route has been discussed. We shall present examples to show that with proper choice of systems and conditions it is possible to obtain nanocomposites in systems showing clustering tendencies in liquid as well as the systems exhibiting ordering tendencies leading to compound formation

Potential-distance relationships of clay-water systems considering the Stern theory

This paper deals with the use of Stem theory as applied to a clay-water electrolyte system, which is more realistic to understand the force system at micro level man the Gouy-Chapman theory. The influence of the Stern layer on potential-distance relationship has been presented quantitatively for certain specified clay-water systems and the results are compared with the Gouy-Chapman model. A detailed parametric study concerning the number of adsorption spots on the clay platelet, the thickness of the Stern layer, specific adsorption potential and the value of dielectric constant of the pore fluid in the Stern layer, was carried out. This study investigates that the potential obtained at any distance using the Stern theory is higher than that obtained by the Gouy-Chapman theory. The hydrated size of the ion is found to have a significant influence on the potential-distance relationship for a given clay, pore fluid characteristics and valence of the exchangeable ion.

Enhancing the mesoporosity of pillared clay catalyst - a study of pillar aggregates and deactivation in alkylation reaction

A sample of montmorillonite was pillared with aluminium polyoxycations in presence of different amounts of tween-80, a nonionic surfactant, ranging from 0.01 to 0.20 mmol/meq of clay. The amount of aluminium sorbed was found to vary with the amount of surfactant added during pillaring. Vapour phase catalytic activity of the samples for alkylation of toluene with methanol in a fixed bed down flow reactor showed that the rate of deactivation, in general, increased with decrease in the pillar density. The samples treated with 0.06 to 0.08 mmol/meq of surfactant showed the lowest deactivation and also an enhancement in the mesopores which did not change on calcining to 540°C. Suppression of deactivation is attributed to the distribution of pillars by the surfactant in such a way as to decrease the coke formation.

Correlated conformation and charge transport in multiwall carbon nanotube-conducting polymer nanocomposites

The strikingly different charge transport behaviours in nanocomposites of multiwall carbon nanotubes (MWNTs) and conducting polymer polyethylenedioxythiophene-polystyrene-sulfonic-acid (PEDOT-PSS) at low temperatures are explained by probing their conformational properties using small-angle x-ray scattering (SAXS). The SAXS studies indicate the assembly of elongated PEDOT-PSS globules on the walls of nanotubes, coating them partially, thereby limiting the interaction between the nanotubes in the polymer matrix. This results in a charge transport governed mainly by small polarons in the conducting polymer despite the presence of metallic MWNTs. At T > 4 K, hopping of the charge carriers following one-dimensional variable range hopping is evident which also gives rise to a positive magnetoresistance (MR) with an enhanced localization length (similar to 5 nm) due to the presence of MWNTs. However, at T < 4 K, the observation of an unconventional positive temperature coefficient of resistivity is attributed to small polaron tunnelling. The exceptionally large negative MR observed in this temperature regime is conjectured to be due to the presence of quasi-1D MWNTs that can aid in lowering the tunnelling barrier across the nanotube-polymer boundary resulting in large delocalization.

Tracking and erosion resistance of silicone rubber nanocomposites under positive and negative dc voltages

ASTM D2303 standard provides a method for evaluating the tracking and erosion resistance of polymeric insulators under ac voltages. In this paper, the above method has been extended for evaluating the performance of the insulators under dc stresses. Tests were conducted on polymeric silicone rubber (SR) insulators under positive and negative dc stresses. Micron sized Alumina trihydrate (uATH) and nano sized Alumina (nALU) were used as fillers in SR matrix to improve the resistance to tracking and erosion. Results suggest that SR composites perform better under negative dc than under positive dc voltages. Eroded mass and leakage current data support the above result. Samples with low concentration of nano alumina fillers performed on par with the samples with large loadings of uATH.

AC breakdown characteristics of epoxy alumina nanocomposites

Experiments were conducted to measure the ac breakdown strength of 0.5 mm, thick epoxy alumina nanocomposites with different filler concentrations of 0.1, 1 and 5wt%. The experiments were performed as per the ASTM D 149 standard. It was observed that the ac breakdown strength was marginally lower up to 1wt% filler concentration and then increased at 5wt% filler concentration as compared to the unfilled epoxy. The Weibull shape parameter (β) increased with the addition of nanoparticles to epoxy. The dependence of thickness on the ac breakdown strength was also analyzed by conducting experiments on 1mm and 3mm thick unfilled epoxy and epoxy alumina nanocomposites of 1wt% and 5wt% filler concentrations. The DSC analysis was done to understand the material properties at the filler resin interface in order to study the effect of the filler concentration and thereby the influence of the interface on the ac breakdown strength of epoxy nanocomposites.

Role of clay content and moisture on characteristics of cement stabilised rammed earth

Rammed earth is an energy efficient and low carbon emission alternative for load bearing walls. This paper attempts to examine the influence of clay content and moisture content on the compressive strength of cement stabilised rammed earth (CSRE) through experimental investigations. Compressive strength of CSRE prisms was monitored both in dry and wet (saturated) conditions. Major conclusions of the study are:(a) Optimum clay content for maximum compressive strength is about 16%, (b) the strength of CSRE is sensitive to the moisture content at the time of testing, (c) Strength in saturated condition is less than half of the dry strength and (d) Water absorption (saturated water content) increases as the clay content of the soil mix increases and it is in the range of 12 to 16% for the CRSE prisms with 8% cement.

Densification and microstructure development in spark plasma sintered WC–6 wt% ZrO2 nanocomposites

In this paper, we report the results of a transmission electron microscopy investigation on WC–6 wt% ZrO2nanocomposite, spark plasma sintered at 1300 °C, for varying times of up to 20 min. The primary aim of this work was to understand the evolution of microstructure during such a sintering process. The investigation revealed the presence of nanocrystalline ZrO2particles (30–50 nm) entrapped within submicron WC grains. In addition, relatively coarser ZrO2(60–100 nm) particles were observed to be either attached to WC grain boundaries or located at WC triple grain junctions. The evidence of the presence of a small amount of W2C, supposed to have been formed due to sintering reaction between WC and ZrO2, is presented here. Detailed structural investigation indicated that ZrO2in the spark plasma sintered nanocomposite adopted an orthorhombic crystal structure, and the possible reasons for o-ZrO2formation are explained. The increase in kinetics of densification due to the addition of ZrO2is believed to be caused by the enhanced diffusion kinetics in the presence of nonstoichiometric nanocrystalline ZrO2.