Electrical and optical characterization of conducting polymers by THz time-domain spectroscopy

The absorption and index of refraction of polypyrrole (PPy) and poly-3-methylthiophene (PMeT), from low frequencies up to 4 THz, have been measured by tera-Herz (THz) time-domain spectroscopy. The complex conductance was obtained over this range of frequency. Highly conducting metallic samples follow the Drude model, whereas less conducting ones fit the localization-modified Drude model. The carrier scattering time and mobility in conducting polymers can be directly determined from these measurements.

Studies on thin film materials on acrylics for optical applications

Deposition of durable thin film coatings by vacuum evaporation on acrylic substrates for optical applications is a challenging job. Films crack upon deposition due to internal stresses and leads to performance degradation. In this investigation, we report the preparation and characterization of single and multi-layer films of TiO2, CeO2, Substance2 (E Merck, Germany), Al2O3, SiO2 and MgF2 by electron beam evaporation on both glass and PMMA substrates. Optical micrographs taken on single layer films deposited on PMMA substrates did not reveal any cracks. Cracks in films were observed on PMMA substrates when the substrate temperature exceeded 80degreesC. Antireflection coatings of 3 and 4 layers have been deposited and characterized. Antireflection coatings made on PMMA substrate using Substance2 (H2) and SiO2 combination showed very fine cracks when observed under microscope. Optical performance of the coatings has been explained with the help of optical micrographs.

The effect of host glass on optical absorption and fluorescence of Nd3+ in xNa(2)O-(30-x)K2O-70B(2)O(3) glasses

The effect of host glass composition on the optical absorption and fluorescence spectra of Nd3+ has been studied in mixed alkali borate glasses of the type xNa(2)O-(30-x)K2O-69.5B(2)O(3)-0.5Nd(2)O(3) (X = 5,10,15,20 and 25). Various spectroscopic parameters such as Racah (E-1, E-2 and E-3), spin-orbit (xi(4f)) and configuration interaction (alpha, beta) parameters have been calculated. The Judd-Ofelt intensity parameters (Omega(lambda)) have been calculated and the radiative transition probabilities (A(rad)), radiative lifetimes (tau(r)), branching ratios (beta) and integrated absorption cross sections (Sigma) have been obtained for certain excited states of the Nd3+, ion and are discussed with respect to x. From the fluorescence spectra, the effective fluorescence line widths (Deltalambda(eff)) and stimulated emission cross sections (sigma(p)) have been obtained for the three transitions F-4(3/2) --> I-4(9/2), F-4(3/2) --> I-4(11/2) and F-4(3/2) --> I-4(13/2) of Nd3+. The stimulated emission cross section (sigma(p)) values are found to be in the range (2.0-4.8) x 10(-2)0 cm(2) and they are large enough to indicate that the mixed alkali borate glasses could be potential laser host materials.

Optical conductivity of perovskite manganites

We calculate the optical conductivity sigma(omega) for doped rare-earth manganites based on the recently proposed microscopic ``two fluid'' l-b model. We study the temperature dependence of sigma(omega) for La(0.825)Sr(0.175)MnO(3), which has a metallic ground state. At low temperatures, the calculated sigma(omega) shows a ``two-peak'' structure consisting of a far-infrared coherent Drude peak and a broad mid-infrared ``polaron'' peak, as observed in experiments. Upon heating, the Drude peak rapidly loses spectral weight, and sigma(omega) crosses over to having just a single broad mid-infrared peak. The temperature dependence of the mid-infrared peak and the spectral weight transfer between the two peaks are also in agreement with experimental findings. We also study the doping dependence of sigma(omega) for the same compound. The integrated spectral weight under the Drude peak increases rapidly as the doping level is increased from an underdoped, insulating state (x = 0.1) to a highly doped, metallic state (x = 0.3), again in agreement with trends seen experimentally.

Studies on the deposition and characterization of silicon oxide films for optical coating applications

Silicon oxide films were deposited by reactive evaporation of SiO. Parameters such as oxygen partial pressure and substrate temperature were varied to get variable and graded index films. Films with a refractive index in the range 1.718 to 1.465 at 550 nm have been successfully deposited. Films deposited using ionized oxygen has the refractive index 1.465 at 550 nm and good UV transmittance like bulk fused quartz. Preparation of graded index films was also investigated by changing the oxygen partial pressure during deposition. A two layer antireflection coating at 1064nm has been designed using both homogeneous and inhomogeneous films and studied their characteristics.