Pulsed Nd:YAG laser welding of Ni-alloy Hastelloy C-276 foils

In this study a pulsed Nd:YAG laser was used to join Hastelloy C-276 thin foil with 100 microns thickness. Pulse energy was varied from 1.0 to 2.25 J at small increments of 0.25 J with a 4 ms pulse duration. The macro and microstructures of the welds were analyzed by optical and electronic microscopy, tensile shear test and microhardness. Sound laser welds without discontinuities were obtained with 1.5 J pulse energy. Results indicate that using a precise control of the pulse energy, and so a control of the dilution rate, it is possible to weld Hastelloy C-276 thin foil by pulsed Nd: YAG laser. (C) 2012 Published by Elsevier B. V. Selection and/or review under responsibility of Bayerisches Laserzentrum GmbH

Preparation and Characterization of Ti-15Mo Alloy used as Biomaterial

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Zuspan's Scheme Versus an Alternative Magnesium Sulfate Scheme: Randomized Clinical Trial of Magnesium Serum Concentrations

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Stability of cp-Ti and Ti-6Al-4V alloy for dental implants as a function of saliva pH - an electrochemical study

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Biomimetic calcium phosphate coating on Ti-7.5Mo alloy for dental application

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effects of aluminum-copper alloy filtration on photon spectra, air kerma rate and image contrast

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Effect of Severe Dietary Magnesium Deficiency on Systemic Bone Density and Removal Torque of Osseointegrated Implants

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effects of magnesium intake deficiency on bone metabolism and bone tissue around osseointegrated implants

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Shear bond strength of aesthetic materials bonded to Ni-Cr alloy

Objectives. This study was undertaken to evaluate the shear bond strength of four materials used as aesthetic material bonded to Ni-Cr alloy.Methods. Sixty-eight alloy discs were prepared and divided equally into four groups, and received four treatments for veneering: conventional feldspathic porcelain (Noritake EX-3) and three light-cured prosthodontic composite resins (Artglass, Solidex and Targis). The aesthetic materials were applied after metal structure conditioning in accordance with the manufacturers' recommendations. The specimens were stored in distilled water at 37 degreesC for 7 days. A universal testing machine was used to measure the shear bond strength of the specimens at a cross head speed of 0.5 mm/min. Fractured specimens were examined by using both optical and scanning electron microscope.Results. The analysis of variance and Tukey's test showed that the strongest mean shear bond was obtained with Noritake EX-3 (mean shear bond strength 42.90 +/- 7.82 MPa). For composites, the highest mean shear bond strength was observed for Targis (12.30 +/- 1.57 MPa); followed by Solidex (11.94 +/- 1.04 MPa) and Artglass (10.04 +/- 0.75 MPa). Optical analysis of the fractured surf aces indicated that for Targis and Noritake EX-3 all failures were a mixture of both cohesive and adhesive patterns. As for Artglass and Solidex, the fractures were mainly adhesive in nature.Conclusions. The Solidex system was equivalent to the Targis system in bond strength and exhibited greater strength than the Artglass system. The porcelain fused-to-metal showed considerably higher shear bond strength than the three metal-resin bonding techniques. (C) 2003 Elsevier B.V. Ltd. Ali rights reserved.

EFFECT of DIFFERENT AIRBORNE-PARTICLE ABRASION/BONDING AGENT COMBINATIONS on THE BOND STRENGTH of A RESIN CEMENT TO A BASE METAL ALLOY

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Adhesive Bonding of Resin Composite to Various Ni-Cr Alloy Surfaces Using Different Metal Conditioners and a Surface Modification System

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)