Synthesis and Physical-Chemical characterization of Metallic Nanoparticles

The stabilization of nanoparticles against their irreversible particle aggregation and oxidation reactions. is a requirement for further advancement in nanoparticle science and technology. For this reason the research aim on this topic focuses on the synthesis of various metal nanoparticles protected with monolayers containing different reactive head groups and functional tail groups. In this work cuprous bromide nanocrystals haave been synthetized with a diameter of about 20 nanometers according to a new sybthetic method adding dropwise ascorbic acid to a water solution of lithium bromide and cupric chloride under continuous stirring and nitrogen flux. Butane thiolate Cu protected nanoparticles have been synthetized according to three different syntesys methods. Their morphologies appear related to the physicochemical conditions during the synthesis and to the dispersing medium used to prepare the sample. Synthesis method II allows to obtain stable nanoparticles of 1-2 nm in size both isolated and forming clusters. Nanoparticle cluster formation was enhanced as water was used as dispersing medium probably due to the idrophobic nature of the butanethiolate layers coating the nanoparticle surface. Synthesis methods I and III lead to large unstable spherical nanoparticles with size ranging between 20 to 50 nm. These nanoparticles appeared in the TEM micrograph with the same morphology independently on the dispersing medium used in the sample preparation. The stability and dimensions of the copper nanoparticles appear inversely related. Using the same methods above described for the butanethiolate protected copper nanoparticles 4-methylbenzenethiol protected copper nanoparticles have been prepared. Diffractometric and spectroscopic data reveal that decomposition processes didn’t occur in both the 4-methylbenzenethiol copper protected nanoparticles precipitates from formic acid and from water in a period of time six month long. Se anticarcinogenic effects by multiple mechanisms have been extensively investigated and documented and Se is defined a genuine nutritional cancer-protecting element and a significant protective effect of Se against major forms of cancer. Furthermore phloroglucinol was found to possess cytoprotective effects against oxidative stress, thanks to reactive oxygen species (ROS) which are associated with cells and tissue damages and are the contributing factors for inflammation, aging, cancer, arteriosclerosis, hypertension and diabetes. The goal of our work has been to set up a new method to synthesize in mild conditions amorphous Se nanopaticles surface capped with phloroglucinol, which is used during synthesis as reducing agent to obtain stable Se nanoparticles in ethanol, performing the synergies offered by the specific anticarcinogenic properties of Se and the antioxiding ones of phloroalucinol. We have synthesized selenium nanoparticles protected by phenolic molecules chemically bonded to their surface. The phenol molecules coating the nanoparticles surfaces form low ordered arrays as can be seen from the wider shape of the absorptions in the FT-IR spectrum with respect to those appearing in that of crystalline phenol. On the other hand, metallic nanoparticles with unique optical properties, facile surface chemistry and appropriate size scale are generating much enthusiasm in nanomedicine. In fact Au nanoparticles has immense potential for both cancer diagnosis and therapy. Especially Au nanoparticles efficiently convert the strongly adsorbed light into localized heat, which can be exploited for the selective laser photothermal therapy of cancer. According to the about, metal nanoparticles-HA nanocrystals composites should have tremendous potential in novel methods for therapy of cancer. 11 mercaptoundecanoic surface protected Au4Ag1 nanoparticles adsorbed on nanometric apathyte crystals we have successfully prepared like an anticancer nanoparticles deliver system utilizing biomimetic hydroxyapatyte nanocrystals as deliver agents. Furthermore natural chrysotile, formed by densely packed bundles of multiwalled hollow nanotubes, is a mineral very suitable for nanowires preparation when their inner nanometer-sized cavity is filled with a proper material. Bundles of chrysotile nanotubes can then behave as host systems, where their large interchannel separation is actually expected to prevent the interaction between individual guest metallic nanoparticles and act as a confining barrier. Chrysotile nanotubes have been filled with molten metals such as Hg, Pb, Sn, semimetals, Bi, Te, Se, and with semiconductor materials such as InSb, CdSe, GaAs, and InP using both high-pressure techniques and metal-organic chemical vapor deposition. Under hydrothermal conditions chrysotile nanocrystals have been synthesized as a single phase and can be utilized as a very suitable for nanowires preparation filling their inner nanometer-sized cavity with metallic nanoparticles. In this research work we have synthesized and characterized Stoichiometric synthetic chrysotile nanotubes have been partially filled with bi and monometallic highly monodispersed nanoparticles with diameters ranging from 1,7 to 5,5 nm depending on the core composition (Au, Au4Ag1, Au1Ag4, Ag). In the case of 4 methylbenzenethiol protected silver nanoparticles, the filling was carried out by convection and capillarity effect at room temperature and pressure using a suitable organic solvent. We have obtained new interesting nanowires constituted of metallic nanoparticles filled in inorganic nanotubes with a inner cavity of 7 nm and an isolating wall with a thick ranging from 7 to 21 nm.

Magnetic tunneling junctions with the Heusler compound Co 2 Cr 0.6 Fe 0.4 Al

Materialen mit sehr hoher Spinpolarisation werden für Anwendungen im Bereich der Spin-Elektronik benötigt. Deshalb werden große Forschungsanstrengungen zur Untersuchung der Eigenschaften von Verbindungen mit potentiell halbmetallischem Charakter, d. h.mit 100% Spinpolarisation, unternommen. In halbmetallischen Verbindungen, erwartet man eine Lücke in der Zustandsdichte an der Fermi Energie für Ladungsträger einer Spinrichtung, wahrend die Ladungsträger mit der anderen Spinrichtung sich metallisch verhalten. Eine Konsequenz davon ist, dass ein Strom, der durch solche Verbindung fließt, voll spinpolarisiert ist. Die hohe Curie-Temperatur Tc (800 K) und der theoretisch vorhergesagte halbmetallische Charakter machen Co2Cr0.6Fe0.4Al (CCFA) zu einem guten Kandidaten für Spintronik-Anwendungen wie magnetische Tunnelkontakte (MTJs = Magnetic Tunneling Junctions). In dieser Arbeit werden die Ergebnisse der Untersuchung der elektronischen und strukturellen Eigenschaften von dünnen CCFA Schichten dargestellt. Diese Schichten wurden in MTJs integriert und der Tunnel-Magnetowiderstands-Effekt untersucht. Hauptziele waren die Messung der Spinpolarisation und Untersuchungen der elektronischen Struktur von CCFA. Der Einfluss verschiedener Depositionsparameter auf die Eigenschaften der Schichten, speziell auf der Oberflächenordnung und damit letztlich auf den Tunnel-Magnetowiderstand (TMR), wurde bestimmt. Epitaktische d¨unne CCFA Schichten mit zwei verschiedenen Wachstumsrichtungen wurden auf verschiedene Substrate und Pufferschichten deponiert. Ein Temperverfahren wurde eingesetzt um die strukturelle Eigenschaften der dünnen Schichten zu verbessern. Für die MTJs wurde Al2O3 als Barrierenmaterial verwendet und Co als Gegenelektrode gewählt. Die Mehrschicht-Systeme wurden in Mesa-Geometrie mit lithographischen Methoden strukturiert. Eine maximal Jullière Spinpolarisation von 54% wurde an Tunnelkontakte mit epitaktischen CCFA Schichten gemessen. Ein starker Einfluss der Tempernbedingungen auf dem TMR wurde festgestellt. Eine Erhörung des TMR wurde mit einer Verbesserung der Oberflächenordung der CCFA Schichten korreliert. Spektroskopische Messungen wurden an den MTJs durchgeführt. Diesen Messungen liefern Hinweise auf inelastische Elektron-Magnon und Elektron-Phonon Stossprozesse an den Grenzflächen. Einige der beobachteten Strukturen konnten mit der berechneten elektronischen Struktur von CCFA korreliert worden.

Fatigue Crack Propagation in Pressurized metallic Fuselages

On the basis of well-known literature, an analytical tool named LEAF (Linear Elastic Analysis of Fracture) was developed to predict the Damage Tolerance (DT) proprieties of aeronautical stiffened panels. The tool is based on the linear elastic fracture mechanics and the displacement compatibility method. By means of LEAF, an extensive parametric analysis of stiffened panels, representative of typical aeronautical constructions, was performed to provide meaningful design guidelines. The effects of riveted, integral and adhesively bonded stringers on the fatigue crack propagation performances of stiffened panels were investigated, as well as the crack retarder contribution using metallic straps (named doublers) bonded in the middle of the stringers bays. The effect of both perfectly bonded and partially debonded doublers was investigated as well. Adhesively bonded stiffeners showed the best DT properties in comparison with riveted and integral ones. A great reduction of the skin crack growth propagation rate can be achieved with the adoption of additional doublers bonded between the stringers.

Numerische und analytische Untersuchungen stark korrelierter fermionischer Mehrbandsysteme

In dieser Arbeit werden vier unterschiedliche, stark korrelierte, fermionische Mehrbandsysteme untersucht. Es handelt sich dabei um ein Mehrstörstellen-Anderson-Modell, zwei Hubbard-Modelle sowie ein Mehrbandsystem, wie es sich aus einer ab initio-Beschreibung für ein korreliertes Halbmetall ergibt.rnrnDie Betrachtung des Mehrstörstellen-Anderson-Modells konzentriert sich auf die Untersuchung des Einflusses der Austauschwechselwirkung und der nicht-lokalen Korrelationen zwischen zwei Störstellen in einem einfach-kubischen Gitter. Das zentrale Resultat ist die Abstandsabhängigkeit der Korrelationen der Störstellenelektronen, welche stark von der Gitterdimension und der relativen Position der Störstellen abhängen. Bemerkenswert ist hier die lange Reichweite der Korrelationen in der Diagonalrichtung des Gitters. Außerdem ergibt sich, dass eine antiferromagnetische Austauschwechselwirkung ein Singulett zwischen den Störstellenelektronen gegenüber den Kondo-Singuletts der einzelnen Störstellen favorisiert und so den Kondo-Effekt der einzelnen Störstellen behindert.rnrnEin Zweiband-Hubbard-Modell, das Jz-Modell, wird im Hinblick auf seine Mott-Phasen in Abhängigkeit von Dotierung und Kristallfeldaufspaltung auf dem Bethe-Gitter untersucht. Die Entartung der Bänder ist durch eine unterschiedliche Bandbreite aufgehoben. Wichtigstes Ergebnis sind die Phasendiagramme in Bezug auf Wechselwirkung, Gesamtfüllung und Kristallfeldparameter. Im Vergleich zu Einbandmodellen kommen im Jz-Modell sogenannte orbital-selektive Mott-Phasen hinzu, die, abhängig von Wechselwirkung, Gesamtfüllung und Kristallfeldparameter, einerseits metallischen und andererseits isolierenden Charakter haben. Ein neuer Aspekt ergibt sich durch den Kristallfeldparameter, der die ionischen Einteilchenniveaus relativ zueinander verschiebt, und für bestimmte Werte eine orbital-selektive Mott-Phase des breiten Bands ermöglicht. Im Vergleich mit analytischen Näherungslösungen und Einbandmodellen lassen sich generische Vielteilchen- und Korrelationseffekte von typischen Mehrband- und Einteilcheneffekten differenzieren.rnrnDas zweite untersuchte Hubbard-Modell beschreibt eine magneto-optische Falle mit einer endlichen Anzahl Gitterplätze, in welcher fermionische Atome platziert sind. Es wird eine z-antiferromagnetische Phase unter Berücksichtigung nicht-lokaler Vielteilchenkorrelationen erhalten, und dabei werden bekannte Ergebnisse einer effektiven Einteilchenbeschreibung verbessert.rnrnDas korrelierte Halbmetall wird im Rahmen einer Mehrbandrechnung im Hinblick auf Korrelationseffekte untersucht. Ausgangspunkt ist eine ab initio-Beschreibung durch die Dichtefunktionaltheorie (DFT), welche dann durch die Hinzunahme lokaler Korrelationen ergänzt wird. Die Vielteilcheneffekte werden an Hand einer einfachen Wechselwirkungsnäherung verdeutlicht, und für ein Wechselwirkungsmodell in sphärischer Symmetrie präzisiert. Es ergibt sich nur eine schwache Quasiteilchenrenormierung. Besonders für röntgenspektroskopische Experimente wird eine gute Übereinstimmung erzielt.rnrnDie numerischen Ergebnisse für das Jz-Modell basieren auf Quanten-Monte-Carlo-Simulationen im Rahmen der dynamischen Molekularfeldtheorie (DMFT). Für alle anderen Systeme wird ein Mehrband-Algorithmus entwickelt und implementiert, welcher explizit nicht-diagonale Mehrbandprozesse berücksichtigt.rnrn

Thermoelectric properties in phase-separated half-Heusler materials

The conversion of dissipated heat into electricity is the basic principle of thermoelectricity. In this context, half-Heusler (HH) compounds are promising thermoelectric (TE) materials for waste heat recovery. They meet all the requirements for commercial TE applications, ranging from good efficiencies via environmentally friendliness to being low cost materials. This work focused on the TE properties of Ti0.3Zr0.35Hf0.35NiSn-based HH materials. This compound undergoes an intrinsic phase separation into a Ti-poor and Ti-rich HH phase during a rapid solidification process. The resulting dendritic microstructure causes a drastic reduction of the thermal conductivity, leading to higher TE efficiencies in these materials. The TE properties and temperature dependence of the phase-separated Ti0.3Zr0.35Hf0.35NiSn compound were investigated. The TE properties can be adjusted depending on the annealing treatment. The extension of annealing time for 21 days at 1000 °C revealed a reduction of the thermal conductivity and thus an enhancement of the TE performance in this sample. An increase of annealing temperature caused a change of the phase fraction ratio in favor of the Ti-rich phase, leading to an improvement of the electronic properties. rnInspired by the TE properties of the Ti0.3Zr0.35Hf0.35NiSn HH compound, the performance of different n- and p-type materials, realized via site substitution with donor and acceptor elements was examined. The fabrication of a TE n- and p-type material pair based on one starting compound can guarantee similar TE and mechanical properties and is enormous beneficial for device engineering. As donor dopants V, Nb and Sb were tested. Depending on the lattice position small doping levels were sufficient to attain distinct improvement in their TE efficiency. Acceptor-induced doping with Sc, Y and Co caused a change in the transport behavior from n- to p- type conduction, revealing the highest Seebeck coefficients obtained in the MNiSn system. rnThen, the long-term stability of an exemplary n- and p-type HH compound was proven. Surprisingly, the dendritic microstructure can be maintained even after 500 cycles (1700 h) from 373 to 873 K. The TE performance of both n- and p-type materials showed no significant change under the long-term treatment, indicating the extraordinary temperature stability of these compounds. Furthermore both HH materials revealed similar temperature-dependence of their mechanical properties. This work demonstrates the excellent suitability of phase-separated HH materials for future TE applications in the moderate temperature range.rn

Investigation of acceptor dopants in ZrNiSn half-Heusler materials

Thermoelectric generators (TEG) are solid state devices and are able to convert thermal energy directly into electricity and thus could play an important role in waste heat recovery in the near future. Half-Heusler (HH) compounds with the general formula MNiSn (M = Ti, Zr, Hf) built a promising class of materials for these applications because of their high Seebeck coefficients, their environmentally friendliness and their cost advantage over conventional thermoelectric materials.rnrnMuch of the existing literature on HH deals with thermoelectric characterization of n-type MNiSn and p-type MCoSb compounds. Studies on p-type MNiSn-based HHs are far fewer in number. To fabricate high efficient thermoelectric modules based on HH compounds, high performance p-type MNiSn systems need to be developed that are compatible with the existing n-type HH compounds. This thesis explores synthesis strategies for p-type MNiSn based compounds. In particular, the efficacy of transition metals (Sc, La) and main group elements (Al, Ga, In) as acceptor dopants on the Sn-site in ZrNiSn, was investigated by evaluating their thermoelectric performance. The most promising p-type materials could be achieved with transition metal dopants, where the introduction of Sc on the Zr side, yielded the highest Seebeck coefficient in a ternary NiSn-based HH compound up to this date. Hall effect and band gap measurements of this system showed, that the high mobility of minority carrier electrons dominate the transport properties at temperatures above 500 K. It could be shown that this is the reason, why n-type HH are successful TE materials for high temperature applications, and that p-types are subjected to bipolar effects which will lead to diminished thermoelectric efficiencies at high temperatures.rnrnTo complement the experimental investigations on different metal dopants and their influence on the TE properties of HH compounds, numerical solutions to the Boltzmann transport equation were used to predict the optimum carrier concentration where the maximum TE efficiency occurs for p-type HH compounds. The results for p-type samples showed that can not be treated within a simple parabolic band model approach, due to bipolar and multi-band effects.rnrnThe parabolic band model is commonly used for bulk TE materials. It is most accurate when the transport properties are dominated by one single carrier type. Since the transport properties of n-type HH are dominated by only one carrier type (high mobility electrons), it could be shown, that the use of a simple parabolic band model lead to a successful prediction of the optimized carrier concentration and thermoelectric efficiency in n-type HH compounds. rn

Thermoelectric performance of p-type TiCoSb half-Heusler compounds - Intrinsic phase separation and charge carrier concentration optimization as key to high efficiency

The world's rising demand of energy turns the development of sustainable and more efficient technologies for energy production and storage into an inevitable task. Thermoelectric generators, composed of pairs of n-type and p-type semiconducting materials, di¬rectly transform waste heat into useful electricity. The efficiency of a thermoelectric mate¬rial depends on its electronic and lattice properties, summarized in its figure of merit ZT. Desirable are high electrical conductivity and Seebeck coefficients, and low thermal con¬ductivity. Half-Heusler materials are very promising candidates for thermoelectric applications in the medium¬ temperature range such as in industrial and automotive waste heat recovery. The advantage of Heusler compounds are excellent electronic properties and high thermal and mechanical stability, as well as their low toxicity and elemental abundance. Thus, the main obstacle to further enhance their thermoelectric performance is their relatively high thermal conductivity.rn rnIn this work, the thermoelectric properties of the p-type material (Ti/Zr/Hf)CoSb1-xSnx were optimized in a multistep process. The concept of an intrinsic phase separation has recently become a focus of research in the compatible n-type (Ti/Zr/Hf)NiSn system to achieve low thermal conductivities and boost the TE performance. This concept is successfully transferred to the TiCoSb system. The phase separation approach can form a significant alternative to the previous nanostructuring approach via ball milling and hot pressing, saving pro¬cessing time, energy consumption and increasing the thermoelectric efficiency. A fundamental concept to tune the performance of thermoelectric materials is charge carrier concentration optimization. The optimum carrier concentration is reached with a substitution level for Sn of x = 0.15, enhancing the ZT about 40% compared to previous state-of-the-art samples with x = 0.2. The TE performance can be enhanced further by a fine-tuning of the Ti-to-Hf ratio. A correlation of the microstructure and the thermoelectric properties is observed and a record figure of merit ZT = 1.2 at 710°C was reached with the composition Ti0.25Hf0.75CoSb0.85Sn0.15.rnTowards application, the long term stability of the material under actual conditions of operation are an important issue. The impact of such a heat treatment on the structural and thermoelectric properties is investigated. Particularly, the best and most reliable performance is achieved in Ti0.5Hf0.5CoSb0.85Sn0.15, which reached a maximum ZT of 1.1 at 700°C. The intrinsic phase separation and resulting microstructure is stable even after 500 heating and cooling cycles.

Looking for silicene: studies of silicon deposition on metallic and semiconductor substrates

Nel presente lavoro espongo i risultati degli esperimenti svolti durante la mia internship all’Institut des NanoSciences de Paris (INSP), presso l’Università Pierre et Marie Curie (Paris VI), nel team "Phisico-Chimie et Dynamique des Surfaces", sotto la supervisione del Dott. Geoffroy Prévot. L’elaborato è stato redatto e in- tegrato sotto la guida del Dott. Pasquini, del dipartimento di Fisica e Astronomia dell’Università di Bologna. La tesi s’inserisce nel campo di ricerca del silicene, i.e. l’allotropo bidimensionale del silicio. Il cosidetto free-standing silicene è stato predetto teoricamente nel 2009 utilizzando calcoli di Density Functional Theory, e da allora ha stimolato un’intensa ricerca per la sua realizzazione sperimentale. La sua struttura elettronica lo rende particolarmente adatto per eventuali appli- cazioni tecnologiche e sperimentali, mentre lo studio delle sue proprietà è di grande interesse per la scienza di base. Nel capitolo 1 presento innanzitutto la struttura del silicene e le proprietà previste dagli studi pubblicati nella letteratura scientifica. In seguito espongo alcuni dei risultati sperimentali ottenuti negli ultimi anni, in quanto utili per un paragone con i risultati ottenuti durante l’internship. Nel capitolo 2 presento le tecniche sperimentali che ho utilizzato per effettuare le misure. Molto tempo è stato investito per ottenere una certa dimistichezza con gli apparati in modo da svolgere gli esperimenti in maniera autonoma. Il capitolo 3 è dedicato alla discussione e analisi dei risultati delle misure, che sono presentati in relazione ad alcune considerazioni esposte nel primo capitolo. Infine le conclusioni riassumono brevemente quanto ottenuto dall’analisi dati. A partire da queste considerazioni propongo alcuni esperimenti che potrebbero ulteriormente contribuire alla ricerca del silicene. I risultati ottenuti su Ag(111) sono contenuti in un articolo accettato da Physical Review B.

Metallic copper as an antimicrobial surface

Bacteria, yeasts, and viruses are rapidly killed on metallic copper surfaces, and the term "contact killing" has been coined for this process. While the phenomenon was already known in ancient times, it is currently receiving renewed attention. This is due to the potential use of copper as an antibacterial material in health care settings. Contact killing was observed to take place at a rate of at least 7 to 8 logs per hour, and no live microorganisms were generally recovered from copper surfaces after prolonged incubation. The antimicrobial activity of copper and copper alloys is now well established, and copper has recently been registered at the U.S. Environmental Protection Agency as the first solid antimicrobial material. In several clinical studies, copper has been evaluated for use on touch surfaces, such as door handles, bathroom fixtures, or bed rails, in attempts to curb nosocomial infections. In connection to these new applications of copper, it is important to understand the mechanism of contact killing since it may bear on central issues, such as the possibility of the emergence and spread of resistant organisms, cleaning procedures, and questions of material and object engineering. Recent work has shed light on mechanistic aspects of contact killing. These findings will be reviewed here and juxtaposed with the toxicity mechanisms of ionic copper. The merit of copper as a hygienic material in hospitals and related settings will also be discussed.

The Other Half

Leaders and faculty at private colleges and universities should support funding for public higher education.

Circulation dynamics and its influence on European and Mediterranean January-April climate over the past half millennium: results and insights from instrumental data, documentary evidence and coupled climate models

We use long instrumental temperature series together with available field reconstructions of sea-level pressure (SLP) and three-dimensional climate model simulations to analyze relations between temperature anomalies and atmospheric circulation patterns over much of Europe and the Mediterranean for the late winter/early spring (January–April, JFMA) season. A Canonical Correlation Analysis (CCA) investigates interannual to interdecadal covariability between a new gridded SLP field reconstruction and seven long instrumental temperature series covering the past 250 years. We then present and discuss prominent atmospheric circulation patterns related to anomalous warm and cold JFMA conditions within different European areas spanning the period 1760–2007. Next, using a data assimilation technique, we link gridded SLP data with a climate model (EC-Bilt-Clio) for a better dynamical understanding of the relationship between large scale circulation and European climate. We thus present an alternative approach to reconstruct climate for the pre-instrumental period based on the assimilated model simulations. Furthermore, we present an independent method to extend the dynamic circulation analysis for anomalously cold European JFMA conditions back to the sixteenth century. To this end, we use documentary records that are spatially representative for the long instrumental records and derive, through modern analogs, large-scale SLP, surface temperature and precipitation fields. The skill of the analog method is tested in the virtual world of two three-dimensional climate simulations (ECHO-G and HadCM3). This endeavor offers new possibilities to both constrain climate model into a reconstruction mode (through the assimilation approach) and to better asses documentary data in a quantitative way.