Structural and photoelectrochemical properties of porous TiO2 nanofibers decorated with Fe2O3 by sol-flame

The hybrid structure of Fe2O3 nanoparticles/TiO2 nanofibers (NFs), combines the merits of large surface areas of TiO2 NFs and absorption in ultraviolet light–visible light range. This structure can be used for many applications such as photoelectrochemical water splitting and photo-catalysis. Here, a sol-flame method is used for depositing Fe2O3 on TiO2 NFs that were prepared by hydrothermal on Ti sheets. The obtained materials were characterized by XRD, SEM, UV/Vis diffuse reflectance, Raman, and XPS. The results revealed the formation of rutile and anatase crystalline phases together with Fe2O3. This process moves the absorption threshold of TiO2 NFs support into visible spectrum range and enhances the photocurrent in comparison to bare TiO2 NFs, although no hole scavenger was used. The impedance measurement at low and high frequencies revealed an increase in series resistance and a decrease in resistance of charge transfer with sol-flame treatment time. A mechanism for explaining the charge transfer in these TiO2 NFs decorated with Fe2O3 nanoparticles was proposed.

Potentiostatic Reversible Photoelectrochromism: An Effect Appearing in Nanoporous TiO2/Ni(OH)2 Thin Films

In the field of energy saving, finding composite materials with the ability of coloring upon both illumination and change of the applied electrode potential keeps on being an important goal. In this context, chemical bath deposition of Ni(OH)2 into nanoporous TiO2 thin films supported on conducting glass leads to electrodes showing both conventional electrochromic behavior (from colorless to dark brown and vice versa) together with photochromism at constant applied potential. The latter phenomenon, reported here for the first time, is characterized by fast and reversible coloration upon UV illumination. The bleaching kinetics shows first order behavior with respect to the NiIII centers in the film, and an order 1.2 with respect to electrons in the TiO2 film. From a more applied point of view, this study opens up the possibility of having two-mode smart windows showing not only conventional electrochromism but also reversible darkening upon illumination.

A Two-Step Sol–Gel Method for Synthesis of Nanoporous TiO2

This article reports a study of the effects of synthesis parameters on the preparation and formation of mesoporous titania nanopowders by employing a two-step sol-gel method. These materials displayed crystalline domains characteristic of anatase. The first step of the process involved the hydrolysis of titanium isopropoxide in a basic aqueous solution mediated by neutral surfactant. The solid product obtained from step 1 was then treated in an acidified ethanol solution containing the same titanium precursor to thicken the pore walls. Low pH and higher loading of the Ti precursor in step 2 produced better mesoporosity and crystallinity of titanium dioxide polymorphs. The resultant powder exhibited a high surface area (73.8 m(2)/g) and large pore volume (0.17 cm(3)/g) with uniform mesopores. These materials are envisaged to be used as precursors for mesoporous titania films as a wide band gap semiconductor in dye-sensitized nanocrystalline TiO2 solar cells.

Cobalt promoted TiO2/GO for the photocatalytic degradation of oxytetracycline and Congo Red

A family of titania derived nanocomposites synthesized via sol-gel and hydrothermal routes exhibit excellent performance for the photocatalytic degradation of two important exemplar water pollutants, oxytetracycline and Congo Red. Low loadings of Co3O4 nanoparticles dispersed over the surfaces of anatase TiO2 confer visible light photoactivity for the aqueous phase decomposition of organics through the resulting heterojunction and reduced band gap. Subsequent modification of these Co3O4/TiO2 composites by trace amounts of graphene oxide nanosheets in the presence of a diamine linker further promotes both oxytetracycline and Congo Red photodegradation under simulated solar and visible irradiation, through a combination of enhanced photoresponse and consequent radical generation. Radical quenching and fluorescence experiments implicate holes and hydroxyl radicals as the respective primary and secondary active species responsible for oxidative photodegradation of pollutants.

Size-controlled TiO2 nanoparticles on porous hosts for enhanced photocatalytic hydrogen production

Nanocystalline TiO2 particles were successfully synthesized on porous hosts (SBA-15 and ZSM-15) via a sol-gel impregnation method. Resulting nanocomposites were characterized by XRD, TEM, BET surface analysis, Raman and UV-vis diffuse reflectance spectroscopy, and their photocatalytic activity for H2 production evaluated. XRD evidences the formation of anatase nanoparticles over both ZSM-5 and SBA-15 porous supports, with TEM highlighting a strong particle size dependence on titania precursor concentration. Photocatalytic activities of TiO2/ZSM-5 and TiO2/SBA-15 composites were significantly enhanced compared to pure TiO2, owing to the smaller TiO2 particle size and higher surface area of the former. TiO2 loadings over the porous supports and concomitant photocatalytic hydrogen production were optimized with respect to light absorption, available surface reaction sites and particle size. 10%TiO2/ZSM-5 and 20%TiO2/SBA-15 proved the most active photocatalysts, exhibiting extraordinary hydrogen evolution rates of 10,000 and 8800μmolgTiO2 -1 h-1 under full arc, associated with high external quantum efficiencies of 12.6% and 5.4% respectively under 365nm irradiation.

Novel sol–gel preparation of (P2O5)0.4–(CaO)0.25–(Na2O)X–(TiO2)(0.35−X) bioresorbable glasses (X = 0.05, 0.1, and 0.15)

Quaternary phosphate-based glasses in the P2O5–CaO–Na2O–TiO2 system with a fixed P2O5 and CaO content of 40 and 25 mol% respectively have been successfully synthesised via sol–gel method and bulk, transparent samples were obtained. The structure, elemental proportion, and thermal properties of stabilised sol–gel glasses have been characterised using X-ray diffraction (XRD), energy dispersive X-ray spectroscopy (EDX), 31P nuclear magnetic resonance (31P NMR), titanium K-edge X-ray absorption near-edge structure (XANES), fourier transform infrared (FTIR) spectroscopy, and differential thermal analysis (DTA). The XRD results confirmed the amorphous nature for all stabilized sol–gel derived glasses. The EDX result shows the relatively low loss of phosphorus during the sol–gel process and Ti K-edge XANES confirmed titanium in the glass structure is in mainly six-fold coordination environment. The 31P NMR and FTIR results revealed that the glass structure consist of mainly Q1 and Q2 phosphate units and the Ti4+ cation was acting as a cross-linking between phosphate units. In addition DTA results confirmed a decrease in the glass transition and crystallisation temperature with increasing Na2O content. Ion release studies also demonstrated a decrease in degradation rates with increasing TiO2 content therefore supporting the use of these glasses for biomedical applications that require a degree of control over glass degradation. These sol–gel glasses also offer the potential to incorporate proactive molecules for drug delivery application due to the low synthesis temperature employed.

UV-stable paper coated with APTES-modified P25 TiO2 nanoparticles

In order to inhibit the photocatalytic degradation of organic material supports induced by small titania (TiO2) nanoparticles, highly photocatalytically active, commercially available P25-TiO2 nanoparticles were first modified with a thin layer of (3-aminopropyl) triethoxysilane (APTES), which were then deposited and fixed onto the surface of paper samples via a simple, dip-coating process in water at room temperature. The resultant APTES-modified P25 TiO2 nanoparticle-coated paper samples exhibit much greater stability to UV-illumination than uncoated blank reference paper. Very little, or no, photo-degradation in terms of brightness and whiteness, respectively, of the P25-TiO2-nanoparticle-treated paper is observed. There are many other potential applications for this Green Chemistry approach to protect cellulosic fibres from UV-bleaching in sunlight and to protect their whiteness and maintain their brightness. © 2014 Elsevier Ltd.

Improved lithium storage properties of electrospun TiO2 with tunable morphology:from porous anatase to necklace rutile

Three-dimensional TiO2 with tunable morphology and crystalline phase was successfully prepared by the electrospinning technique and subsequent annealing. Porous-shaped anatase TiO2, cluster-shaped anatase TiO2, hierarchical-shaped rutile (minor) TiO2 and nano-necklace rutile (major) TiO2 were achieved at 500, 600, 700 and 800°C, respectively. The mechanism of the formation of these tailored morphologies and crystallinity was investigated. Lithium insertion properties were evaluated by galvanostatic and potentiostatic modes in half-cell configurations. By combining the large surface area, open mesoporosity and stable crystalline phase, the porous-shaped anatase TiO2 exhibited the highest capacity, best rate and cycling performance among the four samples. The present results demonstrated the usefulness of three-dimensional TiO 2 as an anode for lithium storage with improved electrode performance. © 2013 The Royal Society of Chemistry.

On the impact of Cu dispersion on CO2 photoreduction over Cu/TiO2

A family of Cu/TiO2 catalysts was prepared using a refined sol–gel method, and tested in the photocatalytic reduction of CO2 by H2O to CH4 using a stirred batch, annular reactor. The resulting photoactivity was benchmarked against pure TiO2 nanoparticles (synthesised by an identical sol–gel route). CO2 photoreduction exhibited a strong volcano dependence on Cu loading, reflecting the transition from 2-dimensional CuOx nanostructures to 3-dimensional crystallites, with optimum CH4 production observed for 0.03 wt.% Cu/TiO2.

Studio di stati fotoeccitati in nanoparticelle di V-TiO2 mediante scattering inelastico risonante di raggi X

La TiO2 è uno dei materiali più studiati degli ultimi decenni. I motivi sono da ricercarsi nelle sue numerose applicazioni, possibili in molti campi come dispositivi fotovoltaici, depurazione da agenti inquinanti o filtraggio di raggi UV. Per le celle elettrochimiche in particolare, il biossido di titanio offre molti vantaggi, ma non è privo di ostacoli. Il limite principale è lo scarso assorbimento dello spettro visibile, dovuto all’energy gap elevato (circa 3.2 eV). La ricerca da diversi anni si concentra sul tentativo di aumentare l’assorbimento di luce solare: promettenti sono i risultati raggiunti grazie alla forma nanoparticellare della TiO2, che presenta proprietà diverse dal materiale bulk. Una delle strategie più studiate riguarda il drogaggio tramite impurità, che dovrebbero aumentare le prestazioni di assorbimento del materiale. Gli elementi ritenuti migliori a questo scopo sono il vanadio e l’azoto, che possono essere usati sia singolarmente che in co-doping. In questo lavoro abbiamo realizzato la crescita di nanoparticelle di V-TiO2, tramite Inert Gas Condensation. La morfologia e la struttura atomica sono state analizzate attraverso microscopia a trasmissione, analizzandone la mappe tramite image processing. Successivamente abbiamo studiato le proprietà di assorbimento ottico dei campioni, nello spettro visibile e nel vicino ultravioletto, attraverso il metodo della riflettanza diffusa, determinando poi il bandgap tramite Tauc Plot. L’esperimento centrale di questo lavoro di tesi è stato condotto sulla beamline ID26 dell’European Synchrotron Radiation Facility, a Grenoble. Lì, abbiamo effettuato misure XANES, allo scopo di studiare gli stati fotoeccitati del materiale. L’eccitazione avveniva mediante laser con lunghezza d’onda di 532 nm. Tramite gli spettri, abbiamo analizzato la struttura locale e lo stato di ossidazione del vanadio. Le variazioni indotta dal laser hanno permesso di capire il trasferimento di carica e determinare la vita media.