Development of an Active Superconducting Magnetic Bearing

The potential use of YBa2Cu3C7as an active component in a magnetic bearing is being investigated. Measurements are being made of the load bearing capacity and related stiffnesses in comparison to predictions from the critical state model. Although the load bearing capacity is high and increases with the square of the magnetic field trapped the stiffness is low. We report on a novel design concept to overcome this problem. © 1995 IEEE

Characterization of YBCO Bulk samples by local AC-susceptometry

Melt processed HTSC bulk samples usually show a high inhomogeneity. These inhomogeneities influence application-relevant properties such as the lévitation force or the trapped field. In this contribution a technique is presented which allows investigation of these inhomogeneous properties. The measurements are performed by scanning the sample surface with a small coil system and detecting the first and third harmonic of the inductive response. The critical current density jc is calculated from the measured signal using a modified critical state model. Jcdistributions yielded by this technique are shown. © 1997 IEEE.

Distribution of critical current density in large YBa2Cu3O7-δ grains fabricated using seeded peritectic solidification

High quality large grain high Tc superconducting ceramics offer enormous potential as 'permanent' magnets and in magnetic screening applications at 77K. This requires sample dimensions -cm with uniform high critical current densities of the order 105 A/cm2 in applied magnetic fields of IT. We report a study of the magnetic characterisation of a typical large YBa2Cu3O7-δ grain, prepared by seeded peritectic solidification, and correlate the magnetically determined critical current density, Jc, with microstuctural features from different regions of the bulk sample. From this data we extract the temperature, field and positional dependence of the critical current density of the samples and the irreversibility line. We find that whilst the bulk sample exhibits a good Jc of order 104 A/cm2 (77K, 1T), the local Jc is strongly correlated with the sample microstructure towards the edge of the sample and more severely at the centre of the sample by the presence of SmBa2Cu3O7-δ seed crystal. © 1997 IEEE.

Dynamic properties of superconducting magnetic bearings

The potential use of YBa2j as an active component in a magnetic bearing is being investigated. Although the load bearing capacity is high and increases with the square of the magnetic field trapped, the stiffness is low. Both the stiffness and the lévitation height are a function of the loading history of the bearing. At Cambridge we have been investigating the effects of dynamic loading such as single large excursions from steady state loads and cyclically applied loads such as vibrations. Since a superconducting bearing has little inherent damping cyclic loads applied at or near its natural frequency can have catastrophic effects. The information being gathered at Cambridge will be used to enable these effects to be mitigated in the bearing design process. © 1997 IEEE.

Development of non-weak link bulk YBCO grain boundaries for high magnetic field eegimeering applications

A non-weak link joining technique has been developed for YBCO pseudo-crystals fabricated by seeded peritectic solidification based on the formation of a liquid phase which segregates from the platelet boundaries at temperatures above = 920 °C. Electrical and magnetic measurements on these boundaries suggest that their irreversibility field can be as high as 7 T at 77 K in fully oxygenated pseudo-crystals joined along their crystallographic ab-planes which is comparable to the irreversibility behaviour of the adjacent YBCO grains. © 1999 IEEE.

Crystal growth of melt-textured Nd-123 under 1% oxygen partial pressure atmosphere

Crystal growth of melt-textured Nd-123 pseudo-crystals was investigated via an isothermal solidification with top-seeding technique under a 1%O2 in N2 atmosphere. Non-steady state solidification was observed at low undercooling, in contrast to an almost linear growth at higher undercooling. Similar to processing in air, the substitution of Nd/Ba was found to decrease from the seed position to the edge of the crystal. In addition, the volume fraction of Nd-422 particles decreased in the solid as solidification proceeded. As a result of these microstructural inhomogeneities, the critical temperature and the critical current density varied within the crystal even for samples processed isothermally, despite the narrow solid solution range of the Nd-123 phase under a reduced pO2 atmosphere.

Magnetic field and current distributins in melt-textured YBa 2Cu 3O 7-x with an artificial grain boundary

Using a magneto-optical (MO) technique, magnetic field distributions have been measured in a melt-textured YBa 2Cu 3O 7-x bulk superconductor, joined to form an artificial grain boundary (GB), in an external magnetic field perpendicular to the sample surface. The magnetic field at a weak section of the GB shows different values between the field increasing up to 150mT and decreasing down to 0T after zero-field-cooling. Namely, the magnetic field in increasing field is higher than that in decreasing field, even in the same external field. This result supports a model in which such differences in magnetic field at the weak-link GB give rise to the hysteresis behavior in the field dependence of transport critical current density in polycrystalline samples. The field distributions across a well-joined region of the GB behave similarly to the adjoining bulk material and this result indicates the possibility of creating useful artifacts provided that the strongly coupled sections can be reproduced on a larger scale.

Comment on 'processing and microstructure of single grain uranium-doped Y-Ba-Cu-O superconductor'

We comment on the paper by N Hari Babu et al. (2002 Supercond. Sci. Technol. 15 104-10) and point out misinterpretations of the chemical composition of U-bearing deposits observed in Y123. The observed small deposits are those of new compounds which do not contain Cu, rather than refined Y211 plus U, as stated by the authors. We further note that extensive literature, not quoted, is in disagreement by nearly an order of magnitude concerning the values of Pt and U doping at which the optimum value of Jc is obtained. Other related information, presently in the literature, which may be helpful to those working with this high temperature superconducting chemical system, is presented.

Development of the microstructure of uranium-doped Nd-Ba-Cu-O

Melt grown Nd-Ba-Cu-O (NdBCO) has been reported to exhibit higher values of critical current density, Jc and irreversibility field, Hirr, than other (RE)BCO superconductors, such as YBCO. The microstructure of NdBCO typically contains 5-10 μm sized inclusions of the Nd4Ba2Cu2O10 phase (Nd-422) in a superconducting NdBa2Cu3O7-δ phase (Nd-123) matrix. The average size of these inclusions is characteristically larger than that of the Y2BaCuO5 (Y-211) inclusions in YBCO. As a result, there is scope to further refine the Nd-422 size to enhance Jc in NdBCO. Large grain samples of NdBCO superconductor doped with various amounts of depleted UO2 and containing excess Nd-422 have been fabricated by top seeded melt growth under reduced oxygen partial pressure. The effect of the addition of depleted UO2 on the NdBCO microstructure has been studied systematically in samples with and without added CeO2. It is observed that the addition of UO2 refines the NdBCO microstructure via the formation of uranium-containing phase particles in the superconducting matrix. These particles are of approximately spherical geometry with dimensions of around 1 μm. The average size of the nonsuperconducting phase particles in the uranium-doped microstructure is an order of magnitude less than their size in un-doped Nd-123 prepared with excess Nd-422. The critical current density of uranium-doped NdBCO is observed to increase significantly compared to the undoped material.

Behavior of bulk melt-textured YBCO single domains subjected to crossed magnetic fields

We have experimentally investigated the crossed magnetic field effects on bulk melt-processed YBCO single domains. The samples were first permanently magnetized along their c-axis and then subjected to several cycles of a transverse magnetic field parallel to the ab planes. The magnetic properties along the c and ab directions were simultaneously measured using a couple of orthogonal pick-up coils as well as a Hall probe placed against the sample surface. The effects of both sweep amplitude and polarity were investigated. Field sweeps of alternate polarities are shown to affect the decay of the c-axis magnetization much more strongly than field sweeps of unique polarity do. However, the c-axis magnetization does not show any saturation even after a large number of field sweeps. Next, a micro-Hall probe scanning system was used to measure the distribution of magnetic induction over the top surface of the single domain subjected to the same combination of magnetic fields. The results are shown to be consistent with those determined with the sensing coils and bring out the role played by geometric effects.

Reduction of porosity in RE1Ba2Cu3Oy pseudo crystals

The distribution of porosity in Y1Ba2Cu3Oy (Y-123) pseudo-crystals prepared by hot seeded melt growth of precursor pellet samples pre-sintered at elevated temperatures in air or vacuum has been investigated. The results demonstrate that the porosity within the Y-123 pseudo-crystal matrix could be reduced dramatically by pre-sintering in vacuum, compared with that for precursor pellets processed in air.