The occurrence of porosity in reline acrylic resins. Effect of microwave disinfection

Microwave energy has proved to be an effective method for disinfecting acrylic dentures. However, the effect of microwave heating on the porosity of autopolymerising denture reline resins has not been investigated.The purpose of the study was to determine the effect of microwave disinfection on the porosity of autopolymerised denture reline materials (Kooliner-K, New Truliner-NT, Tokuso Rebase Fast-TR and Ufi Gel Hard-UGH) and a conventional heat-polymerised denture base resin (Lucitone 550-L).Specimens (10 mm x 20 mm x 1 mm) were obtained from the impression surface of the palatal mucosa in a single person and divided into four groups (n = 5). The porosity was evaluated after polymerisation (C1), after two cycles of microwave disinfection (MW2), after seven cycles of microwave disinfection (MW7) and after 7 days storage in water at 37 degrees C (C2). Specimens from group MW7 were exposed to microwave disinfection daily being stored in water at 37 degrees C between exposures. All the replicas were sputter coated with gold and micrographs/digital images were taken of each replica using scanning electron microscopy at magnification x 100. The SEM micrographs were then examined using an image analyser to determine the number of pores. Comparison between materials and groups were made using Kruskal-Wallis tests.MW7 resulted in a significant increase in the number from the pores of material K, but decreased in number in reline material TR and UGH reline resin. The number of pores in materials NT and L remained unaffected following microwave disinfection.Differences in the porosity amongst the materials and for different experimental conditions were observed following microwave disinfection.

Comparative assessment of the flow rate of root canal sealers

OBJETIVO: Este estudo avaliou o escoamento do Acroseal, AH Plus, Endomethasone N, Sealapex e ActiV GP de acordo com a especificação ISO 6876/2001. METODOLOGIA: Um volume de 0,05 mL do cimento manipulado de acordo com as recomendações do fabricante foi colocado numa placa de vidro. Aos 180±5 s após o início da espatulação, uma segunda placa de vidro foi colocada sobre o cimento, seguida por um peso de massa de 100 g para fazer um total de 120±2 g. Dez minutos após o começo da manipulação o peso foi removido e o valor do diâmetro do disco de cimento foi mensurado. A média de 3 mensurações para cada cimento foi tomada como o escoamento do material. Os dados foram comparados estatisticamente pelos testes ANOVA e Tukey. RESULTADOS: Os escoamentos obtidos foram: Acroseal 21.,4 mm, AH Plus 22,72 mm, ActiV GP 24,90 mm, Endomethasone N 18,76 mm e Sealapex 25,15 mm. CONCLUSÃO: Apenas o Endomethasone N não se enquadrou na especificação ISO a qual requer que o cimento tenha um diâmetro não inferior a 20 mm. O Sealapex alcançou o melhor escoamento, mas não foi estatisticamente diferente do Activ GP e AH Plus (P>0,05).

Myocardial dysfunction induced by food restriction is related to calcium cycling and beta-adrenergic system changes

Food restriction (FR) has been shown to promote myocardial dysfunction in rats. The aim of this study was to verify the participation of calcium and beta-adrenergic system on myocardial mechanical alteration in rats submitted to FR. Myocardial performance was studied in isolated left ventricular papillar muscle from young Wistar-Kyoto rats (WKY) submitted to FR or to control diet. The groups subjected to FR were fed 50% less food than the control group for 90 days. Mechanical function was studied in isometric contraction at post-rest contraction of 30 seconds (PRC), calcium chloride concentration 5.20 mM, and beta-adrenergic stimulation with isoproterenol 10(-6) M. FR decreased the body weight, and left and right ventricular weight. In basal condition (1.25 MM of calcium) time to peak tension (TPT) and time from peak tension to 50% relaxation (RT50) were greater in the FR group. Muscle function was. The same in both PRC groups. TPT decrease in both high calcium groups, more in FR rats; RT50 dropped only in FR animals. TPT decreased in both Isoproterenol groups, more intensely in the FR group. This result suggests that food restriction impairs myocardial performance and these changes may be attributed to alterations in the intracellular calcium cycling and beta-adrenergic system. (C) 2003 Elsevier B.V. All rights reserved.

Synchronization of ovulation in crossbred dairy heifers using gonadotrophin-releasing hormone agonist, prostaglandin F2a and human chorionic gonadotrophin or estradiol benzoate

Girolando (Gir x Holstein) is a very common dairy breed in Brazil because it combines the rusticity of Gir (Bos indicus) with the high milk yield of Holstein (Bos taurus). The ovarian follicular dynamics and hormonal treatments for synchronization of ovulation and timed artificial insemination were studied in Girolando heifers. The injection of a gonadotrophin-releasing hormone (GnRH) agonist was followed 6 or 7 days (d) later by prostaglandin F2a (PGF2a). Twenty-four hours after PGF2a injection either human chorionic gonadotropin (hCG, GPh-d6 and GPh-d7 groups) or estradiol benzoate (EB, GPE-d6 and GPE-d7 groups) was administered to synchronize ovulation and consequently allow timed artificial insemination (AI) 24 and 30 h after hCG and EB injection, respectively. Follicular dynamics in Girolando heifers was characterized by the predominance of three follicular waves (71.4%) with sizes of dominant follicles (10-13 mm) and corpus luteum (approximately 20 mm) similar to those for Bos indicus cattle. In the GnRH-PGF-hCG protocol, hCG administration induced earlier ovulation (67.4 h, P<0.01) compared to the control group (GnRH-PGF) and a better synchronization of ovulation, since most of it occurred within a period of 12 to 17 h. Pregnancy rate after timed AI was 42.8 (3/7, GPh-d6) to 50% (7/14, GPh-d7). In contrast, estradiol benzoate (GnRH-PGF-EB protocol) synchronized ovulation of only 5 of 11 heifers from the GPE-d7 group and of none (0/7) from the GPE-d6 group, which led to low pregnancy rates after timed AI (27.3 and 0%, respectively). However, since a small number of Girolando heifers was used to determine pregnancy rates in the present study, pregnancy rates should be confirmed with a larger number of animals.

Reprodução em cativeiro do jurupecê Sorubim lima (Siluriformes, Pimelodidae) por meio de indução hormonal

Sorubim lima is a migratory catfish that do not reproduce in lenthic environments such as those formed after construction of hydroelectric power plants. An alternative for conservation of the species in these environments is the stocking with fingerlings produced in captivity. The technique used to reproduce it in captivity was the induction by carp pituitary hormone, with dosage of 5 mg.kg(-1) for females (1 mg.kg(-1) in the first dose and 4 mg.kg(-1) in the second) and 3 mg.kg(-1) for males (1 mg.kg(-1) in the first dose and 2 mg.kg(-1) in the second), with an interval of 14 hours. The determination of extrusion moment of oocytes was made by monitoring the migration of nucleus from central to peripheral position. After UTA 264.5 (accumulated thermal units) the oocytes were obtained by compression of the ventral region of the female, and male were sacrificed for extraction of sperm. The eggs were kept in an incubator and the time of hatching of larvae was 370 UTA. The larvae were initially fed with plankton and showed no cannibalism. Moreover, they were not demanding about the food, accepting prepared rations after fifteenth day of life. The weight gain of larvae was very low even close to 20 mm in length (14 days), not exceeding 0.05 mg per day. After that both weight and length increased rapidly.

Viés Analítico em Estudos Tafonômicos com Macroinvertebrados: Implicações (Paleo)Ambientais e (Paleo)Ecológicas

A review of recent literature shows that most taphonomic studies of Holocene and fossil macrovertebrates are not methodologically standardized. Hence, results from distinct studies are not comparable, even among researches sharing virtually identical goals, targeting the same biological group of similar age and depositional environment. The effects of the shell size in the taphonomic analysis are still poorly understood. In order to study this issue, the taphonomic signatures (articulation, valve type, fragmentation, abrasion, corrosion, edge modification, color alteration, bioerosion and encrustation) of brachiopod shells (Bouchardia rosea (Mawe)), from Ubatuba Bay in the northern coast of São Paulo State, were investigated according to the sieve sizes. In the study area, 14 collecting stations were sampled via Van Veen grab sampler, along a bathymetric gradient, ranging from 0 to 35 m of depth. Bulk samples were sieved through 8 mm, 6 mm, and 2 mm mesh sizes, yielding a total of 5.204 shells. The results indicate that, when taphonomic signatures were independently analyzed per size classes (8 mm, 6 mm, and 2 mm), the taphonomic signatures are recorded in a complex and random way. Additionally, cluster analysis showed that the similarity among the clusters vary according to the considered sieve size. Thus, the sieve size plays an important role in the distribution of taphonomic signatures in shells of distinct sizes. These results suggest that the concentration of the taphonomic analysis on one class (e.g., the largest sieve size, 8 mm) is not always the best method. Rather, the total data (all sieves included) seems more accurate in recording the whole spectrum of taphonomic processes recorded in shells of a given assemblage.

Effect of Airborne-Particle Abrasion and Mechanico-Thermal Cycling on the Flexural Strength of Glass Ceramic Fused to Gold or Cobalt-Chromium Alloy

Purpose: To evaluate the effect of airborne-particle abrasion and mechanico-thermal cycling on the flexural strength of a ceramic fused to cobalt-chromium alloy or gold alloy.Materials and Methods: Metallic bars (n = 120) were made (25 mm x 3 mm x 0.5 mm): 60 with gold alloy and 60 with Co-Cr. At the central area of the bars (8 mm x 3 mm), a layer of opaque ceramic and then two layers of glass ceramic (Vita VM13, Vita Zahnfabrick) were fired onto it (thickness: 1 mm). Ten specimens from each alloy group were randomly allocated to a surface treatment [(tungsten bur or air-particle abrasion (APA) with Al(2)O(3) at 10 mm or 20 mm away)] and mechanico-thermal cycling (no cycling or mechanically loaded 20,000 cycles; 10 N distilled water at 37 degrees C and then thermocycled 3000 cycles; 5 degrees C to 55 degrees C, dwell time 30 seconds) combination. Those specimens that did not undergo mechanico-thermal cyclingwere stored inwater (37 degrees C) for 24 hours. Bond strength was measured using a three-point bend test, according to ISO 9693. After the flexural strength test, failure types were noted. The data were analyzed using three factor-ANOVA and Tukey's test (alpha = 0.05).Results: There were no significant differences between the flexural bond strength of gold and Co-Cr groups (42.64 +/- 8.25 and 43.39 +/- 10.89 MPa, respectively). APA 10 and 20 mm away surface treatment (45.86 +/- 9.31 and 46.38 +/- 8.89 MPa, respectively) had similar mean flexural strength values, and both had significantly higher bond strength than tungsten bur treatment (36.81 +/- 7.60 MPa). Mechanico-thermal cycling decreased the mean flexural strength values significantly for all six alloy-surface treatment combinations tested when compared to the control groups. The failure type was adhesive in the metal/ceramic interface for specimens surface treated only with the tungsten bur, and mixed for specimens surface treated with APA 10 and 20 mm.Conclusions: Considering the levels adopted in this study, the alloy did not affect the bond strength; APA with Al(2)O(3) at 10 and 20 mm improved the flexural bond strength between ceramics and alloys used, and the mechanico-thermal cycling of metal-ceramic specimens resulted in a decrease of bond strength.

Effects of annealing on the crystallization and roughness of PLZT thin films

Lead lanthanum zirconate titanate (PLZT) thin films with stoichiometry (9/65/35) were prepared by a dip-coating process using a polymeric organic solution. The solution viscosity was adjusted in the range of 15-56 cP. Silicon (100) substrates were previously cleaned and then immersed in the solution. The withdrawal speed of substrate from the solution was adjusted within a range of 5 to 20 mm/min. The coated substrates were thermally treated in the 450-700 degreesC temperature range. Surface roughness and crystallization of these films are strongly dependent on the annealing conditions. Infrared and X-ray diffraction data for PLZT powders heat-treated at 650 degreesC for 3 h show that the material is free of carbonate phases and crystalline. (C) 2001 Elsevier B.V. B.V. All rights reserved.

Optimization of incubation time of protein Tc85 in the construction of biosensor: Is the EIS a good tool?

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Determinação simultânea de resíduos de cloranfenicol, tianfenicol e florfenicol em leite bovino por cromatografia eletrocinética micelar

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Diversidade de pulgões e de seus parasitóides e predadores na cultura da alfafa

O objetivo deste trabalho foi verificar a diversidade de pulgões, seus predadores e parasitóides, e a influência de fatores climáticos nas suas populações. Foram realizadas coletas semanais no período de abril/1995 a março/1996, no campo de alfafa da Universidade Federal de Lavras (UFLA), em Lavras, MG. As espécies de pulgões coletadas foram Therioaphis trifolii (Monel) f. maculata, Acyrthosiphon pisum (Harris), A. kondoi Shinji e Aphis craccivora Kock, presentes na cultura durante todo o período de estudo, com picos populacionais em novembro/1995, julho/1995, dezembro/1995 e abril/1996, respectivamente. Foram amostrados insetos predadores das famílias Coccinellidae, Syrphidae, Anthocoridae, Geocoridae e Chrysopidae, tendo as duas últimas ocorrência esporádica. Espécies da família Coccinellidae ocorreram durante todo o período amostral, apresentando o pico populacional no final de dezembro/1995, com precipitação de 20 mm e temperatura de 22,6ºC. A família Syrphidae alcançou maiores números em abril, à precipitação de 53 mm e temperatura de 21ºC. A família Anthocoridae não se manteve por todo o período amostral, porém um pico populacional ocorreu no final de dezembro nas mesmas condições que aquele apresentado pela família Coccinellidae. Os parasitóides da família Aphididae alcançaram pico em junho/1995, à temperatura de 16ºC.

Secagem e armazenamento de sementes de juçara

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Método alternativo de avaliação da absorção de atrazine por plantas de Brachiaria plantaginea

Dois experimentos foram conduzidos em casa de vegetação da Universidade Estadual de Maringá (UEM)-PR, objetivando desenvolver metodologia alternativa para avaliar a absorção foliar e radicular de herbicidas. O delineamento experimental utilizado foi o inteiramente casualizado com 11 e 5 tratamentos para os solos arenoso e argiloso, respectivamente, ambos os experimentos com quatro repetições, constituídos por plantas de B. plantaginea em dois estádios. O herbicida atrazine foi aplicado nas doses de 2,5 e 3,0 kg ha¹ em solos arenoso e argiloso, utilizando um pulverizador costal pressurizado por CO2. Os tratamentos foram constituídos por plantas protegidas com canudos plásticos em solo descoberto e plantas desprotegidas em solo coberto com papel-alumínio, associadas a condições de solo seco e úmido, ou em ambas as condições, acrescidas de irrigação de 20 mm apenas ao solo após aplicação. A absorção foliar da atrazine foi eficiente no controle de B. plantaginea com duas a três folhas em solo arenoso e argiloso, ao contrário do estádio de quatro a cinco folhas, onde houve necessidade de associar os efeitos da absorção foliar e radicular para se obter controle satisfatório. A irrigação de 20 mm ampliou o controle da absorção radicular de B. plantaginea em diferentes estádios de plantas, solo e umidade do solo. A metodologia apresentou-se viável como ferramenta alternativa para avaliação da absorção foliar e radicular de herbicidas, no controle de gramíneas em estádio inicial de desenvolvimento.

Dinâmica do herbicida amicarbazone (Dinamic) aplicado sobre palha de cana-de-açúcar (Saccarum officinarum)

O objetivo deste trabalho foi estudar a dinâmica do herbicida amicarbazone (Dinamic) aplicado sobre palha de cana-de-açúcar deixada sobre o solo, em sistema de cana crua. Três ensaios foram realizados para avaliar a dinâmica desse herbicida aplicado sobre diferentes quantidades de palha de cana-de-açúcar, em diferentes intervalos de tempo e volumes de simulação de chuvas após aplicação do herbicida. No primeiro ensaio, foi avaliada a interceptação do herbicida por 0, 1, 2,5, 5, 7,5, 10, 15 e 20 t de palha de cana-de-açúcar ha-1. A lixiviação do herbicida em 5, 10, 15 e 20 t de palha ha-1 foi avaliada sob simulação de chuva de 2,5, 5, 10, 15, 20, 35 e 65 mm, um dia após a aplicação (DAPC) do segundo ensaio. As chuvas foram acumulativas, aplicando-se de 2,5 em 2,5 mm. No terceiro ensaio, foi avaliado o efeito dos intervalos de tempo entre a aplicação do herbicida e a primeira chuva na lixiviação do herbicida Dinamic (0, 1, 7, 15 e 30 dias) em 10 t de palha ha-1, em função das mesmas precipitações simuladas no segundo ensaio. Nos segundo e terceiro ensaios foi realizada uma simulação de 20 mm em intensidade de 115 mm h-¹ aos 7 e 14 dias após as primeiras chuvas (DAPC). Os resultados obtidos no segundo e terceiro ensaios foram ajustados pelo modelo de Mitscherlich (Y = a * (1-10-c * (b + x))). A quantificação do herbicida foi realizada por cromatografia líquida de alta eficiência. Quantidades de palha iguais ou superiores a 5 t ha-1 apresentam interceptação quase que total do herbicida no momento da aplicação, sendo nula a transposição. Com o aumento da quantidade de palha, ocorreu diminuição na quantidade de herbicida lixiviado pela ação da chuva simulada, principalmente para valores de 15 e 20 t de palha de cana-de-açúcar ha-1. Quanto maior o intervalo de tempo entre a aplicação do herbicida e a primeira chuva, menor é a lixiviação total do produto. em relação às chuvas aos 7 e 14 DAPC, no segundo e terceiro ensaios, foram observadas pequenas quantidades extraídas do herbicida, considerando-se que grande parte do amicarbazone foi lixiviada com as primeiras chuvas, que indicaram que os primeiros 20 mm de chuva simulada foram importantes para lixiviação da maior parte do amicarbazone (Dinamic) retido pela palha no momento da aplicação.

Sulfentrazone efficiency on Ipomoea hederifolia and Ipomoea quamoclit as influenced by rain and sugarcane straw

Objetivou-se neste trabalho avaliar o controle em pré-emergência de Ipomoea hederifolia e Ipomoea quamoclit pelo herbicida sulfentrazone em função do intervalo de tempo entre a aplicação e a ocorrência de chuva e da manutenção ou não de palha de cana-de-açúcar na superfície do solo. Três experimentos foram desenvolvidos: dois em casa de vegetação e um em campo. Nos experimentos em casa de vegetação, foram estudadas três doses de sulfentrazone (0, 0,6 e 0,9 kg ha-1) pulverizado em duas quantidades de palha na superfície do solo (0 e 10 t ha-1) e cinco intervalos de tempo entre a sua aplicação e a simulação de chuva (0, 20, 40, 60 e 90 dias). No experimento em campo, foram avaliados cinco tratamentos de herbicida (sulfentrazone a 0,6 e 0,9 kg ha-1; sulfentrazone + hexazinone a 0,6 + 0,25 kg ha-1; amicarbazone a 1,4 kg ha-1; e imazapic a 0,147 kg ha-1) e duas testemunhas sem aplicação. A manutenção ou não da palha de cana sobre o solo também foi estudada. em casa de vegetação, a aplicação de 0,6 kg ha-1 de sulfentrazone foi suficiente para o controle adequado de I. hederifolia e I. quamoclit num ambiente seco com até 90 dias sem chuva após a aplicação. Os 20 mm de chuva simulados após a aplicação do herbicida foram suficientes para remover o sulfentrazone da palha para o solo, pois o efeito biológico de controle de I. hederifolia e I. quamoclit não foi alterado. em campo, sem ou com a permanência de palha de cana sobre o solo, o sulfentrazone isolado (0,6 e 0,9 kg ha-1) ou em mistura com hexazinone (0,6 + 0,25 kg ha-1) foi eficaz para I. hederifolia e I. quamoclit, com resposta similar ou melhor que a do amicarbazone (1,4 kg ha-1) e imazapic (0,147 kg ha-1).