BOND STRENGTH DURABILITY of SELF-ETCHING ADHESIVES and RESIN CEMENTS TO DENTIN

Objectives: To evaluate the microtensile bond strength (mu TBS) of one-(Xeno III, Dentsply) and two-step (Tyrian-One Step Plus, Bisco) self-etching adhesive systems bonded to dentin and cemented to chemically cured (C&B Metabond) or light-cured paste of a dual-cure resin cement (Variolink II, Ivoclar) within a short (24 h) and long period of evaluation (90 days). Material and Methods: Forty recently extracted human molars had their roots removed and their occlusal dentin exposed and ground wet with 600-grit SiC paper. After application of one of the adhesives, the resin cement was applied to the bonded surface and a composite resin block was incrementally built up to a height of 5 mm (n = 10). The restored teeth were stored in distilled water at 37 C for 7 days. The teeth were then cut along two axes (x and y), producing beam-shaped specimens with 0.8 mm(2) cross-sectional area, which were subjected to mu TBS testing at a crosshead speed of 0.05 mm/min and stressed to failure after 24 h or 90 days of storage in water. The mu TBS data in MPa were subjected to three-way analysis of variance and Tukey's test (alpha = 0.05). Results: The interaction effect for all three factors was statistically significant (three-way ANOVA, p < 0.001). All eight experimental means (MPa) were compared by the Tukey's test (p < 0.05) and the following results were obtained: Tyrian-One Step Plus /C&B/24 h (22.4 +/- 7.3); Tyrian-One Step Plus /Variolink II/24 h (39.4 +/- 11.6); Xeno III/C&B/24 h (40.3 +/- 12.9); Xeno III/Variolink II/24 h (25.8 +/- 10.5); Tyrian-One Step Plus / C&B/90 d (22.1 +/- 12.8) Tyrian-One Step Plus/VariolinkII/90 d (24.2 +/- 14.2); Xeno III/C&B/90 d (27.0 +/- 13.5); Xeno III/Variolink II/90 d (33.0 +/- 8.9). Conclusions: Xeno III/Variolink II was the luting agent/adhesive combination that provided the most promising bond strength after 90 days of storage in water.

Bond strength and morphology of resin materials applied to the occlusal surface of primary molars

International Journal of Paediatric Dentistry 2012; 22: 435441 Background. Hydrophilic adhesives may be used as pit and fissure sealants (sealants), but there is concern about the ability of self-etching adhesives to bond sealants to enamel. Aim. To study the bond strength (BS) and morphology of adhesive systems used as sealants. Design. OptiBond FL, OptiBond All-in-One, combined OptiBond All-in-One + OptiBond FL adhesive, and Fluroshield were applied to the occlusal surfaces of 16 primary molars (n = 4). Teeth were stored in distilled water (24 h at 37 degrees C) and sectioned through the interface to obtain sticks (0.8 mm2) tested under a tensile load (0.5 mm/min). Failure modes were observed. Data were analysed by ANOVA and Tukeys tests (a = 5%). The morphology of 12 primary molars was examined in terms of the etching pattern and resin reproduction. Results. Differences in the BS were found (P = 0.001), with OptiBond FL showing the highest (36.84 +/- 5.7 MPa), Fluroshield (24.26 +/- 2.13 MPa) and OptiBond All-in-One (17.12 +/- 4.97 MPa) similar, and OptiBond All-in-One + OptiBond FL adhesive the lowest (9.8 +/- 2.94 MPA). OptiBond FL showed the best results in terms of morphology. Conclusion. Under the conditions of this study, OptiBond FL was the best material to be used for sealing.

Application of Nonisothermal Cure Kinetics to the Interaction of Poly(ethylene terephthalate) with Alkyd Resin Varnish

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Anodic Stripping Voltammetric Determination of Lead (II) and Cadmium (II) by Using a Carbon Nanotubes Paste Electrode Modified with Ion Exchange Synthetic Resin

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Knoop hardness of dental resin cements: Effect of veneering material and light curing methods

This study evaluated the Knoop hardness of one resin cement (dual-cure mode or light-cure mode) when illuminated directly or through restorative materials-ceramic (HeraCeram) or composite (Artglass)-by two light curing units. Light curing was carried out using a conventional quartz tungsten halogen (QTH) light source (XL2500) for 40 s, and a light emitting diodes (LED) light source (Ultrablue Is) for 40 s. Bovine incisors had their buccal faces flattened and hybridised. on these surfaces, a mould was seated and filled with cement. A disc of the veneering material (1.5 mm thickness) was positioned over this set for light curing. After storage (24 h/37 degrees C), samples (n = 10) were sectioned for hardness (KHN) measurements. Data were submitted to ANOVA and to Tukey's test (alpha = 0.05). In general, light curing with LED resulted in higher hardness values than QTH. Distinct cement behaviour was observed with different veneering material in association with different light curing units (LCUs). (C) 2006 Elsevier Ltd. All rights reserved.

Effect of the composite surface sealant application moment on marginal sealing of compactable composite resin restoration

An analysis was carried out to observe whether the application or not of a composite surface sealant (CSS), as well the moment for CSS application were able to reduce marginal microleakage in compactable composite resin restoration. All the preparations were restored with a compactable composite resin. The restored teeth were randomly assessed. G1 (control group): finished and polished; G2: finished, polished, etched and cover with CSS; G3: immediately after the restoration done the CSS was applied, then finished and polished; G4: CSS applied immediately after the restoration was done, the finished and polished, etched, and covered with CSS. The specimens were isolated with nail polish, thermocycled, immersed in aqueous solution of silver nitrate, and followed in a photo developing solution. The microleakage scores obtained from the occlusal and cervical walls were analyzed with the Kruskall-Wallis nonparametric test. No microleakage was found at the enamel margins. Comparing the microleakage scores at dentin/cementum margins (p < 0.05) it was found that G3 (p = 0.0162) and G4 (p = 0.0187) were able to reduce microleakage when compared with group G2. However the results were not statistically different from the control group. The application of CSS was not able to completely eliminate marginal microleakage at the dentin/cementum margins.

Effect of furfuryl alcohol addition on the cure of furfuryl alcohol resin used in the glassy carbon manufacture

Glassy carbon can be manufactured practically without pores, named Monolithic Vitreous Carbon (MVC) or presenting up to 98% in transport pore volume, foam form, denominated Reticulated Vitreous Carbon (RVC). The glassy carbon processing is affected by some processing parameters, among them it can be cited the resin viscosity. The present work involves the optimization of RVC manufacture by monitoring the polyurethane (PU) foam impregnation with furfuryl alcohol resin with different viscosity values, which were obtained by dilution of the resin with different amounts of furfuryl alcohol. The resin samples used in the PU impregnation were characterized by thermal and rheological analyses. These results were correlated with scanning electron microscopy observations and compression test results of the impregnated polyurethane foam. The results show that the rheological behavior of the resin has significant influence on the polymerization step, affecting the homogeneity of impregnated foam and, consequently, its final properties, mainly the mechanical one. The impregnated foam prepared with the furfuryl alcohol resin diluted with 10% of furfuryl alcohol (eta = 11.4 Pa s) showed higher compression values (0.26 MPa). (c) 2007 Wiley Periodicals, Inc.

Bond strength of resin modified glass ionomer cement to primary dentin after cutting with different bur types and dentin conditioning

The aim of this in vitro study was to evaluate the effect of different bur types and acid etching protocols on the shear bond strength (SBS) of a resin modified glass ionomer cement (RM-GIC) to primary dentin. Forty-eight clinically sound human primary molars were selected and randomly assigned to four groups (n=12). In G1, the lingual surface of the teeth was cut with a carbide bur until a 2.0-mm-diameter dentin area was exposed, followed by the application of RM-GIC (Vitremer - 3M/ESPE) prepared according to the manufacturer's instructions. The specimens of G2, received the same treatment of G1, however the dentin was conditioned with phosphoric acid. In groups G3 and G4 the same procedures of G1 and G2 were conducted respectively, nevertheless dentin cutting was made with a diamond bur. The specimens were stored in distilled water at 37 degrees C for 24h, and then tested in a universal testing machine. SBS. data were submitted to 2-way ANOVA (= 5%) and indicated that SBS values of RM-GIC bonded to primary dentin cut with different burs were not statistically different, but the specimens that were conditioned with phosphoric acid presented SBS values significantly higher that those without conditioning. To observe micromorphologic characteristics of the effects of dentin surface cut by diamond or carbide rotary instruments and conditioners treatment, some specimens were examined by scanning electron microscopy. Smear layer was present in all specimens regardless of the type of rotary instrument used for dentin cutting, and specimens etched with phosphoric acid presented more effective removal of smear layer. It was concluded that SBS of a RM-GIC to primary dentin was affected by the acid conditioning but the bur type had no influence.