975 resultados para ND-GDVO4 LASER


Relevância:

80.00% 80.00%

Publicador:

Resumo:

Formation of nanocrystalline TiN at low temperatures was demonstrated by combining Pulsed Laser Deposition (PLD) and ion implantation techniques. The Ti films of nominal thickness similar to 250 nm were deposited at a substrate temperature of 200 degrees C by ablating a high pure titanium target in UHV conditions using a nanosecond pulsed Nd:YAG laser operating at 1064 nm. These films were implanted with 100 keV N+ ions with fluence ranging from 1.0 x 10(16) ions/cm(2) to 1.0 x 10(17) ions/cm(2). The structural, compositional and morphological evolutions were tracked using Transmission Electron Microscopy (TEM), Secondary Ion Mass Spectrometry (SIMS) and Atomic Force Microscopy (AFM), respectively. TEM analysis revealed that the as-deposited titanium film is an fcc phase. With increasing ion fluence, its structure becomes amorphous phase before precipitation of nanocrystalline fcc TiN phase. Compositional depth profiles obtained from SIMS have shown the extent of nitrogen concentration gradient in the implantation zone. Both as-deposited and ion implanted films showed much higher hardness as compared to the bulk titanium. AFM studies revealed a gradual increase in surface roughness leading to surface patterning with increase in ion fluence.

Relevância:

80.00% 80.00%

Publicador:

Resumo:

Single crystals of the metalorganic nonlinear optical material zinc tris (thiourea) sulfate (ZTS) were grown from aqueous solution. The morphology of the crystals was indexed. The grown crystals were characterized by recording the powder X-ray diffraction pattern and by identifying the diffracting planes. Spectrophotometric studies on ZTS reveal that it has good transparency for the Nd: YAG laser fundamental wavelength. Differential thermal analysis of ZTS indicates that the material does not sublime before melting but decomposes immediately after melting. The defect content of the crystals was estimated using etching and X-ray topography. The mechanical hardness anisotropy was evaluated in the (100) plane, which indicates the presence of soft directions.

Relevância:

80.00% 80.00%

Publicador:

Resumo:

This paper reports, the Laser Induced Breakdown Spectroscopy (LIBS) studies and structure elucidation of compounds isolated from the fruit extract of Moringa oleifera and also deals with their possible effects on some bacterial strains viz. Staphylococcus aureus, Klebsiella pneumonia, Escherichia coli and Pseudomonas aeruginosa. The extract was found to be active against all four microorganisms used. Extent of inhibitory effect of extract was assessed at different concentrations of 25, 50, 75 mg/ml by measuring diameter of inhibition zone (DIZ). Our results clearly showed that the 75 mg/ml concentration of the extract had 14, 12 and 18 mm of the DIZ against Staphylococcus aureus, Klebsiella pneumonia and Pseudomonas aeruginosa and 14 mm with 50 mg/ml concentration against Escherichia coli. The results were compared with the standard antibiotic `ampicillin' of 1 mg/ml concentration. LIBS was recorded with high power pulsed laser beam from Nd: YAG Laser (Continuum Surelite III-10), focused on the surface of the material, which was in liquid form, to generate plasma on the surface of the sample. LIBS data clearly demonstrate the presence of trace elements, magnesium and iron, in high concentration in the extract. Whereas, from the phytochemical profile reveals the presence of two new compounds, S-ethyl-N-{4-[(alpha-L-rhamnosyloxy) benzyl]} thiocarbamate and 2-acetoxy {4-[(2',3',4'-tri-O-acetyl-alpha-L-rhamnosyloxy) benzyl]} acetonitrile as the major constituents. This study is the first report on synergetic effect of the phytoconstituents and certain set of elements present in their defined role in bacterial management against different bacterial strains.

Relevância:

80.00% 80.00%

Publicador:

Resumo:

ZnS quantum dots (QDs) of different sizes are synthesized by a simple chemical co-precipitation method at room temperature, by varying pH value of the reaction mixture. Samples are characterized by an X-ray diffractometer, transmission electron microscope, energy-dispersive X-ray analysis, etc. Linear optical properties, including UV-visible absorption and photoluminescence emission characteristics, of as-prepared QDs are measured. Size dependent nonlinear optical property, such as second harmonic generation (SHG) of 1064 nm Nd:YAG laser fundamental radiation in the synthesized ZnS QDs, is reported for the first time, to the best of our knowledge, by using the standard Kurtz-Perry powder method. In not to study the possibility of the synthesized ZnS QDs in different device applications ZnS/PMMA (polymethylmethacrylate) nanocomposites are also synthesized. The presence of weak chemical interaction between the polymer matrix and ZnS QDs is confirmed by Fourier transform infrared spectroscopy. Thermal properties of the nanocomposites are studied by differential scanning calorimetry and thermo-gravimetric analysis techniques, which show that the composites are stable up to similar to 300 degrees C temperature. (C) 2013 Elsevier B.V. All rights reserved.

Relevância:

80.00% 80.00%

Publicador:

Resumo:

Transparent glasses in CaO-Bi2O3-B2O3 system were fabricated via the conventional melt-quenching technique. X-ray powder diffraction (XRD) and differential thermal analysis (DTA) carried out on the as-quenched samples confirmed their amorphous and glassy nature respectively. The surface crystallization behaviour of these glasses with and without ultrasonic surface treatment (UST) was monitored using XRD, optical microscopy and scanning electron microscopy (SEM). The volume fraction, depth of crystallization and the (001) orientation factor for the heat treated samples with and without UST were compared. The ultrasonically-treated samples on subsequent heat treatment were found to crystallize at lower temperatures associated with the highest degree of orientation factor (0.95) in contrast with those of non-UST samples. These surface crystallized glasses were found to exhibit nonlinear optical behaviour emitting green light (532 nm) when they were exposed to the infrared radiation (1064 nm) using Nd:YAG laser.

Relevância:

80.00% 80.00%

Publicador:

Resumo:

Nonlinear optical properties (NLO) of a graphene oxide-silver (GO-Ag) nanocomposite have been investigated by the Z-scan setup at Q-switched Nd:YAG laser second harmonic radiation i.e., at 532 nm excitation in a nanosecond regime. A noteworthy enhancement in the NLO properties in the GO-Ag nanocomposite has been reported in comparison with those of the synthesized GO nanosheet. The extracted value of third order nonlinear susceptibility (chi(3)), at a peak intensity of I-0 = 0.2 GW cm(-2), for GO-Ag has been found to be 2.8 times larger than that of GO. The enhancement in NLO properties in the GO-Ag nanocomposite may be attributed to the complex energy band structures formed during the synthesis which promote resonant transition to the conduction band via surface plasmon resonance (SPR) at low laser intensities and excited state transition (ESA) to the conduction band of GO at higher intensities. Along with this photogenerated charge carriers in the conduction band of silver or the increase in defect states during the formation of the GO-Ag nanocomposite may contribute to ESA. Open aperture Z-scan measurement indicates reverse saturable absorption (RSA) behavior of the synthesized nanocomposite which is a clear indication of the optical limiting (OL) ability of the nanocomposite.

Relevância:

80.00% 80.00%

Publicador:

Resumo:

An Nd:glass laser pulse (18 ns, 1.38 J) is focused in a tiny area of about 100-mum diam under ambient conditions to produce micro-shock waves. The laser is focused above a planar surface with a typical standoff distance of about 4 mm, The laser energy is focused inside a supersonic circular jet of carbon dioxide gas produced by a nozzle with internal diameter of 2.9 mm and external diameter of 8 mm, Nominal value of the Mach number of the jet is around 2 with the corresponding pressure ratio of 7.5 (stagnation pressure/static pressure at the exit of the nozzle), The interaction process of the micro-shock wave generated inside the supersonic jet with the plane wall is investigated using double-pulse holographic interferometry. A strong surface vortex field with subsequent generation of a side jet propagating outward along the plane wail is observed. The interaction of the micro-shock wave with the cellular structure of the supersonic jet does not seem to influence the near surface features of the flowfield. The development of the coherent structures near the nozzle exit due to the upstream propagation of pressure waves seems to be affected by the outward propagating micro-shock wave. Mach reflection is observed when the micro-shock wave interacts with the plane wall at a standoff distance of 4 mm, The Mach stem is slightly deflected, indicating strong boundary-layer and viscous effects near the wall. The interaction process is also simulated numerically using an axisymmetric transient laminar Navier-Stokes solver. Qualitative agreement between experimental and numerical results is good.

Relevância:

80.00% 80.00%

Publicador:

Resumo:

实验研究了连续波Nd:YAG激光焊接速度、侧吹保护气流量和离焦量等参量对激光穿透焊接K418和42CrMo焊缝成形的影响。结果表明,K418与42CrMo激光穿透焊接有X形和T形两种典型的焊缝形貌,且焊缝形貌是不对称的。随着焊接速度的提高,焊接线能量降低,焊缝尺寸变小,且焊缝上部尺寸变化比下部尺寸变化慢,焊缝形貌由X形过渡到T形。当离焦量在瑞利长度范围内时,焊缝正面宽度变化很小;当离焦量超出瑞利长度范围时,在足够高的激光功率密度下,焊缝正面宽度快速增加。在激光功率为3kW,侧吹保护气角度为35°条件下,通过优化焊接速度、侧吹保护气流量和离焦量等参量可以得到最佳焊缝质量。

Relevância:

80.00% 80.00%

Publicador:

Resumo:

基于目前国内规模最大的激光驱动器——“神光Ⅱ”八路基频光已经实现功率平衡运行,通过改变其中若干路三倍频系统各调谐量的偏离,对输出三倍频波形进行束与束之间的横向对比研究.研究发现,对于Ⅱ类-Ⅱ类偏振失配三倍频系统,在影响转换效率的三个调谐量中,偏振分配角失配△θp,对三倍频波形影响最大;在入射基频功率密度约为1.0GW/cm^2情况下,当三倍频系统三个调谐量都处在最佳匹配时,三倍频波形半峰全宽τ最小。研究工作为最终实现“神光Ⅱ”八路光束三倍频功率平衡输出提供了晶体调试的方法。

Relevância:

80.00% 80.00%

Publicador:

Resumo:

研究了平均功率超过30 W的稳定高效全固态绿光激光器,分析得出影响全固态腔内倍频激光器倍频效率和输出稳定性的主要因素是倍频晶体局部温升造成的相位失配和热透镜效应,采用温度梯度补偿控温法对大尺寸倍频晶体进行温度控制,降低激光器工作中倍频晶体内外温度梯度从而有效地克服因晶体局部温升造成的倍频相位匹配角失配和热透镜效应。采用三条60 W的半导体激光二极管阵列板条侧面抽运Nd:YAG激光增益介质棒,采用声光调Q,平凹直腔和腔内倍频结构配合温度梯度补偿控温法对大尺寸倍频晶体进行温度控制,得到了稳定高效的532 nm

Relevância:

80.00% 80.00%

Publicador:

Resumo:

The three-photon absorption effect (3PA) of two novel symmetrical charge transfer fluorene-based molecules (abbreviated as BASF and BMOSF) has been determined by using a Q-switched Nd:YAG laser pumped with 38 ps pulses at 1064 nm in DMF. The measured 3PA cross-sections are 84 x 10(-78) and 114 x 10(-78) cm(6) s(2), respectively. The geometries and electronic excitations of these two molecules are systematically studied by PM3 and ZINDO/S methods. The relationships between 3PA cross-sections and intramolecular charge transfer are discussed micromechanically. The experimental and theoretical results have shown that the larger intramolecular charge transfer, which was characterized by the charge density difference between the ground state (SO) and the first excited state (S-I), the greater enhancement of the 3PA cross-sections. (c) 2005 Elsevier B.V. All rights reserved.

Relevância:

80.00% 80.00%

Publicador:

Resumo:

Two novel symmetrical charge transfer fluorene derivatives (abbreviated as BCZF and BVCZF) with carbazole end-group as the donor moieties have been synthesized. Three-photon absorption cross-sections of these two compounds have been determined by using a Q-switched Nd:YAG laser pumped with 38 ps pulses at 1064 nm in DMF. The measured 3PA cross-sections are 140 x 10(-78) and 400 x 10(-78) cm(6) s(2) for BCZF and BVCZF, respectively. The geometries, electronic structures and electronic spectra of these two compounds are systematically studied by AM1 and ZINDO/S methods. On the basis of correct UV-vis spectra, the influence of different molecular structure on three-photon absorption cross-sections is discussed micromechanically. (C) 2005 Elsevier B.V. All rights reserved.

Relevância:

80.00% 80.00%

Publicador:

Resumo:

Three-photon absorption (3PA) of two fluorene-based molecules with D-pi-D structural motifs (abbreviated as BPAF and BCZF) has been determined by using a Q-switched Nd: YAG laser pumped with 38 ps pulses at 1064 nm in DMF. The measured 3PA cross-sections are 222 and 140 x 10(-78) cm(6) s(2) for BPAF and BCZF, respectively. AM1 calculations show that attaching different donors changes the charge density distribution of the fluorene skeleton, and it is observed that the 3PA cross-section can be enhanced with increasing intramolecular charge transfer character, measured by the parameter Delta p(1)/Delta p(2)/Delta p(1)'. (c) 2005 Elsevier B.V. All fights reserved.

Relevância:

80.00% 80.00%

Publicador:

Resumo:

The three-photon absorption (3PA) properties of two thiophene-fluorene derivatives (abbreviated as MOTFTBr and ATFTBr) have been determined by using a Q-switched Nd:YAG laser pumped wish 38ps pulses at 1064nm in DMF. The measured 3PA cross-sections are 152x10(-78)cm(6)s(2) and 139x10(-78)cm(6)s(2), respectively. The optimized structures were obtained by AM1 calculations and the results indicate that these two molecules show nonplanar structures, and attaching different donors has different effects on the molecular structure. The charge density distributions during the excitation were also systematically studied by using AM1 method. In addition, an obvious optical power limiting effect induced by 3PA has been demonstrated for both derivatives.

Relevância:

80.00% 80.00%

Publicador:

Resumo:

报道了利用声光振幅调制锁模的方法,在激光二极管端面抽运Nd:YVO4激光器上获得320MHz高重复频率脉冲列的实验结果。实验采用平一平腔结构,腔长452mm,耦合输出镜透过率为3.6%。所用声光介质为熔融石英晶体,以铌酸锂作换能器,在驱动功率4.5W时,对1064nm波长衍射效率为50,相应的调制深度为0.31。在最佳锁模状态下,激光二极管抽运功率为3.5W,此时激光平均输出功率为15mw。示波器记录脉冲宽度680ps,实测光束质量因子M^2小于1.5。并在实验基础上对激光器工作的稳定性进行了分析,结果表