Preparation of highly conductive, self-assembled gold/polyaniline nanocables and polyaniline nanotubes

One-dimensional gold/polyaniline (Au/PANI-CSA) coaxial nanocables with an average diameter of 5060 nm and lengths of more than 1 mu m were successfully synthesized by reacting aniline monomer with chlorauric acid (HAuCl4) through a self-assembly process in the presence Of D-camphor-10-sulfonic acid (CSA), which acts as both a dopant and surfactant. It was found that the formation probability and the size of the Au/PANI-CSA nanocables depends on the molar ratio of aniline to HAuCl4 and the concentration of CSA, respectively. A synergistic growth mechanism was proposed to interpret the formation of the Au/PANI-CSA nanocables. The directly measured conductivity of a single gold/polyaniline nanocable was found to be high (approximate to 77.2S cm(-1)). Hollow PANI-CSA nanotubes, with an average diameter of 50-60 nm, were also obtained successfully by dissolving the Au nanowire core of the Au/PANI-CSA nanocables.

Synthesis of highly faceted multiply twinned gold nanocrystals stabilized by polyoxometalates

A novel and facile chemical synthesis of highly faceted multiply twinned gold nanocrystals is reported. The gold nanocrystals are hexagonal in transmission electron microscopy and icosahedral in scanning electron microscopy. Phosphotungstic acid (PTA), which was previously reduced, serves as a reductant and stabilizer for the synthesis of gold nanocrystals. The PTA-gold nanocomposites are quite stable in aqueous solutions, and electrochemically active towards the hydrogen evolution reaction.

A new type of highly efficient luminescent material - The system Al2O3-B2O3 containing Ce3+ and Tb3+ ions

The system Al2O3-B2O3 containing Ce3+ and Tb3+ ions was investigated for the first time. It was found that certain compositions give rise to a new highly efficient green luminescent material.

Nanostructure and mechanical measurement of highly oriented lamellae of melt-drawn HDPE by scanning probe microscopy

Scanning probe microscopy was used to simultaneously determine the molecular chain structure and intrinsic mechanical properties, including anisotropic elastic modulus and friction, for lamellae of highly oriented high-density polyethylene (HDPE) obtained by the melt-drawn method. The molecular-scale image of the highly oriented lamellae by friction force microscopy (FFM) clearly shows that the molecular chains are aligned parallel to the drawing direction, and the periodicities along and perpendicular to the drawing direction are 0.26 and 0.50 nm, respectively. The results indicate that the exposed planes of the lamellae resulting from the melt-drawn method are (200), which is consistent with results of transmission electron microscopy and electron diffraction. Because of the high degree of anisotropy in the sample, coming from alignment of the molecular chains along the drawing direction, the measured friction force, F, determined by FFM is strongly dependent on the angle, theta, between the scanning direction and the chain axis. The force increases as theta is increased from 0 degrees (i.e., parallel to the chain axis) to 90 degrees (i.e., perpendicular to the chain axis). The structural anisotropy was also found to strongly influence the measurements of the transverse chain modulus of the polymer by the nanoindentation technique. The measured value of 13.8 GPa with transverse modulus was larger than the value 4.3 GPa determined by wide-angle X-ray diffraction, which we attributed to anisotropic deformation of the lamellae during nanoindentation measurements that was not accounted for by the elastic treatment we adopted from Oliver and Pharr. The present approach using scanning probe microscopy has the advantage that direct correlations between the nanostructure, nanotribology, and nanomechanical properties of oriented samples can be determined simultaneously and simply.

Some unusual features of highly oriented pyrolytic graphite observed by electrochemical scanning tunneling microscopy

Highly oriented pyrolytic graphite (HOPG) is the substrate often used in scanning tunneling microscopy (STM). It is well known that STM images of the basal plane of HOPG show some unusual structural patterns. In this letter, we present in situ STM images of some unusual features on HOPG in solutions, including normal or abnormal chain-like features and hexagonal or oblique superperiodic structures. These features emerge both next to and apart from the step of HOPG.

EFFECTS OF ANODIC-OXIDATION ON THE SURFACE-STRUCTURE OF HIGHLY ORIENTED PYROLYTIC-GRAPHITE REVEALED BY IN-SITU ELECTROCHEMICAL SCANNING-TUNNELING-MICROSCOPY IN H2SO4 SOLUTION

Effects of the potential of anodic oxidation and of potential cycling on the surface structure of a highly oriented pyrolytic graphite (HOPG) electrode were observed by in situ electrochemical scanning tunnelling microscopy (ECSTM) in dilute H2SO4 solution with atomic resolution. With potential cycling between -0.1 V and 1.8 V vs. Ag/AgCl (sat. KCI), some atoms on the top layer of HOPG protrude out of the base plane, and the graphite lattice of these protrusions is still intact but is strained and expanded. With further potential cycling, some protrusions coalesced and some grew larger, and an anomalous superperiodic feature was observed (spacing 90 Angstrom with a rotation 30 degrees relative to atomic corrugations) which superimposed on the atomic corrugation of HOPG. On the topmost of these protrusions, some atoms form oxides and others are still resolved by the ECSTM image. With potential cycling between -0.1 V and + 2.0 V vs. Ag/AgCl (sat. KCl), damage to freshly cleaved HOPG surface is more serious and fast, some ridges are observed, the atomic structure of the HOPG surface is partially and then completely damaged due to the formation of oxide. We also found that anodic oxidation occurred nonuniformly on the surface of HOPG near defects during potential cycling.

EPITAXIAL BEHAVIOR OF HDPE ON THE BOUNDARY OF HIGHLY ORIENTED IPP SUBSTRATES

The epitaxial crystallization behavior of high-density polyethylene on the boundary of highly oriented isotactic polypropylene (iPP) substrates has been investigated by means of atomic force microscopy (AFM) and transmission electron microscopy (TEM). The results obtained from AFM and TEM indicate that the epitaxial nucleation of HDPE on the highly oriented iPP substrates occurs earlier than that in the pure HDPE phase, i.e., homogeneous nucleation. Therefore the epitaxially grown HDPE lamellae can grow across the boundary of the iPP substrate into the HDPE spherulitic phase with the epitaxial orientation relationship remaining.

Surface structure and reaction performances of highly dispersed and supported bimetallic catalysts

Surface structures of Pt-Sn and Pt-Fe bimetallic catalysts have been investigated by means of Mossbauer spectroscopy, Pt-L-III -edge EXAFS and H-2-adsorption. The results showed that the second component, such as Sn or Fe, remained in the oxidative state and dispersed on the gamma-Al2O3 surface after reduction, while Pt was completely reduced to the metallic state and dispersed on either the metal oxide surface or the gamma-Al2O3 surface. By correlating the distribution of Pt species on different surfaces with the reaction and adsorption performances, it is proposed that two kinds of active Pt species existed on the surfaces of both catalysts, named M-1 sites and M-2 sites. M-1 sites are the sites in which Pr directly anchored on the gamma-Al2O3 surface, while M-2 sites are those in which Pt anchored on the metal oxide surface. M-1 sites are favorable for low temperature H-2 adsorption, and responsible for the hydrogenolysis reaction and carbon deposition, while M-2 sites which adsorb more H-2 at higher temperature, are more resistant to the deactivation due to less carbon deposition, and provide major contribution to the dehydrogenation reaction.

Direct synthesis of highly ordered Fe-SBA-15 mesoporous materials under weak acidic conditions

Iron-substituted SBA-15 (Fe-SBA-15) materials have been synthesized via a simple direct hydrothermal method under weak acidic conditions. The powder X-ray diffraction (XRD), NZ sorption and transmission electron microscopy (TEM) characterizations show that the resultant materials have well-ordered hexagonal meso-structures. The diffused reflectance UV-vis and UV resonance Raman spectroscopy characterizations show that most of the iron ions exist as isolated framework species for calcined materials when the Fe/Si molar ratios are below 0.01 in the gel. The presence of iron species also has significant salt effects that can greatly improve the ordering of the mesoporous structure. Different iron species including isolated framework iron species, extraframework iron clusters and iron oxides are formed selectively by adjusting the pH values of the synthesis solutions and Fe/Si molar ratios. (c) 2005 Elsevier Inc. All rights reserved.