Terminology of metal–organic frameworks and coordination polymers (IUPAC Recommendations 2013)

A set of terms, definitions, and recommendations is provided for use in the classification of coordination polymers, networks, and metal–organic frameworks (MOFs). A hierarchical terminology is recommended in which the most general term is coordination polymer. Coordination networks are a subset of coordination polymers and MOFs a further subset of coordination networks. One of the criteria an MOF needs to fulfill is that it contains potential voids, but no physical measurements of porosity or other properties are demanded per se. The use of topology and topology descriptors to enhance the description of crystal structures of MOFs and 3D-coordination polymers is furthermore strongly recommended.

A treatise on chemistry,

Vol. I: 1st edition, 1877; 5th edition, 1920. Vol. II: 1st edition, 1878; 6th edition, 1923.

Molten carbonate fuel cells

Over the past 12 months, developments in both porous and non-porous materials for the molten carbonate fuel cell (MCFC) should lead to significantly increased stack lifetimes. Lithium-sodium carbonate is emerging as the material of choice for the electrolyte and has been tested in a 10 kW scale stack. Several new cathode materials, with lower dissolution rates in the electrolyte than state-of-the-art NiO, have been tested. However a significant finding is that the dissolution rate of NiO can also be reduced by an order of magnitude by preparing it as a functional nanomaterial. Although most developers continue to use nickel anodes, recent tests with ceramic oxides anodes open up the prospects of reduced carbon deposition and future cells running directly on dry methane. (c) 2004 Published by Elsevier Ltd.

The ability of current gas monitoring techniques to adequately detect spontaneous combustion

This paper investigates the adequacy of current gas monitoring techniques to adequately detect spontaneous combustion in underground coalmines. Despite being in the 21st century spontaneous combustion continues to occur in underground coalmines sometimes being detected only at a very advanced stage. Control of the incident is often then very expensive and time consuming. The adequacy needs to be assessed not only from the point of view of the analysis technique be it tube bundle, gas chromatograph or real time sensor but also the number, location and sampling frequency of the monitoring locations. Recommendations are made to optimise monitoring processes and recognise limitations of current techniques.

Direct femtosecond laser inscription in transparent dielectrics

Since 1996 direct femtosecond inscription in transparent dielectrics has become the subject of intensive research. This enabling technology significantly expands the technological boundaries for direct fabrication of 3D structures in a wide variety of materials. It allows modification of non-photosensitive materials, which opens the door to numerous practical applications. In this work we explored the direct femtosecond inscription of waveguides and demonstrated at least one order of magnitude enhancement in the most critical parameter - the induced contrast of the refractive index in a standard borosilicate optical glass. A record high induced refractive contrast of 2.5×10-2 is demonstrated. The waveguides fabricated possess one of the lowest losses, approaching level of Fresnel reflection losses at the glassair interface. High refractive index contrast allows the fabrication of curvilinear waveguides with low bend losses. We also demonstrated the optimisation of the inscription regimes in BK7 glass over a broad range of experimental parameters and observed a counter-intuitive increase of the induced refractive index contrast with increasing translation speed of a sample. Examples of inscription in a number of transparent dielectrics hosts using high repetition rate fs laser system (both glasses and crystals) are also presented. Sub-wavelength scale periodic inscription inside any material often demands supercritical propagation regimes, when pulse peak power is more than the critical power for selffocusing, sometimes several times higher than the critical power. For a sub-critical regime, when the pulse peak power is less than the critical power for self-focusing, we derive analytic expressions for Gaussian beam focusing in the presence of Kerr non-linearity as well as for a number of other beam shapes commonly used in experiments, including astigmatic and ring-shaped ones. In the part devoted to the fabrication of periodic structures, we report on recent development of our point-by-point method, demonstrating the shortest periodic perturbation created in the bulk of a pure fused silica sample, by using third harmonics (? =267 nm) of fundamental laser frequency (? =800 nm) and 1 kHz femtosecond laser system. To overcome the fundamental limitations of the point-by-point method we suggested and experimentally demonstrated the micro-holographic inscription method, which is based on using the combination of a diffractive optical element and standard micro-objectives. Sub-500 nm periodic structures with a much higher aspect ratio were demonstrated. From the applications point of view, we demonstrate examples of photonics devices by direct femtosecond fabrication method, including various vectorial bend-sensors fabricated in standard optical fibres, as well as a highly birefringent long-period gratings by direct modulation method. To address the intrinsic limitations of femtosecond inscription at very shallow depths we suggested the hybrid mask-less lithography method. The method is based on precision ablation of a thin metal layer deposited on the surface of the sample to create a mask. After that an ion-exchange process in the melt of Ag-containing salts allows quick and low-cost fabrication of shallow waveguides and other components of integrated optics. This approach covers the gap in direct fs inscription of shallow waveguide. Perspectives and future developments of direct femtosecond micro-fabrication are also discussed.

Spectroscopic studies of field-induced electron emission from isolated microstructures

A detailed investigation has been undertaken into the field induced electron emission (FIEE) mechanism that occurs at microscopically localised `sites' on uncoated and dielectric coated metallic electrodes. These processes have been investigated using two dedicated experimental systems that were developed for this study. The first is a novel combined photo/field emission microscope, which employs a UV source to stimulate photo-electrons from the sample surface in order to generate a topographical image. This system utilises an electrostatic lens column to provide identical optical properties under the different operating conditions required for purely topographical and combined photo/field imaging. The system has been demonstrated to have a resolution approaching 1m. Emission images have been obtained from carbon emission sites using this system to reveal that emission may occur from the edge triple junction or from the bulk of the carbon particle. An existing UHV electron spectrometer has been extensively rebuilt to incorporate a computer control and data acquisition system, improved sample handling and manipulation and a specimen heating stage. Details are given of a comprehensive study into the effects of sample heating on the emission process under conditions of both bulk and transient heating. Similar studies were also performed under conditions of both zero and high applied field. These show that the properties of emission sites are strongly temperature and field dependent thus indicating that the emission process is `non-metallic' in nature. The results have been shown to be consistent with an existing hot electron emission model.

Mechanisms of convective drying in thick beds of solids

The literature on heat and mass transfer mechanisms in the convective drying of thick beds of solids has been critically reviewed. Related mathematical models of heat transfer are also considered. Experimental and theoretical studies were made of the temperature distribution within beds, and of drying rates, with various materials undergoing convective drying. The experimental work covered thick beds of hygroscopic and non-hygroscopic materials (glass beads of different diameters, polystyrene pellets, activated alumina and wood powder) at air temperatures of 54°C to 84°C. Tests were carried out in a laboratory drying apparatus comprising a wind tunnel through which the air, of controlled temperature and humidity, was passed over a sample suspended from a balance. Thermocouples were inserted at different depths within the sample bed. The temperature distribution profiles for both hygroscopic and non-hygroscopic beds exhibited a clear difference between the temperatures at the surface and bottom during the constant rate period. An effective method was introduced for predicting the critical moisture content. During the falling rate the profiles showed the existence of a receding evaporation plane; this divided the system into a hotter dry zone in the upper section and a wet zone near the bottom. A graphical procedure was established to predict accurately the position of the receding evaporation front at any time. A new mathematical model, based on the receding evaporation front phenomenon, was proposed to predict temperature distributions throughout a bed during drying. Good agreement was obtained when the model was validated by comparing its predictions with experimental data. The model was also able to predict the duration of each drying stage. In experiments using sample trays of different diameters, the drying rate was found to increase with a decrease in the effective length of the bed surface. During the constant rate period with trays of a small effective length, i.e. less than 0.08 m, an 'inversion' in temperature distribution occurred in the bed; the bottom temperature increased and became greater than that of the surface. Experimental measurements were verified in several ways to ensure this phenomenon was real. Theoretical explanations are given for both the effective length and temperature inversion phenomena.

Nonmetallic inclusion modification and its effect on the final properties of a linepipe steel

Five linepipe type steels were produced in order to study the effect of calcium and magnesium injection on their final properties. Two of these steels were at the extremes of the sulphide range i.e. 0.003 and 0.017% sulphur with no injection attempted; thereby, providing standards to compare with the injected steels. The oxygen level varied from 21 to 63 p.p.m. The cast ingots were controlled-rolled and isothermally rolled in order to study the deformation characteristics of the residual non-metallic inclusions. The structure and cleanliness of these steels was evaluated metallographically using the light microscope, SEM, and image analysis and the results related to their Charpy toughness and HIC resistance. Increasing sulphur levels decreased final properties of the steel. In the untreated state, with as little as 0.003% sulphur, test orientation was highly influential. Modification of sulphur bearing steels was achieved with low modifying element to sulphur ratios provided that the oxygen content was very low. Injection of calcium into steel caused interaction with oxide and sulphide inclusions which was biased toward oxide reduction relative to sulphur removal. Magnesium again reduced oxides and appeared to be linked with aluminia containing inclusions in the final product. It produced improved toughness values relative to a similar sulphur containing calcium treated steel. The results of this work could be extended to establish the mechanism of inclusion modification with magnesium additions to sulphur bearing steels.

Biological interactions with synthetic polymers

Anchorage dependent cell culture is a useful model for investigating the interface that becomes established when a synthetic polymer is placed in contact with a biological system. The primary aim of this interdisciplinary study was to systematically investigate a number of properties that were already considered to have an influence on cell behaviour and thereby establish the extent of their importance. It is envisaged that investigations such as these will not only further the understanding of the mechanisms that affect cell adhesion but may ultimately lead to the development of improved biomaterials. In this study, surface analysis of materials was carried out in parallel with culture studies using fibroblast cells. Polarity, in it's ability to undergo hydrogen bonding (eg with water and proteins), had an important affect on cell behaviour, although structural arrangement and crystallinity were not found to exert any marked influence. In addition, the extent of oxidation that had occurred during the process of manufacture of substrates was also important. The treatment of polystyrene with a selected series of acids and gas plasmas confirmed the importance of polarity, structural groups and surface charge and it was shown that this polymer was not unique among `hydrophobic' materials in it's inability to support cell adhesion. The individual water structuring groups within hydrogel polymers were also observed to have controlling effects on cell behaviour. An overall view of the biological response to both hydrogel and non-hydrogel materials highlighted the importance of surface oxidation, polarity, water structuring groups and surface charge. Initial steps were also taken to analyse foetal calf serum, which is widely used to supplement cell culture media. Using an array of analytical techniques, further experiments were carried out to observe any possible differences in the amounts of lipids and calcium that become deposited to tissue culture and bacteriological grade plastic under cell culture conditions.

Effect of calcium source on structure and properties of sol-gel derived bioactive glasses

The aim was to determine the most effective calcium precursor for synthesis of sol-gel hybrids and for improving homogeneity of sol-gel bioactive glasses. Sol-gel derived bioactive calcium silicate glasses are one of the most promising materials for bone regeneration. Inorganic/organic hybrid materials, which are synthesized by incorporating a polymer into the sol-gel process, have also recently been produced to improve toughness. Calcium nitrate is conventionally used as the calcium source, but it has several disadvantages. Calcium nitrate causes inhomogeneity by forming calcium-rich regions, and it requires high temperature treatment (>400 C) for calcium to be incorporated into the silicate network. Nitrates are also toxic and need to be burnt off. Calcium nitrate therefore cannot be used in the synthesis of hybrids as the highest temperature used in the process is typically 40-60 C. Therefore, a different precursor is needed that can incorporate calcium into the silica network and enhance the homogeneity of the glasses at low (room) temperature. In this work, calcium methoxyethoxide (CME) was used to synthesize sol-gel bioactive glasses with a range of final processing temperatures from 60 to 800 C. Comparison is made between the use of CME and calcium chloride and calcium nitrate. Using advanced probe techniques, the temperature at which Ca is incorporated into the network was identified for 70S30C (70 mol % SiO, 30 mol % CaO) for each of the calcium precursors. When CaCl was used, the Ca did not seem to enter the network at any of the temperatures used. In contrast, Ca from CME entered the silica network at room temperature, as confirmed by X-ray diffraction, Si magic angle spinning nuclear magnetic resonance spectroscopy, and dissolution studies. CME should be used in preference to calcium salts for hybrid synthesis and may improve homogeneity of sol-gel glasses.