Filmes de titânio-silício preparados por spin e dip-coating

The conditions for the preparation of luminescent materials, consisting of Eu3+ ions entrapped in a titanium matrix, in the forma of a thin film, using the sol-gel process, are described. The films were obtained from sols prepared with TEOS and TEOT, in the presence of acetylacetone as the hidrolysis-retarding agent, using the dip-coating and spin-coating techniques. The influence of these techniques on the films based on titanium and silicon are presented. The Eu3+ was used as a luminescent probe. The films have been characterized by luminescence, reflection and transmittance. The thickness of the films could be related to the preparation procedure. Transparent thin films have been prepared by dip-coating technique.

Functionalized silica synthesized by sol-gel process

This work considers some aspects of the chemistry involved in the preparation and description of silicon oxide functionalized by sol-gel process. In this work we studied the synthesis and measured the properties of silicon oxide functionalized with 3-chloropropyl, through a sol-gel process. Thermogravimetic analysis, infrared spectra, and elemental analyses were measured. The samples were prepared in the following proportions of tetraethylorthosilicate (TEOS): 3-chloropropyl trimethoxisilane molar ratio: 1:0, 1:1, 2:1, 3:1 and 4:1. The thermogravimetric data for the resulting materials established the 'minimum formulae' 2:0, 3:1, 4.1, 7:1 and 11:1, respectively. As expected, the relative amount of water is inversely proportional to the presence of propyl groups. Infrared data show Si-C and -CH2-vibration modes at 1250 to 1280 and 2920 to 2940 cm(-1), respectively. Thermogravimetric data and infrared spectra showed that inorganic polymers contained organic polymers. (C) 1999 Elsevier B.V. B.V. All rights reserved.

Preparation and characterization of spherical silica-porphyrin catalysts obtained by the sol-gel methodology

This work describes the synthesis of a first-generation iron porphyrin catalyst entrapped in a silica matrix by the sol-gel route, leading to spherical particles. The catalyst was synthesized by the method of Stober, through hydrolysis and condensation of the alkoxysilane TEOS in a mixture of alcohol, water and ammonia, in the presence of the iron porphyrin Fe(TPP)Cl. The relation between particle morphology and catalytic activity of the different Fe(TPP)-SiO2, obtained using different H2O/silane molar ratios and ammonia concentrations in the xerogel syntheses, was studied.The obtained catalysts were characterized by UV-vis spectroscopy, NMR Si-29. thermogravimetric analysis and transmission electron microscopy. Their ability to catalyze (Z)-cyclooctene epoxidation and cyclohexane oxidation was tested using iodosylbenzene as oxygen donor; the oxidation products were analyzed by gas chromatography and the catalysts obtained in a form of particles spherical and monodispersed showed to be a promising catalytic system for selective oxidation. (c) 2005 Elsevier B.V. All rights reserved.

Mass fractal characteristics of sonogels prepared from sonohydrolysis of tetraethoxysilane with additions of dimethylformamide

Wet silica gels with similar to 1.4 x 10(-3) mol SiO2/cm(3) and similar to 90 vol.% liquid phase were prepared from the sonohydrolysis of tetraethoxysilane (TEOS) with different additions of dimethylformamide (DMF). Aerogels were obtained by CO2 supercritical extraction. The samples were studied mainly by small-angle X-ray scattering (SAXS) and nitrogen adsorption. Wet gels exhibit a mass fractal structure with fractal dimension D increasing from 2.23 to 2.35 and characteristic length xi decreasing from similar to 9.4 nm to similar to 5.1 nm, as the DMF/TEOS molar ratio is increased from 0 to 4. The supercritical process apparently eliminates some porosity, shortening the fractality domain in the mesopore region and developing an apparent surface/mass fractal (with correlated mass fractal dimension D-m similar to 2.6 and surface fractal dimension D-s similar to 2.3) in the micropore region. The fundamental role of the DMF addition on the structure of the aerogels is to diminish the porosity and the pore mean size, without, however, modify substantially the specific surface area and the average size of the silica particle of the solid network. (c) 2006 Elsevier B.V. All rights reserved.

A nonisothermal study of the kinetics of the nanoporosity elimination in sonogels-derived silica xerogels

A nonisothermal study of the kinetics of the nanoporosity elimination in monolithic silica xerogels, prepared from acid and ultrasound catalyzed hydrolysis of tetraethylortosilicate (TEOS), has been carried out by means of in situ linear shrinkage measurements performed with different heating rates. The study could be applied up to almost alpha similar to 0.6 of the volume fraction alpha of eliminated pores. The activation energy was found increasing from about 3.2 x 10(2) kJ/mol for alpha similar to 0.06 up to about 4.4 x 10(2) kJ/mol for alpha. similar to 0.44. The sintering process accompanying the nanopore elimination in this set of xerogels is in agreement with a viscous flux sintering process with the hydroxyl content diminishing with the volume fraction of eliminated pores. All the volume fraction of eliminated pores versus temperature (T) curves can be matched onto a unique curve with an appropriate rescaling of the T axis, independent of the heating rate. This scaling property suggests that the path of sintering seems the same, regardless of the heating rate; the difference is that the rate is faster at higher temperature.

Laserlike emission from silica inverse opals infiltrated with rhodamine 6G

Monodisperse latex spheres were obtained by a surfactant free styrene polymerization method and used to obtain colloidal crystals by controlled centrifugation settling. Silica inverse opals were then prepared by using the colloidal crystals as templates and TEOS/ethanol solution. The inverse opals were infiltrated with Rhodamine 6G and laserlike emission was observed at 590 nm under 532 nm pump wavelength. The data show line narrowing of the dye fluorescence and a laser threshold of similar to 0.1 mJ/pulse. Local-field effects and light scattering due to structural defects are the main mechanisms contributing to generation of the laser-action observed. (c) 2005 Elsevier B.V. All rights reserved.

Rare earth doped synthetic opals and inverse opals

Monodisperse spheres of silica and latex were obtained by a surfactant free styrene polimerization and the Stober method respectively. Controlling settling either by centrifugation or by dip-coating colloidal crystals could be obtained. Silica inverse opals were prepared by using the latex colloidal crystals as templates and TEOS/ethanol solution. Eu3+ containing silica spheres were obtained dispersing silica spheres in Eu(NO3)(3) isopropanol solutions. Emission spectra suggest the formation of an amorphous Eu3+ containing phase well adhered at the spheres surface. The utilization of solutions of trifluoroacetates salts of Pb2+ and Eu3+ was observed to destroy the silica spherical pattern when samples are treated at 1000degreesC. In that case nanocrystals of PbF2 and amorphous silica were obtained after heat treatment.

Structural properties of silica gels prepared from oxalic-acid-catalyzed tetraethoxysilane sonohydrolysis

About similar to 2.1 x 10(-3) Mol SiO2 cm(-3) and similar to 88%-volume liquid-phase silica wet gels were prepared from oxalic-acid-catalyzed tetraethoxysilane (TEOS) sonohydrolysis. Aerogels were obtained by supercritical CO2 extraction. The samples were analyzed by thermogravimetry, small-angle X-ray scattering and nitrogen adsorption. Wet gels can be described as mass fractal structures with fractal dimension D similar to 1.94 and structural characteristic length zeta changing between similar to 3.3 to similar to 3.0 nm in the studied range of the catalyst concentration. A fraction of the porosity is apparently eliminated in the supercritical process. The values of the BET specific surface S-BET, the total pore volume V-p and the mean pore size l(p) of the aerogels were found to change almost randomly around the mean values S-BET = 874 m(2) g(-1), V-p = 0.961 cm(3) g(-1) and l(p) = 4.4 nm with catalyst concentration variation. These values were not substantially different from those from an equivalent HCl-catalyzed aerogel. (c) 2007 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

A kinetic study of the effect of ultrasound power on the sonohydrolysis of tetraethyl orthosilicate

A kinetic study of the ultrasound-stimulated and acid-catalyzed sonohydrolysis of tetraethyl orthosilicate (TEOS) in solventless TEOS-water heterogeneous mixtures was carried out by means of a calorimetric method as a function of the ultrasound power. The hydrolysis reaction starts in acidulated heterogeneous water-TEOS mixtures after an induction period under ultrasonic stimulation. The ultrasound power seems to play a role on the dynamical coupling of the system originating a continuum upward shifting of the base line during the induction period of sonication. The rate in which the base line is upward shifted diminishes with the power. The best coupling between the ultrasound and the reactant heterogeneous mixtures for this experimental setup was found to occur at 50 W, for which the gelation time was found to be a minimum. The kinetics of the heterogeneous TEOS sonohydrolysis was studied on the basis of a dissolution and reaction modeling. The heterogeneous reaction pathway as deduced from the kinetic study was drawn in a ternary diagram as a function of the ultrasound power. (C) 2006 Elsevier B.V. All rights reserved.

Structural characteristics of silica sonogels prepared with additions of isopropyl alcohol

Wet silica gels with similar to 1.4 x 10(-3) mol SiO2/cm(3) and similar to 92 vol% liquid phase were obtained from sonohydrolysis of tetraethoxysilane (TEOS) with different additions of isopropyl alcohol ( IPA). The IPA/TEOS molar ratio R was changed from 0 to 4. Aerogels were obtained by supercritical CO2 extraction. The samples were analyzed by small-angle X-ray scattering (SAXS) and nitrogen adsorption. The wet gels exhibit mass fractal structure with fractal dimension increasing from D similar to 2.10 to D similar to 2.22, characteristic length xi decreasing from similar to 9.5 to similar to 6.9 nm, as R increases from 0 to 4, and an estimated characteristic length for the primary silica particles lower than similar to 0.3 nm. The supercritical process apparently eliminates a fraction of the porosity, increasing the mass fractal dimension and shortening the fractality domain in the mesopore region. The fundamental role of isopropyl alcohol on the structure of the resulting aerogels is to decrease the porosity and the pore mean size as R changes from pure TEOS to R = 4. A secondary structure appearing in the micropore region of the aerogels can be described as a mass/surface fractal structure, with correlated mass fractal dimension D-m similar to 2.7 and surface fractal dimension D-s similar to 2.3, as inferred from SAXS and nitrogen adsorption data.

Preparation and properties of colloidal particles. Silica on yttrium iron garnet

Various properties of particles can be altered by coating them with a layer of different chemical composition. Yttrium iron garnet (YIG) particles has been coated with silica for control of their sintering, corrosion resistance, and stabilization of magnetic properties. This silica cover was obtained by hydrolysis of tetraethylorthosilicate (TEOS) in 2-propanol. This material was characterized by transmission (TEM) electron microscopy, (XEDS) X-ray energy-dispersive spectrometry, (XPS) X-ray photoemission spectroscopy and (VSM) vibrating sample magnetometry. YIG was heterocoagulated by silica as indicated by TEM micrographies. XPS measurements indicated that only binding energy for silicon and oxygen was found on the silica shell, which confirms that the YIG was covered. The values of the saturation magnetization differ from the heterocoagulated system to well-crystallized YIG.

Structural study of composites of aerosil fumed silica and tetraethoxysilane-derived sonogels

Composites of aerosil fumed silica and tetraethoxysilane-derived sonogel were prepared by changing the aerosil content between 0 and 30wt% with respect to the silica content in the original tetraethoxysilane (TEOS). The structural characteristics were studied by density and Vickers microhardness measurements and analyzed by means of small-angle X-ray scattering (SAXS). The structure of the composite aerosil/TEOS-derived sonogel can be described as inclusions of the aerosil particles embedded in the matrix of the TEOS-derived sonogel, forming an aerosil/matrix interfacial surface inside the composite. The weakening of the bonding of aerosil/matrix interface, as suggested by the reported decrease in microhardness, increases the fracture toughness of the composite. The additive effect of the aerosil particles on the structure of the sonogel accounts for the increase of the bulk density and reduction of the specific surface of the composite. Some internal structure associated with the microclusters making up the sonogels is apparent from systematic deviations from Porod's law found in the system with small aerosil contents. (c) 2005 Elsevier B.V. All rights reserved.

Improvement of the corrosion resistance of polysiloxane hybrid coatings by cerium doping

Polysiloxane hybrid films were deposited on stainless steel by dip-coating using a sol prepared by hydrolytic co-polycondensation of tetraethoxysilane (TEOS) and 3-methacryloxy propyltrimethoxysilane (MPTS), followed by radical polymerization of methacrylic moieties. The TEOS/MPTS ratio was chosen equal to 2 and the Ce/Si ratio varied between 0.01 and 0.1. The effects of cerium concentration and valence (Ce(III) and Ce (IV)) on the structural features of polysiloxane films were studied by X-ray photoelectron spectroscopy (XPS) and (29)Si nuclear magnetic resonance (NMR). The corrosion protection of stainless steel by the hybrid coatings was investigated by XPS, electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization curves, after immersion in saline and acid solutions. The NMR results have shown for Ce(IV) doped films a high degree of polycondensation of up to 89%. Electrochemical analysis has evidenced that hybrid films with the lowest Ce concentration act as an efficient diffusion barrier by increasing the corrosion resistance and reducing the current densities up to 3 orders of magnitude compared to bare stainless steel. The analysis of structural effects induced by Ce(III) and Ce(IV) species, performed by XPS, indicates that the improved corrosion protection of Ce(IV) doped films might be mainly related to the enhanced polymerization of siloxane groups. (C) 2010 Elsevier B.V. All rights reserved.

SAXS study of monodispersed silica nanospheres obtained by an amino acid route

Spherical silica nanoparticles were prepared using a basic amino acid catalysis route and the kinetics of the particles growth was investigated by small angle X-ray scattering (SAXS). L-arginine was used in the polar aqueous phase as the basic catalyst whereas the tetraethylorthosilicate (TEOS) was dissolved in the cyclohexane oil phase as the silicate monomer source. The SAXS measurements were taken in the aqueous phase at different reaction times. A high degree of monodispersity was clearly evidenced for the spherical nanoparticles as a result of the pronounced high-order oscillations observed in the SAXS curves. The SAXS data show that the particles number density remains unchanged since both the particle size as well as the volume fraction gradually increase. This process was discussed based on a reaction-controlled addition of monomer species at the surface of the growing particles. Consequently, the monodispersed spherical nanoparticles radius can as such be finely tuned from 7 to 12 nm by varying the reaction time. (C) 2010 Elsevier B.V. All rights reserved.

Characterization of Si : O : C : H films fabricated using electron emission enhanced chemical vapour deposition

Silicon-based polymers and oxides may be formed when vapours of oxygen-containing organosilicone compounds are exposed to energetic electrons drawn from a hot filament by a bias potential applied to a second electrode in a controlled atmosphere in a vacuum chamber. As little deposition occurs in the absence of the bias potential, electron impact fragmentation is the key mechanism in film fabrication using electron-emission enhanced chemical vapour deposition (EEECVD). The feasibility of depositing amorphous hydrogenated carbon films also containing silicon from plasmas of tetramethylsilane or hexamethyldisiloxane has already been shown. In this work, we report the deposition of diverse films from plasmas of tetraethoxysilane (TEOS)-argon mixtures and the characterization of the materials obtained. The effects of changes in the substrate holder bias (Vs) and of the proportion of TEOS in the mixture (XT) on the chemical structure of the films are examined by infrared-reflection absorption spectroscopy (IRRAS) at near-normal and oblique incidence using unpolarised and p-polarised, light, respectively. The latter is particularly useful in detecting vibrational modes not observed when using conventional near-normal incidence. Elemental analyses of the film were carried out by X-ray photoelectron spectroscopy (XPS), which was also useful in complementary structural investigations. In addition, the dependencies of the deposition rate on Vs and XT are presented. (c) 2007 Elsevier B.V. All rights reserved.