Ruthenium nanoparticles prepared from ruthenium dioxide precursor: Highly active catalyst for hydrogenation of arenes under mild conditions

The hydrogenation of benzene and benzene derivatives was studied using Ru(0) nanoparticles prepared by a very simple method based on the in situ reduction of the commercially available precursor ruthenium dioxide under mild conditions (75 degrees C and hydrogen pressure 4atm) in imidazolium ionic liquids. Total turnovers (TTO) of 2700 mol/mol Ru were obtained for the conversion of benzene to cyclohexane under solventless conditions and TTO of 1200 mol/mol Ru were observed under ionic liquid biphasic conditions. When corrected for exposed ruthenium atoms, TTO values of 7940 (solventless) and 3530 (biphasic) were calculated for benzene hydrogenation. These reaction rates are higher than those observed for Ru nanoparticles prepared from decomposition of an organometallic precursor in similar conditions. The presence of the partially hydrogenated product cyclohexene was also detected at low conversion rates. (C) 2008 Elsevier B.V. All rights reserved.

Ligand-Assisted Preparation of Palladium Supported Nanoparticles: a Step toward Size Control

Supported nanoparticles (SNPs) with narrow size distribution were prepared by H(2) reduction of Pd(2+) previously bound, to ligand-modified silica surfaces. Interestingly, the size of the Pd SNPs was tuned by the ligand grafted on the support surface. Amino- and ethylenediamino-functionalized supports formed Pd(0) SNPs of ca. 6 and 1 nm, respectively. The catalytic properties of both Pd(0) SNPs were investigated.

Silver Nanoparticles Obtained in PAH/PAA-Based Multilayers by Photochemical Reaction

Carboxylic acid groups in PAH/PAA-based multilayers bind silver cations by ion exchange with the acid protons. The aggregation and spatial distribution of the nanoparticles proved to be dependent oil the process used to reduce the silver acetate aqueous solution. The reducing method with ambient light formed larger nanoparticles with diameters ranging from 4-50 nm in comparison with the reduction method using UV light, which gave particles with diameters of 2-4 nm The high toughness of samples reduced by ambient light is a result of two population distributions of particle sizes caused by different mechanisms when compared with the UV light process. According to these phenomena, a judicious choice of the spectral source call be used as a way to control the type and size of silver nanoparticles formed on PEMs. Depending on the energy of the light source, the Ag nanoparticles present cubic and/or hexagonal crystallographic structures, as confirmed by XRD. Beyond the kinetically controlled process of UV photoinduced cluster formation, the annealing produced by UV light allowed a second mechanism to modify the growth rates, spatial distribution, and phases.

Optical properties of polydisperse submicrometer aggregates of sulfur-containing zinc oxide consisting of spherical nanocrystallites

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Experimental and theoretical studies on the enhanced photoluminescence activity of zinc sulfide with a capping agent

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Structure of magnetic poly(oxyethylene)-siloxane nanohybrids doped with Fe-II and Fe-III

Hybrid organic - inorganic nanocomposites doped with Fe-II and Fe-III ions and exhibiting interesting magnetic properties have been obtained by the sol - gel process. The hybrid matrix of these ormosils ( organically modified silicates), classed as di-ureasils and termed U( 2000), is composed of poly( oxyethylene) chains of variable length grafted to siloxane groups by means of urea crosslinkages. Iron perchlorate and iron nitrate were incorporated in the diureasil matrices, leading to compositions within the range 80 greater than or equal to n greater than or equal to 10, n being the molar ratio of ether-type O atoms per cation. The structure of the doped diureasils was investigated by small-angle X-ray scattering (SAXS). For Fe-II-doped samples, SAXS results suggest the existence of a two-level hierarchical structure. The primary level is composed of spatially correlated siloxane clusters embedded in the polymeric matrix and the secondary, coarser level consists of domains where the siloxane clusters are segregated. The structure of Fe-III-doped hybrids is different, revealing the existence of iron oxide based nanoclusters, identified as ferrihydrite by wide-angle X-ray diffraction, dispersed in the hybrid matrix. The magnetic susceptibility of these materials was determined by zero-field-cooling and field-cooling procedures as functions of both temperature and field. The different magnetic features between Fe-II- and Fe-III-doped samples are consistent with the structural differences revealed by SAXS. While Fe-II-doped composites exhibit a paramagnetic Curie-type behaviour, hybrids containing Fe-III ions show thermal and field irreversibilities.

Oxidative dissolution of research-grade minerals by Thiobacillus ferrooxidans and Thiobacillus thiooxidans

Solution- and solid-phase changes associated with galena (PbS) and sphalerite (ZnS) oxidation by T. ferrooxidans and T. thiooxidans, were determined. In experiments with galena, anglesite (PbSO4) was detected as a solid-phase product in biotic and abiotic experiments. In T. ferrooxidans cultures supplemented with FeSO4, jarosite [MFe3 (SO4)(2) (OH)(6)] was also detected as a new solid phase product, whereas SO was not detected in the residues. In sphalerite experiments, minor amounts of SO accumulated in FeSO4-amended sphalerite media with or without T. ferrooxidans or T. thiooxidans. Jarosite was only detected in T. ferrooxidans culture with FeSO4. By comparison with T. thiooxidans, T. ferrooxidans was more efficient in the oxidation of galena and sphalerite.

Enhanced photoluminescence features of Eu3+-modified di-ureasil-zirconium oxocluster organic-inorganic hybrids

In this work, a series of transparent di-ureasil hybrids containing different amounts of methacrylic acid modified zirconium tetrapropoxide (ZrMcOH) nanoclusters (5-85 mol%) and incorporating EuCl3 and [Eu(tta)(3)(H2O)(2)](tta = thenoyltrifluoroacetonate) complex were prepared. These hybrids are multi-wave-length emitters due to the convolution of the host intrinsic emission (electron-hole recombinations occurring in siliceous and urea cross-linkages) Eu3+ intra-4f(6) transitions. The ZrMcOH incorporation deviates the maximum excitation wavelength of the hybrid host intrinsic emission from the UV (365 nm) to the blue (420 nm) and enhances the absolute emission quantum yield from 6.0 +/- 0.6% to 9.0 +/- 0.9%, and contributes to an increase in the D-5(0) lifetime values, quantum efficiency due to a decrease in the non-radiative transition probability and OH groups coordinated to the Eu3+ ions. (C) 2010 Elsevier B.V. All rights reserved.

Structure and properties of Ti4+-Ureasil organic-inorganic hybrids

Hybrid planar waveguides were prepared from Ti4+-acetylacetone (acac)-Ureasil sols deposited on glass substrates. Structural features have been investigated by spectroscopic measurements (Fourier Transform Infrared Spectroscopy (FTIR), X-ray Photoelectron Spectroscopy (XPS) and Raman scattering) and Small Angle X-ray Scattering (SAXS). Addition of Ti 4+-acac to the ureasil (Ti:Si molar ratio 1:1) leads to the formation of bonds between the Ti complex and the siloxane groups, whereas further addition of Ti4+ (Ti:Si molar ratio 5:1) leads to the additional formation of titanium-rich nanoclusters. The optical parameters of the waveguides such as refractive index, thickness, propagating modes and attenuation coefficient were measured at 632.8, 543.5 and 1550 nm by the prism coupling technique. The refractive index can be tuned by the Ti4+ relative content. The few microns thick planar waveguides support well confined propagating modes with low attenuation loss for all compositions. ©2006 Sociedade Brasileira de Química.

Sonochemical synthesis and magnetism in co-doped ZnO nanoparticles

The understanding and control of ferromagnetism in diluted magnetic semiconducting oxides (DMO) is a special challenge in solid-state physics and materials science due to its impact in magneto-optical devices and spintronics. Several studies and mechanisms have been proposed to explain intrinsic ferromagnetism in DMO compounds since the theoretical prediction of room-temperature ferromagnetism. However, genuine and intrinsic ferromagnetism in 3d-transition metal-doped n-type ZnO semiconductors is still a controversial issue. Furthermore, for DMO nanoparticles, some special physical and chemical effects may also play a role. In this contribution, structural and magnetic properties of sonochemically prepared cobalt-doped ZnO nanoparticles were investigated. A set of ZnO samples was prepared varying cobalt molar concentration and time of ultrasonic exposure. The obtained results showed that single phase samples can be obtained by the sonochemical method. However, cobalt nanoclusters can be detected depending on synthesis conditions. Magnetic measurements indicated a possible ferromagnetic response, associated to defects and cobalt substitutions at the zinc site by cobalt. However, ferromagnetism is depleted at higher magnetic fields. Also, an antiferromagnetic response is detected due to cobalt oxide cluster at high cobalt molar concentrations. © 2012 Springer Science+Business Media, LLC.

Photocatalytic activity of semiconductor sulfide heterostructures

This paper reports a theoretical and experimental study of the heterostructure photocatalytic activity in a CdS or ZnS and CdS@ZnS decorated system prepared by a microwave assisted solvothermal (MAS) method. A theoretical model of the decorated system was created in order to analyze the electronic transition mainly in their interface. The results show that CdS and ZnS interfaces produce an electron charge transfer from the CdS electron-populated clusters to the ZnS hole-populated clusters which helps to enhance the photocatalytic activity of the CdS@ZnS decorated system. © 2013 The Royal Society of Chemistry.

Biolixiviação de minério de cobre da mina de Sossego, PA - Companhia Vale do Rio Doce

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Desenvolvimento e caracterização de dispositivos de visualização eletroluminescentes

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Avaliação instrumental da correspondência de cor de resinas compostas em função de escala de referência, tonalidade, composição e espessura

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Incorporação de tiofosfatos em vidros calcogenetos: estrutura e fenômenos fotoinduzidos

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)