Avaliação in vitro da resistência adesiva ao cisalhamento entre a dentina bovina, cimentos resinosos e materiais restauradores indiretos, tratados ou não com jato de óxido de alumínio, ácido fluorídrico e silano

The purpose of this study was to evaluate in vitro the shear bond strenght to bovine dentin, during 24h and 30 days with the following variables: resin cements Enforce and Panavia F; aesthetics restorative materials Art Glass, IPS Empress 2 and Targis, with surface treatment with microetching with aluminium oxide, fluoridric acid and silane. Two hundred eighty eight sound bovine teeth from 3 years old animals constituted the samples after inclusion on polyester resin box. lnstron model 430 Universal Testing Machine, a crosshead speed 0,5 mm/min and load cells of 500 Kg, was used for shear bond strenght testing (MPa). The results were statistically analysed by ANOVA The best result was obtained with /PS Empress 2, microetched with aluminium oxide, fluoridric acid and silane, cemented with Panavia F and stored in distilled water, 3f'C during 30 days

Avaliação da eficácia de primers para metal na resistência ao cisalhamento da união entre cimentos resinosos e metais não nobres. Efeito do armazenamento em água

O sucesso das restaurações metálicas indiretas depende, dentre outros fatores, de uma união eficaz entre a estrutura metálica e o cimento dentário empregados. Sabe-se que os primers para metal atuam com comprovada eficácia na resistência adesiva dos cimentos resinosos às ligas nobres. Entretanto, pouco foi estudado sobre o efeito de tais materiais em ligas não nobres. O propósito deste estudo foi avaliar a eficácia de primers para metal na resistência ao cisalhamento da união entre cimentos resinosos e metais não nobres. Discos (9 mm de diâmetro e 3 mm de altura) foram fundidos em liga de NiCr (n=80) e em titânio comercialmente puro (Ti c.p.) (n=80) e foram incluídos em anel de PVC com resina acrílica quimicamente ativada. As superfícies dos discos foram regularizadas com lixas de carbeto de silício de granulação 320, 400 e 600 e jateadas com partículas de óxido de alumínio de 50 µm. Espécimes de cada metal foram divididos em quatro grupos (n=20). Uma matriz metálica bi-partida (5 mm de diâmetro interno e 2 mm de altura) foi posicionada na superfície do espécime. As áreas adesivas receberam um dos seguintes tratamentos: 1) Panavia F; 2) Alloy Primer e Panavia F; 3) Bistite DC e 4) Metaltite e Bistite DC. Para evitar a exposição dos cimentos à luz, estes foram espatulados e inseridos na matriz dentro de uma câmara de revelação radiográfica. Quarenta minutos após a confecção, os espécimes foram armazenados em água destilada a 37ºC por 24 horas e então termociclados (1.000 ciclos, 5ºC e 55ºC, 30 segundos cada banho). Após a termociclagem, os espécimes foram armazenados novamente nas mesmas condições descritas anteriormente por um período de 24 horas (n=10) ou de 6 meses (n=10) antes do ensaio de cisalhamento em uma máquina de ensaios mecânicos (Material Test System 810).

Desempenho adesivo de sistemas de união à dentina aplicados in vivo e in vitro: efeito da pressão intrapulpar e profundidade dentinária

O objetivo do presente estudo foi investigar a influência da pressão intrapulpar e da profundidade dentinária sobre o desempenho adesivo de dois agentes de união à dentina, Single Bond (3M ESPE, St. Paul, MN, EUA) e Clearfil SE Bond (Kuraray, Tokyo, Japão), aplicados in vitro e in vivo. Quarenta e oito prémolares superiores hígidos foram selecionados e os pares pertencentes aos mesmos pacientes foram aleatoriamente distribuídos em 4 grupos experimentais de acordo com o sistema adesivo e a pressão intrapulpar, presente ou ausente. Dos dentes pertencentes ao mesmo par, um foi tratado in vivo e o outro in vitro. A ausência ou presença de pressão intra-pulpar foi determinada in vivo pelo uso de anestésicos locais com ou sem vasoconstritor, respectivamente. In vitro, os dentes foram mantidos sob pressão hidrostática de 15 cm de água por 24 horas. Cavidades de classe I foram preparadas e os sistemas adesivos aplicados de acordo com a recomendação dos fabricantes, seguidos da restauração incremental em resina composta. Para os dentes tratados in vitro, os mesmos procedimentos restauradores foram realizados após 6 meses de armazenagem em solução contendo timol 0,1%. Espécimes com área de secção transversal de 1 mm2 foram obtidos e submetidos ao ensaio mecânico de microtração. In vivo, ambos os sistemas adesivos apresentaram desempenho adesivo comparável, enquanto in vitro, o sistema Single Bond foi superior ao sistema Clearfil SE Bond. Esse último não foi influenciado por nenhuma das variáveis estabelecidas no estudo, ou seja, aplicação in vitro ou in vitro, presença de pressão intrapulpar e profundidade em dentina. O sistema Single Bond aplicado sob pressão intrapulpar positiva sofreu variação significante de resistência de união em função da profundidade da dentina, ou seja, em dentina profunda seu desempenho adesivo... (Resumo completo, clicar acesso eletrônico abaixo)

Estrutura do esmalte humano e sua interface com sistemas adesivos

Esta tese sistematiza uma série de estudos dedicados à compreensão da interface do esmalte e sistemas adesivos. Para tanto, a estrutura da camada aprismática do esmalte em alta resolução pela microscopia eletrônica de varredura foi avaliada quanto a sua continuidade, espessura, distribuição nas faces coronárias e em fossas e fissuras, predominantemente em dentes decíduos não erupcionados. Foi também analisado pela microscopia eletrônica de varredura os efeitos do condicionamento de diferentes tipos de ácido e, em especial, do ácido fosfórico em diferentes concentrações, metodologias e tempos de aplicação. Estes trabalhos permitiram visualizar as principais ações ácidas desmineralizantes e os tipos de retenções no centro ou periferias dos prismas ou em ambas as regiões, bem como a profundidade e forma dos “tags” resinosos com carga e sem carga na intimidade do esmalte. No caso particular da aplicação dos selantes em fossas e fissuras foi também avaliada comparativamente a eficácia das técnicas invasivas ou não invasivas. Os últimos experimentos foram dedicados ao estudo da microinfiltração de diferentes sistemas adesivos e da resistência destes sistemas adesivos na estrutura do esmalte. Novos estudos merecem dar continuidade à linha de pesquisa de sempre priorizando o propósito de vincular os procedimentos aplicados com uma consistente e indispensável fundamentação de pesquisa básica no interesse da clínica odontopediátrica.

Resistência de união de cimentos resinosos em superfície de cerâmica de Y-TZP após aplicação de filme vitrocerâmico

Pós-graduação em Odontologia Restauradora - ICT

Resistência ao cisalhamento de bráquetes fotopolimerizados com arco de plasma, LED e luz halógena utilizando diferentes tempos

This study evaluated in vitro the shear bond strength of brackets bonded with xenon plasma arc light, light-emitting diode (LED) and conventional halogen light using different curing times. Brackets were bonded to the buccal surface of 60 human maxillary premolars allocated to five groups. In groups 1 and 2, the resin was cured with the plasma arc for three and six seconds (s), respectively; in groups 3 and 4, the LED was used for five and ten s, respectively; and in group 5, the halogen light was used for 40 s. The specimens were stored in water for 24 hours and subjected to a shear force until bracket failure. The debonding pattern was classified according to the adhesive remnant index (ARI). The results were assessed by Anova and the SNK post-hoc test. No differences were detected among groups 2, 4 and 5, which showed higher averages than groups 1 and 3, which were not different between themselves. The ARI scores showed no differences among the three types of light sources in all times tested. Plasma arc and LED lights can be used with shorter curing times, within certain limits, than conventional halogen light for bonding orthodontic brackets, without decreasing bond strength.

Influência da espessura da infraestrutura em Zircônia (3Y-TZP)na resistência mecânica da porcelana de cobertura

Pós-graduação em Reabilitação Oral - FOAR

Can Application of Universal Primers Alone Be a Substitute for Airborne-Particle Abrasion to Improve Adhesion of Resin Cement to Zirconia?

Purpose: To determine whether universal primers alone can deliver similar levels of adhesion of resin cement to zirconia ceramic when compared to their application in conjunction with airborne-particle abrasion.Materials and Methods: Sintered zirconia blocks (N = 160) (Lava, 3M ESPE), (5.25 x 5.25 x 3 mm(3)) were embedded in acrylic resin, polished, and randomly distributed into 16 groups (n = 10 per group), according to the factors "universal primer" (8 levels) and "air-particle abrasion" (2 levels): 1. ctr: control, without application of a universal primer; 2. AP: Alloy Primer; 3. MP: Monobond Plus; 4. MZP: Metal Zirconia Primer; 5. MZ: MZ Primer; 6. Sg: Signum Zirconia Bond; 7. SbU: Singlebond Universal; 8. ZP: Z Prime Plus. The universal primers were also used after air abrasion (A) of zirconia to form the following 8 groups: Ctr-A, AP-A, MP-A, MZP-A, MZ-A, Sg-A, SbU-A, and ZP-A. After ultrasonic cleaning, air abrasion was performed using Al2O3 particles (110 mu m, 2.5 bar, 20 s at 10 mm) in a chairside air-abrasion device. After ultrasonic cleaning again, universal primers were applied according to each manufacturer's recommendation. The resin cement (RelyX ARC, 3M ESPE) was built up incrementally and photo-polymerized on the zirconia surface using a silicone mold (empty set = 3.5, height = 3 mm). All specimens were stored in distilled water (60 days at 37 degrees C) and then subjected to shear bond strength testing (SBS) in a universal testing machine (1 mm/min). On a separate set of zirconia specimens, contact angle measurements were made using the sessile drop technique with a goniometer after the application of universal primers on control and air-abraded zirconia surfaces. Data (MPa) were analyzed using one-way ANOVA, Tukey's test, and Student's t-test (alpha = 0.05).Results: When universal primers were used alone, SbU presented significantly higher mean SBS (19.5 +/- 5.8) that did the other primers (0 to 9.9 +/- 6.6) (p = 0.001). When air abraded, the groups AP-A (14.1 +/- 6.1), MP-A (15.9 +/- 5.4), ZP-A (16.9 +/- 7.3), SG-A (19.1 +/- 2.1), SbU-A (12 +/- 1.5) showed significant differences (p = 0.03). Adhesive performance of all universal primers was enhanced after air abrasion, with the exception of the SbU and MZ primers. After air abrasion, contact angle measurements were lower for the each primer (without air abrasion: 28.9 to 83.9; with air abrasion: 27.1 to 63.0), except for MZP.Conclusion: Air abrasion with 110 mu m Al2O3 followed by universal primer application increased the bond strength of tested resin cement to zirconia, with the exception of SbU and MZ.

Bonding ability of paste-paste glass ionomer systems to tooth structure: in vitro studies

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Adesivos multi-uso-avaliação da resistência adesiva a dentina frente a teste de cisalhamento, estereomicroscopia e microscopia eletrônica de varredura

Recent bonding systems have been advocated as multi-purpose bonding agents. The aim of this study was to determine if some of these bonding systems could be associated to composite resins from different manufacturers. This investigation was conducted to test lhe shear bond strength of three bonding systems: Scotchbond Multi-Purpose (3M Dental Products), Optibond Light Cure (Kerr) and Optibond Dual Cure (Kerr), when each of them was associated to lhe composite resins: Z1 00 (3M Dental Products), Prisma - APH (Dentsply) and Herculite XRV (Kerr). Seventy-two flat dentin bonding sites were prepared to 600 grit on human premolars mounted using acrilic resins. The teeth were assigned at random to 9 groups of 8 samples each. A split die with a 3mm diameter was placed over lhe surface of lhe dentin treated with one of lhe adhesive systems, and lhe selected composite resin was inserted and light cured. The split mold was removed and all samples were termocycled and stored in 37ºC water for 24 hours before testing. Shear bond strength was determined using an lnstron Universal testing machine. Some failures were examined under lhe S.E.M. Data was analysed by one-way analysis of variance, that demonstrated a significant difference (p<0,05) in the mean shear bond strength among Optibond Light Cure (15,446 MPa), Scotchbond Multi-Purpose (13,339 MPa) and Optibond Dual Cure (10,019 MPa). These values did not depend on the composite resin used. The association between bonding system/composite resin was statistycally significant (p<0,05) and the best results were obtained when the composite resins Z100 and Herculite were used with the adhesive system Optibond Light Cure, and when the composite resin APH was used with the adhesive system Scotchbond Multi-Purpose

Avaliação in vitro da resistência de união de dois sistemas adesivos dentinários à dentina bovina antes e após a termociclagem: teste de cisalhamento e análise estereomicroscópia

Pós-graduação em Odontologia Restauradora - ICT

Resistência ao cisalhamento de diferentes sistemas adesivos no esmalte dental

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Influência de agentes clareadores na resistência de união de um sistema restaurador ao esmalte em função do tempo de armazenamento em saliva artificial

Pós-graduação em Odontologia Restauradora - ICT

Pré tratamento dentinário influência do condicionamento ácido, irradiação laser e hipermineralização na resistência ao cisalhamento de sistema adesivo multi uso

The disadvantages generated by the acid etching of the dentin, such as an increase in its permeability, in the surface moisture and in the potential to denature the external dentinal collagen, the formation of a fragility zone and the citotoxicity of the adhesive monomers; which are all aggravated by the depth of the dentin, have stimulated new and different treatment philosophies of the dentin. The purpose of the present study, therefore, was to investigate the effects of three dentin treatments: laser irradiation, acid etching and hypermineralization, in the shear bond strength of the SMP Plus bonding system. Sixty bovine incisors were extracted and randomly selected immediatly alter the animal's death. They were kept frozen (-18°C) for no longer than 14 days. After buccal dentinal surface had been exposed, X-Rays were taken to control the dentin thickness. The specimens were separated into two groups: (1) Control, kept in distilled water at 4ºC; (2) Mineralized, kept in hypermineralized solution at 4°C for 14 days. Each group was divided into three sub-groups according to the type of dentin treatment used: group F - followed the manufacturer instructions (acid-etching + primer + bond), group AL (acid-etching + primer + bond + laser) and group LA (laser + (laser + acid-etching + primer + bond). A composite resin standard cylinder (Z100-3M) was bond to the dentinal surface and the shear bond strength performed on a Universal lnstron machine 4301, with 500 Kg load and at 0,5mm/min. speed. The analysis of variance (ANOVA) determined that the treatments influenced the shear bond strength values (p<0,05) with the following average shearing load at failure: AL (9,96 MPa), F (7,28MPa) e LA (4,87 MPa). The interaction between the two factors analyzed Group (control and mineralized) and treatment (F, AL, LA) also influenced the shear bond strength (p<0,05). The highest values were obtained...

Avaliação da influência de materiais obturadores endodônticos sobre a resistência de união adesiva de pinos de fibra de vidro cimentados

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)