Improvement of the corrosion resistance of polysiloxane hybrid coatings by cerium doping

Polysiloxane hybrid films were deposited on stainless steel by dip-coating using a sol prepared by hydrolytic co-polycondensation of tetraethoxysilane (TEOS) and 3-methacryloxy propyltrimethoxysilane (MPTS), followed by radical polymerization of methacrylic moieties. The TEOS/MPTS ratio was chosen equal to 2 and the Ce/Si ratio varied between 0.01 and 0.1. The effects of cerium concentration and valence (Ce(III) and Ce (IV)) on the structural features of polysiloxane films were studied by X-ray photoelectron spectroscopy (XPS) and (29)Si nuclear magnetic resonance (NMR). The corrosion protection of stainless steel by the hybrid coatings was investigated by XPS, electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization curves, after immersion in saline and acid solutions. The NMR results have shown for Ce(IV) doped films a high degree of polycondensation of up to 89%. Electrochemical analysis has evidenced that hybrid films with the lowest Ce concentration act as an efficient diffusion barrier by increasing the corrosion resistance and reducing the current densities up to 3 orders of magnitude compared to bare stainless steel. The analysis of structural effects induced by Ce(III) and Ce(IV) species, performed by XPS, indicates that the improved corrosion protection of Ce(IV) doped films might be mainly related to the enhanced polymerization of siloxane groups. (C) 2010 Elsevier B.V. All rights reserved.

Investigation of New Ion Conducting Ormolytes Silica-Polypropyleneglycol

Two groups of hybrid organic-inorganic composites exhibiting ionic conduction properties, so called ORMOLYTES (organically modified electrolytes), have been prepared by the sol-gel process. The first group has been prepared from mixture of a lithium salt and 3-isocyanatopropyltriethoxysilane(IsoTrEOS),O,O′-bis(2-aminopropyl) polypropyleneglycol. These materials produce chemical bonds between the organic (polymer) and the inorganic (silica) phases. The second group has been prepared by an ultrasonic method from a mixture of tetraethoxysilane (TEOS), polypropyleneglycol and a lithium salt. The organic and inorganic phases are not chemically bonded in these samples. The Li+ ionic conductivity, σ, of all these materials has been studied by AC impedance spectroscopy up to 100°C. Values of σ up to 10-6 Ω-1·cm-1 have been found at room temperature. A systematic study of the effects of lithium concentration, polymer chain length and the polymer to silica weight ratio on σ shows that there is a strong dependence of σ on the preparation conditions. The dynamic properties of the Li+ ion and the polymer chains as a function of temperature between -100 and 120°C were studied using 7Li solid-state NMR measurements. The ionic conductivity of both families are compared and particular attention is paid to the nature of the bonds between the organic and inorganic components.

White light emission of Eu3+-based hybrid xerogels

The luminescence spectra and extended x-ray-absorption fine-structure (EXAFS) measurements of a series of Eu3+-based organic/inorganic xerogels were reported and related to the local coordination of the lanthanide cations. The hybrid matrix of these organically modified silicates, classed as U(2000) ureasils, is a siliceous network to which short organic chains containing oxyethylene units are covalently grafted by means of urea bridges. The luminescent centers were incorporated as europium triflate, Eu(CF3SO3)3, and europium bromide, EuBr3, with concentrations 200≥n≥20 and n=80, 40, and 30, respectively - where n is the number of ether oxygens in the polymer chains per Eu3+ cation. EXAFS measurements were carried out in some of the U(2000)nEu(CF3SO3)3 xerogels (n=200, 80, 60, and 40). The obtained coordination numbers N ranging from 12.8, n=200, to 9.7, n=40, whereas the average Eu3+ first neighbors distance R is 2.48-2.49 Å. The emission spectra of these multiwavelength phosphors superpose a broad green-blue band to a series of yellow-red narrow 5D0→7F0-4 Eu3+ lines and to the eye the hybrids appeared to be white, even at room temperature. The ability to tune the emission of the xerogels to colors across the chromaticity diagram is achieved by changing the excitation wavelength and the amount of salt incorporated in the hybrid host. The local environment of Eu3+ is described as a continuous distribution of closely similar low-symmetry network sites. The cations are coordinated by the carbonyl groups of the urea moieties, water molecules, and, for U(2000)nEu(CF3SO3)3, by the SO3 end groups of the triflate anions. No spectral evidences have been found for the coordination by the ether oxygens of the polyether chains. A mean radius for the first coordination shell of Eu3+ is calculated on the basis of the emission energy assignments. The results obtained for U(2000)nEu(CF3SO3)3, 2.4 Å for 90 ≥n≥40 and 2.6 and 2.5 Å for n=30 and 20, respectively, are in good agreement with the values calculated from EXAFS measurements. The energy of the intraconfigurational charge-transfer transitions, the redshift of the 5D0→7F0 line, with respect to the value calculated for gaseous Eu3+, and the hypersensitive ratio between the 5D0→7F2 and 5D0→7F1 transitions, point out a rather low covalency nature of the Eu3+ first coordination shell in these xerogels, comparing to the case of analogous polymer electrolytes modified by europium bromide. ©1999 The American Physical Society.

Novel cellulose/NbOPO 4.nH 2O hybrid material from sugarcane bagasse

In recent years studies concerning the applications of lignocellulosic/ inorganic couples have resulted in the development of an interesting class of functional materials. In this work a cellulose/NbOPO 4.nH 2O hybrid using cellulose from surgacane bagasse was prepared and characterized in order to test for adsorption applications. The preparation process was conducted by carrying out metallic niobium dilution in hydrofluoric acid in the presence of nitric acid, then adding boric acid to form the complex and, finally, the cellulose sugar cane bagasse was added. Concentrated phosphoric acid was also inserted to precipitate hydrous niobium phosphate particles in the cellulose fiber. This material was characterized by X-ray diffractometry (XRD), thermogravimetry (TG/DTG), and scanning electronic microscopy (SEM) connected to an energy dispersive spectrophotometer (EDS). Results by SEM/EDS show that NbOPO 4.nH 2O was present in structure of the cellulose. During the preparation of the material, using boric acid it was observed that the formation of precipitate occurred in a shorter time than the material prepared without boric acid.

Luminescent properties of hybrid materials prepared by the polymeric precursor method

Rare earth complexes (RE) can be incorporated in silica matrixes, originating organic/inorganic hybrid materials with good thermal stability and high rare earth emission lines. In this work, the hybrid material was obtained by the polymeric precursor method and ultrasonic dispersed with spherical silica particles prepared by the Stöber Method. The Raman spectra indicated that the Eu3+ ions are involved in a polymeric structure formed as consequence of the chelation and polyesterification reactions of this ion with citric acid and ethylene glycol. After the ultrasonic stirring, 2-hydroxynicotinic ligand will also compose this polymeric rigid structure. The TGA/DTA analysis showed that this polymeric material was thermal decomposed at 300 °C. Moreover, this process allows the chelating process of the 2-hydroxynicotinic acid ligand to the Eu3+ ions. The 29Si NMR showed that the ultrasonic dispersion of the reactants was not able to promote the functionalization of the silica particles with the 2-hydroxynicotinic acid ligand. Moreover, heat treatment promotes the [Eu(HnicO2)3] complex particles incorporation into silica pores. At this temperature, the TGA curve showed that only the thermal degradation of ethylene glycol and citric acid used during the experimental procedure occurs. The silica and hybrid materials are composed by spherical and aggregated particles with particle size of approximately 450 nm, which can be influenced by the heat treatment. These materials also present an absorption band located at 337 nm. The photoluminescent study showed that when the hybrid samples were excited at 337 nm wavelength, the ligand absorbs the excitation light. Part of this energy is transferred to the Eu3+ ion, which main emission, 5D0→ 7F2, is observed in the emission spectrum at 612 nm. As the heating temperature increases to 300 C, the energy transfer is more favorable. The lifetime values showed that the Eu3+ emission is enhanced due to the energy transfer process in the powders. © 2013 Elsevier B.V. All rights reserved.

Formadores de filmes híbridos orgânicos inorgânicos do tipo ureasil-poliéter para liberação controlada de fármacos

Pós-graduação em Ciências Farmacêuticas - FCFAR

Efeito fotocrômico em Ormosil's dopados com molibdênio preparados por síntese de Sol-Gel

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Desenvolvimento de revestimentos híbridos do sistema siloxano-PMMA com aplicações anticorrosivas

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Síntese e caracterização de híbridos orgânico-inorgânicos luminescentes para aplicação em ensaios biológicos

Pós-graduação em Química - IBILCE

Estudos preliminares da preparação de fibras ópticas plásticas e híbridos orgânicos-inorgânicos luminescentes a partir de poli(metacrilato de metila) comercial

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Nanopartículas de sílica e ácido p-amino benzóico: um estudo de associação para protetores solares

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Híbridos orgânicos-inorgânicos siloxanos àcidos-graxos emissores de luz branca

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Híbridos orgânicos-inogânicos aminosilano-ácido ricinoleico

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Materiais compósitos orgânicos-inorgânicos a base de celulose bacteriana com peptídeos regulatórios de fatores de crescimento, OGP e OGP [10-14], para regeneração óssea

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Atributos microbiológicos, químicos e granulométricos de organossolo e latossolos vermelhos: efeito sazonal e uso do solo

Pós-graduação em Agronomia (Ciência do Solo) - FCAV