Structural and magnetic characterization of MnxZn1-xFe2O4 (x=0.2; 0.35; 0.65; 0.8; 1.0) ferrites obtained by the citrate precursor method

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

QEXAFS and UV/Vis Simultaneous Monitoring of the TiO2-Nanoparticles Formation by Hydrolytic Sol-Gel Route

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Quantum Mechanics Insight into the Microwave Nucleation of SrTiO3 Nanospheres

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Synthesis and sintering of PZT ceramics

Lead zirconate powder, with Zr/Ti ratio of 50/50 was prepared by polymeric precursor method and doped with 3, 5 and 7 mol% of Sr+2 Or Ba+2, as well as by 0.2 to 5 mol% of Nb+5. The powder was calcined at 750 degrees C by 4 hours and milled during 1.5 h in isopropilic alcohol. Powders were characterized by surface area measurements (BET method), by infrared spectroscopy and by X-ray diffraction to characterize the crystal structure. Isostatically pressed samples were sintered in a dilatometer furnace by using a constant heating rate of 10 degrees C/min from ambient to 1200 degrees C. Synthetic air and air with water vapor were used as atmospheres. Both Sr+2 and Ba+2 substitute Pb+2 and favor the formation of rhombohedral phase. Otherwise, Nb+5 substitute preferentially Zr+4 favoring tetragonal phase. The concentration of dopants and the atmosphere influence the densification and the microstructure of the PZT, which alters the dielectric and piezoelectric properties of the ceramics.

Synthesis and sintering of ZrO2-CeO2 powder by use of polymeric precursor based on Pechini process

Nanocrystalline ZrO2-12 mol % CeO2 powders were synthesized using a polymeric precursor method based on the Pechini process. X-ray diffraction (XRD) patterns showed that the method was effective to synthesize tetragonal zirconia single-phase. The mean crystallite size attained ranges from 6 to 15 nm. The BET surface areas were relatively high reaching 97 m(2)/g. Studies by nitrogen adsorption/desorption on powders, dilatometry of the compacts, and transmission electron microscopy (TEM) of the powders, were also developed to verify the particles agglomeration state. Both citric acid : ethylene glycol ratio and calcination temperature affected the powder morphology, which influenced the sinterability and microstructure of the sintered material, as showed by scanning electron microscopy (SEM). (C) 2001 Kluwer Academic Publishers.

Attainment of lead titanate - Through the thermal decomposition of coprecipitated 8-hydroxyquinolinate precursors

Crystalline PbTiO3 was obtained through the thermal decomposition of 8-hydroxyquinolinate of lead(II) and that of titanium(IV), which was monitored by TG/DTG/DTA under different atmospheric conditions and with varying heating rates. The compound was prepared from adding 8-hydroxyquinoline solution in the solution of metallic ions Pb(II):Ti(IV) (1:1) Linder constant stirring at 3degreesC, having the pH adjusted to 10. The results of these investigations show that different thermal behavior related to the precursor occurred and also the consequent formation of residues which have different crystallinities. No carbonate residues from the thermal decomposition could be determined by XRD and IR. Only PbTiO3 was observed and confirmed by DSC at 470degreesC, temperature lower than the tetragonal-cubic transition.

Use of impedance spectroscopy in the study of the effect of Cr concentration on the electrical properties of SnO2-based ceramics

This paper reports a study of influence of Cr concentration on the electrical properties and microstructure of SnO2-based powders doped with Mn and Nb, prepared by an organic route (Pechini method). All the samples were compacted into discs and sintered at 1300 degrees C for 3h, resulting in ceramics with relative density varying between 78% and 98%. The powders were characterized by X-ray diffraction analysis. Impedance spectroscopy characterization indicated that the conductivity decreases as Cr concentration increases, probably due to Cr segregation at grain boundaries, which reduces grain size, increasing the number of resistive boundaries.

Structural characterization of organometallic-derived 9.5/65/35 PLZT ceramics

This study consisted of an investigation of the influence of powder preparation on the phase and chemical compositions and microstructure of 9.5/65/35 PLZT materials sintered in an oxygen atmosphere. The powders with the formula Pb0.905La0.095(Zr0.65Ti0.35)(0.976)O-3+3.5 wt.% PbO were prepared by the polymeric organometallic precursor method (the Pechini method and the partial oxalate procedure). Phase composition was determined by X-ray diffraction of powder and EDS analysis, while grain size was determined based on the micrograph obtained from SEM. (C) 2001 Elsevier B.V. B.V. All rights reserved.

The influence of internal surface treatments on tensile bond strength for two ceramic systems

Statement of the Problem: the ceramic composition and surface microstructure of all-ceramic restorations are important components of an effective bonding substrate. Hydrofluoric acid and sandblasting are well-known procedures for surface treatment; however, surface treatment for high alumina-containing and lithium disilicate ceramics have not been fully investigated.Purpose: This in vitro study evaluated the tensile bond strength of resin cement to two types of ceramic systems with different surface treatments.Methods and Materials: Thirty specimens of each ceramic system were made according to the manufacturer's instructions and embedded in polyester resin. Specimens of In-Ceram Alumina [1] and IPS Empress 2 [E] were distributed to three groups with differing surface treatments (n=10): sandblasting with 50 jam aluminum oxide (APA); sandblasting with 110 pm aluminum oxide modified with silica particles (ROCATEC System-RS); a combination of sandblasting with APA and 10% hydrofluoric acid etching (HA) for two minutes on In-Ceram and for 20 seconds for IPS Empress 2. After the respective surface treatments, all the specimens were silanated, and Rely-X resin cement was injected onto the ceramic surface and light polymerized. The specimens were stored in distilled water at 37 degrees C for 24 hours and thermally cycled 1,100 times (5 degrees C/55 degrees C). The tensile bond strength test was performed in a universal testing machine at a 0.5 mm/minute crosshead speed.Results: the mean bond strength values (AWa) for IPS Empress 2 were 12.01 +/- 5.93 (EAPA), 10.34 +/- 1.77 (ERS) and 14.49 +/- 3.04 (EHA). The mean bond strength values for In-Ceram Alumina were 9.87 +/- 2.40 JAPA) and 20.40 +/- 6.27 (IRS). All In-Ceram specimens treated with 10% hydrofluoric acid failed during thermal cycling.Conclusion: the Rocatec system was the most effective surface treatment for In-Ceram Alumina ceramics; whereas, the combination of aluminum oxide sandblasting and hydrofluoric acid etching for 20 seconds worked more effectively for Empress 2 ceramics.

Characterization of bismuth titanate ceramics derived by mechanochemical synthesis

Bismuth titanate, Bi(4)Ti(3)O(12) (BIT) nanosized powders have been successfully synthesized via high energy mechanochemical activation. The phase formation of BIT, crystal structure, microstructure, crystallite size and specific surface area were followed by XRD, scanning electron microscopy (SEM) and the BET specific surface area measurements. The BIT milled 2 h shows the orthorhombic crystalline structure with small amount of amorphous phase. The microstructure of Bi(4)Ti(3)O(12) ceramics sintered at 1000 degrees C for 12h exhibit plate-like grain structure.

Localized mechanics of dentin self-etching adhesive system

The bond strength of composite resins (CRs) to dentin is influenced by the interfacial microstructure of the hybrid layer (HL) and the resin tags (TAG). The contemporary self-etching primer adhesive systems overcame the inconvenient of the etch-and-rinse protocol. Studies, however, have demonstrated that HL thickness and TAG length vary according to the wetting time and additional use of acid-etching prior to self-etching primers. This study investigated the localized stress distribution in the HL and the dentin/adhesive interface. Two HL thicknesses (3 or 6 mu m), two TAG lengths (13 or 17 mu m) and two loading conditions (perpendicular and oblique-25 degrees) were investigated by the finite element (FE) analysis. Five two-dimensional FE models (M) of a dentin specimen restored with CR (38 x 64 mu m) were constructed: M1 - no HL and no TAG; M2 - 3 mu m of HL and 13 mu m of TAG; M3 - 3 mu m of HL and 17 mu m of TAG; M4 - 6 mu m of HL and 13 mu m of TAG; and M5 - 6 mu m of HL and 17 mu m of TAG. Two distributed loadings (L) (20N) were applied on CR surface: L1 - perpendicular, and L2 - oblique (25 degrees). Fixed interfacial conditions were assigned on the border of the dentin specimen. Ansys 10.0 (Ansys (R), Houston, PA, USA) software was used to calculate the stress fields. The peak of von Mises (sigma(vM)) and maximum principal stress (sigma(max)) was higher in L2 than in L1. Microstructures (HL and TAG) had no effect on local stresses for L1. Decreasing HL decreased sigma(vM) and sigma(max) in all structures for L2, but the TAG length had influence only on the peributular dentin. The thickness of HL had more influence on the sigma(vM) and sigma(max) than TAG length. The peritubular dentin and its adjacent structures showed the highest sigma(vM) and sigma(max), mainly in the oblique loading.

THE INFLUENCE OF THE ELECTROCHEMICAL TREATMENT ON CU-AL-AG ALLOYS IN DEAERATED 0.5M NAOH

The effect of consecutive cyclic polarization in de-aerated 0.5 M NaOH solutions on the surface microstructure of mechanically polished Cu-Al-Ag alloys of different compositions and heat treatments has been studied using optical microscopy, SEM and EDS. The current peaks of the cyclic polarization curves do not depend on the alloy composition in the composition range studied. The repetitive potential scans between H2 and O2 evolution in alkaline media lead to preferential dissolution of aluminium, the roughness and phase composition of the surface of the alloys changing significantly. The quasistationary I-E curves of the different Cu-Al-Ag alloys studied consist in the superposition of the quasistationary I-E curves of high-purity Cu and Ag, the EDS microanalysis showing that aluminium is not present on the surface of the alloy in these conditions.

PROCESSING AND CHARACTERIZATION OF LOW-VOLTAGE VARISTORS

ZnO seed particles and Cr2O3 were used in this study to control the microstructure of ZnO varistors. The seed particles were prepared by adding 1.0 mol % BaO to ZnO. The powder was then calcined at 800-degrees-C for 2 h, pressed into pellets and sintered at 1400-degrees-C for 8 h. The sintered ZnO was ground and the BaO eliminated by washing in water. The remaining ZnO powder was classified into a size fraction ranging from 38 to 149 mum. The addition of a small amount (1 weight %) ZnO seed grains produces varistors with low breakdown voltages (7.6 V/mm) and an alpha coefficient of approximately 10. The addition of Cr2O3 stabilizes the spinel phase yielding a more homogeneous microstructure, but degraded electrical behaviour of the ZnO varistor.

Size effect on structure and dielectric properties of Nb-doped barium titanate

It is known that the dielectric properties of BaTiO3 (BT) are strongly dependent on its grain size. Coarse-grained ceramics of pure BT showed lower dielectric constant at room temperature then fine grained. Many authors considered that when the grain size is lower than 700 nm, the lattice of BT changes from tetragonal to pseudocubic, and the dielectric constant value is very low. In the doped BT this effect is more complex, because it is necessary to consider also the influence of dopants. The grain size effect on the structure and dielectric properties of niobium-doped barium titanate was investigated. Niobium-doped barium titanate was prepared from powders obtained by doping of commercial barium titanate and from organometallic complex using citrates as precursors (Pechini procedure). The crystal and microstructure of sintered niobium-doped barium titanate were determined. Dielectric constant and dissipation factor were measured. The observation confirmed that the structure and properties are strongly dependent on grain size. (C) 2003 Elsevier B.V. B.V. All rights reserved.

Secondary phases in Nb-doped BaTiO3 ceramics

In this work, the effect of Nb2O5 addition on the microstructure of BaTiO3 was studied. From XRD diagrams, a diminution in tetragonality parameters with an increase in dopant concentration was observed. In order to determine morphology and composition of secondary phases in niobium-doped barium titanate, EDAX and SEM analyses were carried out. It was found that a concentration of dopant higher than 0.15 mol% leads to fine-grained BaTiO3 without abnormal grain growth. Otherwise, compositions of secondary phases correspond to the titanium-rich region in the BaO-TiO2 phase diagram. Besides, the titanium content in the precipitate increases with the Nb2O5 addition. (C) 2002 Elsevier B.V. Ltd and Techna S.r.l. All rights reserved.